CN109013517A - A kind of dust removal method of LED projector lamp plastic shell - Google Patents
A kind of dust removal method of LED projector lamp plastic shell Download PDFInfo
- Publication number
- CN109013517A CN109013517A CN201810947864.2A CN201810947864A CN109013517A CN 109013517 A CN109013517 A CN 109013517A CN 201810947864 A CN201810947864 A CN 201810947864A CN 109013517 A CN109013517 A CN 109013517A
- Authority
- CN
- China
- Prior art keywords
- shell
- parts
- minutes
- vibrating motor
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of dust removal method of LED projector lamp plastic shell is related to Projecting Lamp processing technical field, it is characterised in that: including following operating procedure, is impregnated, is rinsed, is blowed, impregnated again, dried again, impregnate, dried up for the third time.The method of the present invention is reasonable, easy to implement, cleaning is convenient, timeliness is long.
Description
Technical field
The present invention relates to Projecting Lamps to process technical field, and in particular to a kind of dedusting of LED projector lamp plastic shell
Method.
Background technique
LED projector lamp LEDFlood Light also known as LED spotlight, LED projection lamp.LED projector lamp passes through built-in micro- core
The control of piece, existing two classes product, one kind uses power-type chip portfolio, another kind of to use single high-power chip, Qian Zhexing
Can be more stable, single high-power product structure is huge, and small-scale light projector is suitble to irradiate, and the latter can achieve very high power,
It can carry out remote large area light projector.
LED projector lamp makes the lamps and lanterns of the projecting environment of illumination on specified face to be illuminated, also known as spotlight.In general, its energy
Any direction is enough aimed at, and has the structure that climate condition does not influence.It is mainly used for large area operation field mine, building wheel
Exterior feature, stadium, viaduct, monument, park and flower bed etc..Therefore, the large area lighting lamps and lanterns of nearly all outdoor application are all
Projecting Lamp can be regarded as.
The shell of LED projector lamp has dust, impurity etc. during processing, often due to cleaning causes not in time
Grey serious, just unusual trouble when packaging in this way is fallen, and may require that and re-start cleaning, and when dust accretions
Between it is long do not allow easy to clean yet, the holding timeliness of present most of cleanings is not grown, all only a couple of days, if being stacked
Cleaning repeatedly is needed, is very wasted time and manpower.
Summary of the invention
Technical problem to be solved by the present invention lies in overcome existing technological deficiency provide a kind of method rationally, embodiment party
Just, a kind of dust removal method for LED projector lamp plastic shell that cleaning is convenient, timeliness is long.
The following technical solution is employed for the technical problems to be solved by the invention to realize:
A kind of dust removal method of LED projector lamp plastic shell, it is characterised in that: including following operating procedure,
Step 1: being impregnated: shell being placed in the slot equipped with cleaning solution, is fixed with vibrating motor outside slot, shell is put
It sets 19-24 minutes, placement while opens vibrating motor;
Step 2: being rinsed: the shell after placement is carried out surface punching with the mist or column spray gun that clear water is housed
It washes, rinses 15-20 minutes;
Step 3: being blowed: the shell after flushing being carried out to the water on hot blast drying surface with air-heater, with fibre after drying
Wei Bu is wiped one time;
Step 4: impregnating again: shell being put into the sink for filling clear water, vibrating motor, and shell are fixed with outside slot
It places 19-24 minutes, placement while opens vibrating motor;
Step 5: drying again: shell being taken out from water, then carries out the water on hot blast drying surface;
Step 6: third time is impregnated: shell being put into another slot, cleaning solution is filled in slot, shell places 25-30 points
Clock, placement while, open vibrating motor;
Step 7: being dried up: then naturally dry after shell is taken out continues to blow 20-25 minutes, blow with air-heater
Shell is wiped with clean non-woven fabrics immediately;
The cleaning solution includes that the material of following parts by weight is made,
It is cetyl betaine part, 3 parts of polyethylene glycol, 1 part of lauroylamidopropyl betaine, 1 part of Dodecyl Polyglucosides, secondary
1 part of sodium chlorate, 4 parts of cocamidopropyl propyl amide amine oxide, 1 part of melissa oil, 6 parts of replenishers, 37 parts of deionized water;
Preparation method are as follows: above-mentioned material is put into agitator, and keeps barrel temperature constant at 75-80 DEG C, is then stirred
Mix mixing 60-65 minutes;
The replenishers include that the material of following parts by weight is made,
1 part of monkshood, 2 parts of fevervine, 3 parts of rose, 4 parts of lophatherum gracile, 5 parts of waxgourd peel, 6 parts of malt, 24 parts of clear water;
Preparation method: above-mentioned material is put into casserole, 3-3.5 hour of infusion with high heat, then slag and decoction point
From, slag is smashed to pieces, be then placed in by the liquid separation in slag and liquids recovery in centrifuge, then by the liquid of recycling and decoction after
Continuous mixing 2.5-3 hour of infusion.
