CN109112246A - 一种直接冷弯成型的铁路弹条扣件用钢盘条的生产方法 - Google Patents
一种直接冷弯成型的铁路弹条扣件用钢盘条的生产方法 Download PDFInfo
- Publication number
- CN109112246A CN109112246A CN201710496961.XA CN201710496961A CN109112246A CN 109112246 A CN109112246 A CN 109112246A CN 201710496961 A CN201710496961 A CN 201710496961A CN 109112246 A CN109112246 A CN 109112246A
- Authority
- CN
- China
- Prior art keywords
- temperature
- less
- steel
- wire rod
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种直接冷弯成型的铁路弹条扣件用钢盘条的生产方法。铁水脱硫预处理将硫含量控制在≤0.002%,Ti含量控制在≤0.03%;双渣法转炉炼钢,转炉冶炼终点P≤0.080%,钢水温度1600~1650℃;LF终点钢水硫含量控制在≤0.006%;VD破空后弱吹氩气15分钟以上;连铸钢水过热度小于30℃;拉速0.65~0.71m/s,铸坯在预热段加热温度小于750℃,一加热段温度900~970℃,二加热段温度1060~1100℃,均热段温度1000~1060℃,在炉时间小于110分钟;精轧温度800~890℃,吐丝温度810~860℃,辊道速度0.17~0.40m/s,保温罩全部关闭,风机和下部百叶全部关闭。
Description
技术领域
本发明属于盘条生产技术领域,涉及一种直接冷弯成型的铁路弹条扣件用弹簧钢盘条的生产方法。
背景技术
根据国务院《中长期铁路网规划》,国家将大规模建设高速铁路客运专线,未来客运专线营运里程达到1.2万公里以上。随着高速铁路的建设,对铁路弹条钢的需求也日益加大。
高速铁路扣件在使用时要承受多种形式的应力,易发生变形和破坏,因此要求钢具有较高的纯净度和均匀性,以保证弹条具有高的弹性极限、屈服极限和疲劳寿命,确保火车运行的稳定性和安全。
高速铁路扣件在生产的过程中不经过拉拔直接冷弯成型,因此对盘条原料的组织和性能要求较高。与此同时,为了保证弹条扣件疲劳寿命达到500万次的要求,对盘条原料的表面质量要求也极为苛刻,盘条表面存在裂纹、叠等缺陷均会影响成品弹条的疲劳寿命。
题为“高速铁路弹条用钢在南钢的生产实践”的会议论文(作者为张妍等,2009年高品质特殊钢技术与市场论坛)公开了一种生产铁路弹条扣件的盘条原料生产工艺:100t电炉→100tLF→VD→连铸150mm×150mm方坯→连铸坯抛丸、探伤、修磨→步进梁式加热炉加热→高速线材轧制→斯太尔摩风冷线控冷→检查、检验→包装、入库。该工艺采用电炉冶炼和小方坯一火成材工艺生产。电炉冶炼能源消耗大,而且一火成材的总压缩比小,会影响钢的组织致密,不利于夹杂物的细化,疲劳性能差。
专利CN 102162068A“一种弹簧钢及其制造和热处理方法”、题名为“弹簧钢38Si7的研制与开发”(作者:吴朝兵,孙光涛,2007年中国钢铁年会论文集)、“铁路弹条用水淬弹簧钢38Si7的开发及应用”(作者:翟正龙,李丰功等;《特殊钢》,2001年第22卷第4期)的论文中所公开的弹簧钢盘条的生产工艺也都是采用电炉冶炼,能源消耗大。
发明内容
为了克服现有技术中的不足,本发明提供了一种铁路扣件弹条用弹簧钢盘条的生产方法,通过铁水脱硫预处理、转炉双渣冶炼、LF精炼、VD真空脱气、大方坯连铸、连轧开坯、步进式加热炉加热和高速线材控轧控冷工艺设计,所生产的弹簧钢盘条纯净度高、钢质均匀,盘条组织和力学性能优异,表面质量良好,制成弹条扣件疲劳寿命达1000万次以上。
具体的技术方案是:
本发明中涉及的铁路弹条扣件用钢盘条的生产工艺如下:铁水脱硫预处理→钢水冶炼→LF→VD→连铸→连轧开坯→抛丸、探伤、修磨→加热→轧制→控冷→检查、检验→包装、入库。
