CN108864838A - Imitative metal lagging and production technology - Google Patents
Imitative metal lagging and production technology Download PDFInfo
- Publication number
- CN108864838A CN108864838A CN201710324553.6A CN201710324553A CN108864838A CN 108864838 A CN108864838 A CN 108864838A CN 201710324553 A CN201710324553 A CN 201710324553A CN 108864838 A CN108864838 A CN 108864838A
- Authority
- CN
- China
- Prior art keywords
- illusion
- colour
- layer
- coloured
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This application discloses a kind of imitative metal laggings,Including substrate,Coat elastic coating on base material,Coloured middle layer of the roller coating on elastic coating,Illusion-colour metallic paint is sprayed on to the effect layer formed on coloured middle layer,And coated in the protective layer on effect layer,The protective layer is nano-fluorine carbon paint,The illusion-colour metallic paint is by slurry,Mass fraction is that 10%~15% illusion-colour metal powder and 45%~59% fluorine carbon-nano resin are constituted,The wherein dimethylbenzene that slurry is 20%~28% by mass fraction,8%~15% acetate butyl,The CAB that 8% concentration is 20%,0.7% Levaslip432,0.4%~1% Disponer904s,0.6%~0.8% Aisponer912,0.6%~1% Defom6500,2% 201p composition,The present invention has transport,It is easy for construction,Style is stablized,Feel is smooth,Moist feature.
Description
Technical field
The present invention relates to decorative panel fields, more specifically, it relates to a kind of imitative metal lagging and production technology.
Background technique
Currently, building wall is affixed directly to building wall when carrying out metal finishing, or using metal material
Face surface, or be sprayed on composite sheet material using metallic paint, then composite sheet material is covered in the surface of building.
When being decorated using metal, since metal is heavier, so that transport and construction are extremely not easy, higher cost, and
And metal material easily corrodes；When being sprayed on composite sheet material using metallic paint, such facing stone style is unstable, feel
Difference, and since coating is exposed in external environment, process is wet by the rain and burnt by the sun, easily coating is caused to fade, color duration mistake
It is short.
Summary of the invention
In view of the deficiencies of the prior art, the present invention intends to provide a kind of imitative metal lagging, the imitative metal
Decorative panel has material light, transports, is easy for construction, and style is stablized, feel smoothness, moist feature.
To achieve the above object, the present invention provides following technical solutions：A kind of imitative metal lagging, including substrate apply
Elastic coating on base material is covered, illusion-colour metallic paint is sprayed on coloured middle layer by coloured middle layer of the roller coating on elastic coating
The effect layer of formation, and coated in the protective layer on effect layer, the protective layer is nano-fluorine carbon paint, the illusion-colour metallic paint
It is made of slurry, illusion-colour metal powder and fluorine carbon-nano resin, the mass fraction of illusion-colour metal powder is 5%~8%, fluorine carbon-nano
The mass fraction of resin is 45%~59%.
The dimethylbenzene that slurry is 20%~28% by metal quality score, 8%~15% acetate butyl, 8% concentration are
20% CAB, 0.7% Levaslip432,0.4%~1% Disponer904s, 0.6%~0.8%
Aisponer912,0.6%~1% Defom6500,2% 201p composition.
The present invention is further arranged to：The illusion-colour metallic paint is by slurry, 5% illusion-colour metal powder and 46% fluorine
Carbon nano-resin composition；Slurry includes the dimethylbenzene that mass fraction is 21%, and 10% acetate butyl, 8% concentration is 20%
CAB, 0.7% Levaslip432,0.7% Disponer904s, 0.7% Aisponer912,0.9%
Defom6500,2% 201p composition.
