CN109079364A - A kind of band slag system class machinery welding material - Google Patents
A kind of band slag system class machinery welding material Download PDFInfo
- Publication number
- CN109079364A CN109079364A CN201810923953.3A CN201810923953A CN109079364A CN 109079364 A CN109079364 A CN 109079364A CN 201810923953 A CN201810923953 A CN 201810923953A CN 109079364 A CN109079364 A CN 109079364A
- Authority
- CN
- China
- Prior art keywords
- slag system
- system class
- welding material
- band slag
- class machinery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is a kind of band slag system class machinery welding material, include additive and carrier, raw material in formula forms by weight percentage: 0.5~6% silica, 10~35% diatomite, 1~10% diatom miberal powder, 0~3% quartz sand, 0~2.5% ultra micro sodium selenite, 5~20% manganese amino acids, 10~20% viscous fillers, 30~60% nano-titanium dioxides, the product prepared by this method, disposably it can screen and be formed, it is few to be formulated quantity, avoid the link that a large amount of formula adjustings are needed when conventional solder material design, it is high-efficient, period is short, reliable performance, the especially anti-defect ability and mechanical performance of product.
Description
Technical field
The invention discloses a kind of band slag system class machinery welding materials.
Background technique
Band slag system class welding material includes that welding rod, submerged arc flux, electroslag welding solder flux, flux-cored wire, soldering paste etc. produce
Product, constituent generally include mineral, compound, alloy, organic matter, binder, and constituent is several up to ten, each component
It plays important function, the formula features such as gas making, slag making, deoxidation, alloying respectively in the welding process and directly determines welding
The technology stability and weldquality of process are the core technologies of welding material research and manufacture.
Summary of the invention
In view of the above existing problems in the prior art, the present invention provides a kind of band slag system class machinery welding materials, can be with one
Secondary property screening and sizing, formula quantity is few, avoids the link that a large amount of formula adjustings are needed when conventional solder material design, efficiency
Height, the period is short, reliable performance, especially the anti-defect ability and mechanical performance of product.
To achieve the goals above, the invention is realized by the following technical scheme: a kind of band slag system class machinery welding material,
Raw material in formula forms by weight percentage: 0.5~6% silica, 10~35% diatomite, 1~10% diatom mine
Powder, 0~3% quartz sand, 0~2.5% ultra micro sodium selenite, 5~20% manganese amino acids, 10~20% viscous fillers, 30~60% receive
Rice titanium dioxide.
The utility model has the advantages that the product prepared by this method, disposably can screen and be formed, formula quantity is few, avoids
Conventional solder material needs the links of a large amount of formula adjustings when designing, high-efficient, the period is short, reliable performance, especially product
Anti- defect ability and mechanical performance.
Specific embodiment
Embodiment 1
A kind of band slag system class machinery welding material, the raw material in formula forms by weight percentage is respectively: 0.5% silica,
10% diatomite, 1% diatom miberal powder, 1% quartz sand, 1% ultra micro sodium selenite, 5% manganese amino acid, 10% viscous filler, 30% nanometer two
Titanium oxide, performance is lacking at this time.
Embodiment 2
A kind of band slag system class machinery welding material, the raw material in formula forms by weight percentage is respectively: 6% silica,
35% diatomite, 10% diatom miberal powder, 3% quartz sand, 2.5% ultra micro sodium selenite, 20% manganese amino acid, 20% viscous filler, 60% receives
Rice titanium dioxide, efficiency is lower at this time.
Embodiment 3
A kind of band slag system class machinery welding material, the raw material in formula forms by weight percentage is respectively: 4% silica,
23% diatomite, 5% diatom miberal powder, 1.5% quartz sand, 1.25% ultra micro sodium selenite, 13% manganese amino acid, 15% viscous filler,
45% nano-titanium dioxide, high-efficient at this time, the period is short, reliable performance, especially the anti-defect ability and mechanical performance of product.
Claims (4)
1. a kind of band slag system class machinery welding material includes additive and carrier, which is characterized in that the raw material in formula is by weight
Percentage composition is respectively: 0.5~6% silica, 10~35% diatomite, 1~10% diatom miberal powder, 0~3% quartz sand, 0~
2.5% ultra micro sodium selenite, 5~20% manganese amino acids, 10~20% viscous fillers, 30~60% nano-titanium dioxides.
2. band slag system class machinery welding material according to claim 1, which is characterized in that the raw material by weight hundred in formula
Divide is respectively than composition: 0.5% silica, 10% diatomite, 1% diatom miberal powder, 1% quartz sand, 1% ultra micro sodium selenite, 5% ammonia
Base acid manganese, 10% viscous filler, 30% nano-titanium dioxide.
3. band slag system class machinery welding material according to claim 1, which is characterized in that the raw material by weight hundred in formula
Divide is respectively than composition: 6% silica, 35% diatomite, 10% diatom miberal powder, 3% quartz sand, 2.5% ultra micro sodium selenite, 20%
Manganese amino acid, 20% viscous filler, 60% nano-titanium dioxide.
4. band slag system class machinery welding material according to claim 1, which is characterized in that the raw material by weight hundred in formula
Divide is respectively than composition: 4% silica, 23% diatomite, 5% diatom miberal powder, 1.5% quartz sand, 1.25% ultra micro sodium selenite,
13% manganese amino acid, 15% viscous filler, 45% nano-titanium dioxide.