CN109081586A - A kind of sanitary ware glaze and its application in robot glaze spraying - Google Patents
A kind of sanitary ware glaze and its application in robot glaze spraying Download PDFInfo
- Publication number
- CN109081586A CN109081586A CN201811264511.9A CN201811264511A CN109081586A CN 109081586 A CN109081586 A CN 109081586A CN 201811264511 A CN201811264511 A CN 201811264511A CN 109081586 A CN109081586 A CN 109081586A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- sanitary ware
- robot
- spraying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of sanitary ware glaze and its application in robot glaze spraying.The glaze includes 40 ~ 50 parts of kaolin, 15 ~ 20 parts of quartz, 6 ~ 12 parts of spodumene, 10 ~ 18 parts of bentonite, 2 ~ 4 parts of borax, 4 ~ 6 parts of zirconium silicate, 3 ~ 6 parts of perovskite, 7 ~ 12 parts of tourmaline powder, 4 ~ 10 parts of wollastonite.Sanitary ware glaze of the present invention is applied in robot glaze spraying.The characteristics of by the adjustment to ceramic glaze formula in the present invention, so that the ceramic glaze of glaze spraying, granularity is of moderate size, and the stability of glaze is good, is adapted to machine glaze spraying.
Description
Technical field
The invention belongs to pottery field, a kind of specific sanitary ware glaze and its application in robot glaze spraying.
Background technique
Modern enterprise, it is increasing that especially manufacturing cost of labor accounts for cost ratio；One is replaced using robot
The work post for dividing high physical strength, is the target that ceramic industry is generally pursued.Glaze spraying is the poor activity of a working environment, due at cigarette
Misty state glaze has an impact the working environment of direct labor.
However the ceramic glaze of glaze spraying, since the size of its granularity directly affects the quality of glaze layer, but particle is spent
Small and influence stability.
Summary of the invention
The present invention overcomes drawbacks described above, provides a kind of sanitary ware glaze and its application in robot glaze spraying.
Technical solution of the present invention is as follows.
A kind of sanitary ware glaze, including 40 ~ 50 parts of kaolin, 15 ~ 20 parts of quartz, 6 ~ 12 parts of spodumene, bentonite 10 ~ 18
Part, 2 ~ 4 parts of borax, 4 ~ 6 parts of zirconium silicate, 3 ~ 6 parts of perovskite, 7 ~ 12 parts of tourmaline powder, 4 ~ 10 parts of wollastonite.
Preferably, including 45 parts of kaolin, 17 parts of quartz, 9 parts of spodumene, 4 parts of bentonite, 3 parts of borax, zirconium silicate 5
Part, 5 parts of perovskite, 8 parts of tourmaline powder, 7 parts of wollastonite.
A kind of sanitary ware glaze is applied in robot glaze spraying.
Compared with prior art, present invention has an advantage that
By the adjustment to ceramic glaze formula in the present invention, so that the ceramic glaze of glaze spraying, granularity is of moderate size, glaze
Stability it is good, the characteristics of being adapted to machine glaze spraying.
Specific embodiment
Embodiment 1
Take 45 parts of kaolin, 17 parts of quartz, 9 parts of spodumene, 4 parts of bentonite, 3 parts of borax, 5 parts of zirconium silicate, 5 parts of perovskite,
Then plus water 8 parts of tourmaline powder and 7 parts of total 1kg of wollastonite, after above-mentioned raw materials are mixed, are ground, and grinding causes 150 mesh,
1.5kg, stir 0.5h to get.
Embodiment 2
Take 40 parts of kaolin, 15 parts of quartz, 6 parts of spodumene, 10 parts of bentonite, 2 parts of borax, 4 parts of zirconium silicate, 3 parts of perovskite,
Then plus water 7 parts of tourmaline powder, 4 parts of wollastonite add up to 1kg, after above-mentioned raw materials are mixed, are ground, and grinding causes 150 mesh,
1.5kg, stir 0.5h to get.
Embodiment 3
Take 50 parts of kaolin, 20 parts of quartz, 12 parts of spodumene, 18 parts of bentonite, 4 parts of borax, 6 parts of zirconium silicate, perovskite 6
Part, 12 parts of tourmaline powder, 10 parts of wollastonite add up to 1kg, after above-mentioned raw materials are mixed, are ground, and grinding causes 150 mesh, then
Add water 1.5kg, stir 0.5h to get.
1 gained glaze of embodiment is applied in robot glaze spraying, glaze is sprayed in ceramic idiosome, then in 1300
Fired at DEG C 5 hours to get.By test, frit surface finish is good, without apparent concave-convex trace.
Claims (3)
1. a kind of sanitary ware glaze, which is characterized in that including 40 ~ 50 parts of kaolin, 15 ~ 20 parts of quartz, 6 ~ 12 parts of spodumene, swollen
Moisten native 10 ~ 18 parts, 2 ~ 4 parts of borax, 4 ~ 6 parts of zirconium silicate, 3 ~ 6 parts of perovskite, 7 ~ 12 parts of tourmaline powder, 4 ~ 10 parts of wollastonite.
2. to remove the 1 sanitary ware glaze according to right, which is characterized in that including 45 parts of kaolin, 17 parts of quartz, spodumene 9
Part, 4 parts of bentonite, 3 parts of borax, 5 parts of zirconium silicate, 5 parts of perovskite, 8 parts of tourmaline powder, 7 parts of wollastonite.
3. sanitary ware glaze described in claim 1 is applied in robot glaze spraying.