CN108997605A - A kind of composite conducting foaming agent and preparation method thereof - Google Patents
A kind of composite conducting foaming agent and preparation method thereof Download PDFInfo
- Publication number
- CN108997605A CN108997605A CN201811030188.9A CN201811030188A CN108997605A CN 108997605 A CN108997605 A CN 108997605A CN 201811030188 A CN201811030188 A CN 201811030188A CN 108997605 A CN108997605 A CN 108997605A
- Authority
- CN
- China
- Prior art keywords
- foaming agent
- parts
- carbon black
- shape
- composite conducting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This application provides a kind of composite conducting foaming agent materials and preparation method thereof, wherein the foaming agent material includes: shape-memory polymer, foaming agent, conductive filler and crosslinking agent;The shape-memory polymer includes: isocyanates and polyether polyol;The conductive filler includes: that acetylene carbon black and Te Migao lead carbon black;It is 45-55 parts that each component is respectively as follows: the shape-memory polymer in parts by weight;The foaming agent is 3-5 parts;The acetylene carbon black is 33-37 parts;It is 38-42 parts that the Te Migao, which leads carbon black,;The crosslinking agent is 0.8-1.2 parts.After composite conducting foaming agent material filling metal material, it can effectively solve the problem that existing metallic ground pole weight is big, corrosion resistance is poor, and the problem that service life is short.
Description
Technical field
This application involves conductive coating preparation fields more particularly to a kind of composite conducting foaming agent and preparation method thereof.
Background technique
In order to solve to build the accident smashed by thunder and lightning, usually draw thunder dress on building top and internal installing lightning rod etc.
It sets, so that dangerous thunder and lightning is introduced underground by thunder carrying-off device, prevents thunder and lightning from directly contacting building, or hoard and cause under construction
Dangerous hidden danger.Thunder carrying-off device introduce underground part be earthing pole, earthing pole refer to the metallic conductor directly contacted with soil or
Conductor group is widely used in lightning protection and transmission system.No matter in lightning protection or in transmission system, earthing pole is made
For one end of electric current conduction, needs to remain excellent electric conductivity, can effectively transmit thunder and lightning, play the role of drawing thunder.
In the prior art, in order to which guarantee earthing pole draws thunder effect, bulk metal component is generallyd use as earthing pole, but
It is the weight that can greatly increase earthing pole in this way, increases the cost of transport and maintenance, and anti-corrosive properties are poor, service life is shorter.For
The practicability for improving earthing pole, is usually made as metal shell or metal framework for integral ground pole metal component, utilizes
Other conductive materials are filled, and other lightweight non-metallic materials, such as coke blacking etc. is generally mostly used to be filled.
But in practical applications, due to the interference by extraneous factor, there will necessarily be gap between coke powder particles,
Conductive and corrosion resistance is caused to be greatly reduced;And coke blacking is coated in the effect of metal outer and persistence is all difficult to ensure,
And coke blacking is also difficult to transport and make, overall weight is still bigger after filling, and the substances such as coke blacking are once scattered, and is also easy
Pollute surrounding soil.
Summary of the invention
This application provides a kind of composite conducting foaming agents and preparation method thereof, utilize composite conducting foaming agent material
After filling metal material, it can effectively solve the problem that existing metallic ground pole weight is big, corrosion resistance is poor, and the problem that service life is short.
The application first aspect provides a kind of composite conducting foaming agent material, and the foaming agent material includes: shape note
Recall polymer, foaming agent, conductive filler and crosslinking agent;
The shape-memory polymer includes: isocyanates and polyether polyol;
The conductive filler includes: that acetylene carbon black and Te Migao lead carbon black;
Each component is respectively as follows: in parts by weight
The shape-memory polymer is 45-55 parts;
The foaming agent is 3-5 parts;
The acetylene carbon black is 33-37 parts;
It is 38-42 parts that the Te Migao, which leads carbon black,;
The crosslinking agent is 0.8-1.2 parts.
With reference to first aspect, the first in first aspect can be in realization mode, and the isocyanates is different using toluene two
Cyanate or benzhydryl methane diisocyanate.
With reference to first aspect, in second of achievable mode of first aspect, the polyether polyol uses polyoxygenated
Propylene glycol or polypropylene oxide triol.
With reference to first aspect, the third in first aspect can be in realization mode, and the foaming agent uses two formyl of azo
Amine foaming agent.
With reference to first aspect, in the 4th kind of achievable mode of first aspect, the crosslinking agent is different using peroxidating two
Propyl benzene.
