CN108868038A - Fire prevention, high temperature resistant porcelain aluminium sheet - Google Patents
Fire prevention, high temperature resistant porcelain aluminium sheet Download PDFInfo
- Publication number
- CN108868038A CN108868038A CN201810722674.0A CN201810722674A CN108868038A CN 108868038 A CN108868038 A CN 108868038A CN 201810722674 A CN201810722674 A CN 201810722674A CN 108868038 A CN108868038 A CN 108868038A
- Authority
- CN
- China
- Prior art keywords
- aluminium sheet
- layer
- sandblasting
- porcelain
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses fire prevention,High temperature resistant porcelain aluminium sheet,Including aluminium sheet,The surface of the aluminium sheet is coated with sandblasting layer,The surface of sandblasting layer is coated with prime coat,The surface of the prime coat is coated with porcelain layer,The substrate thickness of the aluminium sheet is 2.0mm-3.5mm,Sandblasting mode uses air pressure sandblasting,And the sandblasting layer male and fomale(M&F) of surface of aluminum plate is with a thickness of 0.5mm-1.0mm,Basecoat paint fire resistant coating,Base coat thickness is 30 μm -150 μm,The porcelain layer with a thickness of 10 μm -40 μm,Porcelain layer is inorganic resin layer,The ingredient of inorganic resin includes nanoscale Aluminum sol colloidal solution and acrylic resin aqueous solution,Inorganic resin is by Aluminum sol colloidal solution 5%-10%,Acrylic resin aqueous solution 90%-95% mixing match forms,The present invention has superior adhesion strength and shock resistance compared to traditional fluorine carbon aluminium sheet,The inorganic porcelain layer of porcelain surface of aluminum plate does not change under high temperature environment,With property resistant to high temperature,And fire protecting performance reaches A1 grades,It is safe and practical.
Description
Technical field
The present invention relates to porcelain aluminium sheet technical fields, more particularly to fire prevention, high temperature resistant porcelain aluminium sheet.
Background technique
Now, more and more there is aluminium sheet material in exterior walls of buildings, the places such as subway platform, in curtain buildings material
It is that substrate finally exists using technologies such as numerical control bendings by plate forming that aluminium sheet in material, which mostly uses greatly fine aluminum sheet alloy,
Process is made on the surface of sheet forming, to guarantee the appearance and service life of aluminium sheet.
Under the prior art, aluminium sheet materials'use it is more be enamel aluminium sheet, pottery clay plates and fluorine carbon aluminium sheet, but it is above-mentioned these
Using more plate, there are certain deficiency, such as enamel therein and pottery clay plates brittleness it is big, it is easy to it is chipping, fall
Porcelain and cracking phenomena seriously affect using effect, and fluorine carbon aluminium sheet can guarantee that plate is self-cleaning by rainwater, however now aqueous
F-C paint product can not use completely and building field, because F-C paint divides because of high-temperature heating when fire occurs for building
Solution generates ten several pernicious gases such as phosgene, the fluoroolefins of severe toxicity, has very high injury to environment and human body.
Therefore, we have proposed fire prevention, high temperature resistant porcelain aluminium sheets for solving the above problems.
Summary of the invention
The purpose of the present invention is to solve disadvantage existing in the prior art, and propose fire prevention, high temperature resistant porcelain aluminium
Plate.
Fire prevention, high temperature resistant porcelain aluminium sheet, including aluminium sheet, the surface of the aluminium sheet are coated with sandblasting layer, the surface of sandblasting layer
It is coated with prime coat, the surface of the prime coat is coated with porcelain layer, and the substrate thickness of the aluminium sheet is 2.0mm-3.5mm, spray
Sand mode uses air pressure sandblasting, and the sandblasting layer male and fomale(M&F) of surface of aluminum plate is with a thickness of 0.5mm-1.0mm, basecoat paint fire prevention
Paint, base coat thickness are 30 μm -150 μm, the porcelain layer with a thickness of 10 μm -40 μm, porcelain layer is inorganic resin layer, inorganic tree
The ingredient of rouge includes nanoscale Aluminum sol colloidal solution and acrylic resin aqueous solution, and inorganic resin is by Aluminum sol colloidal solution
5%-10%, acrylic resin aqueous solution 90%-95% mixing match form.
