CN109135122A - A kind of interior decoration PVC modified material and preparation method thereof - Google Patents

A kind of interior decoration PVC modified material and preparation method thereof Download PDF

Info

Publication number
CN109135122A
CN109135122A CN201810944904.8A CN201810944904A CN109135122A CN 109135122 A CN109135122 A CN 109135122A CN 201810944904 A CN201810944904 A CN 201810944904A CN 109135122 A CN109135122 A CN 109135122A
Authority
CN
China
Prior art keywords
parts
powder
interior decoration
modified
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810944904.8A
Other languages
Chinese (zh)
Inventor
刘德烽
梁柳艳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liuzhou Jia Fu Lian Decoration Co Ltd
Original Assignee
Liuzhou Jia Fu Lian Decoration Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liuzhou Jia Fu Lian Decoration Co Ltd filed Critical Liuzhou Jia Fu Lian Decoration Co Ltd
Priority to CN201810944904.8A priority Critical patent/CN109135122A/en
Publication of CN109135122A publication Critical patent/CN109135122A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of interior decoration PVC modified materials, which is characterized in that it is made by the raw material of following weight parts: 130-150 parts of polyvinyl chloride resin, 3-8 parts of wollastonite in powder, 2-6 parts of calcium aluminate, 1-3 parts of epoxyoleic acid butyl ester, 0.5-1.5 parts of acryloyl chloride, 0.4-0.8 parts of potassium dihydrogen phosphate, 1-3 parts of ammonium molybdate, 2-4 parts of calcium zinc stabilizer, 5-10 parts of titanium dioxide, 1.5-2.5 parts of mould inhibitor, 4-6 parts of modified additive.The present invention had not only enhanced the mechanical property and weatherability of material, but also improved the sucting wet air permeability of material, and the interior decoration PVC modified material made has good mechanical performance and moisture absorption humidity, can effectively improve the comfort level of indoor environment, skid resistance is excellent.

