CN108949076A - A kind of steel bonding glue and preparation method thereof for economizer steel bonding - Google Patents
A kind of steel bonding glue and preparation method thereof for economizer steel bonding Download PDFInfo
- Publication number
- CN108949076A CN108949076A CN201810840686.3A CN201810840686A CN108949076A CN 108949076 A CN108949076 A CN 108949076A CN 201810840686 A CN201810840686 A CN 201810840686A CN 108949076 A CN108949076 A CN 108949076A
- Authority
- CN
- China
- Prior art keywords
- parts
- steel bonding
- antioxidant
- economizer
- bonding glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of steel bonding glue and preparation method thereof for economizer steel bonding.The steel bonding glue comprises the following components in parts by weight: 50~60 parts of polyimides, 70~80 parts of epoxy resin, 50~60 parts of isopropyl acetate, 20~30 parts of siloxanes, 10~20 parts of nano silica, 10~20 parts of glycerol, 5~15 parts of azobisisoheptonitrile, 0~5 part of carbolic oil, 5~10 parts of toughener, 5~10 parts of double hydroxyphthalimides, 10~20 parts of coupling agent and 5~10 parts of antioxidant.The steel bonding glue that the method for the present invention is prepared not only has excellent high temperature resistance, while bonding force is strong, and stability is good.
Description
Technical field
The invention belongs to steel bonding glue technical fields, and in particular to a kind of steel bonding glue and its system for economizer steel bonding
Preparation Method.
Background technique
Economizer (English name Economizer) be mounted to boiler back end ductwork lower part for recycle discharged fume it is remaining
Boiler feedwater, is heated into the heating surface of the saturated water under drum pressure by a kind of device of heat, since it absorbs high-temperature flue gas
Heat reduces the exhaust gas temperature of flue gas, saves the energy, improve efficiency, is widely used in industrial processes, with into
The effects of row heat recovery.
Existing economizer is to produce by welding, and during the welding process, inevitably can be to economizer tube wall
Pad at generate damage, after leading to long-time use, coiled pipe leads to the problem of leakage, brings security risk to production.
And existing steel bonding glue it is most of be all applied under normal temperature state structural steel bonding or concrete it
Between bonding, and economizer is due to the difference of its working environment, does not require nothing more than steel bonding glue with high temperature resistance, need to also be in high temperature
There is down excellent adhesive property and toughness, existing steel bonding glue obviously can not be suitable under hot environment as a result,
In economizer.
Summary of the invention
For above-mentioned deficiency in the prior art, the present invention provide it is a kind of for economizer steel bonding steel bonding glue and its
Preparation method can effectively solve existing steel bonding gluing relay deficiency, the problem of high temperature resistance difference.
To achieve the above object, the technical solution adopted by the present invention to solve the technical problems is:
A kind of steel bonding glue for economizer steel bonding, comprises the following components in parts by weight:
50~60 parts of polyimides, 70~80 parts of epoxy resin, 50~60 parts of isopropyl acetate, 20~30 parts of siloxanes,
10~20 parts of nano silica, 10~20 parts of glycerol, 5~15 parts of azobisisoheptonitrile, 0~5 part of carbolic oil, toughener 5~10
Part, 5~10 parts of double hydroxyphthalimides, 10~20 parts of coupling agent and 5~10 parts of antioxidant.
Further, it comprises the following components in parts by weight:
55 parts of polyimides, 70 parts of epoxy resin, 50 parts of isopropyl acetate, 28 parts of siloxanes, 18 parts of nano silica,
14 parts of glycerol, 4 parts of carbolic oil, 6 parts of toughener, 8 parts of azobisisoheptonitrile, 8 parts of double hydroxyphthalimides, 15 parts of coupling agent
And 5 parts of antioxidant.
Further, coupling agent is silane resin acceptor kh-550, cumyl hydroperoxide, Aluminate or ethylene-acrylic acid
Methyl esters.
Further, toughener is carboxyl liquid nitrile rubber, carboxyl-terminated liguid nitrile rubber, polysulfide rubber, liquid silicon
Rubber, polyethers or polysulfones.
Further, antioxidant be antioxidant 1076, antioxidant 168, antioxidant 164, antioxidant TNP,
Antioxidant CA or antioxidant DLTP.
Further, reaction temperature is 135 DEG C in step (1).
Further, reaction temperature is 150 DEG C in step (2).
The preparation method of above-mentioned steel bonding glue, comprising the following steps:
(1) epoxy resin and nano silica are stirred by formula, form mixed liquor A;Then by isopropyl acetate
Ester and siloxanes mixing, form mixed liquid B;Mixed liquor A and mixed liquid B are stirred in 120~150 DEG C, are then added even
The different heptonitrile of nitrogen two, continues to be stirred to react 3~5h;
(2) polyimides, glycerol, carbolic oil, antioxidant and toughener are mixed, step (1) products therefrom is then added
In, double hydroxyphthalimides and coupling agent, which are added, in 100~150 DEG C of 5~10h of reaction obtains steel bonding glue.
