CN108913286A - 一种机器人的胯部关节的润滑材料 - Google Patents
一种机器人的胯部关节的润滑材料 Download PDFInfo
- Publication number
- CN108913286A CN108913286A CN201810738349.3A CN201810738349A CN108913286A CN 108913286 A CN108913286 A CN 108913286A CN 201810738349 A CN201810738349 A CN 201810738349A CN 108913286 A CN108913286 A CN 108913286A
- Authority
- CN
- China
- Prior art keywords
- parts
- robot
- crotch joint
- polybenzoate
- triazolone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种机器人的胯部关节的润滑材料,它由以下重量份的原料制成:矿物油30‑40份,聚乙烯30‑40份,二硫化钼2‑4份,油酸甲酯10‑15份,石油磺酸钠2‑6份,***酮3‑6份,烷基酚聚氧乙烯醚2‑5份,有机硅氧烷1‑3份,聚四氟乙烯2‑3份,聚酰亚胺6‑12份,芳纶纤维6‑12份,聚苯酯3‑6份,锡青铜6‑12份。本发明的机器人的胯部关节的润滑材料具有良好的冷却性能、润滑性能、防锈性能、除油清洗功能、防腐功能,并且具备无毒、无味、对人体无侵蚀、对设备不腐蚀、对环境不污染等特点。
Description
技术领域
本发明属于材料技术领域,具体涉及一种机器人的胯部关节的润滑材料。
背景技术
随着现代工业化进程的加快,人们对生活中物质文化需求的增多,机器人也渐渐走入了人们的生活之中,机器人的关节处在金属拉伸过程中须使用一种保护液起润滑、清洗、冷却、抗腐等作用。随着国民经济的发展,电子通讯事业的发达,需求量越来越大。目前国内外用于润滑剂却不同程度地存在着下列问题:
1.产品稳定性差,有的夏天变质,冬天结块。
2.功能不全,如同时具有润滑、清洗、冷却、抗腐、防锈等。
3.有些产品不是水溶性的,有挥发性,在生产、使用过程中对人体和环境不同程度地存在毒害和污染等问题。
4.原材料范围窄,生产成本高。
发明内容
本发明的目的在于提供一种机器人的胯部关节的润滑材料。
本发明的目的可以通过以下技术方案实现:
一种机器人的胯部关节的润滑材料,它由以下重量份的原料制成:矿物油30-40份,聚乙烯30-40份,二硫化钼2-4份,油酸甲酯10-15份,石油磺酸钠2-6份,***酮3-6份,烷基酚聚氧乙烯醚2-5份,有机硅氧烷1-3份,聚四氟乙烯2-3份,聚酰亚胺6-12份,芳纶纤维6-12份,聚苯酯3-6份,锡青铜6-12份。
优选的,所述的一种机器人的胯部关节的润滑材料,它由以下重量份的原料制成:矿物油30份,聚乙烯40份,二硫化钼2份,油酸甲酯15份,石油磺酸钠2份,***酮6份,烷基酚聚氧乙烯醚2份,有机硅氧烷3份,聚四氟乙烯2份,聚酰亚胺6份,芳纶纤维12份,聚苯酯3份,锡青铜12份。
优选的,所述的一种机器人的胯部关节的润滑材料,它由以下重量份的原料制成:矿物油35份,聚乙烯35份,二硫化钼3份,油酸甲酯12份,石油磺酸钠3份,***酮5份,烷基酚聚氧乙烯醚3份,有机硅氧烷2份,聚四氟乙烯2份,聚酰亚胺10份,芳纶纤维10份,聚苯酯5份,锡青铜10份。
本发明的有益效果:本发明的机器人的胯部关节的润滑材料具有良好的冷却性能、润滑性能、防锈性能、除油清洗功能、防腐功能,并且具备无毒、无味、对人体无侵蚀、对设备不腐蚀、对环境不污染等特点。
具体实施方式
下面结合具体实施例对本发明作进一步详细描述。
实施例1:
一种机器人的胯部关节的润滑材料,它由以下重量份的原料制成:矿物油30份,聚乙烯30份,二硫化钼2份,油酸甲酯10份,石油磺酸钠2份,***酮3份,烷基酚聚氧乙烯醚2份,有机硅氧烷1份,聚四氟乙烯2份,聚酰亚胺6份,芳纶纤维6份,聚苯酯3份,锡青铜6份。
实施例2:
一种机器人的胯部关节的润滑材料,它由以下重量份的原料制成:矿物油40份,聚乙烯40份,二硫化钼4份,油酸甲酯15份,石油磺酸钠6份,***酮6份,烷基酚聚氧乙烯醚5份,有机硅氧烷3份,聚四氟乙烯3份,聚酰亚胺12份,芳纶纤维12份,聚苯酯6份,锡青铜12份。
实施例3:
一种机器人的胯部关节的润滑材料,它由以下重量份的原料制成:矿物油35份,聚乙烯35份,二硫化钼3份,油酸甲酯12份,石油磺酸钠3份,***酮5份,烷基酚聚氧乙烯醚3份,有机硅氧烷2份,聚四氟乙烯2份,聚酰亚胺10份,芳纶纤维10份,聚苯酯5份,锡青铜10份。
以上内容仅仅是对本发明所作的举例和说明,所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代,只要不偏离发明的构思或者超越本权利要求书所定义的范围,均应属于本发明的保护范围。
Claims (3)
1.一种机器人的胯部关节的润滑材料,其特征在于,它由以下重量份的原料制成:矿物油30-40份,聚乙烯30-40份,二硫化钼2-4份,油酸甲酯10-15份,石油磺酸钠2-6份,***酮3-6份,烷基酚聚氧乙烯醚2-5份,有机硅氧烷1-3份,聚四氟乙烯2-3份,聚酰亚胺6-12份,芳纶纤维6-12份,聚苯酯3-6份,锡青铜6-12份。
2.根据权利要求1所述的一种机器人的胯部关节的润滑材料,其特征在于,它由以下重量份的原料制成:矿物油30份,聚乙烯40份,二硫化钼2份,油酸甲酯15份,石油磺酸钠2份,***酮6份,烷基酚聚氧乙烯醚2份,有机硅氧烷3份,聚四氟乙烯2份,聚酰亚胺6份,芳纶纤维12份,聚苯酯3份,锡青铜12份。
3.根据权利要求1所述的一种机器人的胯部关节的润滑材料,其特征在于,它由以下重量份的原料制成:矿物油35份,聚乙烯35份,二硫化钼3份,油酸甲酯12份,石油磺酸钠3份,***酮5份,烷基酚聚氧乙烯醚3份,有机硅氧烷2份,聚四氟乙烯2份,聚酰亚胺10份,芳纶纤维10份,聚苯酯5份,锡青铜10份。