CN108927137B - Preparation method of carbon-doped bismuth oxide photocatalytic material - Google Patents
Preparation method of carbon-doped bismuth oxide photocatalytic material Download PDFInfo
- Publication number
- CN108927137B CN108927137B CN201810799992.7A CN201810799992A CN108927137B CN 108927137 B CN108927137 B CN 108927137B CN 201810799992 A CN201810799992 A CN 201810799992A CN 108927137 B CN108927137 B CN 108927137B
- Authority
- CN
- China
- Prior art keywords
- carbon
- bismuth oxide
- doped bismuth
- preparation
- photocatalytic material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a preparation method of a carbon-doped bismuth oxide photocatalytic material, which comprises the steps of putting bismuth nitrate pentahydrate into an aluminum oxide crucible, annealing at 500 ℃ for 6 hours to prepare alpha-Bi2O3Powder material, and the prepared alpha-Bi2O3And placing the powder material in an alumina crucible, adding oxalic acid dihydrate powder, uniformly mixing, and annealing at 280 ℃ for 50-200 min to obtain the carbon-doped bismuth oxide photocatalytic material. The preparation method is simple and feasible in preparation process and short in synthesis period, compared with undoped bismuth oxide, the carbon-doped bismuth oxide photocatalytic material has the advantages that the light absorption edge moves towards the long-wave direction, the utilization rate of light waves in the visible light wavelength range of 400-500 nm is high, the photocatalytic performance is obviously improved, and the carbon-doped bismuth oxide photocatalytic material has potential application value in the aspect of photoelectric materials.
Description
Technical Field
The invention belongs to the technical field of synthesis of photoelectric materials, and particularly relates to a preparation method of a carbon-doped bismuth oxide photocatalytic material.
Background
The bismuth resource in China is rich, the annual output can reach more than 6000 tons in recent years, and the application is very wide. Bismuth-oxygen-based materials have a layered crystal structure, a proper forbidden band width and a special electronic structure of bismuth atoms, often show high activity in actual photocatalytic reactions, become an important photocatalytic material, and have received wide attention. Bismuth oxide is widely used for the manufacture of drugs and bismuth salts as a product after deep processing of bismuth source. Bismuth oxide belongs to bismuth-oxygen-based materials, is light yellow in appearance, has limited visible light response capability and lower photocatalytic activity. Based on the existing problems, the invention designs a preparation method of a carbon-doped bismuth oxide photocatalytic material with enhanced visible light response and improved photocatalytic activity.
Disclosure of Invention
The invention solves the technical problem of providing a preparation method of the carbon-doped bismuth oxide photocatalytic material with simple synthesis process and shorter period.
The invention adopts the following technical scheme for solving the technical problems, and the preparation method of the carbon-doped bismuth oxide photocatalytic material is characterized by comprising the following specific steps of: putting bismuth nitrate pentahydrate into an alumina crucible, and annealing for 6 hours at 500 ℃ to prepare alpha-Bi2O3Powder material, and the prepared alpha-Bi2O3And placing the powder material in an alumina crucible, adding oxalic acid dihydrate powder, uniformly mixing, and annealing at 280 ℃ for 50-200 min to obtain the carbon-doped bismuth oxide photocatalytic material.
Preferably, the alpha-Bi2O3The feeding mass ratio of the powder material to the oxalic acid dihydrate powder is 1: 1-1: 2.
The preparation method is simple and feasible in preparation process and short in synthesis period, compared with undoped bismuth oxide, the carbon-doped bismuth oxide photocatalytic material has the advantages that the light absorption edge moves towards the long-wave direction, the utilization rate of light waves in the visible light wavelength range of 400-500 nm is high, the photocatalytic performance is obviously improved, and the carbon-doped bismuth oxide photocatalytic material has potential application value in the aspect of photoelectric materials.