The invention has the benefit that
1, during preparing the steel bonding glue, epoxy resin be tentatively modified by nano silica, can be had
The temperature tolerance of the promotion epoxy resin of effect, toughness;Then on this basis, using azobisisoheptonitrile as initiator, by connecing
Silicon-containing group is imported the positions such as main chain, the side chain of epoxy molecule by branch copolymerization technique, contains epoxy molecule fire-retardant
Ingredient, make its except possess fire-retardant, high heat resistance, it is anti-oxidant, nonflammable the features such as in addition to, moisture-proof also with higher and strand
Flexibility, good high-temperature resistant result can not only be reached, also will not influence the mobility of steel bonding glue entirety.
2, by the effect of double hydroxyphthalimides and coupling agent, make the epoxy of polyimides Yu modified processing
Resin-bonded together, since double hydroxyphthalimides contain N-OH, is easy production free radical, can effectively be catalyzed poly-
Connection between acid imide and epoxy resin;Meanwhile double hydroxyphthalimides can also be produced with the hydroxyl in epoxy resin
Raw ring-opening reaction, further promotes the connection of polyimides and epoxy resin, imparts the excellent heat resistance of epoxy resin
Energy and toughness;And the epoxy resin after polyimides connects, also there is excellent adhesive property, promote the viscous of whole steel bonding glue
Relay.
3, after polyimides is in conjunction with the epoxy resin of modified processing, cooperate antioxidant, so that steel bonding glue has
Excellent high temperature resistance, meanwhile, under high temperature environment, the epoxy resin of modified processing can form one layer of charcoal on surface
Layer prevents material further by high-temperature oxydation, to protect adhesive effect and steel bonding glue sheet itself.
4, by the way that toughener is added, the bonding force of steel bonding glue entirety can further be enhanced, and can guarantee its toughness, together
When, under the action of glycerol, moreover it is possible to enhance its mobility;And carbolic oil has mobile faintly acid corrosive nature, it can be to steel
Surface generates certain corrosion, promotes the bonding force between steel bonding glue and steel.
Specific embodiment
A specific embodiment of the invention is described below, in order to facilitate understanding by those skilled in the art this hair
It is bright, it should be apparent that the present invention is not limited to the ranges of specific embodiment, for those skilled in the art,
As long as various change is in the spirit and scope of the present invention that the attached claims limit and determine, these variations are aobvious and easy
See, all are using the innovation and creation of present inventive concept in the column of protection.
Embodiment 1
A kind of steel bonding glue for economizer steel bonding, comprises the following components in parts by weight:
55 parts of polyimides, 70 parts of epoxy resin, 50 parts of isopropyl acetate, 28 parts of siloxanes, 18 parts of nano silica,
14 parts of glycerol, 4 parts of carbolic oil, 6 parts of polysulfones, 8 parts of azobisisoheptonitrile, 8 parts of double hydroxyphthalimides, silane coupling agent
15 parts of KH-550 and 168 5 parts of antioxidant.
The preparation method of above-mentioned steel bonding glue, comprising the following steps:
(1) epoxy resin and nano silica are stirred by formula, form mixed liquor A;Then by isopropyl acetate
Ester and siloxanes mixing, form mixed liquid B;Mixed liquor A and mixed liquid B are stirred in 135 DEG C, it is different that azo two is then added
Heptonitrile continues to be stirred to react 4h;
(2) polyimides, glycerol, carbolic oil, antioxidant 168 and polysulfones are mixed, step (1) products therefrom is then added
In, double hydroxyphthalimides and silane resin acceptor kh-550, which are added, in 150 DEG C of reaction 8h obtains steel bonding glue.
Embodiment 2
A kind of steel bonding glue for economizer steel bonding, comprises the following components in parts by weight:
50 parts of polyimides, 80 parts of epoxy resin, 60 parts of isopropyl acetate, 20 parts of siloxanes, 10 parts of nano silica,
10 parts of glycerol, 5 parts of carbolic oil, 5 parts of polyethers, 5 parts of azobisisoheptonitrile, 5 parts of double hydroxyphthalimides, 10 parts of Aluminate with
And 164 5 parts of antioxidant.
The preparation method of above-mentioned steel bonding glue, comprising the following steps:
(1) epoxy resin and nano silica are stirred by formula, form mixed liquor A;Then by isopropyl acetate
Ester and siloxanes mixing, form mixed liquid B;Mixed liquor A and mixed liquid B are stirred in 120 DEG C, it is different that azo two is then added
Heptonitrile continues to be stirred to react 3h;
(2) polyimides, glycerol, carbolic oil, antioxidant 164 and polyethers are mixed, step (1) products therefrom is then added
In, double hydroxyphthalimides and Aluminate, which are added, in 100 DEG C of reaction 5h obtains steel bonding glue.
