CN108912910A - A kind of mildew resistant paint - Google Patents
A kind of mildew resistant paint Download PDFInfo
- Publication number
- CN108912910A CN108912910A CN201810548023.4A CN201810548023A CN108912910A CN 108912910 A CN108912910 A CN 108912910A CN 201810548023 A CN201810548023 A CN 201810548023A CN 108912910 A CN108912910 A CN 108912910A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant paint
- mildew
- mildew resistant
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of mildew resistant paint, is related to building coating technical field, and composition material includes by weight：28-38 parts of pure acrylate elastic cream, 13-22 parts of acrylic emulsion, 5-15 parts of nano zine oxide, 8-16 parts of odium stearate, 2-8 parts of carbon black, 4-12 parts of mould inhibitor, 6-14 parts of camphor ball, 17-25 parts of lavender, 9-16 parts of peppermint grass, 8-17 parts of cinnamic acid, 8-17 parts of citronellal, 8-17 parts of citral, 8-15 parts of titanium dioxide, 14-22 parts of silica flour, 5-12 parts of calcium chloride, 14-20 parts of butyl acetate, 5-12 parts of ethyl cellulose, 8-16 parts of filler.Usefulness of the present invention is that have the material of mildew-proof effect by being added, and so that this coating is had mildew resistance, it is not easy to breed bacterium, clean hygiene.
Description
Technical field
The present invention relates to building coating technical field, especially a kind of mildew resistant paint.
Background technique
Coating, in the entitled paint of Chinese tradition.So-called coating be coated in the body surface being protected or decorated, and
The continuous film of firm attachment can be formed with coated article, usually based on resin or oil or lotion, add or do not add face
Material, filler add corresponding additive, the thick liquid being formulated with organic solvent or water.Chinese paint industry is more authoritative《It applies
Material technique》What one book was defined as：" coating is a kind of material, and this material can be coated in object with different construction technologies
Part surface forms and adheres to securely, with some strength, continuous solid film.The film common name film formed in this way, also known as paint film
Or coating."
Coating belongs to organic chemical industry's macromolecular material, is formed by film and belongs to high-molecular compound type.According to the modern times
The classification of current chemical products, coating belong to fine chemical product.Modern coating is gradually becoming a kind of multi-functional
Engineering material, be an important industry in chemical industry.The effect of coating mainly has at 4 points：Protection, decoration, covers up product
Defect and other special roles, promote the value of product.But the function of current coating is still relatively simple, is used in relative humidity
In the environment of, it is easy to cause the appearance of Signs of Mould, not only unsightly, also bacterium easy to breed.
Summary of the invention
The present invention overcomes the disadvantages of the prior art, provides a kind of mildew resistant paint, has mildew-proof effect by being added
Material makes this coating have mildew resistance, it is not easy to breed bacterium, clean hygiene.
In order to solve the above-mentioned technical problem, the present invention is achieved by the following technical solutions：
A kind of mildew resistant paint, composition material include by weight：28-38 parts of pure acrylate elastic cream, acrylic emulsion 13-22
Part, 5-15 parts of nano zine oxide, 8-16 parts of odium stearate, 2-8 parts of carbon black, 4-12 parts of mould inhibitor, 6-14 parts of camphor ball, lavender
17-25 parts, 9-16 parts of peppermint grass, 8-17 parts of cinnamic acid, 8-17 parts of citronellal, 8-17 parts of citral, 8-15 parts of titanium dioxide, stone
14-22 parts of English powder, 5-12 parts of calcium chloride, 14-20 parts of butyl acetate, 5-12 parts of ethyl cellulose, 8-16 parts of filler.
Preferably, a kind of mildew resistant paint, composition material include by weight：Pure acrylate elastic cream 33 parts, acrylic acid
18 parts of lotion, 10 parts of nano zine oxide, 12 parts of odium stearate, 6 parts of carbon black, 8 parts of mould inhibitor, 10 parts of camphor ball, lavender 22
Part, peppermint careless 13 parts, 12 parts of cinnamic acid, 12 parts of citronellal, 12 parts of citral, 10 parts of titanium dioxide, 18 parts of silica flour, calcium chloride 7
Part, 18 parts of butyl acetate, 7 parts of ethyl cellulose, 12 parts of filler.
Preferably, the mould inhibitor is 8-hydroxyquinoline.
Preferably, the filler is talcum powder.
Compared with prior art, the beneficial effects of the invention are as follows：
Cinnamic acid, citronellal and citral itself are provided with preferable sterilization, antimildew function, are added to this as raw material
In the production of coating, this coating is enabled to have bactericidal properties and mildew resistance, and be also added into mould inhibitor and camphor ball in the present invention,
Have certain mildew-proof effect, enhance the anti-mildew characteristic of this coating, be conducive to keep health, in addition, be also added into lavender and
Peppermint grass has the function that pure and fresh, purification air.
