CN109021749A - A kind of exterior wall latex paint - Google Patents
A kind of exterior wall latex paint Download PDFInfo
- Publication number
- CN109021749A CN109021749A CN201810860796.6A CN201810860796A CN109021749A CN 109021749 A CN109021749 A CN 109021749A CN 201810860796 A CN201810860796 A CN 201810860796A CN 109021749 A CN109021749 A CN 109021749A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- exterior wall
- latex paint
- wall latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of exterior wall latex paints, including following raw material by weight: 150-200 parts of deionized water, 2-4 parts of defoaming agent, 0.5-2 parts of cellulose, 1-3 parts of neutralizer, 4-8 parts of dispersing agent, 1-3 parts of wetting agent, 0.8-1.2 parts of preservative, 8-12 parts of propylene glycol, 50-100 parts of nanometer aging-resistant agent, 150-200 parts of rutile titanium white powder, 40-60 parts of kaolin, 50-80 parts of wollastonite powder, 110-140 parts of dicalcium powder, 10-20 parts of coalescing agent, 250-350 parts of pure-acrylic emulsion, 0.8-1.2 parts of preservative, 1-4 parts of levelling agent, 1-3 parts of thickener.The present invention can significantly improve the stain resistance of exterior wall latex paint, excellent decoration effect.
Description
Technical field
The present invention relates to exterior wall decorating coating technical fields, and in particular to a kind of exterior wall latex paint.
Background technique
The exterior coating of traditional concept is the self-drying type liquid coating of a kind of coating exterior walls of buildings facade, plays beautification dress
Building is adornd, while being played a protective role to the wall of building.It is domestic in the latest 20 years, in the popularization and application side of exterior coating
Method achieves significant progress, and in all kinds of exterior coatings, the water-based exterior wall paint of one pack system is with its easy construction, safety collar
Protect, cost have competitiveness and favored, exterior wall coated surface painting in occupation of 70% higher proportion.But with this
The use of the longer term of class exterior coating, relative to usual outdoor tile for, user to its anti-powdering, it is anti-fade,
It protects the weatherability such as light and stain resistance is not very satisfied.Widely used its weatherability of exterior wall latex paint compares single group on the market at present
Divide the fluorocarbon exterior wall paint weatherability of solvent type exterior wall paint, the polyurethane exterior wall paint of bi-component and bi-component poor, stain resistant is also than double
The fluorocarbon exterior wall paint of component is poor.Therefore, it how on the basis of the unobvious cost of raw material for improving product, farthest mentions
The weatherability and stain resistance for rising such coating become the effective means for promoting the competitiveness of this kind of exterior coating.
Summary of the invention
Technical problem to be solved by the present invention lies in the problems of the weatherability of conventional outer wall emulsion paint and stain resistance difference.
The present invention solves above-mentioned technical problem by the following technical programs:
A kind of exterior wall latex paint, including following raw material by weight:
150-200 parts of deionized water, 2-4 parts of defoaming agent, 0.5-2 parts of cellulose, 1-3 parts of neutralizer, 4-8 parts of dispersing agent,
1-3 parts of wetting agent, 0.8-1.2 parts of preservative, 8-12 parts of propylene glycol, 50-100 parts of nanometer aging-resistant agent, rutile titanium white powder
150-200 parts, 40-60 parts of kaolin, 50-80 parts of wollastonite powder, 110-140 parts of dicalcium powder, 10-20 parts of coalescing agent, pure C cream
250-350 parts of liquid, 0.8-1.2 parts of preservative, 1-4 parts of levelling agent, 1-3 parts of thickener.
Further, the exterior wall latex paint includes following raw material by weight:
180 parts of deionized water, 2.5 parts of defoaming agent, 1 part of cellulose, 2 parts of neutralizer, 6 parts of dispersing agent, 2 parts of wetting agent, prevent
1 part of rotten agent, 10 parts of propylene glycol, 75 parts of nanometer aging-resistant agent, 175 parts of rutile titanium white powder, 50 parts of kaolin, 75 parts of wollastonite powder,
125 parts of dicalcium powder, 15 parts of coalescing agent, 300 parts of pure-acrylic emulsion, 1 part of preservative, 2 parts of levelling agent, 2 parts of thickener.
Further, the neutralizer uses organic amine neuutralizer, and the dispersing agent selects sodium salt dispersing agent, the wetting
Non-ionic wetting agent is selected in agent, and the levelling agent selects polyurethane levelling agent, and the thickener selects association thickener.
Further, the kaolin is the calcined kaolin of 1250 mesh.
Further, the partial size of the dicalcium powder is 800 mesh.
Further, the exterior wall latex paint further includes following raw material by weight: precipitated silica 0.5-2
Part, 0.6-1 parts of nano silica.
Further, the exterior wall latex paint further includes following raw material by weight: 1 part of precipitated silica, being received
0.9 part of silica of rice.
Further, the precipitated silica is passing through dodecyl sodium sulfate modification using preceding.
Further, the partial size of the nano silica is 70-100nm.
Compared with prior art, the present invention have it is following the utility model has the advantages that
The bond strength after brushed between paint film and matrix can be improved in product of the present invention, increases adhesive force, nanometer aging-resistant
Agent has special photovoltaic property, can achieve the effect of shielding ultraviolet rays in coating, improves ageing-resistant and weather resistance,
To effectively extend the service life of paint film coating.Meanwhile by nanometer aging-resistant agent and pure-acrylic emulsion, kaolin, wollastonite powder, again
The components such as calcium powder mix, and in the slit that can add to polymer rapidly during film curing, make the continuity of paint film
It is improved, substantially increases the abrasion resistance and stain resistance of coating.
Dodecyl sodium sulfate is used to be modified processing to precipitated silica as surfactant, it is effective modified
Interface state between silica and polymer improves the hydrophobicity and dispersibility of silica in the polymer, to mention
The surface quality of high paint film.Nano-silicon dioxide particle is added, makes paint layer surface that there is uniform microtexture, can significantly mention
The stain resistance of high exterior wall latex paint, excellent decoration effect.
Specific embodiment
Below with reference to embodiment, the invention will be further described.
Embodiment 1
A kind of exterior wall latex paint, including following raw material by weight:
150 parts of deionized water, 2 parts of defoaming agent, 0.5 part of cellulose, 1 part of neutralizer, 4 parts of dispersing agent, 1 part of wetting agent, prevent
0.8 part of rotten agent, 8 parts of propylene glycol, 50 parts of nanometer aging-resistant agent, 150 parts of rutile titanium white powder, 40 parts of kaolin, 50 parts of wollastonite powder,
110 parts of dicalcium powder, 10 parts of coalescing agent, 250 parts of pure-acrylic emulsion, 0.8 part of preservative, 1 part of levelling agent, 1 part of thickener, precipitating two
0.5 part of silica, 0.6 part of nano silica.
Wherein, the neutralizer uses organic amine neuutralizer, and the dispersing agent selects sodium salt dispersing agent, the wetting agent choosing
With non-ionic wetting agent, the levelling agent selects polyurethane levelling agent, and the thickener selects association thickener.The kaolinite
Soil is the calcined kaolin of 1250 mesh.The partial size of the dicalcium powder is 800 mesh.
The precipitated silica is passing through dodecyl sodium sulfate modification using preceding.The nano silica
Partial size is 70nm.
Embodiment 2
A kind of exterior wall latex paint, including following raw material by weight:
180 parts of deionized water, 2.5 parts of defoaming agent, 1 part of cellulose, 2 parts of neutralizer, 6 parts of dispersing agent, 2 parts of wetting agent, prevent
1 part of rotten agent, 10 parts of propylene glycol, 75 parts of nanometer aging-resistant agent, 175 parts of rutile titanium white powder, 50 parts of kaolin, 75 parts of wollastonite powder,
125 parts of dicalcium powder, 15 parts of coalescing agent, 300 parts of pure-acrylic emulsion, 1 part of preservative, 2 parts of levelling agent, 2 parts of thickener, precipitate dioxy
1 part of SiClx, 0.9 part of nano silica.
Wherein, the neutralizer uses organic amine neuutralizer, and the dispersing agent selects sodium salt dispersing agent, the wetting agent choosing
With non-ionic wetting agent, the levelling agent selects polyurethane levelling agent, and the thickener selects association thickener.The kaolinite
Soil is the calcined kaolin of 1250 mesh.The partial size of the dicalcium powder is 800 mesh.