The invention has the benefit that dust, the impurity on surface etc. can be removed by shaking to impregnate, and glue etc. is not easy
Processing can be removed easily with sticking attachment, then rinse just more cleaning by clear water, and drying is also energy
Enough play the role of clean, and the cleaning effect of hot wind is more good, and multiple immersion, flushing, drying can be repeatedly
It cleans, and third time impregnates and dries later, dries and can form a substance similar to protective film, Neng Gouyou in case surface
The isolation dust of effect, and dust will not be adsorbed, it can effectively keep clean, and the cleaning solution used does not stimulate and makees without pair yet
With the replenishers used are the products after concentration, and the effect of entire cleaning solution is very good.The method of the present invention rationally, embodiment party
Just, cleaning is convenient, timeliness is long.
Specific embodiment
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below into
One step illustrates the present invention.
Embodiment 1
A kind of dust removal method of LED projector lamp plastic shell, it is characterised in that: including following operating procedure,
Step 1: being impregnated: shell being placed in the slot equipped with cleaning solution, is fixed with vibrating motor outside slot, shell is put
It sets 19-24 minutes, placement while opens vibrating motor;
Step 2: being rinsed: the shell after placement is carried out surface punching with the mist or column spray gun that clear water is housed
It washes, rinses 15-20 minutes;
Step 3: being blowed: the shell after flushing being carried out to the water on hot blast drying surface with air-heater, with fibre after drying
Wei Bu is wiped one time;
Step 4: impregnating again: shell being put into the sink for filling clear water, vibrating motor, and shell are fixed with outside slot
It places 19-24 minutes, placement while opens vibrating motor;
Step 5: drying again: shell being taken out from water, then carries out the water on hot blast drying surface;
Step 6: third time is impregnated: shell being put into another slot, cleaning solution is filled in slot, shell places 25-30 points
Clock, placement while, open vibrating motor;
Step 7: being dried up: then naturally dry after shell is taken out continues to blow 20-25 minutes, blow with air-heater
Shell is wiped with clean non-woven fabrics immediately;
The cleaning solution includes that the material of following parts by weight is made,
It is cetyl betaine part, 3 parts of polyethylene glycol, 1 part of lauroylamidopropyl betaine, 1 part of Dodecyl Polyglucosides, secondary
1 part of sodium chlorate, 4 parts of cocamidopropyl propyl amide amine oxide, 1 part of melissa oil, 6 parts of replenishers, 37 parts of deionized water;
Preparation method are as follows: above-mentioned material is put into agitator, and keeps barrel temperature constant at 75-80 DEG C, is then stirred
Mix mixing 60-65 minutes;
The replenishers include that the material of following parts by weight is made,
1 part of monkshood, 2 parts of fevervine, 3 parts of rose, 4 parts of lophatherum gracile, 5 parts of waxgourd peel, 6 parts of malt, 24 parts of clear water;
Preparation method: above-mentioned material is put into casserole, 3-3.5 hour of infusion with high heat, then slag and decoction point
From, slag is smashed to pieces, be then placed in by the liquid separation in slag and liquids recovery in centrifuge, then by the liquid of recycling and decoction after
Continuous mixing 2.5-3 hour of infusion.
Embodiment 2
A kind of dust removal method of LED projector lamp plastic shell, it is characterised in that: including following operating procedure,
Step 1: being rinsed: shell being carried out surface washing with the mist or column spray gun that clear water is housed, is rinsed
15-20 minutes;
Step 2: being blowed: the shell after flushing being carried out to the water on hot blast drying surface with air-heater, with fibre after drying
Wei Bu is wiped one time;
Step 3: impregnating: shell being put into the sink for filling clear water, vibrating motor is fixed with outside slot, and shell is placed
19-24 minutes, placement while, opened vibrating motor;
Step 4: drying again: shell being taken out from water, then carries out the water on hot blast drying surface;
Step 5: impregnating again: shell being put into another slot, cleaning solution is filled in slot, shell places 25-30 points
Clock, placement while, open vibrating motor;
Step 6: being dried up: then naturally dry after shell is taken out continues to blow 20-25 minutes, blow with air-heater
Shell is wiped with clean non-woven fabrics immediately;
The cleaning solution includes that the material of following parts by weight is made,
It is cetyl betaine part, 3 parts of polyethylene glycol, 1 part of lauroylamidopropyl betaine, 1 part of Dodecyl Polyglucosides, secondary
1 part of sodium chlorate, 4 parts of cocamidopropyl propyl amide amine oxide, 1 part of melissa oil, 6 parts of replenishers, 37 parts of deionized water;
Preparation method are as follows: above-mentioned material is put into agitator, and keeps barrel temperature constant at 75-80 DEG C, is then stirred
Mix mixing 60-65 minutes;
The replenishers include that the material of following parts by weight is made,
1 part of monkshood, 2 parts of fevervine, 3 parts of rose, 4 parts of lophatherum gracile, 5 parts of waxgourd peel, 6 parts of malt, 24 parts of clear water;
Preparation method: above-mentioned material is put into casserole, 3-3.5 hour of infusion with high heat, then slag and decoction point
From, slag is smashed to pieces, be then placed in by the liquid separation in slag and liquids recovery in centrifuge, then by the liquid of recycling and decoction after
Continuous mixing 2.5-3 hour of infusion.
