CN109111802A - Metal Roof antirust waterproof mending paste - Google Patents
Metal Roof antirust waterproof mending paste Download PDFInfo
- Publication number
- CN109111802A CN109111802A CN201810645276.3A CN201810645276A CN109111802A CN 109111802 A CN109111802 A CN 109111802A CN 201810645276 A CN201810645276 A CN 201810645276A CN 109111802 A CN109111802 A CN 109111802A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal roof
- mending paste
- lotion
- antirust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of metal Roof antirust waterproof mending paste, the weight proportion range for the constituent for including is as follows: water: 65-70 parts；Waterborne pigment dispersant: 2.0-4.0 parts；Sierozem power: 8-18 parts；Titanium dioxide: 8-18 parts；Trbasic zinc phosphate: 60-90 parts；Aluminium triphosphate: 25-50 parts；Lotion: 450-600 parts；Dicalcium powder: 250-350 parts；Anti- flash rusting auxiliary agent: 5.5-8.5 parts；Defoaming agent: 3.0-5.0 parts；Preservative: 2.0-3.5 parts；Auxiliary rheological agents: 4.0-6.0 parts.The present invention can form the firm protective layer based on ferric phosphate; protective layer densification passivation is not dissolved in water; with good anti-rust action; because lotion has elasticity, flexibility and weatherability well; so as not to because of the resistance to cracking that expands with heat and contract with cold; again because lotion forms fine and close hydrophobic film during doing solid work, there is good waterproof effect.
Description
Technical field
The present invention relates to building material technical fields, particularly relate to a kind of metal Roof antirust waterproof mending paste.
Background technique
Metal Roof by exposing to the weather and drenches with rain at present, and the protective layer meeting glue that roofing can all occur is fallen, and is then corroded
Get rusty, then damaged and leak, the prior art be typically all in the first brush antirust paint in damaged position, after forge iron skin patch, generally
The people of profession is also asked to do, it is time-consuming and laborious.
Summary of the invention
The present invention proposes that a kind of metal Roof antirust waterproof mending paste before it is dried can when the phase because there is anti-flash rusting auxiliary agent
The appearance for preventing rust staining has very strong associative ability with ferric ion, can be formed due to trbasic zinc phosphate and aluminium triphosphate
Firm protective layer based on ferric phosphate, protective layer densification passivation are not dissolved in water, have good anti-rust action, because of lotion
With good elasticity, flexibility and weatherability, so as not to because of the resistance to cracking that expands with heat and contract with cold, and because lotion during doing solid work shape
At fine and close hydrophobic film, there is good waterproof effect.
The technical scheme of the present invention is realized as follows:
A kind of metal Roof antirust waterproof mending paste, the weight proportion range for the constituent for including are as follows:
Water: 65-70 parts；
Waterborne pigment dispersant: 2.0-4.0 parts；
Sierozem power: 8-18 parts；
Titanium dioxide: 8-18 parts；
Trbasic zinc phosphate: 60-90 parts；
Aluminium triphosphate: 25-50 parts；
Lotion: 450-600 parts；
Dicalcium powder: 250-350 parts；
Anti- flash rusting auxiliary agent: 5.5-8.5 parts；
Defoaming agent: 3.0-5.0 parts；
Preservative: 2.0-3.5 parts；
Auxiliary rheological agents: 4.0-6.0 parts.
Preferably, the weight proportion range of the waterborne pigment dispersant is 2.5-3.5 parts.
Preferably, the weight proportion range of the sierozem power is 10-15 parts.
Preferably, the weight proportion range of the titanium dioxide is 10-15 parts.
Preferably, the weight proportion range of the trbasic zinc phosphate is 65-85 parts.
Preferably, the weight proportion range of the aluminium triphosphate is 30-45 parts.
Preferably, the lotion is pure-acrylic emulsion, and weight proportion range is 500-550 parts.
Preferably, the dicalcium powder is 1000 mesh dicalcium powders, and weight proportion range is 280-320 parts.
Preferably, the weight proportion range of the anti-flash rusting auxiliary agent is 6.0-8.0 parts.
The beneficial effects of the present invention are: because there is anti-flash rusting auxiliary agent, the appearance of rust staining can be prevented when the phase before it is dried, by
In trbasic zinc phosphate and aluminium triphosphate, there is very strong associative ability with ferric ion, can be formed based on ferric phosphate
Firm protective layer, protective layer densification passivation be not dissolved in water, have good anti-rust action, because lotion have well elasticity,
Flexibility and weatherability, so as not to because of the resistance to cracking that expands with heat and contract with cold, and because lotion forms fine and close hydrophobic film during doing solid work,
With good waterproof effect.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without creative efforts belongs to the model that the present invention protects
It encloses.
The invention proposes a kind of metal Roof antirust waterproof mending pastes, and the weight proportion range for the constituent for including is such as
Under:
Water: 65-70 parts；
Waterborne pigment dispersant: 2.0-4.0 parts；
Sierozem power: 8-18 parts；
Titanium dioxide: 8-18 parts；
Trbasic zinc phosphate: 60-90 parts；
Aluminium triphosphate: 25-50 parts；
Lotion: 450-600 parts；
Dicalcium powder: 250-350 parts；
Anti- flash rusting auxiliary agent: 5.5-8.5 parts；
Defoaming agent: 3.0-5.0 parts；
Preservative: 2.0-3.5 parts；
Auxiliary rheological agents: 4.0-6.0 parts.