It is imitative metal inorganic master by inorganic mineral gel, kaolin, rutile titanium white powder by using above-mentioned technical proposal
Body, made metal face overlay stone effect is true to nature, is main filmogen by organosilicon-modified acrylic elastic emulsion, adds
The effect layer that illusion-colour metallic paint made of other auxiliary agents is formed has feel exquisiteness, smooth, the big feature of tensile strength, and
The same substrate of the effect layer, elastic coating, coloured middle layer and protective layer are the same, are all made of the organic and inorganic material of lightweight, phase
Have the characteristics that than metal material light, to easily transport, construct, coats one layer on effect layer and be made of nano-fluorine carbon paint
Effect layer can be effectively protected not by external interference in protective layer, so that its color is sufficiently stable, a small amount of illusion-colour metal powder energy
Dosage is enough saved, while there is stronger stable metal effect.
Production method, the imitative metal lagging of preparation such as one of claims 1 or 2, it is characterized in that：Including following
Step：
(1) smooth, drying process is carried out to by the substrate of main material of polyester fiber, uses high-quality cracking resistance seal coat
The one side in substrate, and standing and drying are uniformly brushed comprehensively；
(2) after the high-quality cracking resistance seal coat described in (1) is completely dried, in its surface roller coating elastic coating, the elasticity
Coating is made using polymeric acrylic acid elastic emulsion by film forming matter；
(3) after the elastic coating described in (2) is completely dried, on its surface, uniformly roller coating coloured silk matches priming paint together, is formed with
Color middle layer；
(4) after the coloured middle layer described in (3) is completely dried, illusion-colour metallic paint, shape are sprayed in its surface continuous uniform
At effect layer；
(5) after the effect layer described in (4) is completely dried, nano-fluorine carbon paint is sprayed on its surface, forms protective layer.
By using above-mentioned technical proposal, the tensile strength of metal face overlay stone can be enhanced using polyester fiber as substrate,
High-quality cracking resistance seal coat is coated on one side in substrate plays the role of water-fast, acid and alkali-resistance, mildew resistant moistureproof；With polymeric acrylic acid elasticity
Lotion is that elastic coating made of film forming matter can play enhancing feel, metal face overlay stone generation is answered in compensation temperature variation
The effect of power；Roller coating just matches the color effect that metal face overlay stone can be enhanced in priming paint on elastic coating；In illusion-colour metallic paint
The effect layer surface spraying nano-fluorine carbon paint of formation can be effectively protected effect layer not by external interference, make as protective layer
It is sufficiently stable to obtain its color.
The present invention is further arranged to：The illusion-colour metallic paint is in coloured middle layer surface first pass spraying and completely dry
After dry, spray second time again.
The present invention is further arranged to：The dosage of the high-quality cracking resistance seal coat is 0.1~0.15kg/m2；The bullet
Property coating with a thickness of 1.2mm；The coloured middle layer with a thickness of 0.15mm；The effect layer with a thickness of 0.2mm
By using above-mentioned technical proposal, twice of spraying illusion-colour metallic paint can guarantee that effect layer feel is fine and smooth, appearance
True to nature, not only effect is true to nature for the imitative metal lagging produced by the setting of above-mentioned thickness, and thickness is very thin, is protecting
While protecting effect layer, and impact effect layer appearance does not show.
The preparation method of illusion-colour metallic paint includes the following steps：Sequentially add dimethylbenzene, acetate butyl, 20% concentration
CAB is dispersed into dispersion tank, jitter time 5-10min, until fully transparent grainless；It adds again
Levaslip432, Disponer904s, Aisponer912, Defom6500,201p carry out high speed dispersion into dispersion tank and are made
Slurry；Illusion-colour metal powder is slowly added into slurry, wherein revolving speed is not above 900r/min, jitter time 10-
15min；It is uniform that fluorine carbon-nano resin agitating is added after all raw materials are completely dispersed, obtains illusion-colour metallic paint.
