CN108949293A - A kind of SM grades of gasoline machine oil complexing agent and application - Google Patents
A kind of SM grades of gasoline machine oil complexing agent and application Download PDFInfo
- Publication number
- CN108949293A CN108949293A CN201711296036.9A CN201711296036A CN108949293A CN 108949293 A CN108949293 A CN 108949293A CN 201711296036 A CN201711296036 A CN 201711296036A CN 108949293 A CN108949293 A CN 108949293A
- Authority
- CN
- China
- Prior art keywords
- grades
- machine oil
- content
- gasoline
- gasoline machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of SM grades of gasoline machine oil complexing agent and application, including following raw material: super base number calcium alkylbenzenesulfonate, sulphur phosphorus secondary alcohol groups zinc salt, aminothio ester 3-3.5%, alkylated diphenylamine, dialkyl dithiophosphoric acid oxygen molybdenum, polyisobutylene-bis-succinimide, high molecular weight polyisobutylene base succimide (T161).Raw material is weighed, is added in reconciliation kettle, heats up 60 DEG C -70 DEG C, stirred -3 hours 2 hours under normal pressure, filter, obtain SM grades of gasoline machine oil complexing agent.Advantage is: preparation method is easy to operate, easily prepared, has excellent high temperature oxidation resistance and oxidation stability;It promotes gasoline engine oil composite compound to SL, SM stratification levels by SJ rank, and can be used with staged.
Description
Technical field
The present invention is a kind of SM grades of gasoline machine oil complexing agent.
Background technique
Usage amount is big currently on the market for SM grades of gasoline engine oil composite compounds, and requires staged, i.e., SM rank complexing agent can
To add dosage with different, different stage oil product is concocted.The gasoline engine oil class rank of early stage is low, can only meet SJ rank oil
Product.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of SM grades of gasoline machine oil complexing agent and application, preparation method behaviour
Make simply, it is easily prepared, there is excellent high temperature oxidation resistance and oxidation stability, make gasoline engine oil composite compound by SJ rank
SL, SM stratification levels are promoted, and can be used with staged.
The technical solution of the invention is as follows:
A kind of composite gasoline and engine oil additive composition, which is 100%, including following raw material group
It closes:
A, super base number calcium alkylbenzenesulfonate 16-25%;
B, sulphur phosphorus secondary alcohol groups zinc salt 17.0-20%;
C, aminothio ester 3-3.5%;(T323)
D, alkylated diphenylamine 5-7%;
E, dialkyl dithiophosphoric acid oxygen molybdenum 1.8-2.5%;
F, polyisobutylene-bis-succinimide (T154) 30-35%;
G, high molecular weight polyisobutylene base succimide (T161) 18-24%.
Further, calcium content >=14m% of the super base number calcium alkylbenzenesulfonate, total base number >=395mgKOH/g.
Further, sulphur phosphorus secondary alcohol groups zinc salt Zn content >=9.5%, P content >=7.5%, S content 15-19%.
Further, molybdenum content >=8% of molybdenum dithiocarbamate.
Further, the N content 1.0-1.1% of the high molecular weight polyisobutylene base succimide.
Further, the sulfur content 29-32% of the aminothio ester.
Further, the TBN152-172mgKOH/g of the alkylated diphenylamine, basic nitrogen 3.8-4.3%.
A kind of preparation method of SM grades of gasoline machine oil complexing agent, the specific steps of which are as follows:
By weight ratio according to raw material, it is added in reconciliation kettle, heats up 60 DEG C -70 DEG C, stirred -3 hours 2 hours under normal pressure,
Filtering, obtains SM grades of gasoline machine oil complexing agent.
A kind of SM grades of gasoline machine oil complexing agent is preparing the application in SM grades of gasoline machine oil, is characterized in that
Including following component:
The super base number calcium alkylbenzenesulfonate of A has excellent high temperature detergency, acid neutralization capacity, and has base number height, thermostabilization
Property and rust-preventing characteristic, can effectively reduce the high temperature deposition object on engine components, permanently effective protection engine avoids parts
Sour corrosion extends the oil draining period.
B sulphur phosphorus secondary alcohol groups zinc salt has good corrosion resistance and abrasion resistance, it can efficiently solve cam and endure
The abrasion and corrosion of bar and because high-temperature oxydation increases oil viscosity.
C aminothio ester is multipurpose additive, has abrasion resistant extreme-pressure performance outstanding and good antioxidant effect.
D alkyl diphenylamine is a kind of outstanding high-temperature antioxidant, has remarkable result to the later period oxidation for inhibiting oil product.
E dialkyl dithiophosphoric acid oxygen molybdenum is a kind of excellent friction improver, coefficient of friction can be effectively reduced, in gold
Belong to and forms protective film between attachment.
F polyisobutylene-bis-succinimide is a kind of ashless dispersant, can effectively solve the low temperature greasy filth of engine, subtract
The paint film of few engine hot parts and the deposition of carbon distribution.
