CN108912802A - Bentonite activity thickens anti-settling rheological agent and preparation method thereof - Google Patents
Bentonite activity thickens anti-settling rheological agent and preparation method thereof Download PDFInfo
- Publication number
- CN108912802A CN108912802A CN201810947901.XA CN201810947901A CN108912802A CN 108912802 A CN108912802 A CN 108912802A CN 201810947901 A CN201810947901 A CN 201810947901A CN 108912802 A CN108912802 A CN 108912802A
- Authority
- CN
- China
- Prior art keywords
- grams
- bentonite
- thickens
- reactor tank
- rheological agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Bentonite activity thickens anti-settling rheological agent, by raw material weight ratio:Highly purified bentonite 100 of the granularity less than 50 microns, octadecyltrimethylammonium chloride 15~20, stearyl dimethyl benzyl ammonium chloride 15~20, deionized water 200~300 is aggregated dries;Bentonite activity thickens the preparation method of anti-settling rheological agent, and its step are as follows:1), by raw material stirring and emulsifying 20~30 minutes;2), reactor tank be warming up to 60~80 DEG C be stirred for 20~30 minutes;3), reactor tank heats up 100 DEG C to be stirred into raw material in reactor tank thick and is dried into block stock, 4), block stock be ground into powder of the granularity less than 58 microns get product.It is suitable for the swelling native produce of current sealing wax system, and thickening result of prevention is good.
Description
Technical field
The present invention relates to rheological agent technical fields, more specifically to a kind of rheological agent that can play thickening result of prevention
And preparation method thereof.
Background technique
The organic solvent volatilization of solvent based coating is the main cause that coating industry causes atmosphere pollution.For this purpose, the science and technology of country
Long-and Medium-term Development planning, it was also proposed that widely popularize and use environmentally friendly sealing wax.Many policies and regulations relevant to sealing wax go out at present
Nowadays platform mostly is being proposed the explicit order forbidden from suggesting to limitation.In view of such status, my company is started to develop
Suitable for the swelling native produce of current sealing wax system, dicyandiamide solution usual in sealing wax formula is the mixing of alcohol ether and water at present
Solvent, and tradition is organic or aqueous bentonite cannot all play the role of effectively thickening in this mixed solvent system it is anti-settling.
Summary of the invention
The purpose of the present invention is to the deficiencies of the prior art, and provide bentonite activity and thicken anti-settling rheological agent, it
Suitable for the swelling native produce of current sealing wax system, it is good to thicken result of prevention.
Technology solution of the invention is as follows:
Bentonite activity thickens anti-settling rheological agent, by raw material weight ratio:Highly purified bentonite 100 of the granularity less than 50 microns
Gram, 15~20 grams of octadecyltrimethylammonium chloride, 15~20 grams of stearyl dimethyl benzyl ammonium chloride, deionized water 200
~300 grams aggregated to dry;The highly purified bentonitic purity is not less than 99% by mass, product chemical index
It is as follows:
Appearance:The flowable sprills of white;Fugitive constituent (105 DEG C, 2 hours):≤3.5%;
Granularity (<76 μm or 200 mesh):≥98%;
Specific gravity(25℃):1.6;
Calcination loss (850-900 DEG C):≤40%;
15% colloid viscosity(Butyl glycol ether:Water=1:1 mixed solvent)≥3000mpa.s.
Bentonite activity thickens the preparation method of anti-settling rheological agent, and its step are as follows:
1), claim that 100 grams of highly purified bentonite, octadecyltrimethylammonium chloride are added into stainless steel reaction tank by weight
15~20 grams, 15~20 grams of stearyl dimethyl benzyl ammonium chloride, 200~300 grams of deionized water, 20~30 points of stirring and emulsifying
Clock;
2), reactor tank be warming up to 60~80 DEG C be stirred for 20~30 minutes;
3), by reactor tank heating 100 DEG C raw material in reactor tank stirred into thick and be dried into block stock;
4), block stock be ground into powder of the granularity less than 58 microns get product.
The beneficial effects of the present invention are:
It is suitable for the swelling native produce of current sealing wax system, and thickening result of prevention is good.
Specific embodiment
Embodiment:Bentonite activity thickens anti-settling rheological agent, by raw material weight ratio:Granularity is highly purified less than 50 microns
100 grams of bentonite, 15~20 grams of stearyl dimethyl benzyl ammonium chloride, is gone at 15~20 grams of octadecyltrimethylammonium chloride
200~300 grams of ionized water aggregated to dry;The highly purified bentonitic purity is not less than 99% by mass, product
Chemical index is as follows:
Appearance:The flowable sprills of white;Fugitive constituent (105 DEG C, 2 hours):≤3.5%;
Granularity (<76 μm or 200 mesh):≥98%;
Specific gravity(25℃):1.6;
Calcination loss (850-900 DEG C):≤40%;
15% colloid viscosity(Butyl glycol ether:Water=1:1 mixed solvent)≥3000mpa.s.
Bentonite activity thickens the preparation method of anti-settling rheological agent, and its step are as follows:
1), claim that 100 grams of highly purified bentonite, octadecyltrimethylammonium chloride are added into stainless steel reaction tank by weight
15~20 grams, 15~20 grams of stearyl dimethyl benzyl ammonium chloride, 200~300 grams of deionized water, 20~30 points of stirring and emulsifying
Clock;
2), reactor tank be warming up to 60~80 DEG C be stirred for 20~30 minutes;
3), by reactor tank heating 100 DEG C raw material in reactor tank stirred into thick and be dried into block stock;
4), block stock be ground into powder of the granularity less than 58 microns get product.
The product inspection report produced according to the above method see the table below:
Hangzhou Hai Disi new material Co., Ltd
Examination and test of products report
Number:Q/HDS04—12—10
Claims (2)
1. bentonite activity thickens anti-settling rheological agent, it is characterised in that:By raw material weight ratio:Height of the granularity less than 50 microns mentions
100 grams of pure bentonite, 15~20 grams of octadecyltrimethylammonium chloride, 15~20 grams of stearyl dimethyl benzyl ammonium chloride,
200~300 grams of deionized water aggregated to dry;The highly purified bentonitic purity is not less than 99% by mass, produces
Product chemical index is as follows:
Appearance:The flowable sprills of white;Fugitive constituent (105 DEG C, 2 hours):≤3.5%;
Granularity (<76 μm or 200 mesh):≥98%;
Specific gravity(25℃):1.6;
Calcination loss (850-900 DEG C):≤40%;
15% colloid viscosity(Butyl glycol ether:Water=1:1 mixed solvent)≥3000mpa.s.
2. the preparation method that bentonite activity thickens anti-settling rheological agent, it is characterised in that:Its step are as follows:
1. claiming that 100 grams of highly purified bentonite, octadecyltrimethylammonium chloride are added into stainless steel reaction tank by weight
15~20 grams, 15~20 grams of stearyl dimethyl benzyl ammonium chloride, 200~300 grams of deionized water, 20~30 points of stirring and emulsifying
Clock;
2. reactor tank is warming up to 60~80 DEG C to be stirred for 20~30 minutes;
Raw material in reactor tank is stirred into thick and is dried into block stock 3. reactor tank is heated up 100 DEG C,
4. block stock is ground into powder of the granularity less than 58 microns to get product.