Preferably, the fire prevention, high temperature resistant porcelain aluminium sheet preparation method, preparation step includes：
S1, the aluminium sheet are placed in sand-blasting machine, carry out blasting treatment, and sandblasting sandstone raw material uses mullite and fused alumina zirconia, will
Sandstone is sprayed at the surface of aluminium sheet, it is ensured that sandblasting layer its male and fomale(M&F) on aluminium sheet with a thickness of 0.5mm-1.0mm, sandblasting sandstone is adopted
It is stirred and is made with mullite 40%-60%, fused alumina zirconia 40%-60%；
S2, the surface of aluminum plate finished to blasting treatment, are cleaned, and cleaning mode is blown surface of aluminum plate using high wind, then right
Sandblasting layer carries out primer spray processing, and basecoat paint fireproof varnish is stirred using heating water bath to fully transparent before fireproof varnish brushing
Rear even application is mixed to surface of aluminum plate, and ensures that base coat thickness reaches 30 μm -150 μm；
S3, it is parched to the priming paint of surface of aluminum plate, the spraying of inorganic resin layer is carried out to surface of aluminum plate, is then solidified, is obtained
The porcelain aluminium sheet that coating layer thickness is 10 μm -100 μm.
Preferably, it before the aluminium sheet carries out blasting treatment, needs to carry out burnishing part using surface of the sanding machine to aluminium sheet
Reason, obtains smooth carrot-free aluminium sheet.
Preferably, the process selection dry type sandblasting of the sandblasting, and the pressure of sand-blasting gun mouth when sand-blasting machine work is 0.7
Kilogram.
Preferably, the solid content of Aluminum sol is 20%-25% in the inorganic resin, and inorganic resin layer is heated to 90 DEG C, spray
Be applied to surface of aluminum plate, dry at room temperature, then with 150 DEG C -200 DEG C at solidification 30min-50min obtain porcelain aluminium sheet.
Preferably, twice of the basecoat paint, base coat thickness are 30 μm -150 μm, 4h-6h are divided between spraying, in first pass
Priming paint carries out secondary spraying after parching, spraying is uniform.
The beneficial effects of the invention are as follows：
1, board selection aluminium, because aluminium can be repeatedly circulated, secondly, aluminium sheet is compared to stainless steel plate, density is more
Small, the identical aluminium sheet of such area and stainless steel plate, the quality of aluminium sheet is smaller, aluminium sheet is used for exterior walls of buildings, construction is difficult
Degree is smaller, using the aluminium sheet structure of this programme, the surface hardness of porcelain aluminium sheet can be made to reach 6H or more, in daily life,
Applied in each building, will not occur because wipe touch and the scratch drawn.
2, fire resistant coating is sprayed on aluminium sheet, and fire resistant coating heat, which is decomposed, first generates aphlogistic gas or bubble, can be risen
Buffer action, prevention or retarded combustion, guarantee aluminium sheet substrate, and the heat-resisting quantity of aluminium sheet can be enhanced, and it is anti-to improve aluminium sheet
Combustion property can reduce the risk for causing fire.
3, sandstone is sprayed to the surface of aluminium sheet by sand-blasting machine, is primarily due to the hardness of sandstone, obtains the surface of workpiece
Cleannes centainly, while impact and cutting of such abrasive material to surface of aluminum plate are obtained, aluminium sheet can be improved to a certain extent
The roughness on surface is conducive to the mechanical performance for improving plate surface.
To sum up, the porcelain aluminium sheet in the present invention has superior adhesion strength and anti-impact compared to traditional fluorine carbon aluminium sheet
Performance is hit, the inorganic porcelain layer of porcelain surface of aluminum plate does not change under high temperature environment, has property resistant to high temperature, and prevent fires
Performance reaches A1 grades, safe and practical.
Specific embodiment
Combined with specific embodiments below the present invention is made further to explain.