G high molecular weight polyisobutylene base succimide has excellent high temperature detergency and low energy dispersion.
The present invention is mainly by sulfonate, ashless dispersant, high temperature detersive, oxidation and corrosion inhibitor, dialkyl dithiophosphoric acid
The composition such as oxygen molybdenum.Its advantage is that:
Preparation method is easy to operate, easily prepared, has excellent high temperature oxidation resistance and oxidation stability;This is compound
Agent composition uses molybdenum salt and high molecular weight ashless dispersant technology, focuses on the compounding effect between each additive, more prominent
High-temperature oxidation resistance and wear resistance, the use that high molecular weight is ashless, in terms of low temperature dispersity and high temperature detergency
Optimum efficiency is reached.Using dialkyl dithiophosphoric acid oxygen molybdenum, thus there is wear resistance;And there is high temperature detergency
It is good;Improve domestic compound additives levels;The compound additive is applied in II, III class base oil, the development of the complexing agent
It promotes gasoline engine oil composite compound to SL, SM stratification levels by SJ rank, and can be used with staged.
Specific embodiment
Embodiment 1
Weigh raw material:
A, super base number calcium alkylbenzenesulfonate 18kg;
B, sulphur phosphorus secondary alcohol groups zinc salt 17kg;
C, aminothio ester (T323) 3.5kg;
D, alkylated diphenylamine 5kg;
E, dialkyl dithiophosphoric acid oxygen molybdenum 2.5kg;
F, polyisobutylene-bis-succinimide (T154) 30kg;
G, high molecular weight polyisobutylene base succimide (T161) 24kg.
Calcium content >=14m% of super base number calcium alkylbenzenesulfonate, total base number >=395mgKOH/g;Sulphur phosphorus secondary alcohol groups zinc salt Zn contains
Amount >=9.5%, P content >=7.5%, S content 15-19%;Molybdenum content >=8% of dialkyl dithiophosphoric acid oxygen molybdenum;The height
The N content 1.0-1.1% of molec weight polyisobutylene base succimide.
Weighed raw material is added in reconciliation kettle, is heated up 70 DEG C, is stirred 3 hours under normal pressure, filters, obtains SM grades of gasoline machine
Oily complexing agent.
Embodiment 2
Weigh raw material:
A, super base number calcium alkylbenzenesulfonate 16kg;
B, sulphur phosphorus secondary alcohol groups zinc salt 20kg;;
C, aminothio ester 3kg;
D, alkylated diphenylamine 5kg;
E, dialkyl dithiophosphoric acid oxygen molybdenum 1.8kg;
F, polyisobutylene-bis-succinimide 35kg;
G, high molecular weight polyisobutylene base succimide (T161) 19.2kg.
Calcium content >=14m% of super base number calcium alkylbenzenesulfonate, total base number >=395mgKOH/g;Sulphur phosphorus secondary alcohol groups zinc salt Zn contains
Amount >=9.5%, P content >=7.5%, S content 15-19%;Molybdenum content >=8% of molybdenum dithiocarbamate;The high score
The N content 1.0-1.1% of son amount polyisobutylene succinamide.
Weighed raw material is added in reconciliation kettle, heats up 60 DEG C, is stirred 2 hours under normal pressure, filters, obtains SM grades of gasoline
Machine oil complexing agent.
Embodiment 3
Weigh raw material:
A, super base number calcium alkylbenzenesulfonate 25kg;
B, sulphur phosphorus secondary alcohol groups zinc salt 17kg;
C, aminothio ester 3kg;
D, alkylated diphenylamine 5kg;
E, dialkyl dithiophosphoric acid oxygen molybdenum 2kg;
F, polyisobutylene-bis-succinimide (T154) 30kg;
G, high molecular weight polyisobutylene base succimide (T161) 18kg.
Calcium content >=14m% of super base number calcium alkylbenzenesulfonate, total base number >=395mgKOH/g;Sulphur phosphorus secondary alcohol groups zinc salt Zn contains
Amount >=9.5%, P content >=7.5%, S content 15-19%;Molybdenum content >=8% of dialkyl dithiophosphoric acid oxygen molybdenum;The height
The N content 1.0-1.1% of molec weight polyisobutylene base succimide.
Weighed raw material is added in reconciliation kettle, is heated up 60 DEG C -70 DEG C, is stirred -3 hours under normal pressure, filters, obtains SM grades
Other gasoline engine oil composite compound.
Embodiment 4
Weigh raw material:
A, super base number calcium alkylbenzenesulfonate 18kg;
B, sulphur phosphorus secondary alcohol groups zinc salt 18kg;
C, aminothio ester 3.2kg;(T323)
D, alkylated diphenylamine 7kg;
E, dialkyl dithiophosphoric acid oxygen molybdenum 1.8kg;
F, polyisobutylene-bis-succinimide (T154) 32kg;
G, high molecular weight polyisobutylene base succimide (T161) 20kg.