The precipitated silica is passing through dodecyl sodium sulfate modification using preceding.The nano silica
Partial size is 90nm.
Embodiment 3
A kind of exterior wall latex paint, including following raw material by weight:
200 parts of deionized water, 4 parts of defoaming agent, 2 parts of cellulose, 3 parts of neutralizer, 8 parts of dispersing agent, 3 parts of wetting agent, anti-corrosion
1.2 parts of agent, 12 parts of propylene glycol, 100 parts of nanometer aging-resistant agent, 200 parts of rutile titanium white powder, 60 parts of kaolin, 80 parts of wollastonite powder,
140 parts of dicalcium powder, 20 parts of coalescing agent, 350 parts of pure-acrylic emulsion, 1.2 parts of preservative, 4 parts of levelling agent, 3 parts of thickener, precipitating two
2 parts of silica, 1 part of nano silica.
Wherein, the neutralizer uses organic amine neuutralizer, and the dispersing agent selects sodium salt dispersing agent, the wetting agent choosing
With non-ionic wetting agent, the levelling agent selects polyurethane levelling agent, and the thickener selects association thickener.The kaolinite
Soil is the calcined kaolin of 1250 mesh.The partial size of the dicalcium powder is 800 mesh.
The precipitated silica is passing through dodecyl sodium sulfate modification using preceding.The nano silica
Partial size is 100nm.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although referring to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features.It is all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (9)
1. a kind of exterior wall latex paint, which is characterized in that including following raw material by weight:
150-200 parts of deionized water, 2-4 parts of defoaming agent, 0.5-2 parts of cellulose, 1-3 parts of neutralizer, 4-8 parts of dispersing agent, wetting
1-3 parts of agent, 0.8-1.2 parts of preservative, 8-12 parts of propylene glycol, 50-100 parts of nanometer aging-resistant agent, rutile titanium white powder 150-200
Part, 40-60 parts of kaolin, 50-80 parts of wollastonite powder, 110-140 parts of dicalcium powder, 10-20 parts of coalescing agent, pure-acrylic emulsion 250-
350 parts, 0.8-1.2 parts of preservative, 1-4 parts of levelling agent, 1-3 parts of thickener.
2. a kind of exterior wall latex paint according to claim 1, which is characterized in that including following raw material by weight:
180 parts of deionized water, 2.5 parts of defoaming agent, 1 part of cellulose, 2 parts of neutralizer, 6 parts of dispersing agent, 2 parts of wetting agent, preservative 1
Part, 10 parts of propylene glycol, 75 parts of nanometer aging-resistant agent, 175 parts of rutile titanium white powder, 50 parts of kaolin, 75 parts of wollastonite powder, dicalcium powder
125 parts, 15 parts of coalescing agent, 300 parts of pure-acrylic emulsion, 1 part of preservative, 2 parts of levelling agent, 2 parts of thickener.
3. a kind of exterior wall latex paint according to claim 1, which is characterized in that the neutralizer is neutralized using organic amine
Agent, the dispersing agent select sodium salt dispersing agent, and the wetting agent selects non-ionic wetting agent, and the levelling agent selects polyurethane stream
Flat agent, the thickener select association thickener.
4. a kind of exterior wall latex paint according to claim 1, which is characterized in that the kaolin is that the calcining of 1250 mesh is high
Ridge soil.
5. a kind of exterior wall latex paint according to claim 1, which is characterized in that the partial size of the dicalcium powder is 800 mesh.
6. a kind of exterior wall latex paint according to claim 1, which is characterized in that further include following original by weight
Material: 0.5-2 parts of precipitated silica, 0.6-1 parts of nano silica.
7. a kind of exterior wall latex paint according to claim 6, which is characterized in that further include following original by weight
Material: 1 part of precipitated silica, 0.9 part of nano silica.
8. a kind of exterior wall latex paint according to claim 6, which is characterized in that the precipitated silica is using preceding warp
Cross dodecyl sodium sulfate modification.
9. a kind of exterior wall latex paint according to claim 6, which is characterized in that the partial size of the nano silica is
70-100nm。