CN108976521A - A kind of anti-oxidant predispersed masterbatch - Google Patents
A kind of anti-oxidant predispersed masterbatch Download PDFInfo
- Publication number
- CN108976521A CN108976521A CN201810699567.0A CN201810699567A CN108976521A CN 108976521 A CN108976521 A CN 108976521A CN 201810699567 A CN201810699567 A CN 201810699567A CN 108976521 A CN108976521 A CN 108976521A
- Authority
- CN
- China
- Prior art keywords
- antioxidant
- oxidant
- predispersed masterbatch
- liquid
- predispersed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of anti-oxidant predispersed masterbatch, which is mixed by epoxy glue 5% ~ 30%, dispersing agent 0.01% ~ 8%, liquid antioxidant 10% ~ 80%, processing aid 20% ~ 70%.Contain liquid antioxidant in component of the present invention, conducive to the dispersibility of antioxidant, and avoids powder antioxidant bring dust harzard, it is easy to operate.The present invention solves the disadvantage that poor compatibility between antioxidant dispersion uneven, dust pollution and each material, and the anti-oxidant predispersed masterbatch antioxygenic property of production is good, good dispersion, processability are excellent.
Description
Technical field
Present invention design belongs to technical field of polymer materials, and in particular to a kind of anti-oxidant predispersed masterbatch.
Background technique
Rubber and its product are being processed, and in storage and use process, rubber is caused due to the comprehensive function by internal and external factor
Glue physicochemical properties and mechanical performance gradually degenerate, until last lose use value, in order to restrain or delay aging
Journey, it is necessary to antioxidant (anti-aging agent) be added.
Existing addition manner is all that directly antioxidant is added in rubber, although easy to operate, antioxidant with
Raw rubber is dispersed poor in raw rubber after being kneaded, thus is badly in need of carrying out antioxidant female granulated processed, not only improves so anti-
The dispersibility of oxygen agent can also increase the compatibility between relevant process material.
And most of antioxidant be all in it is powdered, easily generate dust in operation, not only pollute environment, simultaneously
Also the health of operator can be endangered, and is difficult to ensure the quality of rubber product.My company develops a kind of annex solution
The predispersed masterbatch of body antioxidant has well solved antioxidant and has dispersed compatibility between uneven, dust pollution and each material
The problem of difference, and after processing predispersed masterbatch antioxygenic property is good, good dispersion, processability are excellent.
Summary of the invention
Technical problem: it is an object of the invention to solve prior art problem, overcome antioxygen during original rubber processing
Agent dispersion is uneven, between dust pollution and each material the shortcomings that poor compatibility, provides pre- point of a kind of adding liquid antioxidant
Master batch is dissipated, to guarantee that the antioxygenic property of predispersed masterbatch is good, good dispersion.
Technical solution: to achieve the above object, the invention provides the following technical scheme:
A kind of anti-oxidant predispersed masterbatch of the invention, the master batch are grouped as by each group of following weight percent: mixing
Glue 5%~30%, dispersing agent 0.01%~8%, liquid antioxidant 10%~80%, processing aid 20%~70%.
Preferably, anti-oxidant predispersed masterbatch is grouped as by each group of following weight percent in the present invention: epoxy glue
8%~30%, dispersing agent 0.1%~8%, liquid antioxidant 14%~78%, processing aid 25%~70%.
Above-mentioned epoxy glue is SBR, EPDM, EVA, butadiene rubber wherein any two kinds of mixture.
Aforesaid liquid antioxidant is the mixture of one or more of liquid amine antioxidants, liquid phenolic antioxidant,
It better disperses antioxidant in process, improves the antioxygen property of master batch.
Above-mentioned dispersing agent is the mixing of one or more of polyethylene wax, polypentaerythritol stearate, zinc stearate
Object, above-mentioned processing aid are the mixtures of one or more of white carbon black, carbon black, diatomite, calcium carbonate.Dispersing agent can make
Each rapidoprint with raw rubber be kneaded in be uniformly dispersed, the addition of processing aid can reduce production cost.
The utility model has the advantages that compared with prior art, the beneficial effects of the present invention are:
The production operation of master batch of the present invention is easy, contains liquid antioxidant in anti-oxidant predispersed masterbatch of the invention, benefit
In the dispersibility of antioxidant, and avoid powder antioxidant bring dust harzard.It solves antioxidant and disperses uneven, dust
Between pollution and each material the shortcomings that poor compatibility, the anti-oxidant predispersed masterbatch antioxygenic property of production is good, good dispersion, adds
Work is excellent.