每道工序主要的工艺参数如下:
(1)铁水脱硫预处理要求通过铁水脱硫预处理将铁水中的硫含量控制到0.002%以下,铁水中的Ti含量控制在≤0.03%;
(2)采用双渣法转炉炼钢,降低钢液磷含量。转炉冶炼终点要求P≤0.080%,转炉出钢使用低磷锰铁粒、低Al低Ti的专用硅铁、低碳铬铁进行脱氧、合金化;转炉终点钢水温度1600~1650℃;钢包使用无铝的专用罐,避免Al2O3夹杂物生产;
(3)LF精炼采用石灰和铝矾土造高碱度脱硫渣,石灰石加入量6~8kg/t钢,铝钒土加入量1~2kg/t钢,LF终点钢水硫含量控制在0.006%以下;LF精炼过程中不采用Al脱氧,避免Al2O3夹杂物生产;
(4)VD真空脱气,包压15分钟以上用于脱除气体。VD破空后弱吹氩气15分钟以上去除钢水中的夹杂物;
(5)连铸钢水过热度小于30℃;拉速0.65~0.71m/s。采用结晶器电磁搅拌和末端电磁搅拌,搅拌电流400~500A,频率为2~6Hz,控制偏析;
(6)连轧坯表面全修磨,单面修磨深度1~2mm,进而控制成品盘条的表面缺陷;
(7)加热炉:预热段加热温度小于750℃,一加热段温度900~970℃,二加热段温度1060~1100℃,均热段温度1000~1060℃,在炉时间小于110分钟,以控制盘条的表面脱碳;
(8)精轧温度800~890℃,吐丝温度810~860℃,辊道速度0.17~0.40m/s,保温罩全部关闭,风机和下部百叶全部关闭,以控制盘条具有良好的塑性。
有益效果:
本发明采用铁水脱硫预处理、转炉冶炼、大方坯连铸二火成材工艺生产的铁路弹条扣件用钢盘条,钢质纯净度高,K3累积值≤15;钢质成分均匀性好;具有良好的塑性,断后伸长率≥23%、面缩率≥52%;表面质量良好,表面无缺陷、全脱层深度≤0.05mm,总脱碳层深度≤1%D,钢材组织为52%~61%的铁素体+39%~48%的珠光体。制成的铁路弹条扣件疲劳寿命达到1000万次不断裂,远超过疲劳寿命500万次的技术要求。
具体实施方式
以下实施例用于具体说明本发明内容,这些实施例仅为本发明内容的一般描述,并不对本发明内容进行限制。
表1为实施例钢的冶炼工艺,表2为实施例钢的轧制工艺;表3为实施例钢的性能。
表1 实施例钢的冶炼工艺
表2 实施例钢的轧制工艺
表3 实施例钢的性能
由表1~3可见,采用本发明的生产工艺,生产出的可直接冷弯成型的铁路弹条扣件用钢盘条,抗拉强度在700~820MPa,断后伸长率≥23%,断面收缩率≥52%,弹条扣件疲劳寿命达1000万次以上,远超过疲劳寿命500万次的技术要求。
Claims (1)
1.一种直接冷弯成型的铁路弹条扣件用钢盘条的生产方法,钢盘条的生产工艺为:铁水脱硫预处理→钢水冶炼→LF→VD→连铸→连轧开坯→抛丸、探伤、修磨→加热→轧制→控冷→检查、检验→包装、入库,其特征在于,
(1)通过铁水脱硫预处理将铁水中的硫含量控制为≤0.002%,铁水中的Ti含量控制为≤0.03%;
(2)采用双渣法转炉炼钢,转炉冶炼终点要求P≤0.080%,转炉出钢使用低磷锰铁粒、低Al低Ti的专用硅铁、低碳铬铁进行脱氧、合金化;转炉终点钢水温度1600~1650℃;钢包使用无铝的专用罐;
(3)LF精炼采用石灰和铝矾土造高碱度脱硫渣,石灰石加入量为6~8kg/t钢,铝钒土加入量为1~2kg/t钢,LF终点钢水硫含量控制在0.006%以下;LF精炼过程中不采用Al脱氧;
(4)VD真空脱气,包压15分钟以上用于脱除气体,VD破空后弱吹氩气15分钟以上;
(5)连铸钢水过热度小于30℃;拉速0.65~0.71m/s,采用结晶器电磁搅拌和末端电磁搅拌,搅拌电流400~500A,频率为2~6Hz;
(6)连轧坯表面全修磨,单面修磨深度1~2mm;
(7)铸坯在预热段加热温度小于750℃,一加热段温度为900~970℃,二加热段温度为1060~1100℃,均热段温度为1000~1060℃,在炉时间小于110分钟;
(8)精轧温度为800~890℃,吐丝温度为810~860℃,辊道速度为0.17~0.40m/s,保温罩全部关闭,风机和下部百叶全部关闭。