CN109020359A - 一种耐久预拌砂浆 - Google Patents
一种耐久预拌砂浆 Download PDFInfo
- Publication number
- CN109020359A CN109020359A CN201710432045.XA CN201710432045A CN109020359A CN 109020359 A CN109020359 A CN 109020359A CN 201710432045 A CN201710432045 A CN 201710432045A CN 109020359 A CN109020359 A CN 109020359A
- Authority
- CN
- China
- Prior art keywords
- parts
- durable
- premixing mortar
- cement
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种新的耐久预拌砂浆，包括以下重量百分比的组分：水泥30～35份、中细砂60～99份、纤维素醚类高分子聚合物0.05～0.3份、工程纤维0.3～3.0份、木质纤维4‑9份、PP纤维5‑9份、石膏33‑36份、乳胶粉4‑8份、亚硝酸钙3‑9份、电解锰渣35～55份、粉煤灰0～35份、氧化钙6～33份、聚丙烯纤维0.5～3.5份、纤维素醚0.5～3.5份、膨胀剂0.3～4.0份和减水剂0.3～3.0份。该耐久预拌砂浆制备方法简单、成本低、质量好、防水性好、耐久性佳。
Description
技术领域
本发明涉及一种耐久预拌砂浆，还涉及该耐久预拌砂浆的制备方法。
背景技术
耐久预拌砂浆是指由专业化厂家生产的，用于建设工程中的各种砂浆拌合物，是我国近年发展起来的一种新型建筑材料，按性能可分为普通耐久预拌砂浆和特种砂浆。普通砂浆主要包括砌筑砂浆、抹灰砂浆、地面砂浆。砌筑砂浆、抹灰砂浆主要用于承重墙、非承重墙中各种混凝土砖、粉煤灰砖和粘土砖的砌筑和抹灰，地面砂浆用于普通及特殊场合的地面找平。特种砂浆包括保温砂浆、装饰砂浆、自流平砂浆、防水砂浆等，其用途也多种多样，广泛用于建筑外墙保温、室内装饰修补等。
随着建筑业技术进步和文明施工要求的提高，现场拌制砂浆日益显示出其固有的缺陷，如砂浆质量不稳定、材料浪费大、砂浆品种单一、文明施工程度低以及污染环境等。因此，采用工业化生产的耐久预拌砂浆势在必行，它是保证建筑工程质量、提高建筑施工现代化水平、实现资源综合利用、减少城市污染、改善大气环境、发展散装水泥、实现可持续发展的一项实在措施。
30世纪五十年代初，欧洲国家就开始大量生产，使用耐久预拌砂浆，至今已有50多年的发展历史。国内上海，常州等发达地区发展较快。同时，许多城市也在逐步禁止现场搅拌砂浆，推广使用耐久预拌砂浆。优势有健康环保、质量稳定、节能舒适等。
然而，目前使用的耐久预拌砂浆的强度和施工性能不足，仅只能满足现场施工要求；并且自身会干燥收缩，出现开裂、防水性能差、耐久性差等问题。
发明内容
发明目的：为了解决现有耐久预拌砂浆自身干燥收缩、防水性能差、耐久性差的缺陷，本发明提供了一种新的耐久预拌砂浆及其制备方法。
技术方案：为了解决上述技术问题，本发明提供了一种耐久预拌砂浆，包括以下重量百分比的组分：水泥30～35份、中细砂60～99份、纤维素醚类高分子聚合物0.05～0.3份、工程纤维0.3～3.0份、木质纤维4-9份、PP纤维5-9份、石膏33-36份、乳胶粉4-8份、亚硝酸钙3-9份、电解锰渣35～55份、粉煤灰0～35份、氧化钙6～33份、聚丙烯纤维0.5～3.5份、纤维素醚0.5～3.5份、膨胀剂0.3～4.0份和减水剂0.3～3.0份。
