CN108943942A - A kind of preparation method of environment-friendly type high performance composite material door-plate - Google Patents
A kind of preparation method of environment-friendly type high performance composite material door-plate Download PDFInfo
- Publication number
- CN108943942A CN108943942A CN201710373733.3A CN201710373733A CN108943942A CN 108943942 A CN108943942 A CN 108943942A CN 201710373733 A CN201710373733 A CN 201710373733A CN 108943942 A CN108943942 A CN 108943942A
- Authority
- CN
- China
- Prior art keywords
- plate
- door
- environment
- thermoplasticity
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation method of environment-friendly type high performance composite material door-plate, comprising the following steps: 1), by Sandwich materials dual coating epoxy glue;2), in the two-sided laying thermoplasticity damping material of Sandwich materials;3), in thermoplasticity damping material surface continuous fiber prepreg, multilayer composite is obtained;4), multilayer composite is put into mold, molding was placed in press in 1-3 hour of 100-150 DEG C of pressing.Gained environment friendly composite material door-plate high-strength light has superior acoustic, is shellproof, formaldehydeless release;Foam in Sandwich materials mitigates the quality of door-plate significantly, and there is good sound insulation function in the gap in foam;Thermoplasticity damping material PVB, EVA with excellent damping capacity, with it is anti-pound, shellproof characteristic so that door-plate safety greatly improves.Formaldehyde type adhesive, formaldehydeless release in product use process, safety and environmental protection are not necessarily in production process.
Description
Technical field
The invention belongs to technical field of finishing materials, specially a kind of preparation side of environment-friendly type high performance composite material door-plate
Method.
Background technique
With economic development at full speed, continuous improvement of people's living standards, the feature of environmental protection, safety of the people to finishing material
Property is increasingly paid attention to.Door-plate is widely used in the places such as family, office, market, train, steamer.Since people have timber
There is compatibility, thus be often used wooden boards, in order to reach the purpose of beautiful, anti-corrosion, wooden boards are in actual use often
Also need to carry out surface lacquer processing, for wooden boards itself there are some disadvantages, such as easy shrinkage cracking, chance water is easily-deformable, meets wet
It is easily mouldy, fiery easy firing etc. is met, in addition generally can all use formaldehyde base adhesive in process of production.Even across processing,
Also more or less there can be free formaldehyde to release in use process, certain harm is generated to human body.Wooden boards it is strong
Degree is not high, and robber is easy to be destroyed.
Summary of the invention
To solve to need to handle when timber of the existing technology makees door-plate, there is Form aldehyde release, while strength of wood is lower
Defect, the present invention provides a kind of preparation method of environment-friendly type high performance composite material door-plate.
A kind of preparation method of environment-friendly type high performance composite material door-plate, comprising the following steps:
1), by Sandwich materials dual coating epoxy glue;
2), in the two-sided laying thermoplasticity damping material of Sandwich materials;
3), in thermoplasticity damping material surface continuous fiber prepreg, multilayer composite is obtained;
4), multilayer composite is put into mold, molding was placed in press in 1-3 hour of 100-150 DEG C of pressing.
Further, the angle of the continuous fiber prepreg and the thermoplasticity damping material table is 90 °, 45 ° and 0 °
One or more of.
Further, the Sandwich materials are any one in PVC, PET, PMI and PU.
Further, the continuous fiber prepreg is one of PBO, ultra high molecular polyethylene and basalt fibre
Or it is several.Basalt fibre has excellent flame retardant property.
Further, the thermoplasticity damping material is PVB and/or EVA.
The utility model has the advantages that continuous fiber prepreg, Sandwich materials and thermoplasticity damping material are answered the invention discloses a kind of
It closes, high-strength light, the environment friendly composite material door with superior acoustic, shellproof, formaldehydeless release is prepared into using mould pressing process
The method of plate, the foams such as Sandwich materials PVC, PET, PMI, PU mitigate the quality of door-plate significantly, and the gap in foam has
Good sound insulation function.PVB, EVA with excellent damping capacity, with it is anti-pound, shellproof characteristic so that door-plate safety is big
It is big to improve.Formaldehyde type adhesive, formaldehydeless release in product use process, safety and environmental protection are not necessarily in production process.
Specific embodiment
Embodiment 1
A kind of preparation method of environment-friendly type high performance composite material door-plate, comprising the following steps:
1), by Sandwich materials PVC dual coating epoxy glue;
2), in the two-sided laying thermoplasticity damping material of Sandwich materials PVC;
3), in thermoplasticity damping material surface continuous fiber prepreg PBO, multilayer composite is obtained;The continuous fiber
The angle on prepreg PBO and the surface thermoplasticity damping material PVB is 90 °.
4), multilayer composite is put into mold, molding was placed in press in 100 DEG C of 3 hours of pressing.
Embodiment 2
A kind of preparation method of environment-friendly type high performance composite material door-plate, comprising the following steps:
1), by Sandwich materials PMI dual coating epoxy glue;
2), in the two-sided laying thermoplasticity damping material EVA of Sandwich materials PMI;
3), in thermoplasticity damping material surface EVA continuous fiber prepreg ultra high molecular polyethylene, MULTILAYER COMPOSITE is obtained
Body;The angle of the continuous fiber prepreg ultra high molecular polyethylene and the thermoplasticity damping material table is 45 ° and 0 °;
4), multilayer composite is put into mold, molding was placed in press in 150 DEG C of 1 hours of pressing.
Embodiment 3
A kind of preparation method of environment-friendly type high performance composite material door-plate, comprising the following steps:
1), by Sandwich materials PET dual coating epoxy glue;
2), in the two-sided laying thermoplasticity damping material EVA and PVB of Sandwich materials PET;
3), in thermoplasticity damping material surface EVA and PVB continuous fiber prepreg basalt fibre, MULTILAYER COMPOSITE is obtained
Body;The angle of the continuous fiber prepreg basalt fibre and the thermoplasticity damping material EVA are 90 °, the continuous fibre
The angle for tieing up prepreg ultra high molecular polyethylene and the thermoplasticity damping material PVB is 0 °;
4), multilayer composite is put into mold, molding was placed in press in 150 DEG C of 1 hours of pressing.
Claims (5)
1. a kind of preparation method of environment-friendly type high performance composite material door-plate, which comprises the following steps:
1), by Sandwich materials dual coating epoxy glue;
2), in the two-sided laying thermoplasticity damping material of Sandwich materials;
3), in thermoplasticity damping material surface continuous fiber prepreg, multilayer composite is obtained;
4), multilayer composite is put into mold, molding was placed in press in 1-3 hour of 100-150 DEG C of pressing.
2. the preparation method of environment-friendly type high performance composite material door-plate as described in claim 1, which is characterized in that described continuous
The angle on fiber prepreg material and thermoplasticity damping material surface is one or more of 90 °, 45 ° and 0 °.
3. the preparation method of environment-friendly type high performance composite material door-plate as claimed in claim 1 or 2, which is characterized in that described
Sandwich materials are any one in PVC, PET, PMI and PU.
4. the preparation method of environment-friendly type high performance composite material door-plate as described in claim 1, which is characterized in that the company
Continuous fiber prepreg material is one of PBO, ultra high molecular polyethylene and basalt fibre or several.
5. the preparation method of environment-friendly type high performance composite material door-plate as claimed in claim 4, which is characterized in that the heat
Plasticity damping material is PVB and/or EVA.