By using above-mentioned technical proposal, sequentially add dimethylbenzene, acetate butyl, 20% concentration CAB into dispersion tank
Dispersed, jitter time 5-10min, until fully transparent grainless；Levaslip432 is added again,
Disponer904s, Aisponer912, Defom6500,201p carry out high speed dispersion into dispersion tank and slurry are made；By illusion-colour
Metal powder is slowly added into slurry, and wherein revolving speed is not above 900r/min, jitter time 10-15min；When all raw materials
It is uniform that fluorine carbon-nano resin agitating is added after being completely dispersed, obtains illusion-colour metallic paint；Wherein the CAB of 20% concentration is first pre-dissolved,
Illusion-colour metal powder is brewed in advance, is modulated with assorted high-grade illusion-colour metal powder, does not add mill base, finished product possesses 3 kinds or more substantially
Illusion-colour metal powder, construction on the synthesis polyester fiber of my door pass through high-temperature baking, then with fluorine carbon-nano finish protect, at
Paint film has impayable guarantor's color effect and other auxiliary agents, so that the illusion-colour metallic paint formed can provide pole after shaping
High intensity and toughness, the ability of very strong imitative metal, and it is light, intensity is high；After obtaining the illusion-colour metallic paint of mobility, lead to
It crosses spray gun special and illusion-colour metallic paint is sprayed on coloured middle layer surface.
The present invention is further arranged to：In the preparation step of illusion-colour metallic paint, temperature is 25 DEG C, and relative humidity is
40%-60%.
The present invention is further arranged to：By adding thickener, the viscosity of the illusion-colour metallic paint can be controlled in 100-
120KU。
By using above-mentioned technical proposal, by 25 DEG C of temperature control bit in the preparation of illusion-colour metallic paint, relative humidity is
40%-60%, its viscosity of illusion-colour metallic paint produced in this way are 90KU, meet the demand and satisfaction in most of market on the market
The demand of particular client；In the illusion-colour metallic paint finished product the step of, temperature is 25 DEG C, relative humidity 40%-60%, mixing
Time is within 1-5h, so that the illusion-colour metallic paint viscosity produced is 4000-9000mpa.s, and most common in the market
Use viscosity range.
Specific embodiment
A kind of imitative metal lagging, including substrate coat elastic coating on base material, roller coating having on elastic coating
Illusion-colour metallic paint is sprayed on the effect layer formed on coloured middle layer by color middle layer, and coated in the protective layer on effect layer, institute
Stating protective layer is nano-fluorine carbon paint, and the illusion-colour metallic paint is made of slurry, illusion-colour metal powder and fluorine carbon-nano resin, illusion-colour
The mass fraction of metal powder is 5%~8%, and the mass fraction of fluorine carbon-nano resin is 45%~59%.
The dimethylbenzene that slurry is 20%~28% by metal quality score, 8%~15% acetate butyl, 8% concentration are
20% CAB, 0.7% Levaslip432,0.4%~1% Disponer904s, 0.6%~0.8%
Aisponer912,0.6%~1% Defom6500,2% 201p.
The detailed proportion of used classes of agents, raw material and dosage：
1. illusion-colour metallic paint matches：
Dimethylbenzene 20%~28%；
Acetate butyl 8%~15%；
20%CAB8%；
Levaslip4320.7%；
Aisponer9120.6%~0.8%；
Defom65000.6%~1%；
201p2%；
Disponer9040.4%~1%；
Illusion-colour metal powder 5%~8%；
Fluorine carbon-nano resin 45%~59%.
Nano-fluorine carbon paint proportion：
Dimethylbenzene 35~40%
Butyl acetate 10~15%
Disponer904s (Ricinate) 0.3~0.5%
Levaslip432 (silicone levelling agent) 0.3~0.5%
Defoaming agent 6350.4~0.7%
The nano combined fluorocarbon resin 50~55% of solvent type.
Embodiment 1：The preparation step of illusion-colour metallic paint：
The preparation step of illusion-colour metallic paint：Sequentially add dimethylbenzene, acetate butyl, 20% concentration CAB into dispersion tank
Dispersed, jitter time 5-10min, until fully transparent grainless；Levaslip432 is added again,
Disponer904s, Aisponer912, Defom6500,201p carry out high speed dispersion into dispersion tank and slurry are made；By illusion-colour
Metal powder is slowly added in slurry obtained, and wherein revolving speed is not above 900r/min, jitter time 10-15min；When all
Addition fluorine carbon-nano resin agitating is uniform after raw material is completely dispersed, and obtains illusion-colour metallic paint.
