CN109022414A - A kind of bloodstone coupled biological charcoal and the application in removal percolate organic matter - Google Patents
A kind of bloodstone coupled biological charcoal and the application in removal percolate organic matter Download PDFInfo
- Publication number
- CN109022414A CN109022414A CN201811051101.6A CN201811051101A CN109022414A CN 109022414 A CN109022414 A CN 109022414A CN 201811051101 A CN201811051101 A CN 201811051101A CN 109022414 A CN109022414 A CN 109022414A
- Authority
- CN
- China
- Prior art keywords
- bloodstone
- charcoal
- coupled biological
- biological charcoal
- bacteria liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of bloodstone coupled biological charcoal, bloodstone particle is mixed by mechanical mixture or adhesive come coupled biological charcoal, coupling material obtained carries out inoculation membrane formation or natural membrane in alienation Fe (III) reduction mixed bacteria liquid, obtains bloodstone coupled biological charcoal.The invention also discloses the methods for preparing bloodstone coupled biological charcoal.Bloodstone coupled biological charcoal of the invention may be used as the reaction medium of percolate Biochemical processing, improve the removal efficiency of percolate organic matter.
Description
Technical field
The present invention relates to a kind of for handling the bloodstone coupled biological charcoal of landfill leachate.
The invention further relates to the preparation methods of above-mentioned bloodstone coupled biological charcoal.
The invention further relates to above-mentioned bloodstone coupled biological charcoal as biological respinse medium in processing percolate organic matter
Using.
Technical background
In the past ten years, along with the development of the lasting industry and business of many countries all over the world, house refuse
It is being quicklyd increase always with the yield of industrial solid castoff.China's domestic waste annual output is up to 2.0 hundred million tons, and with every
The speed in year 8%-10% increases, and the processing of domestic waste directly injures sustainable development, it has also become China city at present
Most one of pressing problem that Institute of Environmental Health of city faces.The various alternative disposal technologies of municipal solid wastes (are such as filled, burnt
Burning, compost etc.) comparative studies show sanitary landfills method in cost of investment and be relatively inexpensive in terms of the period.Meanwhile it defending
Raw Landfill can reduce the pollution to environment to the maximum extent, decompose rubbish under given conditions, until it is final
It is converted into metastable substance.Therefore, sanitary landfills is the first choice side for handling a large amount of house refuses and industrial solid castoff
Method, this has become global trend.
Landfill leachate is generated after rainwater is mixed by osmosis with solid waste, is that microbial biochemical process generates
The summation of water and solid waste inherently water.The water quality of landfill leachate is considerably complicated, typically contains high-enriched organics (packet
Include biodegradable component and ingredient difficult to degrade), furthermore ammonia nitrogen, heavy metal, inorganic salts are all the important components of percolate.Garbage filter
Liquid not only contaminated soil and earth surface water source, can also pollute underground water.It is existing for the removal of landfill leachate organic matter
Correlation processing technique (COD concentration range is that 2000-62000mg/L, BOD concentration range are 60-45000mg/L) general to adopt more
It is handled with biochemical method, advanced oxidation processes, but due to the biochemical difference of percolate organic matter, leading to treatment effect is not to manage very much very much
Think, and advanced oxidation processes processing cost is relatively high.
In recent years, the degradation that organic pollutant in anaerobic environment is carried out using alienation Fe (III) reduction process, is repaired in biology
Multiple field has certain application prospect.For organic pollutant in landfill leachate, alienation Fe (III) reducing bacteria can
Using organic pollutant as electron donor, Fe (III) is used as electron acceptor, along with having while Fe (III) biological reducing
The mineralising of machine object.For bloodstone as one of Fe (III) ferriferous oxide widely distributed on the earth, scientific circles have bloodstone biology
The correlative study of deoxidization, degradation organic pollutants in water body, and the usual reaction condition of this reaction process is more harsh or is limited to
The problems such as thermodynamic stability height of bloodstone and poor bioavailable property, causes oxidation operation rate whole slower.
