CN108914581A - The surface treatment and EVA coating process of nylon fiber - Google Patents

The surface treatment and EVA coating process of nylon fiber Download PDF

Info

Publication number
CN108914581A
CN108914581A CN201810674731.2A CN201810674731A CN108914581A CN 108914581 A CN108914581 A CN 108914581A CN 201810674731 A CN201810674731 A CN 201810674731A CN 108914581 A CN108914581 A CN 108914581A
Authority
CN
China
Prior art keywords
fiber
eva
coating
treatment
treated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810674731.2A
Other languages
Chinese (zh)
Inventor
马海燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong New Silk Monofilament Polytron Technologies Inc
Original Assignee
Nantong New Silk Monofilament Polytron Technologies Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong New Silk Monofilament Polytron Technologies Inc filed Critical Nantong New Silk Monofilament Polytron Technologies Inc
Priority to CN201810674731.2A priority Critical patent/CN108914581A/en
Publication of CN108914581A publication Critical patent/CN108914581A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of surface treatment of nylon fiber and EVA coating processes to be surface-treated PA66 fiber or PA6 fiber using corona or plasma processing method；Then surface treated PA66 fiber or PA6 fiber further progress EVA coating treatment, EVA coating group are become：EVA is 95-99%, carbon black 1-5%；The process conditions of coating treatment are：Screw extruder temperature is 100 DEG C/110 DEG C/120 DEG C/130 DEG C/130 DEG C, and coating power is 10-40m/min.The present invention prepares simplicity, has excellent performance；It can be used as setline, tennis silk, conductive fiber etc.；Specifeca tion speeification：Electric conductivity reaches 105‑106Ω/cm, wire body is stiffening, and overhang length reaches 10-15cm.

Description

The surface treatment and EVA coating process of nylon fiber
Technical field
The present invention relates to a kind of surface treatment of nylon fiber and EVA coating processes.
Background technique
Existing nylon fiber has excellent mechanical property, function modified by achieving the purpose that in its surface covering, Its wearability, sea water resistance, against weather, stiffness are improved, it is expanded and uses field.
Summary of the invention
Simplicity is prepared the purpose of the present invention is to provide a kind of, the surface treatment for the nylon fiber haveing excellent performance and EVA are applied Layer method.
The technical solution of the invention is as follows：
A kind of surface treatment and EVA coating process of nylon fiber, it is characterized in that：By the PA66 fibre that diameter is 0.08-3.0 mm Dimension or PA6 fiber, are surface-treated using corona or plasma processing method, the work that corona, plasma-treated surface are handled Skill parameter is respectively：The processing voltage of corona is 10-20KV, processing power 1-30m/min；Plasma treatment frequency is 2- 40kHz, processing voltage are 8-16KV, processing power 6-10m/min；Then surface treated PA66 fiber or PA6 is fine Further progress EVA coating treatment is tieed up, EVA coating group becomes：EVA is 95-99%, carbon black 1-5%；The technique item of coating treatment Part is：Screw extruder temperature is 100 DEG C/110 DEG C/120 DEG C/130 DEG C/130 DEG C, and coating power is 10-40m/min.
The present invention prepares simplicity, has excellent performance；It can be used as extraordinary setline, tennis line, conductive fiber etc.；Main performance ginseng Number：Electric conductivity reaches 105-106Ω/cm, wire body is stiffening, and overhang length reaches 10-15cm.
Specific embodiment
A kind of surface treatment and EVA coating process of nylon fiber, by diameter be 0.08-3.0 mm PA66 fiber or PA6 fiber, is surface-treated using corona or plasma processing method, the technique ginseng that corona, plasma-treated surface are handled Number is respectively：The processing voltage of corona is 10-20KV, processing power 1-30m/min；Plasma treatment frequency is 2-40kHz, Processing voltage is 8-16KV, processing power 6-10m/min；Then by surface treated PA66 fiber or PA6 fiber into one Step carries out EVA coating treatment, and EVA coating group becomes：EVA is 95-99%, carbon black 1-5%；The process conditions of coating treatment are： Screw extruder temperature is 100 DEG C/110 DEG C/120 DEG C/130 DEG C/130 DEG C, and coating power is 10-40m/min.

Claims (1)

1. the surface treatment and EVA coating process of a kind of nylon fiber, it is characterized in that：The PA66 for being 0.08-3.0 mm by diameter Fiber or PA6 fiber, are surface-treated using corona or plasma processing method, and corona, plasma-treated surface are handled Technological parameter is respectively：The processing voltage of corona is 10-20KV, processing power 1-30m/min；Plasma treatment frequency is 2- 40kHz, processing voltage are 8-16KV, processing power 6-10m/min；Then surface treated PA66 fiber or PA6 is fine Further progress EVA coating treatment is tieed up, EVA coating group becomes：EVA is 95-99%, carbon black 1-5%；The technique item of coating treatment Part is：Screw extruder temperature is 100 DEG C/110 DEG C/120 DEG C/130 DEG C/130 DEG C, and coating power is 10-40m/min.
CN201810674731.2A 2018-06-27 2018-06-27 The surface treatment and EVA coating process of nylon fiber Pending CN108914581A (en)