Embodiment 3
A kind of dust removal method of LED projector lamp plastic shell, it is characterised in that: including following operating procedure,
Step 1: being impregnated: shell being placed in the slot equipped with cleaning solution, is fixed with vibrating motor outside slot, shell is put
It sets 19-24 minutes, placement while opens vibrating motor;
Step 2: being rinsed: the shell after placement is carried out surface punching with the mist or column spray gun that clear water is housed
It washes, rinses 15-20 minutes;
Step 3: being blowed: the shell after flushing being carried out to the water on hot blast drying surface with air-heater, with fibre after drying
Wei Bu is wiped one time;
Step 4: impregnating again: shell being put into the sink for filling clear water, vibrating motor, and shell are fixed with outside slot
It places 19-24 minutes, placement while opens vibrating motor;
Step 5: drying again: shell being taken out from water, the water on hot blast drying surface is then carried out, has blown and used immediately
Clean non-woven fabrics wipes shell;
The cleaning solution includes that the material of following parts by weight is made,
It is cetyl betaine part, 3 parts of polyethylene glycol, 1 part of lauroylamidopropyl betaine, 1 part of Dodecyl Polyglucosides, secondary
1 part of sodium chlorate, 4 parts of cocamidopropyl propyl amide amine oxide, 1 part of melissa oil, 6 parts of replenishers, 37 parts of deionized water;
Preparation method are as follows: above-mentioned material is put into agitator, and keeps barrel temperature constant at 75-80 DEG C, is then stirred
Mix mixing 60-65 minutes;
The replenishers include that the material of following parts by weight is made,
1 part of monkshood, 2 parts of fevervine, 3 parts of rose, 4 parts of lophatherum gracile, 5 parts of waxgourd peel, 6 parts of malt, 24 parts of clear water;
Preparation method: above-mentioned material is put into casserole, 3-3.5 hour of infusion with high heat, then slag and decoction point
From, slag is smashed to pieces, be then placed in by the liquid separation in slag and liquids recovery in centrifuge, then by the liquid of recycling and decoction after
Continuous mixing 2.5-3 hour of infusion.
Through overtesting, measures 1-3 of the embodiment of the present invention and comparative example and the clean lamp of progress of the embodiment of the present invention is not used
Shell carries out test data comparison, is as follows:
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (2)
1. a kind of dust removal method of LED projector lamp plastic shell, it is characterised in that: including following operating procedure,
Step 1: being impregnated: shell being placed in the slot equipped with cleaning solution, vibrating motor is fixed with outside slot, shell places 19-
24 minutes, placement while, opened vibrating motor;
Step 2: being rinsed: the shell after placement being carried out surface washing with the mist or column spray gun that clear water is housed, is rushed
It washes 15-20 minutes;
Step 3: being blowed: the shell after flushing being carried out to the water on hot blast drying surface with air-heater, uses fiber cloth after drying
Wiping one time;
Step 4: impregnating again: shell being put into the sink for filling clear water, vibrating motor is fixed with outside slot, and shell is placed
19-24 minutes, placement while, opened vibrating motor;
Step 5: drying again: shell being taken out from water, then carries out the water on hot blast drying surface;
Step 6: third time is impregnated: shell is put into another slot, cleaning solution is filled in slot, shell is placed 25-30 minutes,
Vibrating motor is opened while placement;
Step 7: being dried up: then naturally dry after shell is taken out continues to blow 20-25 minutes, blow immediately with air-heater
Shell is wiped with clean non-woven fabrics.
2. a kind of dust removal method of LED projector lamp plastic shell according to claim 1, it is characterised in that: the cleaning
Liquid includes that the material of following parts by weight is made,
Cetyl betaine part, 3 parts of polyethylene glycol, 1 part of lauroylamidopropyl betaine, 1 part of Dodecyl Polyglucosides, hypochlorous acid
1 part of sodium, 4 parts of cocamidopropyl propyl amide amine oxide, 1 part of melissa oil, 6 parts of replenishers, 37 parts of deionized water.