3. the preparation step of metal face overlay stone：
(1) to sufficiently cleaned using polyester fiber as the substrate of main material, it is smooth, be dried, when cleaning, uses
The detergent of PH=8 keeps environment temperature：It T=5 DEG C, is then uniformly brushed in substrate comprehensively using high-quality cracking resistance seal coat
One side, and standing and drying, the dosage of high-quality cracking resistance seal coat is 0.1kg/m2；
(2) after the high-quality cracking resistance seal coat described in (1) is completely dried, in its surface roller coating elastic coating, the elasticity
Coating is made using polymeric acrylic acid elastic emulsion by film forming matter, and the elastic coating is with a thickness of 1.2mm；
(3) after the elastic coating described in (2) is completely dried, on its surface, uniformly roller coating coloured silk matches priming paint together, is formed with
Color middle layer, coloured middle layer with a thickness of 0.15mm；
(4) after the coloured middle layer described in (3) is completely dried, illusion-colour metallic paint, spray are sprayed in its surface continuous uniform
Apply first pass after, standing and drying, then spray second time, formed effect layer, the effect layer with a thickness of 0.2mm；
(5) after the effect layer described in (4) is completely dried, nano-fluorine carbon paint is sprayed on its surface, proportion is：35%
Dimethylbenzene, 10% butyl acetate, 0.3% Disponer904s (Ricinate), 0.3% Levaslip432 (silicone
Levelling agent), the nano combined fluorocarbon resin of the solvent type of 0.4% defoaming agent 635 and 54% forms protective layer, the protective layer
With a thickness of 0.1mm.
Here, during metal face overlay is made of stones standby, high-quality cracking resistance seal coat used in step (1) is using autonomous raw
The seal coat of production has the characteristics that acid and alkali-resistance, water-fast, moisture resistance.
Embodiment 1.
The proportion of illusion-colour metallic paint：
Dimethylbenzene 21%；
Acetate butyl 10%；
20%CAB8%；
Levaslip4320.7%；
Disponer9040.7%；
Aisponer9120.7%；
Defom65000.9%；
201p2%；
Illusion-colour metal powder 5%；
Fluorine carbon-nano resin 46%.
Operating process and condition：
1. sequentially add dimethylbenzene, acetate butyl, 20% CAB dispersion 5-10min, until fully transparent grainless, then
Add 4.5.6.7.8 high speed dispersion；
2. adding Levaslip432 again, Disponer904s, Aisponer912, Defom6500,201p is into dispersion tank
It carries out high speed dispersion and slurry is made；Illusion-colour metal powder is slowly added in slurry obtained, wherein revolving speed is not above 900r/
Min, jitter time 10-15min；
3. prefabricated metal paste is slowly added to, revolving speed disperses 10-15 minutes not above 900r/min.
The preparation step and condition of metal face overlay stone in embodiment 2：
(1) to sufficiently cleaned using polyester fiber as the substrate of main material, it is smooth, be dried, when cleaning, uses
The detergent of PH=8 keeps environment temperature：It T=5 DEG C, is then uniformly brushed in substrate comprehensively using high-quality cracking resistance seal coat
One side, and standing and drying, the dosage of high-quality cracking resistance seal coat is 0.1kg/m2；
(2) after the high-quality cracking resistance seal coat described in (1) is completely dried, in its surface roller coating elastic coating, the elasticity
Coating is made using polymeric acrylic acid elastic emulsion by film forming matter, and the elastic coating is with a thickness of 1.2mm；
(3) after the elastic coating described in (2) is completely dried, on its surface, uniformly roller coating coloured silk matches priming paint together, is formed with
Color middle layer, coloured middle layer with a thickness of 0.15mm；
(4) after the coloured middle layer described in (3) is completely dried, illusion-colour metallic paint, spray are sprayed in its surface continuous uniform
Apply first pass after, standing and drying, then spray second time, formed effect layer, the effect layer with a thickness of 0.2mm；
(5) after the effect layer described in (4) is completely dried, nano-fluorine carbon paint is sprayed on its surface, proportion is：35%
Dimethylbenzene, 10% butyl acetate, 0.3% Disponer904s (Ricinate), 0.3% Levaslip432 (silicone
Levelling agent), the nano combined fluorocarbon resin of the solvent type of 0.4% defoaming agent 635 and 54% forms protective layer, the protective layer
With a thickness of 0.1mm.
