CN108864840A - A kind of fire resistant anticorrosive transformer case paint - Google Patents
A kind of fire resistant anticorrosive transformer case paint Download PDFInfo
- Publication number
- CN108864840A CN108864840A CN201810505487.7A CN201810505487A CN108864840A CN 108864840 A CN108864840 A CN 108864840A CN 201810505487 A CN201810505487 A CN 201810505487A CN 108864840 A CN108864840 A CN 108864840A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire resistant
- transformer case
- resistant anticorrosive
- siloxanes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of fire resistant anticorrosive transformer case paints, are made of following raw material according to parts by weight:5-25 parts of phenolic resin, 6-18 parts of fluorocarbon resin, 6-18 parts of ferric oxide red powder, 3-13 parts of permanent bordeaux, 4-18 parts of catechol, 6-18 parts of zinc sulfate, 3-13 parts of dimethyl siloxane, 5-15 parts of modified epoxy polyurethane, 4-16 parts of ammonium polyacrylate, 2-18 parts of siloxanes, 4-16 parts of methanol, 4-18 parts of zinc oxide, 6-18 parts of mineral oil.The present invention has many advantages, such as high temperature resistant, anti-oxidant and at low cost.
Description
Technical field
The present invention relates to a kind of protective paints more particularly to a kind of fire resistant anticorrosive transformer case to paint.
Background technique
Currently, transformer is widely used as equipment common in industry by people, still with the development of industrial level
The preservation of transformer case can not be permanent, it is easy to be aoxidized by the oxygen in air, people are typically employed in outside transformer
The mode that shell surface coats one layer of protective paint achievees the purpose that protect transformer, but protective paint used in existing people cannot
Transformer is enough effectively protected, it is easy to which the case where being oxidized is unfavorable for the use of people.
Summary of the invention
In order to overcome the defects of the prior art described above, the object of the present invention is to provide outside a kind of fire resistant anticorrosive transformer
Shell paint.
The present invention takes following technical scheme to realize:A kind of fire resistant anticorrosive transformer case paint, by with
Under according to parts by weight raw material composition:5-25 parts of phenolic resin, 6-18 parts of ferric oxide red powder, is consolidated 6-18 parts of fluorocarbon resin forever
3-13 parts red, 4-18 parts of catechol, 6-18 parts of zinc sulfate, 3-13 parts of dimethyl siloxane, 5-15 parts of modified epoxy polyurethane,
4-16 parts of ammonium polyacrylate, 2-18 parts of siloxanes, 4-16 parts of methanol, 4-18 parts of zinc oxide, 6-18 parts of mineral oil.
A kind of above-mentioned fire resistant anticorrosive transformer case paint, is made of following raw material according to parts by weight:Phenol
5-23 parts of urea formaldehyde, 6-16 parts of fluorocarbon resin, 6-16 parts of ferric oxide red powder, 3-11 parts of permanent bordeaux, 4-16 parts of catechol, sulfuric acid
6-16 parts of zinc, 3-11 parts of dimethyl siloxane, 5-13 parts of modified epoxy polyurethane, 4-14 parts of ammonium polyacrylate, siloxanes 2-16
Part, 4-14 parts of methanol, 4-16 parts of zinc oxide, 6-16 parts of mineral oil.
A kind of above-mentioned fire resistant anticorrosive transformer case paint, is made of following raw material according to parts by weight:Phenol
15 parts of urea formaldehyde, 12 parts of fluorocarbon resin, 12 parts of ferric oxide red powder, 8 parts of permanent bordeaux, 11 parts of catechol, 12 parts of zinc sulfate, diformazan
8 parts of radical siloxane, 10 parts of modified epoxy polyurethane, 10 parts of ammonium polyacrylate, 10 parts of siloxanes, 10 parts of methanol, 11 parts of zinc oxide,
12 parts of mineral oil.
In summary the invention has the advantages that:The present invention has high temperature resistant, anti-oxidant and at low cost etc. excellent
Transformer case can be effectively protected in point in use, reach purpose resistant to high temperature, transformer is prevented to be corroded
The case where.