Bloodstone biological reducing process removes the organic matter in landfill leachate, the process can by artificial ligand or
Electron shuttle body is strengthened, and this substance rich in quinonyl ingredient of charcoal, can effectively facilitate going back for organic compound
Originality degradation.A large amount of quinonyl and phenolic hydroxyl group functional group ingredient are had been detected by charcoal at present.This unique structure is special
Sign can make charcoal that can serve as electron shuttle body during redox reaction, accelerate Fe (III) reducing bacteria and bloodstone
Between electron transport rate, and then promote organic matter anaerobic oxidation effect effect, reach quickly removal water body organic contamination
The purpose of object.
Summary of the invention
The purpose of the present invention is to provide a kind of for handling the bloodstone coupled biological charcoal of landfill leachate.
Another object of the present invention is to provide a kind of method for preparing above-mentioned bloodstone coupled biological charcoal.
To achieve the above object, bloodstone coupled biological charcoal provided by the invention is to mix bloodstone particle by mechanical
It closes or adhesive mixing carrys out coupled biological charcoal, coupling material obtained is inoculated in alienation Fe (III) reduction mixed bacteria liquid
Biofilm or natural membrane, obtained solid phase particles are bloodstone coupled biological charcoal.
The method provided by the invention for preparing above-mentioned bloodstone coupled biological charcoal:
Bloodstone particle is mixed by mechanical mixture or adhesive come coupled biological charcoal, coupling material obtained is in alienation
It is bloodstone coupled biological that Fe (III), which restores progress inoculation membrane formation or natural membrane, obtained solid phase particles in mixed bacteria liquid,
Charcoal.
In the method, the partial size of bloodstone particle is 2-4mm.
In the method, charcoal is the 400-600 DEG C of anaerobism heating using stalk as raw material, obtained biology before coupling
Charcoal screens out the charcoal that partial size is 0.25-0.5mm.
In the method, the material quality part of described adhesive is matched are as follows:
Water: cornstarch: ferrous sulfate: 30% hydrogen peroxide: 10% sodium hydroxide: borax: 98% sulfuric acid: Lauxite=
200:90-110:1-3:3-5:60-70:1-3:90-110:11-13。
In the method, alienation Fe (III) restore mixed bacteria liquid using Sphingomonas paucimobilis,
Genera Lactococcus、Genera Azospirillum、Geobacillus stearothermophilus、
Pseudomonas spp., Aquabacterium strains and Hydrogenophaga, by concentration ratio 5-7:10-12:4-6:
4-6:6-8:9-11:10-12 is mixed, mixed bacteria liquid Anaerobic culturel in the medium.
In the method, inoculation membrane formation step is:
1) coupling material is soaked in the culture medium containing mixed bacteria liquid and is continually fed into nitrogen;
2) it is separated by solid-liquid separation, gained solid phase is bloodstone coupled biological charcoal.
In the method, natural membrane is that coupling material is soaked in the culture medium containing mixed bacteria liquid, and solid-liquid is mixed
Zoarium system is used as bloodstone coupled biological charcoal.
The present invention improves the activity of alienation Fe (III) reducing bacteria by way of bloodstone coupled biological charcoal, accelerates reaction
Electron transfer capacity in the process.Bloodstone coupled biological charcoal of the invention may be used as the anti-of percolate Biochemical processing
Medium is answered, the removal efficiency of percolate organic matter is improved.
The invention has the advantages that and the utility model has the advantages that
1) bloodstone used in the present invention is cheap;
2) production method of the present invention is simple, is convenient for practical application;
3) present invention is preferable to the treatment effect of percolate organic matter, and COD removal rate is up to 80%.
Detailed description of the invention
It is biochemical removal effect of the biological reaction medium to percolate COD that Fig. 1, which is with bloodstone coupled biological charcoal,.
In figure: ■ indicates bloodstone-charcoal couplings+landfill leachate after biofilm;Indicates the red iron after biofilm
Mine+landfill leachate;△ indicates non-biofilm charcoal+landfill leachate.