Embodiment 2.
The proportion of illusion-colour metallic paint
Dimethylbenzene 23%；
Acetate butyl 8%；
20%CAB8%；
Levaslip4320.7%；
Disponer9040.5%；
Aisponer9120.8%；
Defom65001%；
201p2%；
Illusion-colour metal powder 7%；
Fluorine carbon-nano resin 45%.
Operating process and condition：
1. sequentially add dimethylbenzene, acetate butyl, 20% CAB dispersion 5-10min, until fully transparent grainless, then
Add 4.5.6.7.8 high speed dispersion；
2. adding Levaslip432 again, Disponer904s, Aisponer912, Defom6500,201p is into dispersion tank
It carries out high speed dispersion and slurry is made；Illusion-colour metal powder is slowly added in slurry obtained, wherein revolving speed is not above 900r/
Min, jitter time 10-15min；
3. prefabricated metal paste is slowly added to, revolving speed disperses 10-15 minutes not above 900r/min.
The preparation step and condition of metal face overlay stone in embodiment 2：
(1) to sufficiently cleaned using polyester fiber as the substrate of main material, it is smooth, be dried, when cleaning, uses
The detergent of PH=8 keeps environment temperature：It T=5 DEG C, is then uniformly brushed in substrate comprehensively using high-quality cracking resistance seal coat
One side, and standing and drying, the dosage of high-quality cracking resistance seal coat is 0.1kg/m2；
(2) after the high-quality cracking resistance seal coat described in (1) is completely dried, in its surface roller coating elastic coating, the elasticity
Coating is made using polymeric acrylic acid elastic emulsion by film forming matter, and the elastic coating is with a thickness of 1.2mm；
(3) after the elastic coating described in (2) is completely dried, on its surface, uniformly roller coating coloured silk matches priming paint together, is formed with
Color middle layer, coloured middle layer with a thickness of 0.15mm；
(4) after the coloured middle layer described in (3) is completely dried, illusion-colour metallic paint, spray are sprayed in its surface continuous uniform
Apply first pass after, standing and drying, then spray second time, formed effect layer, the effect layer with a thickness of 0.2mm；
(5) after the effect layer described in (4) is completely dried, nano-fluorine carbon paint is sprayed on its surface, proportion is：35%
Dimethylbenzene, 10% butyl acetate, 0.3% Disponer904s (Ricinate), 0.3% Levaslip432 (silicone
Levelling agent), the nano combined fluorocarbon resin of the solvent type of 0.4% defoaming agent 635 and 54% forms protective layer, the protective layer
With a thickness of 0.1mm.
Embodiment 3.
The proportion of illusion-colour metallic paint：
Dimethylbenzene 21%；
Acetate butyl 9%；
20%CAB8%；
Levaslip4320.7%；
Disponer9040.5%；
Aisponer9120.8%；
Defom65001%
201p2%；
Illusion-colour metal powder 8%；
Fluorine carbon-nano resin 47%.
Operating process and condition：
1. sequentially add dimethylbenzene, acetate butyl, 20% CAB dispersion 5-10min, until fully transparent grainless, then
Add 4.5.6.7.8 high speed dispersion；
2. adding Levaslip432 again, Disponer904s, Aisponer912, Defom6500,201p is into dispersion tank
It carries out high speed dispersion and slurry is made；Illusion-colour metal powder is slowly added in slurry obtained, wherein revolving speed is not above 900r/
Min, jitter time 10-15min；
3. prefabricated metal paste is slowly added to, revolving speed disperses 10-15 minutes not above 900r/min.