Specific embodiment
The embodiment of the present invention addressed below.The elements and features described in one embodiment of the invention can be with
The elements and features shown in one or more other embodiments combine.It should be noted that for purposes of clarity, saying
The expression and description of component unrelated to the invention, known to persons of ordinary skill in the art and processing are omitted in bright.
A kind of anti-oxidant predispersed masterbatch of the invention, the master batch are grouped as by each group of following weight percent: mixing
Glue 5%~30%, dispersing agent 0.01%~8%, liquid antioxidant 10%~80%, processing aid 20%~70%.
The present invention furthermore provides the preparation method of above-mentioned anti-oxidant predispersed masterbatch, comprising the following steps: the first step,
Epoxy glue is refined in 100 DEG C~150 DEG C mixers;Mixing is added in dispersing agent, processing aid, liquid antioxidant by second step
5~10min of mixing, then epoxy glue addition is continuesd to mix into 5~10min of mixing;Third step feeds premix made from second step
Enter in single screw extrusion machine, wherein each area's temperature of extruder is 50 DEG C~100 DEG C;4th step, extruding pelletization, drying are made pre-
Disperse master batch.
Embodiment 1:
The anti-oxidant predispersed masterbatch of the present embodiment, raw material include each component of following weight percent: epoxy glue 21.3%,
Liquid antioxidant 40%, dispersing agent 0.7%, processing aid 38%.
At normal temperatures and pressures, each component of following mass fraction: SBR and EPDM 1065g, liquid amine antioxidants is weighed
Raw rubber SBR and EPDM is added in 2000g, polyethylene wax 35g, white carbon black 1900g, the first step in 100 DEG C~150 DEG C mixers
Refine into epoxy glue;Mixing 5~10min of mixing is added in polyethylene wax, white carbon black and liquid amine antioxidants by second step, then
Epoxy glue addition after refining is continuesd to mix into 5~10min of mixing, obtains premix;Third step will premix made from second step
In material feeding single screw extrusion machine, wherein each area's temperature of extruder is 50 DEG C~100 DEG C;4th step, extruding pelletization, drying, system
Obtain predispersed masterbatch.
Embodiment 2:
The anti-oxidant predispersed masterbatch of the present embodiment and preparation method raw material include each component of following weight percent: mixing
Glue 21%, liquid phenolic antioxidant 44%, polypentaerythritol stearate 1%, diatomite 34%.
At normal temperatures and pressures, each component of following mass fraction: raw rubber EPDM and EVA1050g, liquid phenols antioxygen is weighed
Life is added in agent 2200g, polypentaerythritol stearate 50g, diatomite 1700g, the first step in 100 DEG C~150 DEG C mixers
Glue EPDM and EVA are refined into epoxy glue;Second step adds polypentaerythritol stearate, diatomite and liquid phenolic antioxidant
Enter to mix 5~10min of mixing, then the epoxy glue addition after refining is continuesd to mix into 5~10min of mixing;Third step, by second step
In premix feeding single screw extrusion machine obtained, wherein each area's temperature of extruder is 50 DEG C~100 DEG C;4th step, extrusion are made
Drying, predispersed masterbatch is made in grain.
Embodiment 3:
The anti-oxidant predispersed masterbatch of the present embodiment and preparation method raw material include each component of following weight percent: mixing
Glue 14%, liquid amine antioxidants 49%, zinc stearate 2%, calcium carbonate 35%.
At normal temperatures and pressures, each component of following mass fraction: SBR and EVA raw rubber 700g, liquid amine antioxidants is weighed
SBR and EVA raw rubber is added in 2450g, zinc stearate 100g, calcium carbonate 1750g, the first step in 100 DEG C~150 DEG C mixers
Refine into epoxy glue;Mixing 5~10min of mixing is added in zinc stearate, calcium carbonate and liquid amine antioxidants by second step, then
Epoxy glue addition after refining is continuesd to mix into 5~10min of mixing;Premix made from second step is fed single spiral shell by third step
In bar extruder, wherein each area's temperature of extruder is 50 DEG C~100 DEG C;Pre-dispersed mother is made in 4th step, extruding pelletization, drying
Grain.