Fire prevention, high temperature resistant porcelain aluminium sheet, including aluminium sheet, the surface of aluminium sheet are coated with sandblasting layer, the surface spraying of sandblasting layer
There is prime coat, the surface of prime coat is coated with porcelain layer, and the substrate thickness of aluminium sheet is 2.0mm-3.5mm, and sandblasting mode is using empty
Atmospheric pressure sandblasting, and the sandblasting layer male and fomale(M&F) of surface of aluminum plate is with a thickness of 0.5mm-1.0mm, basecoat paint fire resistant coating, base coat thickness
Be 30 μm -40 μm, porcelain layer with a thickness of 10 μm -100 μm, porcelain layer is inorganic resin layer, and the ingredient of inorganic resin includes receiving
The Aluminum sol colloidal solution and acrylic resin aqueous solution of meter level, inorganic resin is by Aluminum sol colloidal solution 5%-10%, acrylic acid
Resin aqueous solution 90%-95% mixing match forms, and S1, aluminium sheet are placed in sand-blasting machine, carries out blasting treatment, sandblasting sandstone raw material
Using mullite and fused alumina zirconia, sandstone is sprayed to the surface of aluminium sheet, it is ensured that sandblasting layer its male and fomale(M&F) on aluminium sheet with a thickness of
0.5mm-1.0mm, sandblasting sandstone are stirred and are made using mullite 40%-60%, fused alumina zirconia 40%-60%；S2, to blasting treatment
The surface of aluminum plate finished, is cleaned, and cleaning mode is blown surface of aluminum plate using high wind, is then carried out at primer spray to sandblasting layer
Reason, basecoat paint fireproof varnish, using even application after heating water bath to fully transparent stirring to aluminium sheet before fireproof varnish brushing
Surface, and ensure that base coat thickness reaches 30 μm -150 μm；S3, it parches, surface of aluminum plate is carried out inorganic to the priming paint of surface of aluminum plate
The spraying of resin layer, is then solidified, and the porcelain aluminium sheet that coating layer thickness is 10 μm -100 μm is obtained, and aluminium sheet carries out blasting treatment
Before, it needs to carry out grinding process using surface of the sanding machine to aluminium sheet, obtains smooth carrot-free aluminium sheet, the technique choosing of sandblasting
Pressure with dry type sandblasting, and sand-blasting gun mouth when sand-blasting machine work is 0.7 kilogram, and the solid content of Aluminum sol is in inorganic resin
20%-25%, inorganic resin layer are heated to 90 DEG C, are sprayed at surface of aluminum plate, dry at room temperature, then consolidate at 150 DEG C -200 DEG C
To change 30min-50min and obtains porcelain aluminium sheet, twice of basecoat paint, base coat thickness is 30 μm -150 μm, it is divided into 4h-6h between spraying,
Secondary spraying is carried out after first pass priming paint parches, spraying is uniform.
In the present embodiment, board selection aluminium, because aluminium can be repeatedly circulated, secondly, aluminium sheet is compared to stainless
Steel plate, density is smaller, and the identical aluminium sheet of such area and stainless steel plate, the quality of aluminium sheet is smaller, and aluminium sheet is used for building
Exterior wall, difficulty of construction is smaller, using the aluminium sheet structure of this programme, the surface hardness of porcelain aluminium sheet can be made to reach 6H or more,
In daily life, be applied in each building, will not occur because wipe touch and the scratch drawn, and porcelain layer belong to A1 grades can not
Combustible material, surface of aluminum plate can bear high temperature, secondly, the ingredient in the fire resistant coating on the inside of porcelain layer presses quality proportioning, including
18 parts of lithopone, 8 parts of isopropanol-aluminium isopropoxide, 4 parts of titanium carbide, grey 12 parts fluffy, 15 parts of aluminium powder, 4 parts of methyl methacrylate,
4 parts of trimethylolpropane trimethacrylate, 3 parts of dipropylene glycol dibenzoate, 5 parts of butyl stearate, 5 parts of pentaerythrite, mountain
Fire resistant coating, 7 parts of 4- morpholine phenyl boric acid, is sprayed on aluminium sheet at 19 parts of silica solution by 4 parts of pears alcohol acid anhydride monostearate, is prevented fires first
It paints heat and decomposes the aphlogistic gas of generation or bubble, buffer action, prevention or retarded combustion can be played, guarantee aluminium sheet substrate,
And the heat-resisting quantity of aluminium sheet can be enhanced, and improve aluminium sheet flame resistance, the risk for causing fire can be reduced.
In the present embodiment, for aluminium sheet substrate grit blasting operation using air pressure as power, and sandstone be mullite and
Sandstone is sprayed at the surface of aluminium sheet by sand-blasting machine by the mixture of fused alumina zirconia, is primarily due to the hardness of sandstone, makes the table of workpiece
Face obtains certain cleannes, while impact and cutting of such abrasive material to surface of aluminum plate, can be improved to a certain extent
The roughness of surface of aluminum plate is conducive to the mechanical performance for improving plate surface, and for subsequent paint spraying, improves aluminium sheet
With the combination degree of priming paint.