The application second aspect provides a kind of preparation method of composite conducting foaming agent material, the preparation method packet
It includes:
S100, shape-memory polymer and conductive filler are dried, obtain dry isocyanates, polyether polyols
Alcohol, acetylene carbon black and Te Migao lead carbon black;
S200, the isocyanates of the drying and the conductive black of the drying are stirred in organic solvent, mixes 10-
After 15 minutes, the first mixture is obtained;
S300, it the Te Migao of the pure and mild drying of the polyether polyols of the drying is led into carbon black stirs in organic solvent,
After mixing 10-15 minutes, the second mixture is obtained;
S400, first mixture and second mixture are stirred in cross-linking agent solution, and hybrid reaction 20-
After 30 minutes, third mixture is obtained;
S500, foaming agent is slowly added to the third mixture, and stirred at low speed 10-20 minutes, obtain composite conducting
Foam agent material.
By the above technology it is found that this application provides a kind of composite conducting foaming agent materials and preparation method thereof, wherein institute
Stating foaming agent material includes: shape-memory polymer, foaming agent, conductive filler and crosslinking agent;The shape-memory polymer packet
It includes: isocyanates and polyether polyol;The conductive filler includes: that acetylene carbon black and Te Migao lead carbon black;Each component is by weight
It is 45-55 parts that number, which is respectively as follows: the shape-memory polymer,;The foaming agent is 3-5 parts;The acetylene carbon black is 33-37
Part;It is 38-42 parts that the Te Migao, which leads carbon black,;The crosslinking agent is 0.8-1.2 parts.In use, using high molecular material as base
Body is added conductive filler as conductive materials in matrix, conductive composite polymer material is formed, specifically, due to containing
There is shape-memory polymer, therefore, foaming agent material can constitute various shape easily, to meet the external knot for needing to fill
Structure;Foaming agent can enable foaming agent material form porous structure;Conductive filler can enable foaming agent material have excellent conduction
Property, therefore, it can enable the foaming filled metal structure of agent material that still there is good electric conductivity;Crosslinking agent can enable foaming
Each ingredient in agent material uniformly combines.Composite conducting foaming agent density of material provided herein is small, light weight, has well
Absorption shock loading ability, corrosion resistance is excellent, heat-resist, conductivity is high and pollution-free to soil.Changing significantly
While kind earthing pole overall weight, reduction and maintenance cost, electric conductivity is effectively ensured.
Detailed description of the invention
In order to illustrate more clearly of the technical solution of the application, letter will be made to attached drawing needed in the embodiment below
Singly introduce, it should be apparent that, for those of ordinary skills, without any creative labor,
It is also possible to obtain other drawings based on these drawings.
Fig. 1 is a kind of flow chart of the preparation method of composite conducting foaming agent material provided by the present application.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Whole description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
For a long time, high molecular material is very popular by its excellent performance, but people always return high molecular material
For insulating materials, until the doping type polyacetylene (Poly acetylene, PA) that Hideki Shirakawas in 1977 and Mac are studied can
This traditional idea is just broken after electric conductivity to reach bismuth metal, then, the new term for academia occur is " conductive high
Molecular material ", meanwhile, its discovery and development creates a novel cross discipline --- conductive polymer subdomains.Later
People have found that polyaniline, polyphenylene sulfide, polypyrrole, polythiophene etc. also have similar metallic conductivity in succession again, although leading
The research and development of electric high molecular material start to walk compared with Dinner, but it has lighter weight, the available simple and easy methods such as casting, molding of peeping form, are easy to
Synthesis and carry out Molecular Design, raw material sources than it is wide the advantages that so that in recent years, conductive ion molecule receives generation
The favor of the large quantities of researchers in various countries of boundary, also achieves significant progress.
Conductive polymer material generally can be divided into structural type and compound two class.Structural conductive macromolecular material, such as
Polyethylene, although having the conductivity close to copper, since its environmental stability problem is not resolved always, application foundation
The Comparision for studying aspect is weak, later in order to overcome environmental stability poor, and the polypyrrole, polythiophene, poly- occurred in succession
Aniline and its derivative have become the principal item of conducting polymer.The nineties, part-structure type conductive polymer material is
Into practical stage, but in view of the shortcomings that its own and its material is limited by factors, structural conductive macromolecular material
The market occupied is still very limited.In contrast, conductive polymeric composite is then quickly grown, and is widely used in medicine
Engineering, electromagnetic shielding material, absorbing material, photoelectric material, anti-static material, anti-corrosion of metal material, gas sensitive, electrochromism
The exploitation and application of the materials such as material.Compound-type conducting material is that a certain number of lead is added using high molecular polymer as matrix
The material that isoelectric substance is made up of different combination process has the processability of high molecular material and the electric conductivity of metal concurrently.With
Metal phase ratio, compound-type conducting material has good processability, simple process, corrosion-resistant, resistivity adjustable extent is big, price is low etc.
Advantage.
