CN108911807A - 一种河道淤泥分类处理的方法 - Google Patents
一种河道淤泥分类处理的方法 Download PDFInfo
- Publication number
- CN108911807A CN108911807A CN201811128082.2A CN201811128082A CN108911807A CN 108911807 A CN108911807 A CN 108911807A CN 201811128082 A CN201811128082 A CN 201811128082A CN 108911807 A CN108911807 A CN 108911807A
- Authority
- CN
- China
- Prior art keywords
- mud
- riverway sludge
- surface layer
- classification processing
- completion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及淤泥处理技术领域，更具体地，涉及一种河道淤泥分类处理的方法。将河道淤泥按表层淤泥和底层淤泥分类开采，对表层淤泥进行分拣除杂，再与木屑按一定比例混合后堆肥处理；将底层污泥脱水，与辅料混合造粒成型，经干燥后进行微波烧结，冷却至常温后得到陶粒。本发明将河道淤泥分类处理资源化，具有针对性，并使其得到有效利用，从而得到肥料和陶粒，具有良好的经济社会效益。
Description
技术领域
本发明涉及淤泥处理技术领域，更具体地，涉及一种河道淤泥分类处理的方法
背景技术
随着我国工业发展和人民生活水平的提高，河道作为纳污水体，需要接收大量生活污水和工业废水，造成河道污染日益严重，河道淤泥增厚，微生物大量繁殖，造成河水变黑发臭；同时，大量生活生产垃圾入河，也造成河床抬高，河道水面积下降，防洪排涝能力下降，因而严重危害着人民的健康与安全。
常用的淤泥处置方式有海洋处置、填埋、焚烧以及资源化利用(堆肥、吹填造陆、建材利用等)。而绝大部分的河道淤泥主要由石英、黏土类矿物、长石类矿物组成，与粘土成分相似，同时，部分污染严重的淤泥含有较高的有机质、N、P、K及其他植物生长所需的微量元素，因此淤泥资源化利用，才是淤泥处理处置的最适合方式。
淤泥表层常有藻类活体、浮游动植物、死亡藻类、动植物残骸、生活垃圾以及油脂等，故一般淤泥表层0～25cm处营养盐含量普遍较高，表聚性明显。且随着淤泥深度增加，营养盐含量明显下降。而表层淤泥以下的底层淤泥其矿物组成与粘土相似。传统的淤泥资源化方式并不能充分地针对性地利用淤泥资源，因此，将河道淤泥分为表层和底层淤泥，进行资源化利用处理显得更加科学合理。
发明内容
本发明为克服上述现有技术所述的至少一种缺陷，提供一种河道淤泥分类处理的方法，具有针对性地、有效性地处理河道淤泥，从而得到肥料和陶粒，具有良好的经济社会效益。
为解决上述技术问题，本发明采用的技术方案是：一种河道淤泥分类处理的方法，包括有以下步骤：
S1：将河道淤泥按照表层淤泥和底层淤泥进行分类开采；
S2：步骤1完成后，将表层淤泥进行分拣除杂，去除塑料、玻璃等杂物；
S3：步骤2完成后，将表层淤泥、木屑与堆肥腐熟料按一定比例混合均匀形成堆肥物料，使堆肥物料的C/N(即：有机碳总量和有机氮总量)比为(25～35)∶1，含水率为55％～65％；
S4：步骤3完成后，将堆肥物料送入堆肥设备进行好氧发酵，得到肥料；
S5：步骤1完成后，将底层淤泥进行脱水处理，控制含水率在30～35％之间
S6：步骤5完成后，将底层淤泥与辅料按一定比例充分混合，并经成型机造粒成型；
S7：步骤6完成后，将成型颗粒放入烘箱，105℃干燥24h，然后放入微波烧结炉进行微波烧结，冷却至室温后得到陶粒。
所述的分类以开挖深度为界，开挖深度为20～30cm的是表层淤泥，表层淤泥以下部分为底层淤泥。
所述淤泥、木屑与堆肥腐熟料的质量比为8:1:1。
所述辅料为烧结助剂，可为碳化硅、氧化铁、氧化镁、四氧化三铁等微波敏感介质中的一种或几种所组成的混合物，其添加比例为1％～3％。
所述微波烧结的温度为1000～1200℃，保温时间为10～20min。
本发明中，将淤泥分类处理，一方面，表层淤泥含有较高的有机质、N、P、K及其他植物生长所需的微量元素，适用于堆肥处理，其堆肥后产物应用于园林绿化，具有较高的实用性。同时加入木屑，能够解决淤泥堆肥碳源不足的问题，调整堆肥物料至合适的堆肥条件。
另一方面，底层淤泥有机质含量较低，但有丰富的矿物组成，主要有SiO2、Al2O3、Fe2O3等，与粘土成分极为相似，采用能源利用率高、加热效率高、对环境友好的微波烧结技术，能够高效低耗地处理底层淤泥，并使其资源化，缓解了粘土资源的紧缺。且底层淤泥低有机质，能够减少烧失量以及降低因有机物分解产气形成的孔隙率，从而防止陶粒强度的降低。同时，加入碳化硅、氧化铁、氧化镁、四氧化三铁等微波敏感介质，一是作为烧结助剂，降低烧结所需温度，二是作为微波耦合剂，吸收微波能，提高升温速度以及烧结温度。