Calcium content >=14m% of super base number calcium alkylbenzenesulfonate, total base number >=395mgKOH/g;Sulphur phosphorus secondary alcohol groups zinc salt Zn contains
Amount >=9.5%, P content >=7.5%, S content 15-19%;Molybdenum content >=8% of molybdenum dithiocarbamate;The high score
The N content 1.0-1.1% of son amount polyisobutylene succinamide.
Weighed raw material is added in reconciliation kettle, heats up 65 DEG C, is stirred 2.5 hours under normal pressure, filters, obtains SM rank vapour
Oil machine oil complexing agent.
According to above-mentioned preparation method, SM grades of gasoline engine oil composite compound quality index of gained are as described in Table 1:
Table 1
(2) with SM rank complexing agent of the present invention modulation API SAE 5W/30 grade lubricants, the specific method is as follows:
Quality scale: API SM SAE 5W/30
Two class hydrogenated base oils: 500N 25%
Two class hydrogenated base oils: 150N 20.7%
Polyalphaolefin: 38.5%
Trihydroxymethylpropanyl ester: 8.0%
4 complexing agent of the embodiment of the present invention: 7.8%.
The lubricating oil for deploying other ranks can be by suitably increasing by two class hydrogenated base oils, reducing complexing agent of the present invention
Mode is realized.
The results are shown in Table 2 for the testing inspection of the API SM SAE5W/30 oil product of the complexing agent modulation of the embodiment of the present invention 1
Table 2
(3) the advantages of SM gasoline engine oil composite compound of the invention:
1, plus agent level is at the leading level
Complexing agent SM rank of the present invention adds dosage 7.8%, and SL rank 6.6% adds agent horizontal better than similar products at home and abroad,
It is at the leading level.
Table 3
The name of an article | SM | SL | SJ | SG | SF |
This complexing agent | 7.8 | 6.6 | 5.3 | 4.7 | 4.1 |
LZ16009L | 7.0 | ||||
LZL16009J | 6.8 | 5.2 | 4.5 | ||
LZPV7053 | 8.64 |
2, complexing agent of the present invention belongs to stepwise application, can satisfy the requirement of SG, SF, SL, SM different stage lubricating oil,
It is easy to use, the lubricating oil of different stage can be modulated with different plus dosage, such as: SF 4.1%, SG rank
4.7%, SJ rank 5.3%, SL rank 6.6%, SM rank 7.8%.
3, the invention and listing of this complexing agent changes the history that domestic complexing agent does not have SM rank.
4, cost performance is high, is popular in users.
The above is only specific embodiments of the present invention, are not intended to restrict the invention, for those skilled in the art
For member, the invention may be variously modified and varied.All within the spirits and principles of the present invention, it is made it is any modification,
Equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (9)
1. a kind of SM grades of gasoline machine oil composite additive, which is 100%, it is characterized in that:
Including following material combination:
A, super base number calcium alkylbenzenesulfonate 16-25%;
B, sulphur phosphorus secondary alcohol groups zinc salt 17.0-20%;
C, aminothio ester 3-3.5%;(T323)
D, alkylated diphenylamine 5-7%;
E, dialkyl dithiophosphoric acid oxygen molybdenum 1.8-2.5%;
F, polyisobutylene-bis-succinimide (T154) 30-35%;
G, high molecular weight polyisobutylene base succimide (T161) 18-24%.
2. SM grades of gasoline machine oil composite additive according to claim 1, it is characterized in that: the super base number closes
At calcium content >=14m% of sulfoacid calcium, total base number >=395mgKOH/g.
3. SM grades of gasoline machine oil composite additive according to claim 1, it is characterized in that: sulphur phosphorus secondary alcohol groups zinc
Salt Zn content >=9.5%, P content >=7.5%, S content 15-19%.
4. SM grades of gasoline machine oil composite additive according to claim 1, it is characterized in that: dialkyl dithio
Molybdenum content >=8% of formic acid molybdenum.
5. composite gasoline and engine oil additive composition according to claim 1, it is characterized in that: the high-molecular-weight poly isobutyl
The N content 1.0-1.1% of alkenyl succimide.
6. SM grades of gasoline machine oil composite additive according to claim 1, it is characterized in that: the aminothio
The sulfur content 29-32% of ester.
7. SM grades of gasoline machine oil composite additive according to claim 1, it is characterized in that: the alkylation
The TBN152-172mgKOH/g of diphenylamines, basic nitrogen 3.8-4.3%.
8. a kind of SM grades of gasoline machine oil complexing agent as described in claim 1, it is characterized in that:
Specific preparation process is as follows:
By weight ratio according to raw material, it is added in reconciliation kettle, heats up 60 DEG C -70 DEG C, stirred -3 hours 2 hours under normal pressure, filtered,
Obtain SM grades of gasoline machine oil complexing agent.
9. it is a kind of weigh require 1 as described in gasoline engine oil composite compound in the application prepared in SM grades of gasoline machine oil, it is characterized in that:
Including following component: