CN108912901A - A kind of heat insulation coating and preparation method thereof - Google Patents
A kind of heat insulation coating and preparation method thereof Download PDFInfo
- Publication number
- CN108912901A CN108912901A CN201710236525.9A CN201710236525A CN108912901A CN 108912901 A CN108912901 A CN 108912901A CN 201710236525 A CN201710236525 A CN 201710236525A CN 108912901 A CN108912901 A CN 108912901A
- Authority
- CN
- China
- Prior art keywords
- heat insulation
- insulation coating
- heat
- preparation
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of heat insulation coating and preparation method thereof is suitable for various vehicles, ship, all kinds of tanks in petrochemical industry, slot, pipeline appearance and the exterior wall of all kinds of buildings, tent, the appearance of paulin is heat-insulated, decoration coating uses；It joined the mica powder to ultraviolet light, visible light, the infrared ray in sunlight with fabulous reflecting barrier effect of 1-10% in heat insulation coating of the present invention, with the hollow ceramic heat-barrier material of 1-30%, it forms one layer of fine and close vacuum layer in the object surface being coated, and can effectively completely cut off the conduction of heat radiation in solar radiation heat and air；This heat insulation coating heat reflectivity is up to 89% or more, thermal coefficient is only 0.03, under equal conditions compared with non-this heat insulation coating of coating, body surface temperature declines 10-20 degree, interior of articles temperature declines 4-10 degree, this heat insulation coating has good weatherability, wearability, waterproofness, self-cleaning.
Description
Technical field
The present invention relates to appearances such as all kinds of tanks, slot, pipelines in various vehicles, ship, petrochemical industry and all kinds of build
Build the inner-outer wall of object, the coating that tent, the appearance heat insulation sun of paulin, decoration coating use, a kind of heat insulation coating and its
Preparation method.
Background technique
Existing vehicle, ship, the metal car body of petrochemical industry, hull, tank, slot, pipeline and all kinds of buildings it is inside and outside
What wall, tent for various purposes, paulin coating generallyd use is acrylic coating, aluminium paint, phenolic paint, this paint every
Hot sun-screening function is very poor, and sunlight makes body surface absorb a large amount of thermal energy by way of radiation, conduction, convection current, is transmitted to
Interior of articles increases vehicle, tank, slot, pipeline, all kinds of interior of building temperature, and people must not arrange without mandatory cooling
It applies, such as water drenching, does so not only waste of energy, but also be unfavorable for ecological environment.
Summary of the invention
It, can be in effective reflected sunlight the object of the present invention is to provide a kind of heat insulation coating and preparation method thereof
Ultraviolet light, visible light, infrared ray, completely cut off the conduction of heat radiation in the radiant heat and air of sunlight, and have it is good it is acidproof,
Alkaline-resisting, wear-resisting, waterproof, heat insulating function.
The present invention, which adopts the following technical scheme that, realizes foregoing invention purpose：
Heat insulation coating Ingredient Wt percentage of the present invention is：
Film forming agent 10-40%
Hollow ceramic heat-barrier material 1.0-30%
Mica powder 1.0-10%
Filler 5.0-30%
Pigment 0.5-5.0%
Auxiliary agent 0.5-3.0%
Solvent 30-70%
The main ingredient of hollow ceramic heat-barrier material in described heat insulation coating and preparation method thereof is silica, three
The hollow ceramic particle of Al 2 O, particle diameter are 1-400 μm, and this material has hollow ceramic microspheres, White hollow glass
Glass microballon, hollow ceramic bubble are vacuum shape or for the blister containing inert gas inside hollow ceramic heat-barrier material.
The particle diameter of mica powder in described heat insulation coating and preparation method thereof is 1-400 μm.
Film forming agent in described heat insulation coating and preparation method thereof uses acrylic emulsion, pure-acrylic emulsion, phenylpropyl alcohol
Lotion, organosilicon-modified acrylic emulsion, fluorine carbon emulsion.
Filler in described heat insulation coating and preparation method thereof uses titanium dioxide, talcum powder, precipitated calcium carbonate, height
Ridge soil.
Solvent in described heat insulation coating and preparation method thereof uses ethylene glycol, dimethylbenzene, water.
Pigment in described heat insulation coating and preparation method thereof uses inorganic pigment and organic pigment.
Auxiliary agent in described heat insulation coating and preparation method thereof uses dispersing agent and defoaming agent.
Mica powder in described heat insulation coating and preparation method thereof, can be ultraviolet in effective reflected sunlight
Line, visible light, infrared ray, the radiant heat energy of reflected sunlight can be in heat insulation coatings of the present invention according to different purposes
The mica powder of different weight is added.
Hollow ceramic heat-barrier material in described heat insulation coating and preparation method thereof forms one layer in body surface
Fine and close vacuum layer or layer of inert effectively completely cuts off the conduction of heat radiation in solar radiation heat and air；According to different
The hollow ceramic heat-barrier material of different weight can be added in purposes in heat insulation coating of the present invention.
Described heat insulation coating and preparation method thereof is suitable for doing the Ingredient Wt percentage of intermediate coat to be：
Film forming agent 10-40%
Hollow ceramic heat-barrier material 10-30%
Mica powder 5.0-10%
Filler 5.0-30%
Pigment 0.5-3.0%
Auxiliary agent 0.2-3.0%
Solvent 30-70%
Described heat insulation coating and preparation method thereof is suitable for doing the Ingredient Wt percentage of finishing coat to be：
Film forming agent 10-40%
Hollow ceramic heat-barrier material 1.0-20%
Mica powder 1.0-10%
Filler 5.0-15%
Pigment 1.0-5.0%
Auxiliary agent 0.5-3.0%
Solvent 30-70%
Described heat insulation coating and preparation method thereof be by required composition through premixing, emulsion dispersion, toning, grinding,
Finished product is obtained by filtration.
By adopting the above-described technical solution, the present invention has following good effect：
Described heat insulation coating and preparation method thereof due in coating be added in sunlight ultraviolet light, visible light,
Infrared ray has the mica powder of fabulous shield effectiveness, can ultraviolet light, visible light, infrared ray in effective reflected sunlight, instead
Rate is penetrated up to 89% or more.
Described heat insulation coating and preparation method thereof can applied since hollow ceramic heat-barrier material being added in coating
It fills body surface and forms one layer of fine and close vacuum layer or layer of inert, it is effective to completely cut off hot spoke in solar radiation heat and air
The conduction penetrated, thermal coefficient are only 0.03.
Described heat insulation coating and preparation method thereof, the coating on canister or metallic conduit, under equal conditions
Compared with non-this heat insulation coating of coating, body surface temperature difference 10-20 degree, interior of articles temperature difference 4-10 degree, and
And sunlight is stronger, environment temperature is higher, this heat insulation coating heat insulation sun effect is better.
Described heat insulation coating and preparation method thereof have good weatherability, wearability, waterproofness, self-cleaning and
Excellent painting effect, preparation method is simple, room temperature drying in 1 hour, easy for construction；Can be widely used in all kinds of buildings,
Petroleum, the metal can of chemical industry, slot, pipeline, the appearance coating of automobile, train, ship.
Specific embodiment one：
Match coating by following weight percentages：
Pure-acrylic emulsion 20%
Hollow ceramic microspheres 10%
Mica powder 3.0%
Filler 11%
Pigment 1.0%
Auxiliary agent 1.0%
Solvent 54%
This coating is prepared, all components are got product through premixing, emulsion dispersion, toning, grinding, filtering.
The present embodiment coating can be used as intermediate coat use
Specific embodiment two：
Match coating by following weight percentages：
Styrene-acrylic emulsion 25%
Hollow ceramic bubble 12%
Mica powder 2.0%
Filler 10%
Pigment 0.5%
Auxiliary agent 0.5%
Solvent 50%
This coating is prepared, all components are got product through premixing, emulsion dispersion, toning, grinding, filtering.
The present embodiment coating can be used as intermediate coat use
Specific embodiment three：
Match coating by following weight percentages：
Fluorine carbon emulsion 20%
Hollow ceramic bubble 15%
Mica powder 3.0%
Filler 11%
Pigment 1.0%
Auxiliary agent 1.0%
Solvent 49%
This coating is prepared, all components are got product through premixing, emulsion dispersion, toning, grinding, filtering.
The present embodiment coating can be used as intermediate coat use
Specific embodiment four：
Match coating by following weight percentages：
Pure acrylate elastic emulsion 25%
Hollow ceramic bubble 3.0%
Mica powder 2.0%
Filler 13%
Pigment 2.0%
Auxiliary agent 1.0%
Solvent 56%
This coating is prepared, all components are got product through premixing, emulsion dispersion, toning, grinding, filtering.
The present embodiment coating can be used as finishing coat use
Specific embodiment five：
Match coating by following weight percentages：
Fluorine carbon emulsion 15%
Hollow ceramic bubble 3.0%
Mica powder 3.0%
Filler 12%
Pigment 1.0%
Auxiliary agent 2.0%
Solvent 64%
This coating is prepared, all components are got product through premixing, emulsion dispersion, toning, grinding, filtering.
The present embodiment coating can be used as finishing coat use
Specific embodiment six：
Match coating by following weight percentages：
Organosilicon-modified acrylic emulsion 30%
Hollow ceramic bubble 3.0%
Mica powder 3.0%
Filler 11%
Pigment 2.0%
Auxiliary agent 1.0%
Solvent 50%
This coating is prepared, all components are got product through premixing, emulsion dispersion, toning, grinding, filtering.
The present embodiment coating can be used as finishing coat use.
Claims (6)
1. a kind of heat insulation coating and preparation method thereof, heat insulation coating Ingredient Wt percentage are：Film forming agent 10-
40%, filler 5.0-30%, pigment 0.5-5.0%, auxiliary agent 0.5-3.0%, solvent 30-70%；It is characterized in that：This every
It joined hollow ceramic heat-barrier material that weight percent is 1.0-30% in hot Sunscreen paint composition and weight percent be
The mica powder of 1.0-10%.
2. heat insulation coating according to claim 1 and preparation method thereof, it is characterised in that：The heat insulation sun
Coating composition weight percent is：Film forming agent 10-40%, hollow ceramic heat-barrier material 1.0- 30%, mica powder 1.0-10%,
Filler 5.0-30%, pigment 0.5-5.0%, auxiliary agent 0.5-3.0%, solvent 30-70%.
3. heat insulation coating according to claim 1 and preparation method thereof, it is characterised in that：The hollow ceramic
The main ingredient of heat-barrier material is silica, aluminum oxide, and inside is vacuum shape or inert gas filled hollow ceramic
Material.
4. heat insulation coating according to claim 1 and preparation method thereof, it is characterised in that：The hollow ceramic
The particle diameter of heat-barrier material is 1-400 μm.
5. heat insulation coating according to claim 1 and preparation method thereof, it is characterised in that：The mica powder
Particle diameter is 1-400 μm.
6. implementing heat insulation coating and preparation method thereof described in claim 1, it is characterised in that：The heat insulation sun
The preparation method of coating, operational sequence be by film forming agent, hollow ceramic heat-barrier material, mica powder, filler, pigment, auxiliary agent,
Finished product is made through premixing, emulsion dispersion, toning, grinding, filtering in solvent.