CN109130344A - A kind of composite air-permeable Flocked fabric - Google Patents
A kind of composite air-permeable Flocked fabric Download PDFInfo
- Publication number
- CN109130344A CN109130344A CN201810982089.4A CN201810982089A CN109130344A CN 109130344 A CN109130344 A CN 109130344A CN 201810982089 A CN201810982089 A CN 201810982089A CN 109130344 A CN109130344 A CN 109130344A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- permeable
- cloth
- air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to Flocked fabric technical fields, and disclose a kind of composite air-permeable Flocked fabric, including base fabric, the top of base fabric is equipped with outer cloth, base fabric and outer cloth pass through bonding connection, the bottom of base fabric is equipped with cloth bottom, cloth bottom is made of terylene cotton yarn and polyester fiber, terylene cotton yarn and polyester fiber are using longitude and latitude intertexture as cloth bottom, the bottom at cloth bottom is successively bonded with air-permeable layer from top to bottom, waterproof layer and water absorption layer, air-permeable layer includes yarn and the supporter that is arranged in yarn, supporter is woven together as weft and yarn, air-permeable layer is coated with substrate cloth, the single side of substrate cloth is successively printed with primer coating and face gel coating, waterproof layer is multi-layer thermoplastic polyurethane TPU film pressing composition, every layer of thermoplastic polyurethane TPU film is with a thickness of .mm, pressing uses hot pressing.The composite air-permeable Flocked fabric is able to solve fingerprint identification lock identification and requires excessively high, not convenient enough problem when causing to open.
Description
Technical field
The present invention relates to Flocked fabric technical field, specially a kind of composite air-permeable Flocked fabric.
Background technique
Flocking is to make negative electrical charge on villus band using charge identical charges repel each other the physical characteristic that there is a natural attraction between the sexes, needing flocking
Object be placed under zero potential or grounding requirement, villus by different current potential by the attraction of plant, perpendicular shape acceleration ascend to heaven to
It needs on the body surface of flocking, due to being coated with adhesive by plant, villus is just vertically sticked to by plant, therefore quiet
Electric flocking is a kind of production new technique generated using the natural characteristic of charge.Currently, Flocked fabric is due to the strong, face with three-dimensional sense
Color is bright-coloured, soft touch, luxurious noble, magnificent warmth, lifelike image, non-toxic and tasteless, heat-holding dampproof, non-lint, rub resistance, puts down
Whole zero-clearance etc. a little, is widely used in furniture, craftwork packaging, luggage, shoes industry.Especially on some footwears, flocking
The use of cloth can largely promote product quality.And it is most of at present used on footwear, Flocked fabric is equal
It is dedicated to improving the lint rate and crocking resistance of Flocked fabric, and does not consider gas permeability, therefore use the most of of Flocked fabric
There is also obvious shortcomings on air permeability effect for footwear, and existing Flocked fabric lacks water-proof function.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides a kind of composite air-permeable Flocked fabric, having easily to breathe freely
The advantages that waterproof, solves the problems, such as that existing Flocked fabric air permeability effect is bad and lacks water-proof function.
(2) technical solution
For realize can easily air permeable waterproof purpose, the invention provides the following technical scheme: a kind of composite air-permeable plant
Flannelette, including base fabric, the top of the base fabric are equipped with outer cloth, the base fabric and outer cloth and pass through bonding connection, the bottom of base fabric
Equipped with cloth bottom, the cloth bottom is made of terylene cotton yarn and polyester fiber, and the terylene cotton yarn and polyester fiber are with longitude and latitude intertexture
Cloth bottom, the bottom at the cloth bottom are successively bonded with air-permeable layer, waterproof layer and water absorption layer from top to bottom, and the air-permeable layer includes yarn
With the supporter being arranged in yarn, the supporter is woven together as weft and yarn, the surface packet of the air-permeable layer
It is wrapped with substrate cloth, the single side of the substrate cloth is successively printed with primer coating and face gel coating, and the waterproof layer is Multi-layer thermal
Plastic polyurethane TPU film pressing composition, every layer of thermoplastic polyurethane TPU film use hot pressing with a thickness of .mm, the pressing
It closes, the water absorption layer is the meshed fabric of tool made of hygroscopic fibre warp-knitting, and the top of the outer cloth is from lower past
On be successively stained with waterproof layer and anti oxidation layer, the top of the oxide layer is equipped with flocking layer.
Preferably, rib net is connected between the base fabric and outer cloth jointly, the rib net is by several transverse elasticities
If rib and pole-footing longitudinal elasticity rib form, and transverse elasticity rib and longitudinal elasticity rib in a crisscross manner together with.
