CN109162111A - A kind of processing method of flannelette fur clothing material - Google Patents
A kind of processing method of flannelette fur clothing material Download PDFInfo
- Publication number
- CN109162111A CN109162111A CN201811073323.8A CN201811073323A CN109162111A CN 109162111 A CN109162111 A CN 109162111A CN 201811073323 A CN201811073323 A CN 201811073323A CN 109162111 A CN109162111 A CN 109162111A
- Authority
- CN
- China
- Prior art keywords
- parts
- flannelette
- fur clothing
- aqueous
- processing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing method of flannelette fur clothing material, includes the following steps: after superfine fibre the pre-heat treatment, will directly to apply aqueous back cover material, prefabricated material A is made after dry；The surface prefabricated material A is directly applied into aqueous sheep bar material, prefabricated material B is made after drying and foaming；By prefabricated material B through surface mill skin processing, flannelette fur clothing material is made.The quality exquisiteness of flannelette fur clothing of the invention, good hand touch, wear-resisting property are excellent, and preparation process is easy, at low cost.
Description
Technical field
The present invention relates to garment technology field more particularly to a kind of processing methods of flannelette fur clothing material.
Background technique
Suede, refers to napping leather, also known as Buffed leather, be it is a kind of grain is gently worn into short thin close (such as velvet), though
The leather for its grain pore that still mays be seen indistinctly is dyed, is mostly trampled on and is made through chromium as raw material using ox-hide, quality requirement villus is carefully short
It is close uniform, it is bright and lustrous securely to have mercerising sense.It is soft, plentiful, it is flexible.For making vamp, clothes and sofa artificial leather.
Currently, with the growth of world population, demand multiplication of the mankind to leather, a limited number of natural leathers are already not
It is able to satisfy this demand of people, Synthetic Leather belongs to one kind of polyurethane elastomer, has soft glossy, naturally, feel
Softness, the strong appearance of kishke feel have excellent performance with substrate bonding, are wear-resistant, flex endurant, the excellent mechanical performance such as anti-aging,
It is also equipped with the advantages that cold resistance is good, ventilative, washable, easy to process, price is excellent honest and clean simultaneously, is the ideal of natural leather
Substitute.How to prepare a kind of flannelette fur clothing material based on Synthetic Leather becomes technical problem urgently to be solved.
Summary of the invention
Technical problems based on background technology, the invention proposes a kind of processing method of flannelette fur clothing material, systems
The quality exquisiteness, good hand touch, wear-resisting property for obtaining flannelette fur clothing are excellent, and preparation process of the invention is easy, at low cost.
The processing method that the present invention proposes a kind of flannelette fur clothing material, includes the following steps:
S1, aqueous back cover material after superfine fibre the pre-heat treatment, will be directly applied, prefabricated material A is made after dry；
S2, the surface prefabricated material A is directly applied into aqueous sheep bar material, prefabricated material B is made after drying and foaming；
S3, prefabricated material B is handled through surface mill skin, flannelette fur clothing material is made.
Preferably, aqueous back cover material raw material parts by weights includes: 80-120 parts of Water-based cationic polyurethane resin in S1,
5-10 parts of polyvinyl alcohol, 3-8 parts of nano diatomite, 1.5-3.5 parts of thickener, 0.3-0.6 parts of defoaming agent, levelling agent 0.5-1.5
Part.
Preferably, the coated weight of aqueous back cover material is 80-150g/m in S12。
Preferably, superfine fibre is not figured type superfine fibre in S1.
Preferably, the coated weight 200-300g/m that aqueous sheep bar is expected in S22。
Preferably, aqueous sheep bar material raw material includes: polycarbonate waterborne polyurethane resin 80-120 by weight in S2
Part, 2-8 parts of thin sheep bar powder, 3-10 parts of aqueous color paste, 1-3 parts of thickener, 1-1.5 parts of levelling agent, 0.5-1 parts of defoaming agent.
Preferably, blowing temperature is 130-150 DEG C in S2, foamed time 30-60S.
The present invention is cooperated using superfine fibre back cover, the foaming of aqueous sheep bar material, surface mill skin technique, and flannelette skin is made
Clothing material, wherein use Water-based cationic polyurethane back cover material, one side Water-based cationic polyurethane good film-forming property, with
The binding strength of superfine fibre is high, on the other hand can prevent a large amount of infiltrations of anion-type water-thinned sheep bar material, improve straight coating surface
Equal thin property；Using by polycarbonate waterborne polyurethane resin, thin sheep bar powder, aqueous color paste, thickener, levelling agent, defoaming agent
The aqueous sheep bar of composition expects foaming, and the quality exquisiteness, good hand touch, wear-resisting property that matching surface grinds the obtained flannelette fur clothing of skin technique are excellent
It is different；The present invention is easy using the straight technique preparation process that applies, at low cost.
Specific embodiment
In the following, technical solution of the present invention is described in detail by specific embodiment.
Embodiment 1
A kind of processing method of flannelette fur clothing material, includes the following steps:
It S1, will not be 80g/m by the amount of covering after figured type superfine fibre the pre-heat treatment2Aqueous back cover material is directly applied, is made after dry
Obtain prefabricated material A；
S2, by the amount of covering 200-g/m2The surface prefabricated material A is directly applied into aqueous sheep bar material, is sent out after drying for 130 DEG C of temperature
Prefabricated material B is made after bubble 30S；
S3, prefabricated material B is handled through surface mill skin, flannelette fur clothing material is made.
Aqueous back cover material raw material parts by weights includes: 80 parts of Water-based cationic polyurethane resin, 5 parts of polyvinyl alcohol, is received
3 parts of diatomite, 1.5 parts of thickener, 0.3 part of defoaming agent, 0.5 part of levelling agent of rice.
Aqueous sheep bar material raw material includes: 80 parts of polycarbonate waterborne polyurethane resin by weight, 2 parts of thin sheep bar powder,
3 parts of aqueous color paste, 1 part of thickener, 1 part of levelling agent, 0.5 part of defoaming agent.
Embodiment 2
A kind of processing method of flannelette fur clothing material, includes the following steps:
It S1, will not be 150g/m by the amount of covering after figured type superfine fibre the pre-heat treatment2Aqueous back cover material is directly applied, after dry
Prefabricated material A is made；
S2, by the amount of covering 300g/m2The surface prefabricated material A is directly applied into aqueous sheep bar material, is foamed after drying for 150 DEG C of temperature
Prefabricated material B is made after 60S；
S3, prefabricated material B is handled through surface mill skin, flannelette fur clothing material is made.
Aqueous back cover material raw material parts by weights includes: 120 parts of Water-based cationic polyurethane resin, and 10 parts of polyvinyl alcohol,
8 parts of nano diatomite, 3.5 parts of thickener, 0.6 part of defoaming agent, 1.5 parts of levelling agent.
Aqueous sheep bar material raw material includes: 120 parts of polycarbonate waterborne polyurethane resin by weight, 8 parts of thin sheep bar powder,
10 parts of aqueous color paste, 3 parts of thickener, 1.5 parts of levelling agent, 1 part of defoaming agent.
Embodiment 3
A kind of processing method of flannelette fur clothing material, includes the following steps:
It S1, will not be 120g/m by the amount of covering after figured type superfine fibre the pre-heat treatment2Aqueous back cover material is directly applied, after dry
Prefabricated material A is made；
S2, by the amount of covering 250g/m2The surface prefabricated material A is directly applied into aqueous sheep bar material, is foamed after drying for 140 DEG C of temperature
Prefabricated material B is made after 45S；
S3, prefabricated material B is handled through surface mill skin, flannelette fur clothing material is made.
Aqueous back cover material raw material parts by weights includes: 100 parts of Water-based cationic polyurethane resin, 7 parts of polyvinyl alcohol, is received
5 parts of diatomite, 2.5 parts of thickener, 0.4 part of defoaming agent, 1 part of levelling agent of rice.
Aqueous sheep bar material raw material includes: 100 parts of polycarbonate waterborne polyurethane resin by weight, 5 parts of thin sheep bar powder,
6 parts of aqueous color paste, 2 parts of thickener, 1.2 parts of levelling agent, 0.7 part of defoaming agent.
Embodiment 4
A kind of processing method of flannelette fur clothing material, includes the following steps:
It S1, will not be 140g/m by the amount of covering after figured type superfine fibre the pre-heat treatment2Aqueous back cover material is directly applied, after dry
Prefabricated material A is made；
S2, by the amount of covering 280g/m2The surface prefabricated material A is directly applied into aqueous sheep bar material, is foamed after drying for 145 DEG C of temperature
Prefabricated material B is made after 50S；
S3, prefabricated material B is handled through surface mill skin, flannelette fur clothing material is made.
Aqueous back cover material raw material parts by weights includes: 90 parts of Water-based cationic polyurethane resin, 8 parts of polyvinyl alcohol, is received
6 parts of diatomite, 3 parts of thickener, 0.5 part of defoaming agent, 1.3 parts of levelling agent of rice.
Aqueous sheep bar material raw material includes: 110 parts of polycarbonate waterborne polyurethane resin by weight, 6 parts of thin sheep bar powder,
7 parts of aqueous color paste, 2.5 parts of thickener, 1.3 parts of levelling agent, 0.8 part of defoaming agent.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of processing method of flannelette fur clothing material, which comprises the steps of:
S1, aqueous back cover material after superfine fibre the pre-heat treatment, will be directly applied, prefabricated material A is made after dry；
S2, the surface prefabricated material A is directly applied into aqueous sheep bar material, prefabricated material B is made after drying and foaming；
S3, prefabricated material B is handled through surface mill skin, flannelette fur clothing material is made.
2. the processing method of flannelette fur clothing material according to claim 1, which is characterized in that aqueous back cover material raw material is pressed in S1
Weight point includes: 80-120 parts of Water-based cationic polyurethane resin, 5-10 parts of polyvinyl alcohol, 3-8 parts of nano diatomite, is thickened
1.5-3.5 parts of agent, 0.3-0.6 parts of defoaming agent, 0.5-1.5 parts of levelling agent.
3. the processing method of flannelette fur clothing material according to claim 1, which is characterized in that the coating of aqueous back cover material in S1
Amount is 80-150g/m2。
4. the processing method of flannelette fur clothing material according to claim 1, which is characterized in that superfine fibre is indefinite island in S1
Type superfine fibre.
5. the processing method of flannelette fur clothing material according to claim 1, which is characterized in that the coating of aqueous sheep bar material in S2
Measure 200-300g/m2。
6. the processing method of flannelette fur clothing material according to claim 1, which is characterized in that aqueous sheep bar material raw material is pressed in S2
Parts by weight include: 80-120 parts of polycarbonate waterborne polyurethane resin, 2-8 parts of thin sheep bar powder, and 3-10 parts of aqueous color paste, thickening
1-3 parts of agent, 1-1.5 parts of levelling agent, 0.5-1 parts of defoaming agent.
7. the processing method of flannelette fur clothing material according to claim 1, which is characterized in that blowing temperature is 130- in S2
150 DEG C, foamed time 30-60S.