作为本发明耐久预拌砂浆的一种优选，所述水泥为硅酸盐水泥、普通硅酸盐水泥、矿渣硅酸盐水泥、粉煤灰硅酸盐水泥或复合硅酸盐水泥；以保证该耐久预拌砂浆的强度性能。
作为本发明耐久预拌砂浆的另一种优选，所述中细砂的细度模数为3.6-3.9；从而使耐久预拌砂浆均匀，以保证该耐久预拌砂浆的强度性能。
作为本发明耐久预拌砂浆的另一种优选，所述纤维素醚类高分子聚合物为甲基纤维素醚和羟丙基甲基纤维素醚中的一种或两种。
作为本发明耐久预拌砂浆的另一种优选，所述工程纤维为聚丙烯纤维和玻璃纤维中的一种或两种。
作为本发明耐久预拌砂浆的另一种优选，所述膨胀剂为UEA膨胀剂、氧化钙膨胀剂、铁屑膨胀剂和明矾石膨胀剂中的任一种或几种的混合物。
作为本发明耐久预拌砂浆的另一种优选，所述减水剂为萘系粉剂减水剂、脂肪族粉剂减水剂和聚羧酸粉剂减水剂中的任一种或几种的混合物。
有益效果：本发明提供的耐久预拌砂浆制备方法简单、成本低、质量好、防水性好、耐久性佳。
具体实施方式
耐久预拌砂浆，包括以下重量百分比的组分：水泥30～35份、中细砂60～99份、纤维素醚类高分子聚合物0.05～0.3份、工程纤维0.3～3.0份、木质纤维4-9份、PP纤维5-9份、石膏33-36份、乳胶粉4-8份、亚硝酸钙3-9份、电解锰渣35～55份、粉煤灰0～35份、氧化钙6～33份、聚丙烯纤维0.5～3.5份、纤维素醚0.5～3.5份、膨胀剂0.3～4.0份和减水剂0.3～3.0份。
所述水泥为硅酸盐水泥、普通硅酸盐水泥、矿渣硅酸盐水泥、粉煤灰硅酸盐水泥或复合硅酸盐水泥；以保证该耐久预拌砂浆的强度性能。
所述中细砂的细度模数为3.6-3.9；从而使耐久预拌砂浆均匀，以保证该耐久预拌砂浆的强度性能。
所述纤维素醚类高分子聚合物为甲基纤维素醚和羟丙基甲基纤维素醚中的一种或两种。
所述工程纤维为聚丙烯纤维和玻璃纤维中的一种或两种。
作为本发明耐久预拌砂浆的另一种优选，所述膨胀剂为UEA膨胀剂、氧化钙膨胀剂、铁屑膨胀剂和明矾石膨胀剂中的任一种或几种的混合物。
作为本发明耐久预拌砂浆的另一种优选，所述减水剂为萘系粉剂减水剂、脂肪族粉剂减水剂和聚羧酸粉剂减水剂中的任一种或几种的混合物。
Claims (7)
1.一种耐久预拌砂浆，其特征在于：包括以下重量百分比的组分：水泥30～35份、中细砂60～99份、纤维素醚类高分子聚合物0.05～0.3份、工程纤维0.3～3.0份、木质纤维4-9份、PP纤维5-9份、石膏33-36份、乳胶粉4-8份、亚硝酸钙3-9份、电解锰渣35～55份、粉煤灰0～35份、氧化钙6～33份、聚丙烯纤维0.5～3.5份、纤维素醚0.5～3.5份、膨胀剂0.3～4.0份和减水剂0.3～3.0份。
2.根据权利要求1所述的一种耐久预拌砂浆，其特征在于：所述水泥为硅酸盐水泥、普通硅酸盐水泥、矿渣硅酸盐水泥、粉煤灰硅酸盐水泥或复合硅酸盐水泥。
3.根据权利要求1所述的一种耐久预拌砂浆，其特征在于：所述中细砂的细度模数为3.6-3.9。
4.根据权利要求1所述的一种耐久预拌砂浆，其特征在于：所述纤维素醚类高分子聚合物为甲基纤维素醚和羟丙基甲基纤维素醚中的一种或两种。
5.根据权利要求1所述的一种耐久预拌砂浆，其特征在于：所述工程纤维为聚丙烯纤维和玻璃纤维中的一种或两种。
6.根据权利要求1所述的一种耐久预拌砂浆，其特征在于：所述膨胀剂为UEA膨胀剂、氧化钙膨胀剂、铁屑膨胀剂和明矾石膨胀剂中的任一种或几种的混合物。
7.根据权利要求1所述的一种耐久预拌砂浆，其特征在于：所述减水剂为萘系粉剂减水剂、脂肪族粉剂减水剂和聚羧酸粉剂减水剂中的任一种或几种的混合物。