Preferably, the yarn of the air-permeable layer is cotton fabric, and the outer surface of the yarn is coated with nano oxidized copper coating, institute
State the ingredient and its weight ratio of primer coating are as follows: 76~80% polyurethane, 0.9~2.2% 5~50um artificial zeolite powder,
16~20% DMF solvent, 1~1.2 plasticizer;The ingredient and its weight ratio of the face gel coating are as follows: 72~76% it is poly-
Urethane, 2.5~3.5% 5~50um artificial zeolite powder, 15~18% DMF solvent, 0.3~1.5% anionic surface are living
Property agent, 0.3~0.8 plasticizer.
Preferably, the waterproof layer is complex as a whole by micro- cellular polyurethane film with pressing mode, and the two of the waterproof layer
Side is coated with water-repellent paint.
Preferably, the anti oxidation layer is woven by ramee, weft with cotton fiber repeated arrangement, described anti-oxidant
The two sides of layer are coated with antioxidant coating.
Preferably, the water-repellent paint includes 30-40 parts of water, 0.8-1.5 parts of hydroxyethyl cellulose, surfactant 0.9-
1.6 parts, 1-1.5 parts of mould inhibitor, 8-18 parts of ammonium hydroxide, 5-15 parts of deionized water, 2-10 parts of environment-friendly plasticizer, polyvinyl alcohol 8-12
Part, 1-2 parts of promotor, 2-6 parts of dispersing agent, 0.6-1.0 parts of defoaming agent, 2-7 parts of pure-acrylic emulsion, 1-3 parts of dispersing agent, defoaming agent 1-
3 parts, 5-12 parts of wetting agent be uniformly mixed be made, the water-repellent paint is uniformly coated on waterproof layer.
Preferably, the antioxidant coating is calculated according to weight fraction once, including the following raw material: alkene cholestanol chemical combination
3-8 parts of object, 7-15 parts of ethoxyquinoline, 5-16 parts of Radix Glycyrrhizae antioxidant, 3-12 parts of tert-butylhydroquinone, basic cellulose 5-
13 parts, 6-18 parts of antioxidant, 15-30 parts of resin, 5-8 parts of formalin, 6-10 parts of calcium chloride, 10-13 parts of calcium carbonate, methyl
6-9 parts of ergot steroid, 5-14 parts of crosslinking agent.
(3) beneficial effect
Compared with prior art, the present invention provides a kind of composite air-permeable Flocked fabric, have it is following the utility model has the advantages that
The composite air-permeable Flocked fabric, by the way that base fabric, outer cloth, cloth bottom, air-permeable layer, waterproof layer, water absorption layer, waterproof layer is arranged
And anti oxidation layer, by the way that Flocked fabric is divided into base fabric, outer cloth, cloth bottom, air-permeable layer, waterproof layer, water absorption layer, waterproof layer and anti-oxidant
Layer many levels and make Flocked fabric in realization air permeability effect so that Flocked fabric achievees the effect that ventilative by waterproof layer
Waterproof effect is obtained simultaneously.
Detailed description of the invention
Fig. 1 is a kind of structural schematic diagram of composite air-permeable Flocked fabric proposed by the present invention;
Fig. 2 is the structural schematic diagram of air-permeable layer in a kind of composite air-permeable Flocked fabric proposed by the present invention;
Fig. 3 is the structural schematic diagram of air-permeable layer and substrate cloth in a kind of composite air-permeable Flocked fabric proposed by the present invention;
Fig. 4 is the structural schematic diagram of rib net in a kind of composite air-permeable Flocked fabric proposed by the present invention.