Embodiment 3
A kind of steel bonding glue for economizer steel bonding, comprises the following components in parts by weight:
56 parts of polyimides, 80 parts of epoxy resin, 60 parts of isopropyl acetate, 28 parts of siloxanes, 20 parts of nano silica,
20 parts of glycerol, 10 parts of polysulfones, 15 parts of azobisisoheptonitrile, 10 parts of double hydroxyphthalimides, ethylene-methyl acrylate 15
Part and 10 parts of antioxidant CA.
The preparation method of above-mentioned steel bonding glue, comprising the following steps:
(1) epoxy resin and nano silica are stirred by formula, form mixed liquor A;Then by isopropyl acetate
Ester and siloxanes mixing, form mixed liquid B;Mixed liquor A and mixed liquid B are stirred in 150 DEG C, it is different that azo two is then added
Heptonitrile continues to be stirred to react 5h;
(2) polyimides, glycerol, antioxidant CA and polysulfones are mixed, is then added in step (1) products therefrom, then
Double hydroxyphthalimides and ethylene-methyl acrylate is added and obtains steel bonding glue in 150 DEG C of reaction 10h.
Comparative example 1
Compared with Example 1, isopropyl acetate, siloxanes, carbolic oil are lacked in formula, remaining is same as Example 1.
Comparative example 2
Compared with Example 1, isopropyl acetate, siloxanes, carbolic oil, nano silica, polyimides are lacked in formula,
Remaining is same as Example 1.
Detection
Tensile strength, the cementability of the steel bonding glue that Examples 1 to 3 and comparative example 1, comparative example 2 are prepared are detected respectively
Energy and the crystallinity within the scope of 200~600 DEG C, then the steel of bonding economizer are respectively used to, then in economizer
After 10~15 months, degumming degree is detected, the result is shown in tables 1.
1 steel bonding colloidality energy of table
From the data in table 1, it can be seen that the steel bonding colloidality that Examples 1 to 3 is prepared can be far superior to comparative example 1 and comparative example 2,
Wherein embodiment 1 and embodiment 3 are slightly better than embodiment 2 on adhesive property, show only to refer in the method for the present invention as a result,
Under the cooperation of formula and parameter, the steel bonding glue with excellent adhesive property and high temperature resistance can just be prepared.
Claims (8)
1. a kind of steel bonding glue for economizer steel bonding, which is characterized in that comprise the following components in parts by weight:
50~60 parts of polyimides, 70~80 parts of epoxy resin, 50~60 parts of isopropyl acetate, siloxanes 20~30 part, nanometer
It is 0~20 part of silica 1,10~20 parts of glycerol, 0~5 part of carbolic oil, 5~10 parts of toughener, 5~15 parts of azobisisoheptonitrile, double
5~10 parts of hydroxyphthalimide, 10~20 parts of coupling agent and 5~10 parts of antioxidant.
2. the steel bonding glue according to claim 1 for economizer steel bonding, which is characterized in that including following parts by weight
Component:
55 parts of polyimides, 70 parts of epoxy resin, 50 parts of isopropyl acetate, 28 parts of siloxanes, 18 parts of nano silica, glycerol
14 parts, 4 parts of carbolic oil, 6 parts of toughener, 8 parts of azobisisoheptonitrile, 8 parts of double hydroxyphthalimides, 15 parts of coupling agent and
5 parts of antioxidant.
3. the steel bonding glue according to claim 1 or 2 for economizer steel bonding, which is characterized in that the coupling agent
For silane resin acceptor kh-550, cumyl hydroperoxide, Aluminate or ethylene-methyl acrylate.
4. the steel bonding glue according to claim 1 or 2 for economizer steel bonding, which is characterized in that the toughener
For carboxyl liquid nitrile rubber, carboxyl-terminated liguid nitrile rubber, polysulfide rubber, liquid silastic, polyethers or polysulfones.
5. the steel bonding glue according to claim 1 or 2 for economizer steel bonding, which is characterized in that described anti-oxidant
Agent is antioxidant 1076, antioxidant 168, antioxidant 164, antioxidant TNP, antioxidant CA or antioxidant
DLTP。
6. the preparation method of the described in any item steel bonding glue of Claims 1 to 5, which comprises the following steps:
(1) epoxy resin and nano silica are stirred by formula, form mixed liquor A;Then by isopropyl acetate and
Siloxanes mixing, forms mixed liquid B;Mixed liquor A and mixed liquid B are stirred in 120~150 DEG C, azo two is then added
Different heptonitrile continues to be stirred to react 3~5h;
(2) polyimides, glycerol, carbolic oil, antioxidant and toughener are mixed, is then added in step (1) products therefrom, then
Double hydroxyphthalimides and coupling agent is added and obtains steel bonding glue in 100~150 DEG C of 5~10h of reaction.
7. the steel bonding glue according to claim 6 for economizer steel bonding, which is characterized in that described in step (1)
Reaction temperature is 135 DEG C.
8. the steel bonding glue according to claim 6 for economizer steel bonding, which is characterized in that described in step (2)
Reaction temperature is 150 DEG C.