Description

A kind of interior decoration PVC modified material and preparation method thereof
Technical field
The present invention relates to PVC modified material technical field more particularly to a kind of interior decoration PVC modified material and its preparations Method.
Background technique
PVC material is one kind of Plastic ornament materials, and it is with Corvic that PVC, which is the abbreviation of pvc material, For primary raw material, suitable age resister, modifying agent etc. is added, the material being prepared through techniques such as mixing, calendering, vacuum formings Material.PVC material have the characteristics that lightweight, it is heat-insulated, heat preservation, it is moisture-proof, fire-retardant and easy for construction.Its specification, color, pattern are various, It is rich in dicoration, can be applied to the decoration of room interior wall and furred ceiling, is the ornament materials being most widely used in plastic materials One of.
Summary of the invention
The object of the invention is to remedy the disadvantages of known techniques, provide a kind of interior decoration PVC modified material and its Preparation method.
The present invention is achieved by the following technical solutions:
A kind of interior decoration PVC modified material is made by the raw material of following weight parts: 130-150 parts of polyvinyl chloride resin, silicon ash 3-8 parts of mountain flour, 2-6 parts of calcium aluminate, 1-3 parts of epoxyoleic acid butyl ester, 0.5-1.5 parts of acryloyl chloride, potassium dihydrogen phosphate 0.4-0.8 Part, 1-3 parts of ammonium molybdate, 2-4 parts of calcium zinc stabilizer, 5-10 parts of titanium dioxide, 1.5-2.5 parts of mould inhibitor, 4-6 parts of modified additive;
The modified additive is made from the following raw materials in parts by weight: 2-4 parts of glyceric acid amide, calgon 0.15-0.55 Part, 0.5-0.85 parts of potassium peroxydisulfate, 1-3 parts of barium stearate, 2.5-3.5 parts of zinc stearate, 1-2 parts of functional poly propylene, silane 0.1-0.3 parts of coupling agent, 80-100 parts of water;Glyceric acid amide, calgon, potassium peroxydisulfate and barium stearate equal proportion are mixed It is scaling loss 3-4 hours lower at 500-600 °C after conjunction, it is then ground to powder, admixes the stearic acid for being equivalent to powder weight 3-5% Zinc and functional poly propylene agitating are uniform, drying, then with surplus stock co-grinding at powder to get.
Further, a kind of preparation method of interior decoration PVC modified material, comprising the following steps:
(1) raw material is weighed by weight, and wollastonite in powder, titanium dioxide, calcium aluminate, epoxyoleic acid butyl ester, acryloyl chloride are first first used into 15- 20% salt acid soak is stood, and is clarified, and centrifugation, solid is washed with water to neutrality, co-ground after mixing after drying with potassium dihydrogen phosphate Then 15-20min is added 60-80 °C of ammonium molybdate, stirring 5-10min, obtains mixed slurry;
(2) by the mixed slurry in polyvinyl chloride resin, modified additive, calcium zinc stabilizer, mould inhibitor and (1) prior to 55-65 °C, stirring Then 10-15min is added remaining raw material in 100-120 °C of continuation high speed and 10-20min is blended, is eventually adding double screw extruder It is granulated in 120-130 °C of melting extrusion, up to interior decoration PVC modified material after cooling.
The invention has the advantages that the present invention had not only enhanced the mechanical property and weatherability of material, but also improve the suction of material Green permeability, the interior decoration PVC modified material made have good mechanical performance and moisture absorption humidity, can effectively change The comfort level of kind indoor environment, skid resistance are excellent.
Specific embodiment
The following examples can make professional and technical personnel that the present invention be more fully understood, but therefore not send out this It is bright to be limited among the embodiment described range.
Embodiment 1
A kind of preparation method of interior decoration PVC modified material, comprising the following steps:
(1) raw material is weighed by weight, first by 6 parts of wollastonite in powder, 8 parts of titanium dioxide, 4 parts of calcium aluminate, 2 parts of epoxyoleic acid butyl ester, third 1.2 parts of alkene acyl chlorides is stood first with 18% salt acid soak, is clarified, centrifugation, and solid is washed with water to neutrality, after drying with biphosphate Then co-ground 18min after 0.6 part of potassium mixing is added 2 parts 70 °C of ammonium molybdate, stirring 8min, obtains mixed slurry;
(2) mixed slurry in 140 parts of polyvinyl chloride resin, 5 parts of modified additive, 3 parts of calcium zinc stabilizer, 2 parts of mould inhibitor and (1) is first In 60 °C, stirring 12min, remaining raw material is then added in 110 °C of continuation high speeds, 15min is blended, be eventually adding twin-screw extrusion Machine is granulated in 125 °C of melting extrusions, up to interior decoration PVC modified material after cooling.
The modified additive is made from the following raw materials in parts by weight: 3 parts of glyceric acid amide, 0.35 part of calgon, 0.65 part of potassium peroxydisulfate, 2 parts of barium stearate, 3 parts of zinc stearate, 1.5 parts of functional poly propylene, 0.2 part of silane coupling agent, water 90 Part;It is small in 550 °C of lower scaling loss 3.5 after glyceric acid amide, calgon, potassium peroxydisulfate are mixed with barium stearate equal proportion When, it is then ground to powder, the zinc stearate for being equivalent to powder weight 4% is admixed and functional poly propylene agitating is uniform, is dried, Again with surplus stock co-grinding at powder to get.
Embodiment 2
A kind of preparation method of interior decoration PVC modified material, comprising the following steps:
(1) raw material is weighed by weight, first by 8 parts of wollastonite in powder, 5 parts of titanium dioxide, 6 parts of calcium aluminate, 1 part of epoxyoleic acid butyl ester, third 1.5 parts of alkene acyl chlorides is stood first with 15% salt acid soak, is clarified, centrifugation, and solid is washed with water to neutrality, after drying with biphosphate Then co-ground 15min after 0.8 part of potassium mixing is added 3 parts 60 °C of ammonium molybdate, stirring 10min, obtains mixed slurry;
(2) by the mixed slurry in 130 parts of polyvinyl chloride resin, 6 parts of modified additive, 2 parts of calcium zinc stabilizer, 2.5 parts of mould inhibitor and (1) Prior to 55 °C, stirring 15min, remaining raw material is then added in 100 °C of continuation high speeds, 20min is blended, be eventually adding twin-screw and squeeze Machine is granulated in 120 °C of melting extrusions out, up to interior decoration PVC modified material after cooling.
The modified additive is made from the following raw materials in parts by weight: 4 parts of glyceric acid amide, 0.15 part of calgon, 0.85 part of potassium peroxydisulfate, 1 part of barium stearate, 3.5 parts of zinc stearate, 1 part of functional poly propylene, 0.3 part of silane coupling agent, water 80 Part;After glyceric acid amide, calgon, potassium peroxydisulfate are mixed with barium stearate equal proportion, 600 °C lower scaling loss 3 hours, It is then ground to powder, the zinc stearate for being equivalent to powder weight 5% is admixed and functional poly propylene agitating is uniform, is dried, then With surplus stock co-grinding at powder to get.
Embodiment 3
A kind of preparation method of interior decoration PVC modified material, comprising the following steps:
(1) raw material is weighed by weight, first by 3 parts of wollastonite in powder, 10 parts of titanium dioxide, 6 parts of calcium aluminate, 1 part of epoxyoleic acid butyl ester, third 0.5 part of alkene acyl chlorides is stood first with 20% salt acid soak, is clarified, centrifugation, and solid is washed with water to neutrality, after drying with biphosphate Then co-ground 20min after 0.4 part of potassium mixing is added 1 part 80 °C of ammonium molybdate, stirring 5min, obtains mixed slurry;
(2) by the mixed slurry in 150 parts of polyvinyl chloride resin, 4 parts of modified additive, 4 parts of calcium zinc stabilizer, 1.5 parts of mould inhibitor and (1) Prior to 65 °C, stirring 10min, remaining raw material is then added in 120 °C of continuation high speeds, 10min is blended, be eventually adding twin-screw and squeeze Machine is granulated in 130 °C of melting extrusions out, up to interior decoration PVC modified material after cooling.
The modified additive is made from the following raw materials in parts by weight: 2 parts of glyceric acid amide, 0.55 part of calgon, 0.5 part of potassium peroxydisulfate, 3 parts of barium stearate, 2.5 parts of zinc stearate, 2 parts of functional poly propylene, 0.1 part of silane coupling agent, water 100 Part;After glyceric acid amide, calgon, potassium peroxydisulfate are mixed with barium stearate equal proportion, 500 °C lower scaling loss 4 hours, It is then ground to powder, the zinc stearate for being equivalent to powder weight 3% is admixed and functional poly propylene agitating is uniform, is dried, then With surplus stock co-grinding at powder to get.