Specific embodiment
The biological respinse medium that the present invention is handled using bloodstone coupled biological charcoal as percolate organic matter, passes through bloodstone coupling
The mode for closing charcoal improves the activity of alienation Fe (III) reducing bacteria, accelerates the electron transfer capacity in reaction process.
The technical scheme is that
The bloodstone that partial size is 2-4mm is mixed by mechanical mixture or adhesive come coupled biological charcoal, coupling obtained
Material carries out inoculation membrane formation or natural membrane in alienation Fe (III) reduction mixed bacteria liquid, and treated, and solid phase particles are used to go
Except percolate organic matter.
The preparation step of charcoal before coupling are as follows: use wheat stalk as raw material is prepared, detested at 400-600 DEG C
Oxygen heats 4-6 hours, and the charcoal for obtaining different-grain diameter is sieved using sieve, and the charcoal partial size finally used is
0.25-0.5mm;
Adhesive prepares raw material are as follows:
Water, cornstarch (granularity is 80-100 mesh), ferrous sulfate, hydrogen peroxide (content 30%), sodium hydroxide (content
For 10%), borax, sulfuric acid (98%), Lauxite.The proportion by weight of raw material is water: cornstarch: ferrous sulfate: dioxygen
Water (30%): sodium hydroxide (10%): borax: sulfuric acid (98%): Lauxite=200:90-110:1-3:3-5:60-70:1-
3:90-110:11-13。
The bloodstone coupled biological charcoal reaction medium can be prepared by following two method:
1) prepared by mechanical mixture, i.e., by charcoal and bloodstone 1:1-5:1 in mass ratio, it is small that 1-2 is stirred under blender
When;
2) adhesive is mixed with, and anaerobism Muffle furnace is added in wheat stalk and bloodstone 1:1-5:1 in mass ratio,
Anaerobism is carried out at 400-600 DEG C to heat 4-6 hours;
Described adhesive mixing can be carried out by following steps: 1) by wheat stalk in anaerobism Muffle furnace with 400-600
Anaerobism is carried out at DEG C to heat 4-6 hours.2) amylum adhesive, bloodstone, charcoal 1:10:1-1:10:2 in mass ratio are added
Enter in blender, stirs 1-2 hours;
The mixing iron reduction microbial inoculum uses Sphingomonas paucimobilis, Genera
Lactococcus、Genera Azospirillum、Geobacillus stearothermophilus、Pseudomonas
Spp., Aquabacterium strains and Hydrogenophaga presses concentration ratio 5-7:10-12:4-6:4-6:6-8:9-11:
10-12 is mixed.The mixed microorganism of preparation Anaerobic culturel 10-30 days in the medium;
The inoculation membrane formation method is divided into following steps:
1) bloodstone coupled biological Carbon Materials are soaked in the culture medium for including mixed microorganism and are continually fed into nitrogen
12-24 hours;
2) it is separated by solid-liquid separation, gained solid phase handles reaction medium as percolate Biochemical;
The natural membrane method is that bloodstone coupled biological Carbon Materials are soaked in the culture medium for including mixed microorganism
It comes into full contact with 12-24 hours, then directly handles reaction medium for solid-liquid mixing system as percolate Biochemical.