In figure: 1 base fabric, 2 outer cloth, 3 cloth bottoms, 4 air-permeable layers, 5 waterproof layers, 6 water absorption layers, 7 substrate cloth, 701 primer coatings,
702 face gel coatings, 8 waterproof layers, 9 anti oxidation layers, 10 rib nets, 101 transverse elasticity ribs, 102,11 flocking of longitudinal elasticity rib
Layer.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Fig. 1-4, a kind of composite air-permeable Flocked fabric, including base fabric 1 are please referred to, the top of base fabric 1 is equipped with outer cloth 2, bottom
Cloth 1 and outer cloth 2 are by bonding connection, and the bottom of base fabric 1 is equipped with cloth bottom 3, and cloth bottom 3 is made of terylene cotton yarn and polyester fiber, washs
Using longitude and latitude intertexture as cloth bottom 3, the bottom at cloth bottom 3 is successively bonded with air-permeable layer 4, waterproof layer from top to bottom for synthetic fibre cotton yarn and polyester fiber
5 and water absorption layer 6, air-permeable layer 4 includes yarn 401 and the supporter 402 that is arranged in yarn 401, supporter 402 as weft with
Yarn 401 is woven together, and air-permeable layer 4 is coated with substrate cloth 7, and the single side of substrate cloth 7 is successively printed with primer painting
Layer 701 and face gel coating 702, waterproof layer 5 are multi-layer thermoplastic polyurethane TPU film pressing composition, every layer of thermoplastic polyurethane
For TPU film with a thickness of 0.01mm, pressing uses hot pressing, and water absorption layer 6 is to have net made of hygroscopic fibre warp-knitting
The fabric in hole, the top of outer cloth 2 are successively stained with waterproof layer 8 and anti oxidation layer 9 from the bottom up, and the top of oxide layer 9 is equipped with flocking
Layer 11, by the way that Flocked fabric is divided into base fabric 1, outer cloth 2, cloth bottom 3, air-permeable layer 4, waterproof layer 5, water absorption layer 6, waterproof layer 8 and antioxygen
Change 9 many levels of layer so that Flocked fabric achieve the effect that it is ventilative, and by waterproof layer make Flocked fabric realization air permeability effect
While obtain waterproof effect.
Rib net 10 is connected between base fabric 1 and outer cloth 2 jointly, rib net 10 is by several 101 Hes of transverse elasticity rib
If pole-footing longitudinal elasticity rib 102 forms, and transverse elasticity rib 101 and longitudinal elasticity rib 102 it is criss-cross together with, lead to
Rib net 10 is crossed to separate base fabric 1 and outer cloth 2.
The yarn of air-permeable layer 4 is cotton fabric, and the outer surface of yarn is coated with nano oxidized copper coating, primer coating 701 at
Point and its weight ratio are as follows: 76~80% polyurethane, 0.9~2.2% 5~50um artificial zeolite powder, 16~20% DMF are molten
Agent, 1~1.2 plasticizer;The ingredient and its weight ratio of face gel coating 702 are as follows: 72~76% polyurethane, 2.5~3.5%
5~50um artificial zeolite powder, 15~18% DMF solvent, 0.3~1.5% anionic surfactant, 0.3~0.8 increasing
Agent is moulded, the air permeability effect of air-permeable layer 4 is improved.
Waterproof layer 5 is complex as a whole by micro- cellular polyurethane film with pressing mode, and the two sides of waterproof layer 5 are coated with waterproof painting
Material.
Anti oxidation layer 6 is woven by ramee, weft with cotton fiber repeated arrangement, and the two sides of anti oxidation layer 6 apply
There is antioxidant coating.
Water-repellent paint includes 30-40 parts of water, 0.8-1.5 parts of hydroxyethyl cellulose, 0.9-1.6 parts of surfactant, mould proof
1-1.5 parts of agent, 8-18 parts of ammonium hydroxide, 5-15 parts of deionized water, 2-10 parts of environment-friendly plasticizer, 8-12 parts of polyvinyl alcohol, promotor 1-2
Part, 2-6 parts of dispersing agent, 0.6-1.0 parts of defoaming agent, 2-7 parts of pure-acrylic emulsion, 1-3 parts of dispersing agent, 1-3 parts of defoaming agent, wetting agent 5-
12 parts uniformly mixed obtained, and water-repellent paint is uniformly coated on waterproof layer.
Preferably, antioxidant coating is calculated according to weight fraction once, including the following raw material: alkene cholestanol compound 3-
8 parts, 7-15 parts of ethoxyquinoline, 5-16 parts of Radix Glycyrrhizae antioxidant, 3-12 parts of tert-butylhydroquinone, basic cellulose 5-13
Part, 6-18 parts of antioxidant, 15-30 parts of resin, 5-8 parts of formalin, 6-10 parts of calcium chloride, 10-13 parts of calcium carbonate, methyl wheat
Steroid 6-9 parts of angle, 5-14 parts of crosslinking agent.
In conclusion the composite air-permeable Flocked fabric, by the way that Flocked fabric is divided into base fabric 1, outer cloth 2, cloth bottom 3, air-permeable layer
4, waterproof layer 5,9 many levels of water absorption layer 6, waterproof layer 8 and anti oxidation layer, so that Flocked fabric achievees the effect that ventilative, Er Qietong
Crossing waterproof layer makes Flocked fabric obtain waterproof effect while realizing air permeability effect.
It should be noted that the terms "include", "comprise" or its any other variant are intended to the packet of nonexcludability
Contain, so that the process, method, article or equipment for including a series of elements not only includes those elements, but also including
Other elements that are not explicitly listed, or further include for elements inherent to such a process, method, article, or device.