Claims (2)

1. a kind of interior decoration PVC modified material, which is characterized in that it is made by the raw material of following weight parts: polyvinyl chloride resin 130-150 parts, 3-8 parts of wollastonite in powder, 2-6 parts of calcium aluminate, 1-3 parts of epoxyoleic acid butyl ester, 0.5-1.5 parts of acryloyl chloride, phosphoric acid It is 0.4-0.8 parts of potassium dihydrogen, 1-3 parts of ammonium molybdate, 2-4 parts of calcium zinc stabilizer, 5-10 parts of titanium dioxide, 1.5-2.5 parts of mould inhibitor, modified 4-6 parts of auxiliary agent;
The modified additive is made from the following raw materials in parts by weight: 2-4 parts of glyceric acid amide, calgon 0.15-0.55 Part, 0.5-0.85 parts of potassium peroxydisulfate, 1-3 parts of barium stearate, 2.5-3.5 parts of zinc stearate, 1-2 parts of functional poly propylene, silane 0.1-0.3 parts of coupling agent, 80-100 parts of water;Glyceric acid amide, calgon, potassium peroxydisulfate and barium stearate equal proportion are mixed It is scaling loss 3-4 hours lower at 500-600 °C after conjunction, it is then ground to powder, admixes the stearic acid for being equivalent to powder weight 3-5% Zinc and functional poly propylene agitating are uniform, drying, then with surplus stock co-grinding at powder to get.
2. a kind of preparation method of interior decoration PVC modified material according to claim 1, which is characterized in that including with Lower step:
(1) raw material is weighed by weight, and wollastonite in powder, titanium dioxide, calcium aluminate, epoxyoleic acid butyl ester, acryloyl chloride are first first used into 15- 20% salt acid soak is stood, and is clarified, and centrifugation, solid is washed with water to neutrality, co-ground after mixing after drying with potassium dihydrogen phosphate Then 15-20min is added 60-80 °C of ammonium molybdate, stirring 5-10min, obtains mixed slurry;
(2) by the mixed slurry in polyvinyl chloride resin, modified additive, calcium zinc stabilizer, mould inhibitor and (1) prior to 55-65 °C, stirring Then 10-15min is added remaining raw material in 100-120 °C of continuation high speed and 10-20min is blended, is eventually adding double screw extruder It is granulated in 120-130 °C of melting extrusion, up to interior decoration PVC modified material after cooling.
CN201810944904.8A 2018-08-19 2018-08-19 A kind of interior decoration PVC modified material and preparation method thereof Pending CN109135122A (en)