本发明的有益效果是：实现河道淤泥分类处理资源化，通过不同开挖深度分为表层淤泥和底层淤泥，使淤泥更具有针对性地采取有效的处理技术，并根据淤泥不同的化学组成，对表层淤泥采取堆肥处理，底层淤泥微波烧结处理。改变传统的表层底层淤泥混合处理方式，且根据分层后淤泥性质改变调整到最优反应参数，得到肥料和陶粒，从而实现污染物处理与资源化的目的，具有较高的经济社会效益。
附图说明
图1是本发明在实施例中方法步骤示意图。
具体实施方式
附图仅用于示例性说明，不能理解为对本发明的限制；为了更好说明本实施例，附图某些部件会有省略、放大或缩小，并不代表实际产品的尺寸；对于本领域技术人员来说，附图中某些公知结构及其说明可能省略是可以理解的。附图中描述位置关系仅用于示例性说明，不能理解为对本发明的限制。
实施例1
如图1所示，本发明提供一种河道淤泥分类处理的方法，包括有以下步骤：
S1：将河道淤泥按照表层淤泥和底层淤泥进行分类开采；
S2：步骤1完成后，将表层淤泥进行分拣除杂，去除塑料、玻璃等杂物；
S3：步骤2完成后，将表层淤泥、木屑与堆肥腐熟料按一定比例混合均匀形成堆肥物料，使堆肥物料的C/N比为(25～35)∶1，含水率为55％～65％；
S4：步骤3完成后，将堆肥物料送入堆肥设备进行好氧发酵，得到肥料；
S5：步骤1完成后，将底层淤泥进行脱水处理，控制含水率在30～35％之间
S6：步骤5完成后，将底层淤泥与辅料按一定比例充分混合，并经成型机造粒成型；
S7：步骤6完成后，将成型颗粒放入烘箱，105℃干燥24h，然后放入微波烧结炉进行微波烧结，冷却至室温后得到陶粒。
在步骤S1中，分类以开挖深度为界，开挖深度为30cm的是表层淤泥，30cm以下部分为底层淤泥。
再按照表层淤泥、木屑与堆肥腐熟料的质量比为8:1:1混合均匀形成堆肥物料，使堆肥物料的C/N比为(25～35)∶1，含水率为55％～65％；堆肥发酵30天，得到腐熟料。
而按照底层淤泥98％，四氧化三铁2％的比例进行造粒干燥，微波烧结，控制烧结温度为1100℃，保温时间为20min，冷却至室温得到陶粒。
实施例2
本实施例中，提供一种河道淤泥分类处理的方法，具体方法为：
将河道淤泥按照开挖深度进行分类开采，开挖深度为25cm的是表层淤泥，25cm以下部分为底层淤泥；
将表层淤泥进行分拣除杂，去除塑料、玻璃等杂物后，按照表层淤泥、木屑与堆肥腐熟料的质量比为7:2:1混合均匀形成堆肥物料，使堆肥物料的C/N比为(25～35)∶1，含水率为55％～65％；将堆肥物料送入堆肥设备进行好氧发酵，堆肥发酵35天，得到腐熟料。
将底层淤泥进行脱水处理，控制含水率在30～35％之间，按照底层淤泥98％，四氧化三铁2％的比例进行充分混合，并经成型机造粒成型，105℃干燥24h，然后放入微波烧结炉进行微波烧结，控制烧结温度为1200℃，保温时间为10min，冷却至室温得到陶粒。
以此实现河道淤泥分类处理资源化，通过不同开挖深度分为表层淤泥和底层淤泥，使淤泥更具有针对性地采取有效的处理技术，并根据淤泥不同的化学组成，对表层淤泥采取堆肥处理，底层淤泥微波烧结处理。改变传统的表层底层淤泥混合处理方式，且根据分层后淤泥性质改变调整到最优反应参数，得到肥料和陶粒，从而实现污染物处理与资源化的目的，具有较高的经济社会效益。
显然，本发明的上述实施例仅仅是为清楚地说明本发明所作的举例，而并非是对本发明的实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明权利要求的保护范围之内。
Claims (6)
1.一种河道淤泥分类处理的方法，其特征在于，包括有以下步骤：
S1：将河道淤泥按照表层淤泥和底层淤泥进行分类开采；
S2：步骤1完成后，将表层淤泥进行分拣除杂，去除塑料、玻璃等杂物；
S3：步骤2完成后，将表层淤泥、木屑与堆肥腐熟料按一定比例混合均匀形成堆肥物料，使堆肥物料的C/N比为(25～35)∶1，含水率为55％～65％；
S4：步骤3完成后，将堆肥物料送入堆肥设备进行好氧发酵，得到肥料；
S5：步骤1完成后，将底层淤泥进行脱水处理，控制含水率在30～35％之间；
S6：步骤5完成后，将底层淤泥与辅料按一定比例充分混合，并经成型机造粒成型；
S7：步骤6完成后，将成型颗粒放入烘箱，105℃干燥24h，然后放入微波烧结炉进行微波烧结，冷却至室温后得到陶粒。
2.根据权利要求1所述的一种河道淤泥分类处理的方法，其特征在于，步骤S1中，表层淤泥开挖深度为20～30cm，底层淤泥开挖深度为表层淤泥高度以下。
3.根据权利要求1所述的一种河道淤泥分类处理的方法，其特征在于，步骤S3中，淤泥、木屑与堆肥腐熟料以质量比为8:1:1进行混匀发酵。
4.根据权利要求1所述的一种河道淤泥分类处理的方法，其特征在于，辅料为烧结助剂，为碳化硅、氧化铁、氧化镁、四氧化三铁等微波敏感介质中的一种或几种所组成的混合物。
5.根据权利要求1所述的一种河道淤泥分类处理的方法，其特征在于，辅料的添加比例为1％～3％。
6.根据权利要求1所述的一种河道淤泥分类处理的方法，其特征在于，步骤S7中，所述微波烧结的温度为1000～1200℃，保温时间为10～20min。