In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that including the element
Process, method, article or equipment in there is also other identical elements.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of composite air-permeable Flocked fabric, including base fabric (1), it is characterised in that: the top of the base fabric (1) is equipped with outer cloth
(2), the base fabric (1) and outer cloth (2) are by bonding connection, and the bottom of base fabric (1) is equipped with cloth bottom (3), and the cloth bottom (3) is by washing
Synthetic fibre cotton yarn and polyester fiber composition, the terylene cotton yarn and polyester fiber using longitude and latitude intertexture as cloth bottom (3), the cloth bottom (3)
Bottom is successively bonded with air-permeable layer (4), waterproof layer (5) and water absorption layer (6) from top to bottom, and the air-permeable layer (4) includes yarn
(401) and supporter (402) in yarn (401) is set, the supporter (402) is weaved as weft and yarn (401)
Together, the air-permeable layer (4) is coated with substrate cloth (7), and the single side of the substrate cloth (7) is successively printed with primer
Coating (701) and face gel coating (702), the waterproof layer (5) they are that the pressing of multi-layer thermoplastic polyurethane TPU film forms, every layer
For thermoplastic polyurethane TPU film with a thickness of 0.01mm, the pressing uses hot pressing, and the water absorption layer (6) is that moisture absorbing and sweat releasing is fine
The meshed fabric of tool made of warp-knitting is tieed up, the top of the outer cloth (2) is successively stained with waterproof layer (8) from the bottom up and resists
The top of oxide layer (9), the oxide layer (9) is equipped with flocking layer (11).
2. a kind of composite air-permeable Flocked fabric according to claim 1, it is characterised in that: the base fabric (1) and outer cloth (2)
Between be connected with jointly rib net (10), the rib net (10) by several transverse elasticity ribs (101) and if pole-footing it is longitudinal
Elastic bar (102) composition, and transverse elasticity rib (101) and longitudinal elasticity rib (102) are criss-cross together.
3. a kind of composite air-permeable Flocked fabric according to claim 1, it is characterised in that: the yarn of the air-permeable layer (4)
For cotton fabric, the outer surface of the yarn is coated with nano oxidized copper coating, the ingredient and its weight ratio of the primer coating (701)
Are as follows: 76~80% polyurethane, 0.9~2.2% 5~50um artificial zeolite powder, 16~20% DMF solvent, 1~1.2
Plasticizer;The ingredient and its weight ratio of the face gel coating (702) are as follows: 72~76% polyurethane, 2.5~3.5% 5~
50um artificial zeolite powder, 15~18% DMF solvent, 0.3~1.5% anionic surfactant, 0.3~0.8 plasticising
Agent.
4. a kind of composite air-permeable Flocked fabric according to claim 1, it is characterised in that: the waterproof layer (5) is by micro- more
Hole polyurethane film is complex as a whole with pressing mode, and the two sides of the waterproof layer (5) are coated with water-repellent paint.
5. a kind of composite air-permeable Flocked fabric according to claim 1, it is characterised in that: the anti oxidation layer (6) is by ramie
Flaxen fiber, weft are woven with cotton fiber repeated arrangement, and the two sides of the anti oxidation layer (6) are coated with antioxidant coating.
6. a kind of composite air-permeable Flocked fabric according to claim 4, it is characterised in that: the water-repellent paint includes water
30-40 parts, 0.8-1.5 parts of hydroxyethyl cellulose, 0.9-1.6 parts of surfactant, 1-1.5 parts of mould inhibitor, 8-18 parts of ammonium hydroxide, go
5-15 parts of ionized water, 2-10 parts of environment-friendly plasticizer, 8-12 parts of polyvinyl alcohol, 1-2 parts of promotor, 2-6 parts of dispersing agent, defoaming agent
0.6-1.0 parts, 2-7 parts of pure-acrylic emulsion, 1-3 parts of dispersing agent, 1-3 parts of defoaming agent, 5-12 parts of wetting agent be uniformly mixed be made, it is described
Water-repellent paint is uniformly coated on waterproof layer.
7. a kind of composite air-permeable Flocked fabric according to claim 5, it is characterised in that: the antioxidant coating is according to one
Lower weight fraction calculates, including the following raw material: 3-8 parts of alkene cholestanol compound, 7-15 parts of ethoxyquinoline, Radix Glycyrrhizae are anti-oxidant
5-16 parts of agent, 3-12 parts of tert-butylhydroquinone, cellulose 5-13 parts basic, 6-18 parts of antioxidant, 15-30 parts of resin, first
5-8 parts of aldehyde solution, 6-10 parts of calcium chloride, 10-13 parts of calcium carbonate, 6-9 parts of methyl ergot steroid, 5-14 parts of crosslinking agent.