Specific embodiment
Hereinafter, preferred embodiments of the present invention will be described, it should be understood that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
The production method of this mildew resistant paint is, (1) is by camphor ball, lavender, peppermint grass, cinnamic acid, citronellal, lemon
Aldehyde, silica flour, calcium chloride are put the mixture into a stirrer, and stir 20min with the speed of 50r/min, spare；(2) that pure acrylate elastic is newborn,
Acrylic emulsion, nano zine oxide, odium stearate, carbon black, mould inhibitor, titanium dioxide, butyl acetate, ethyl cellulose, filler are mixed
After conjunction, with 50 DEG C of preheating 15min, then step (1) material is poured into, 40min is stirred with the speed of 35r/min.
Formula is selected as follows：
Embodiment 1
35 parts of pure acrylate elastic cream, 10 parts of nano zine oxide, 12 parts of odium stearate, 6 parts of carbon black, is prevented 18 parts of acrylic emulsion
Mould dose 8 parts, 10 parts of camphor ball, 22 parts of lavender, peppermint careless 12 parts, 12 parts of cinnamic acid, 13 parts of citronellal, 13 parts of citral, titanium
11 parts of white powder, 18 parts of silica flour, 8 parts of calcium chloride, 18 parts of butyl acetate, 9 parts of ethyl cellulose, 10 parts of filler.
Embodiment 2
38 parts of pure acrylate elastic cream, 15 parts of nano zine oxide, 16 parts of odium stearate, 8 parts of carbon black, is prevented 22 parts of acrylic emulsion
Mould dose 12 parts, 14 parts of camphor ball, 25 parts of lavender, peppermint careless 16 parts, 17 parts of cinnamic acid, 17 parts of citronellal, 17 parts of citral, titanium
15 parts of white powder, 22 parts of silica flour, 12 parts of calcium chloride, 20 parts of butyl acetate, 12 parts of ethyl cellulose, 16 parts of filler.
Embodiment 3
It is 28 parts of pure acrylate elastic cream, 13 parts of acrylic emulsion, 5 parts of nano zine oxide, 8 parts of odium stearate, 2 parts of carbon black, mould proof
4 parts of agent, 6 parts of camphor ball, 17 parts of lavender, peppermint grass 9 parts, 8 parts of cinnamic acid, 8 parts of citronellal, 8 parts of citral, 8 parts of titanium dioxide,
14 parts of silica flour, 5 parts of calcium chloride, 14 parts of butyl acetate, 5 parts of ethyl cellulose, 8 parts of filler.
Finally it should be noted that：These are only the preferred embodiment of the present invention, is not intended to restrict the invention, although
Referring to embodiment, invention is explained in detail, for those skilled in the art, still can be to aforementioned
Technical solution documented by each embodiment is modified or equivalent replacement of some of the technical features, but it is all
Within the spirit and principles in the present invention, any modification, equivalent replacement, improvement and so on should be included in protection of the invention
Within the scope of.
Claims (4)
1. a kind of mildew resistant paint, which is characterized in that composition material includes by weight：28-38 parts of pure acrylate elastic cream, propylene yogurt
13-22 parts of liquid, 5-15 parts of nano zine oxide, 8-16 parts of odium stearate, 2-8 parts of carbon black, 4-12 parts of mould inhibitor, camphor ball 6-14
Part, 17-25 parts of lavender, 9-16 parts of peppermint grass, 8-17 parts of cinnamic acid, 8-17 parts of citronellal, 8-17 parts of citral, titanium dioxide 8-
15 parts, 14-22 parts of silica flour, 5-12 parts of calcium chloride, 14-20 parts of butyl acetate, 5-12 parts of ethyl cellulose, 8-16 parts of filler.
2. a kind of mildew resistant paint according to claim 1, which is characterized in that composition material includes by weight：Pure C bullet
Property newborn 33 parts, 18 parts of acrylic emulsion, 10 parts of nano zine oxide, 12 parts of odium stearate, 6 parts of carbon black, 8 parts of mould inhibitor, camphor ball
10 parts, 22 parts of lavender, peppermint careless 13 parts, 12 parts of cinnamic acid, 12 parts of citronellal, 12 parts of citral, 10 parts of titanium dioxide, silica flour
18 parts, 7 parts of calcium chloride, 18 parts of butyl acetate, 7 parts of ethyl cellulose, 12 parts of filler.
3. a kind of mildew resistant paint according to claim 1 or 2, which is characterized in that the mould inhibitor is 8-hydroxyquinoline.
4. a kind of mildew resistant paint according to claim 1 or 2, which is characterized in that the filler is talcum powder.