The phenomenon that carbon black/PE composite material shows ptc characteristics is Frydman1945 first discovery, but until
1966, Kohler was mixed with LDPE with carbon black, and after obtaining obviously PTC effect, this phenomenon just causes widely to close
Note, and put into the research and development to this material.Conductive foaming agent is and pure as one of carbon black/PE composite material
Polymers Phase ratio, it has many valuable performances.Such as, density is small, specific strength is high, has the ability, heat-insulated for absorbing impact load
Property is good, sound insulation capabilities are strong.And in foaming process, the special cellular structure of foamed material can be to nanofiller mechanism of action
It is relocated, to control in foaming material charge level and conductivity therethrough, and then instructs its application range.Therefore,
Conductive foaming composite material may be applied to the numerous areas such as automobile or electronic product as novel substitute products at present.
Although normal metal material conducts electricity very well, but quality is excessive, if biggish conductive member all uses
Metal material is made, then will cause various difficulties such as transport, maintenance, installation and disassembly, therefore, it is necessary to use a germplasm
Light and conductive substance partially to replace metal material.
Embodiment one
This application provides a kind of composite conducting foaming agent material, the foaming agent material includes:
Shape-memory polymer, foaming agent, conductive filler and crosslinking agent;
The shape-memory polymer includes: isocyanates and polyether polyol;
The conductive filler includes: that acetylene carbon black and Te Migao lead carbon black;
Each component is respectively as follows: in parts by weight
The shape-memory polymer is 45-55 parts;
The foaming agent is 3-5 parts;
The acetylene carbon black is 33-37 parts;
It is 38-42 parts that the Te Migao, which leads carbon black,;
The crosslinking agent is 0.8-1.2 parts.
Composite conducting foaming agent material provided in this embodiment substantially belongs to conductive polymer material, by macromolecule material
Material is used as matrix, is added conductive filler as conductive materials in matrix, forms conductive composite polymer material, specifically
Ground, due to containing shape-memory polymer, foaming agent material can constitute various shape easily, need to fill out to meet
The external structure filled;Foaming agent can enable foaming agent material form porous structure;Conductive filler can enable foaming agent material have
Therefore excellent electric conductivity can enable the foaming filled metal structure of agent material still have good electric conductivity;Crosslinking agent
Each ingredient in foaming agent material can be enabled uniformly to combine.Composite conducting foaming agent density of material provided herein is small, matter
Amount is light, has that the good ability for absorbing shock loading, corrosion resistance are excellent, heat-resist, conductivity is high and to soil without dirt
Dye.While substantially improving earthing pole overall weight, reduction and maintenance cost, electric conductivity is effectively ensured.
Embodiment two
The embodiment of the present application provides a kind of composite conducting foaming agent material, comprising: 45 parts of shape-memory polymers;3 parts
Foaming agent;33 parts of acetylene carbon blacks;38 parts of Te Migao lead carbon black;0.8 part of crosslinking agent.
Embodiment three
The embodiment of the present application provides a kind of composite conducting foaming agent material, comprising: 55 parts of shape-memory polymers;5 parts
Foaming agent;37 parts of acetylene carbon blacks;42 parts of Te Migao lead carbon black;1.2 parts of crosslinking agents.
Example IV
The embodiment of the present application provides a kind of composite conducting foaming agent material, comprising: 50 parts of shape-memory polymers;4 parts
Foaming agent;35 parts of acetylene carbon blacks;40 parts of Te Migao lead carbon black;1 part of crosslinking agent.
Embodiment five
The embodiment of the present application provides a kind of composite conducting foaming agent material, and toluene diisocyanate can be selected in the isocyanates
One of acid esters and benzhydryl methane diisocyanate.
Embodiment six
The embodiment of the present application provides a kind of composite conducting foaming agent material, and polyoxygenated third can be selected in the polyether polyol
One of enediol and polypropylene oxide triol.
Embodiment seven
The embodiment of the present application provides a kind of composite conducting foaming agent material, and the foaming agent is sent out using azodicarbonamide
Infusion.
In order to improve bubbling efficiency, chemical foaming agent is generally selected, the application mainly selects azo (AC) foaming agent, excellent
Select azodicarbonamide foaming agent.AC foaming agent gas forming amount is big, superior performance and widely used, adaptable.The present embodiment is adopted
Foaming agent performance is stable, nonflammable, pollution-free, will not impact to soil, and under normal pressure or pressurized conditions
It can foam, and uniform in foaming, pore-forming is tiny, and structure is ideal.
Embodiment eight
This application provides a kind of composite conducting foaming agent material, the crosslinking agent uses cumyl peroxide.