Preferably, the weight proportion range of the waterborne pigment dispersant is 2.5-3.5 parts.
Preferably, the weight proportion range of the sierozem power is 10-15 parts.
Preferably, the weight proportion range of the titanium dioxide is 10-15 parts.
Preferably, the weight proportion range of the trbasic zinc phosphate is 65-85 parts.
Preferably, the weight proportion range of the aluminium triphosphate is 30-45 parts.
Preferably, the lotion is pure-acrylic emulsion, and weight proportion range is 500-550 parts.
Preferably, the dicalcium powder is 1000 mesh dicalcium powders, and weight proportion range is 280-320 parts.
Preferably, the weight proportion range of the anti-flash rusting auxiliary agent is 6.0-8.0 parts.
The present invention can prevent the appearance of rust staining, due to trbasic zinc phosphate and trimerization because there is anti-flash rusting auxiliary agent before it is dried when the phase
Aluminum phosphate has very strong associative ability with ferric ion, can form the firm protective layer based on ferric phosphate, this
Firm protective layer densification passivation based on ferric phosphate is not dissolved in water, has good anti-rust action, because lotion has very
Good elasticity, flexibility and weatherability, so as not to because of the resistance to cracking that expands with heat and contract with cold, and because lotion forms densification during doing solid work
Hydrophobic film, have good waterproof effect.
Antibacterial surface agent is added in the present embodiment, generally uses antimildew and antibacterial agent, antimildew function is provided.
Metal Roof antirust waterproof mending paste in above-mentioned all examples, can be added various mill bases, provide abundant
Color is to meet actual needs.
In another embodiment of the present invention, the proportion of metal Roof antirust waterproof mending paste of the present invention is as follows:
The making step of the present embodiment is as follows:
1, container is added by requirement in water, starts high speed dispersion agent, revolving speed is that dispersing agent is added in 500RPM
2,3-6 are sequentially added, after adding, high speed disperser revolving speed is opened to 1000RPM, high speed dispersion to fineness≤
60um obtains predispersion
3, predispersion is transferred in big container, lotion is added, after adding, starts dispersion machine, revolving speed is adjusted to
500RPM is added coarse whiting, adds rear revolving speed and be adjusted to 700RPM, be dispersed to fineness≤60um
4, dispersing speed is adjusted to 600RPM, sequentially adds 9-12, dispersion 15 minutes can the embodiment of the present invention system
At metal Roof antirust waterproof mending paste reach following performance indicator:
Compared with prior art, the present invention having the following beneficial effects:
1, metal Roof antirust waterproof mending paste of the invention combines antirust and water-proof function organically, does not have to brush antirust
Paint；
2, metal Roof antirust waterproof mending paste of the invention has very strong cementability, not as needing to beat benefit with iron sheet repairing
Nail, it is easy to operate；
3, color paste toning is easily added in metal Roof antirust waterproof mending paste of the invention, keeps color richer, provides
Decorative performance.
Above-mentioned technical proposal discloses improvement of the invention, the technology contents not being disclosed in detail, can be by art technology
Personnel are achieved by the prior art.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (9)
1. a kind of metal Roof antirust waterproof mending paste, it is characterised in that: the weight proportion range for the constituent for including is as follows:
Water: 65-70 parts；
Waterborne pigment dispersant: 2.0-4.0 parts；
Sierozem power: 8-18 parts；
Titanium dioxide: 8-18 parts；
Trbasic zinc phosphate: 60-90 parts；
Aluminium triphosphate: 25-50 parts；
Lotion: 450-600 parts；
Dicalcium powder: 250-350 parts；
Anti- flash rusting auxiliary agent: 5.5-8.5 parts；
Defoaming agent: 3.0-5.0 parts；
Preservative: 2.0-3.5 parts；
Auxiliary rheological agents: 4.0-6.0 parts.
2. metal Roof antirust waterproof mending paste according to claim 1, it is characterised in that: the waterborne pigment dispersant
Weight proportion range be 2.5-3.5 parts.
3. metal Roof antirust waterproof mending paste according to claim 1, it is characterised in that: the weight of the sierozem power is matched
It is 10-15 parts than range.
4. metal Roof antirust waterproof mending paste according to claim 1, it is characterised in that: the weight of the titanium dioxide is matched
It is 10-15 parts than range.
5. metal Roof antirust waterproof mending paste according to claim 1, it is characterised in that: the weight of the trbasic zinc phosphate is matched
It is 65-85 parts than range.
6. metal Roof antirust waterproof mending paste according to claim 1, it is characterised in that: the weight of the aluminium triphosphate
Measuring ratio range is 30-45 parts.
7. metal Roof antirust waterproof mending paste according to claim 1, it is characterised in that: the lotion is pure C cream
Liquid, weight proportion range are 500-550 parts.
8. metal Roof antirust waterproof mending paste according to claim 1, it is characterised in that: the dicalcium powder is 1000 mesh
Dicalcium powder, weight proportion range are 280-320 parts.
9. metal Roof antirust waterproof mending paste according to claim 1, it is characterised in that: the weight of the anti-flash rusting auxiliary agent
Measuring ratio range is 6.0-8.0 parts.