Drawings
FIG. 1 is an X-ray diffraction pattern of a carbon-doped bismuth oxide powder material prepared in example 1 of the present invention;
FIG. 2 is a powder absorption spectrum of a carbon-doped bismuth oxide powder material obtained in example 1 of the present invention;
FIG. 3 is a scanning electron micrograph of a carbon-doped bismuth oxide powder material prepared according to example 1 of the present invention;
FIG. 4 is a performance curve of rhodamine B degradation catalyzed by visible light of the carbon-doped bismuth oxide powder material prepared in example 1 of the present invention.
Detailed Description
The present invention is described in further detail below with reference to examples, but it should not be construed that the scope of the above subject matter of the present invention is limited to the following examples, and that all the technologies realized based on the above subject matter of the present invention belong to the scope of the present invention.
Example 1
4.85g of bismuth nitrate pentahydrate is put into an alumina crucible to be annealed for 6 hours at 500 ℃ to prepare alpha-Bi2O3Powder material, and 0.5g of the obtained alpha-Bi2O3The powder material is placed in an alumina crucible, added with 1.0g of oxalic acid dihydrate powder and annealed for 200min at 280 ℃ after being mixed evenly, thus obtaining the carbon-doped bismuth oxide powder material.
XRD analysis of the prepared carbon-doped bismuth oxide powder material revealed that the carbon-doped bismuth oxide powder material and α -Bi were present as shown in FIG. 12O3The diffraction peaks of the powder material are consistent with those of standard JCPDS cards 71-2274, no impurity peak appears, and the chemical formula is Bi2O3The crystal structure is monoclinic phase.
As shown in FIG. 2, the prepared carbon-doped bismuth oxide powder material is compared with alpha-Bi2O3The absorption of light by the powder material is enhanced and the wavelength band of light absorption appears red-shifted.
As shown in FIG. 3, the obtained carbon-doped bismuth oxide powder material has a prismatic morphology and many fine pores are distributed on the surface.
As shown in FIG. 4, after being excited by visible light for 120min, the degradation rate of the carbon-doped bismuth oxide powder material for degrading rhodamine B pollutants is 99.7%, which is much higher than that of undoped bismuth oxide.
Example 2
4.85g of bismuth nitrate pentahydrate is put into an alumina crucible to be annealed for 6 hours at 500 ℃ to prepare alpha-Bi2O3The product, 0.5g of the obtained alpha-Bi2O3The product is put into an alumina crucible, added with 0.5g of oxalic acid dihydrate powder, evenly mixed and annealed for 200min at 280 ℃ to prepare the carbon-doped bismuth oxide powder material.
Example 3
4.85g of bismuth nitrate pentahydrate is put into an alumina crucible to be annealed for 6 hours at 500 ℃ to prepare alpha-Bi2O3The product, 0.5g of the obtained alpha-Bi2O3The product is placed in aluminaAdding 1.0g of oxalic acid dihydrate powder into the crucible, uniformly mixing, and annealing at 280 ℃ for 50min to obtain the carbon-doped bismuth oxide powder material.
The foregoing embodiments illustrate the principles, principal features and advantages of the invention, and it will be understood by those skilled in the art that the invention is not limited to the foregoing embodiments, which are merely illustrative of the principles of the invention, and that various changes and modifications may be made therein without departing from the scope of the principles of the invention.
Claims (1)
1. A preparation method of a carbon-doped bismuth oxide photocatalytic material is characterized by comprising the following specific steps: putting bismuth nitrate pentahydrate into an alumina crucible, and annealing for 6 hours at 500 ℃ to prepare alpha-Bi2O3Powder material, and the prepared alpha-Bi2O3Placing the powder material in an alumina crucible, adding oxalic acid dihydrate powder, uniformly mixing, and annealing at 280 ℃ for 50-200 min to obtain the carbon-doped bismuth oxide photocatalytic material, wherein alpha-Bi is2O3The feeding mass ratio of the powder material to the oxalic acid dihydrate powder is 1: 1-1: 2.