In the present embodiment, before porcelain aluminium sheet, most of construction material can use fluorine carbon aluminium sheet, therefore, with the present invention
The performance of porcelain aluminium sheet and the performance comparison of fluorine carbon aluminium sheet.
Therefore, the porcelain aluminium sheet in the present invention has superior adhesion strength and anti-impact compared to traditional fluorine carbon aluminium sheet
Performance is hit, the inorganic porcelain layer of porcelain surface of aluminum plate does not change under high temperature environment, has property resistant to high temperature, and prevent fires
Performance reaches A1 grades, will not generate toxic gas because of burning in a fire, have the unrivaled fire protecting performance of organic coating.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. fire prevention, high temperature resistant porcelain aluminium sheet, including aluminium sheet, which is characterized in that the surface of the aluminium sheet is coated with sandblasting layer, sandblasting
The surface of layer is coated with prime coat, and the surface of the prime coat is coated with porcelain layer, and the substrate thickness of the aluminium sheet is 2.0mm-
3.5mm, sandblasting mode uses air pressure sandblasting, and the sandblasting layer male and fomale(M&F) of surface of aluminum plate is with a thickness of 0.5mm-1.0mm, priming paint
Sprayed fire proofing paint, base coat thickness be 30 μm -150 μm, the porcelain layer with a thickness of 10 μm -40 μm, porcelain layer is inorganic resin
Layer, the ingredient of inorganic resin includes nanoscale Aluminum sol colloidal solution and acrylic resin aqueous solution, and inorganic resin is molten by aluminium
Micelle colloid solution 5%-10%, acrylic resin aqueous solution 90%-95% mixing match form.
2. the preparation method of fire prevention according to claim 1, high temperature resistant porcelain aluminium sheet, it is characterised in that：Preparation step packet
It includes：
S1, the aluminium sheet are placed in sand-blasting machine, carry out blasting treatment, and sandblasting sandstone raw material uses mullite and fused alumina zirconia, will
Sandstone is sprayed at the surface of aluminium sheet, it is ensured that sandblasting layer its male and fomale(M&F) on aluminium sheet with a thickness of 0.5mm-1.0mm, sandblasting sandstone is adopted
It is stirred and is made with mullite 40%-60%, fused alumina zirconia 40%-60%；
S2, the surface of aluminum plate finished to blasting treatment, are cleaned, and cleaning mode is blown surface of aluminum plate using high wind, then right
Sandblasting layer carries out primer spray processing, and basecoat paint fireproof varnish is stirred using heating water bath to fully transparent before fireproof varnish brushing
Rear even application is mixed to surface of aluminum plate, and ensures that base coat thickness reaches 30 μm -150 μm；
S3, it is parched to the priming paint of surface of aluminum plate, the spraying of inorganic resin layer is carried out to surface of aluminum plate, is then solidified, is obtained
The porcelain aluminium sheet that coating layer thickness is 10 μm -100 μm.
3. fire prevention according to claim 1, high temperature resistant porcelain aluminium sheet, which is characterized in that the aluminium sheet carries out blasting treatment
Before, it needs to carry out grinding process using surface of the sanding machine to aluminium sheet, obtains smooth carrot-free aluminium sheet.
4. fire prevention according to claim 1, high temperature resistant porcelain aluminium sheet, which is characterized in that the process selection of the sandblasting is dry
Formula sandblasting, and the pressure of sand-blasting gun mouth when sand-blasting machine work is 0.7 kilogram.
5. fire prevention according to claim 1, high temperature resistant porcelain aluminium sheet, which is characterized in that Aluminum sol in the inorganic resin
Solid content be 20%-25%, inorganic resin layer is heated to 90 DEG C, is sprayed at surface of aluminum plate, dries at room temperature, then with 150 DEG C-
Solidify 30min-50min at 200 DEG C and obtains porcelain aluminium sheet.
6. fire prevention according to claim 1, high temperature resistant porcelain aluminium sheet, which is characterized in that twice of the basecoat paint, priming paint
With a thickness of 30 μm -150 μm, it is divided into 4h-6h between spraying, secondary spraying is carried out after first pass priming paint parches, spraying is uniform.