The application uses DPC crosslinking agent, and the substance after crosslinking can be improved hot property, mechanical performance and have very high modulus
With heat distortion temperature, heat resistance can be effectively improved, resistance to room temperature shrinkage also can be improved, and can be improved proof stress cracking
Property, the transparency and tensile strength.
Embodiment nine
Referring to Fig. 1, a kind of flow chart of the preparation method of composite conducting foaming agent material.
Present embodiments provide a kind of preparation method of composite conducting foaming agent material, which is characterized in that the preparation side
Method includes:
S100, shape-memory polymer and conductive filler are dried, obtain dry isocyanates, polyether polyols
Alcohol, acetylene carbon black and Te Migao lead carbon black;
Making material is dried, the influence to material purity and subsequent reactions such as moisture can be effectively avoided.
S200, the isocyanates of the drying and the conductive black of the drying are stirred in organic solvent, mixes 10-
After 15 minutes, the first mixture is obtained;
S300, it the Te Migao of the pure and mild drying of the polyether polyols of the drying is led into carbon black stirs in organic solvent,
After mixing 10-15 minutes, the second mixture is obtained;
S400, first mixture and second mixture are stirred in cross-linking agent solution, and hybrid reaction 20-
After 30 minutes, third mixture is obtained;
S500, foaming agent is slowly added to the third mixture, and stirred at low speed 10-20 minutes, obtain composite conducting
Foam agent material.
In order to generate uncontrollable bubbles volume to prevent the too fast addition of foaming agent, enables pore-forming undesirable, need to control foaming agent
It is slowly added to, and stirs at low speed, to prevent impacting to the structure of matter, or introduce other gaseous impurities.
Construction when, by composite conducting foaming agent material after evenly mixing, after it sufficiently solidifies, carry out using.
Composite conducting foaming agent material provided by the present application and preparation method thereof, can obtain the composite conducting of function admirable
Foam agent material, and density is small, light weight, has that the good ability for absorbing shock loading, corrosion resistance be excellent, heat resistance
Well, conductivity is high and pollution-free to soil.While substantially improving earthing pole overall weight, reduction and maintenance cost, effectively
Guarantee electric conductivity.
Those skilled in the art after considering the specification and implementing the invention disclosed here, will readily occur to of the invention its
Its embodiment.This application is intended to cover any variations, uses, or adaptations of the invention, these modifications, purposes or
Person's adaptive change follows general principle of the invention and including the undocumented common knowledge in the art of the present invention
Or conventional techniques.The description and examples are only to be considered as illustrative, and true scope and spirit of the invention are by following
Claim is pointed out.
It should be understood that the application is not limited to the precise structure that has been described above and shown in the drawings, and
And various modifications and changes may be made without departing from the scope thereof.Scope of the present application is only limited by the accompanying claims.
Claims (6)
- The agent material 1. a kind of composite conducting foams, which is characterized in that the foaming agent material includes: shape-memory polymer, hair Infusion, conductive filler and crosslinking agent;The shape-memory polymer includes: isocyanates and polyether polyol;The conductive filler includes: that acetylene carbon black and Te Migao lead carbon black;Each component is respectively as follows: in parts by weightThe shape-memory polymer is 45-55 parts;The foaming agent is 3-5 parts;The acetylene carbon black is 33-37 parts;It is 38-42 parts that the Te Migao, which leads carbon black,;The crosslinking agent is 0.8-1.2 parts.
- 2. foaming agent material according to claim 1, which is characterized in thatThe isocyanates uses toluene di-isocyanate(TDI) or benzhydryl methane diisocyanate.
- 3. foaming agent material according to claim 1, which is characterized in thatThe polyether polyol uses polyoxypropyleneglycol or polypropylene oxide triol.
- 4. foaming agent material according to claim 1, which is characterized in thatThe foaming agent uses azodicarbonamide foaming agent.
- 5. foaming agent material according to claim 1, which is characterized in thatThe crosslinking agent uses cumyl peroxide.
- 6. a kind of preparation method of composite conducting foaming agent material, which is characterized in that the preparation method includes:S100, shape-memory polymer and conductive filler are dried, obtain dry isocyanates, polyether polyol, Acetylene carbon black and Te Migao lead carbon black;S200, the isocyanates of the drying and the conductive black of the drying are stirred in organic solvent, 10-15 points of mixing Zhong Hou obtains the first mixture;S300, it the Te Migao of the pure and mild drying of the polyether polyols of the drying is led into carbon black stirs in organic solvent, mix After 10-15 minutes, the second mixture is obtained;S400, first mixture and second mixture are stirred in cross-linking agent solution, and hybrid reaction 20-30 points Zhong Hou obtains third mixture;S500, foaming agent is slowly added to the third mixture, and stirred at low speed 10-20 minutes, obtain composite conducting foaming Agent material.