In one particular embodiment of the present invention:
Use wheat stalk as raw material is prepared, anaerobism is carried out at 400-600 DEG C and is heated 4-6 hours, different grains are obtained
The charcoal of diameter makes.Then it is sieved with sieve, the charcoal partial size finally used is 0.25-0.5mm;
The bloodstone particle for being 2-4mm by partial size is coupled by mechanical mixture or adhesive mixing with charcoal.Institute
The step of stating mechanical mixture are as follows: by charcoal and bloodstone 1:1-5:1 in mass ratio, stirred 1-2 hours under blender;It is described
The step of adhesive mixes are as follows: add amylum adhesive, bloodstone, charcoal 1:10:1-1:10:2 in mass ratio into stirring
In machine, stir 1-2 hours;
Wherein the material quality part ratio of amylum adhesive is water: cornstarch: ferrous sulfate: hydrogen peroxide (30%): hydrogen-oxygen
Change sodium (10%): borax: sulfuric acid (98%): Lauxite=200:100:2:4:65:2:100:12;
The mixing iron reduction microbial inoculum uses Sphingomonas paucimobilis, Genera
Lactococcus、Genera Azospirillum、Geobacillus stearothermophilus、Pseudomonas
Spp., Aquabacterium strains and Hydrogenophaga is mixed by concentration ratio 6:11:5:5:7:10:11.Match
The mixed microorganism of system Anaerobic culturel 10-30 days in the medium;
Inoculation membrane formation method is divided into following steps:
1) bloodstone coupled biological Carbon Materials are soaked in the culture medium for including mixed microorganism and are continually fed into nitrogen
12-24 hours;
2) it is separated by solid-liquid separation, gained solid phase handles reaction medium as percolate Biochemical;
Natural membrane method is to be soaked in bloodstone coupled biological Carbon Materials in the culture medium for include mixed microorganism sufficiently
Contact 12-24 hours then directly handles reaction medium for solid-liquid mixing system as percolate Biochemical.Fig. 1 is shown
It is biochemical removal effect of the biological reaction medium to percolate COD with bloodstone coupled biological charcoal, it can be seen from the figure that this
Invention is preferable to the treatment effect of percolate organic matter, and COD removal rate is up to 80%.
Claims (9)
1. a kind of bloodstone coupled biological charcoal mixes bloodstone particle come coupled biological charcoal by mechanical mixture or adhesive,
Coupling material obtained carries out inoculation membrane formation or natural membrane in alienation Fe (III) reduction mixed bacteria liquid, obtains bloodstone coupling
Close charcoal.
2. the method for preparing bloodstone coupled biological charcoal described in claim 1:
Bloodstone particle is mixed by mechanical mixture or adhesive come coupled biological charcoal, coupling material obtained is in alienation Fe
(III) restoring progress inoculation membrane formation or natural membrane, obtained solid phase particles in mixed bacteria liquid is bloodstone coupled biological charcoal.
3. according to the method described in claim 2, wherein, the partial size of bloodstone particle is 2-4mm.
4. according to the method described in claim 2, wherein, charcoal is using stalk as raw material before coupling, and 400-600 DEG C of anaerobism adds
Heat, obtained charcoal screen out the charcoal that partial size is 0.25-0.5mm.
5. according to the method described in claim 2, wherein, the material quality part proportion of described adhesive is water: cornstarch: sulphur
It is sour ferrous: 30% hydrogen peroxide: 10% sodium hydroxide: borax: 98% sulfuric acid: Lauxite=200:90-110:1-3:3-5:60-
70:1-3:90-110:11-13。
6. according to the method described in claim 2, wherein, alienation Fe (III) restores mixed bacteria liquid and uses Sphingomonas
paucimobilis、Genera Lactococcus、Genera Azospirillum、Geobacillus
Stearothermophilus, Pseudomonas spp., Aquabacterium strains and Hydrogenophaga, are pressed
Concentration ratio 5-7:10-12:4-6:4-6:6-8:9-11:10-12 is mixed, mixed bacteria liquid Anaerobic culturel in the medium.
7. according to the method described in claim 2, wherein, inoculation membrane formation step is:
1) coupling material is soaked in the culture medium containing mixed bacteria liquid and is continually fed into nitrogen;
2) it is separated by solid-liquid separation, gained solid phase is bloodstone coupled biological charcoal.
8. according to the method described in claim 2, wherein, natural membrane is that coupling material is soaked in the culture containing mixed bacteria liquid
In base, using solid-liquid mixing system as bloodstone coupled biological charcoal.
9. application of the iron ore coupled biological charcoal described in claim 1 as percolate Biochemical processing reaction medium.