Specific embodiment
Embodiment 1
A kind of fire resistant anticorrosive transformer case paint, is made of following raw material according to parts by weight:5 parts of phenolic resin,
6 parts of fluorocarbon resin, 3 parts of permanent bordeaux, 4 parts of catechol, 6 parts of zinc sulfate, 3 parts of dimethyl siloxane, changes 6 parts of ferric oxide red powder
Property 5 parts of epoxy polyurethane, 4 parts of ammonium polyacrylate, 2 parts of siloxanes, 4 parts of methanol, 4 parts of zinc oxide, 6 parts of mineral oil.
Embodiment 2
A kind of fire resistant anticorrosive transformer case paint, is made of following raw material according to parts by weight:15 parts of phenolic resin,
12 parts of fluorocarbon resin, 12 parts of ferric oxide red powder, 8 parts of permanent bordeaux, 11 parts of catechol, 12 parts of zinc sulfate, dimethyl siloxane 8
Part, 10 parts of modified epoxy polyurethane, 10 parts of ammonium polyacrylate, 10 parts of siloxanes, 10 parts of methanol, 11 parts of zinc oxide, mineral oil 12
Part.
Embodiment 3
A kind of fire resistant anticorrosive transformer case paint, is made of following raw material according to parts by weight:25 parts of phenolic resin,
18 parts of fluorocarbon resin, 18 parts of ferric oxide red powder, 13 parts of permanent bordeaux, 18 parts of catechol, 18 parts of zinc sulfate, dimethyl siloxane 13
Part, 15 parts of modified epoxy polyurethane, 16 parts of ammonium polyacrylate, 18 parts of siloxanes, 16 parts of methanol, 18 parts of zinc oxide, mineral oil 18
Part.
The present invention has many advantages, such as high temperature resistant, anti-oxidant and at low cost, and change can be effectively protected in use
The case where depressor shell reaches purpose resistant to high temperature, transformer is prevented to be corroded.
The above is the embodiment of the present invention, therefore all is done according to structure, feature and principle described in the present patent application range
Equivalent change or modification, be included in the scope of the patent application of the present invention.
Claims (3)
1. a kind of fire resistant anticorrosive transformer case paint, which is characterized in that be made of following raw material according to parts by weight:
5-25 parts of phenolic resin, 6-18 parts of fluorocarbon resin, 6-18 parts of ferric oxide red powder, 3-13 parts of permanent bordeaux, 4-18 parts of catechol, sulphur
Sour zinc 6-18 parts, 3-13 parts of dimethyl siloxane, 5-15 parts of modified epoxy polyurethane, 4-16 parts of ammonium polyacrylate, siloxanes 2-
18 parts, 4-16 parts of methanol, 4-18 parts of zinc oxide, 6-18 parts of mineral oil.
2. a kind of fire resistant anticorrosive transformer case paint according to claim 1, which is characterized in that by below according to
The raw material of parts by weight forms:5-23 parts of phenolic resin, 6-16 parts of fluorocarbon resin, 6-16 parts of ferric oxide red powder, permanent bordeaux 3-11
Part, 4-16 parts of catechol, 6-16 parts of zinc sulfate, 3-11 parts of dimethyl siloxane, 5-13 parts of modified epoxy polyurethane, polypropylene
Sour ammonium 4-14 parts, 2-16 parts of siloxanes, 4-14 parts of methanol, 4-16 parts of zinc oxide, 6-16 parts of mineral oil.
3. a kind of fire resistant anticorrosive transformer case paint according to claim 1, which is characterized in that by below according to
The raw material of parts by weight forms:15 parts of phenolic resin, 12 parts of fluorocarbon resin, 12 parts of ferric oxide red powder, 8 parts of permanent bordeaux, adjacent benzene two
11 parts of phenol, 12 parts of zinc sulfate, 8 parts of dimethyl siloxane, 10 parts of modified epoxy polyurethane, 10 parts of ammonium polyacrylate, siloxanes 10
Part, 10 parts of methanol, 11 parts of zinc oxide, 12 parts of mineral oil.