Embodiment 4:
The anti-oxidant predispersed masterbatch of the present embodiment and preparation method raw material include each component of following weight percent: mixing
Glue 14%, liquid phenolic antioxidant 52%, polypentaerythritol stearate 3%, carbon black 31%.
At normal temperatures and pressures, each component of following mass fraction: EVA and butadiene rubber raw rubber 700g, liquid phenols is weighed
Antioxidant 2600g, polypentaerythritol stearate 150g, carbon black 1550g, the first step add in 100 DEG C~150 DEG C mixers
Enter EVA and the refining of butadiene rubber raw rubber into epoxy glue;Second step resists polypentaerythritol stearate, carbon black and liquid phenols
Mixing 5~10min of mixing is added in oxygen agent, then the epoxy glue addition after refining is continuesd to mix 5~10min of mixing;Third step, will
Premix made from second step is fed in single screw extrusion machine, and wherein each area's temperature of extruder is 50 DEG C~100 DEG C;4th step,
Drying, predispersed masterbatch is made in extruding pelletization.
Embodiment 5:
The anti-oxidant predispersed masterbatch of the present embodiment and preparation method raw material include each component of following weight percent: mixing
Glue 12%, liquid antioxidant 57%, dispersing agent 4%, processing aid 27%.
At normal temperatures and pressures, each component of following mass fraction: raw rubber 600g, liquid antioxidant 2850g, dispersing agent is weighed
Raw rubber refining is added into epoxy glue in 200g, processing aid 1350g, the first step in 100 DEG C~150 DEG C mixers;Second step,
Mixing 5~10min of mixing is added in dispersing agent, processing aid and liquid antioxidant, then the epoxy glue after refining is added and is continued
Mix 5~10min of mixing;Third step feeds premix made from second step in single screw extrusion machine, wherein each area of extruder
Temperature is 50 DEG C~100 DEG C;Drying, predispersed masterbatch is made in 4th step, extruding pelletization.
The production operation of master batch of the present invention is easy, contains liquid antioxidant in anti-oxidant predispersed masterbatch of the invention, benefit
In the dispersibility of antioxidant, and avoid powder antioxidant bring dust harzard.It solves antioxidant and disperses uneven, dust
Between pollution and each material the shortcomings that poor compatibility, the anti-oxidant predispersed masterbatch antioxygenic property of production is good, good dispersion, adds
Work is excellent.
The material and experimental facilities that the embodiment of the present invention is designed into meet high polymer material technology unless otherwise instructed
The commercial product in field.
The above is merely a preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise of not departing from core of the invention technology, improvements and modifications can also be made, these improvements and modifications are also answered
Belong to scope of patent protection of the invention.With any change in the comparable meaning and scope of claims of the present invention, all
It is considered as being included within the scope of the claims.
Claims (6)
1. a kind of anti-oxidant predispersed masterbatch, which is characterized in that the master batch is grouped as by each group of following weight percent:
Epoxy glue 5% ~ 30%, dispersing agent 0.01% ~ 8%, liquid antioxidant 10% ~ 80%, processing aid 20% ~ 70%.
2. anti-oxidant predispersed masterbatch according to claim 1, which is characterized in that the master batch is by following weight percent
Each group be grouped as: epoxy glue 8% ~ 30%, dispersing agent 0.1% ~ 8%, liquid antioxidant 14% ~ 78%, processing aid 25% ~ 70%.
3. anti-oxidant predispersed masterbatch according to claim 1 or 2, which is characterized in that the epoxy glue be SBR, EPDM,
EVA, butadiene rubber wherein any two kinds of mixture.
4. anti-oxidant predispersed masterbatch according to claim 1 or 2, which is characterized in that the liquid antioxidant is liquid
The mixture of one or more of amine antioxidants, liquid phenolic antioxidant.
5. anti-oxidant predispersed masterbatch according to claim 1 or 2, which is characterized in that the dispersing agent be polyethylene wax,
The mixture of one or more of polypentaerythritol stearate, zinc stearate.
6. anti-oxidant predispersed masterbatch according to claim 1 or 2, which is characterized in that the processing aid be white carbon black,
The mixture of one or more of carbon black, diatomite, calcium carbonate.