The preparation step and condition of metal face overlay stone in embodiment 3：
(1) to sufficiently cleaned using polyester fiber as the substrate of main material, it is smooth, be dried, when cleaning, uses
The detergent of PH=8 keeps environment temperature：It T=5 DEG C, is then uniformly brushed in substrate comprehensively using high-quality cracking resistance seal coat
One side, and standing and drying, the dosage of high-quality cracking resistance seal coat is 0.1kg/m2；
(2) after the high-quality cracking resistance seal coat described in (1) is completely dried, in its surface roller coating elastic coating, the elasticity
Coating is made using polymeric acrylic acid elastic emulsion by film forming matter, and the elastic coating is with a thickness of 1.2mm；
(3) after the elastic coating described in (2) is completely dried, on its surface, uniformly roller coating coloured silk matches priming paint together, is formed with
Color middle layer, coloured middle layer with a thickness of 0.15mm；
(4) after the coloured middle layer described in (3) is completely dried, illusion-colour metallic paint, spray are sprayed in its surface continuous uniform
Apply first pass after, standing and drying, then spray second time, formed effect layer, the effect layer with a thickness of 0.2mm；
(5) after the effect layer described in (4) is completely dried, nano-fluorine carbon paint is sprayed on its surface, proportion is：35%
Dimethylbenzene, 10% butyl acetate, 0.3% Disponer904s (Ricinate), 0.3% Levaslip432 (silicone
Levelling agent), the nano combined fluorocarbon resin of the solvent type of 0.4% defoaming agent 635 and 54% forms protective layer, the protective layer
With a thickness of 0.1mm.
Claims (5)
1. a kind of imitative metal lagging, including substrate, coat elastic coating on base material, roller coating is coloured on elastic coating
Illusion-colour metallic paint is sprayed on the effect layer formed on coloured middle layer by middle layer, and coated in the protective layer on effect layer, special
Sign is：The protective layer is nano-fluorine carbon paint, and the illusion-colour metallic paint is by slurry, illusion-colour metal powder and fluorine carbon-nano resin structure
At；The mass fraction of illusion-colour metal powder is 5%~8%, and the mass fraction of fluorine carbon-nano resin is 45%~59%；
The dimethylbenzene that the slurry is 20%~28% by metal quality score, 8%~15% acetate butyl, 8% concentration
For 20% CAB, 0.7% Levaslip432,0.4%~1% Disponer904s, 0.6%~0.8%
Aisponer912,0.6%~1% Defom6500,2% 201p composition.
2. imitative metal lagging according to claim 1, it is characterized in that：The illusion-colour metallic paint by slurry, 5% it is unreal
Color metal powder and 46% fluorine carbon-nano resin composition；Slurry includes the dimethylbenzene that mass fraction is 21%, 10% acetic acid
Fourth rouge, the CAB's, 0.7% Levaslip432,0.7% Disponer904s, 0.7% that 8% concentration is 20%
Aisponer912,0.9% Defom6500,2% 201p composition.
3. a kind of production method of imitative metal lagging, the imitative metal lagging of preparation one of such as claims 1 or 2,
It is characterized in：Include the following steps：
Smooth, drying process is carried out to by the substrate of main material of polyester fiber, it is comprehensively equal using high-quality cracking resistance seal coat
The even one side brushed in substrate, and standing and drying；
After the high-quality cracking resistance seal coat described in (1) is completely dried, in its surface roller coating elastic coating, the elastic coating is with poly-
Acrylic elastic emulsion is closed to be made of film forming matter；
After the elastic coating described in (2) is completely dried, on its surface, uniformly roller coating coloured silk matches priming paint together, forms coloured middle layer；
After the coloured middle layer described in (3) is completely dried, illusion-colour metallic paint is sprayed in its surface continuous uniform, forms effect
Layer；
After the effect layer described in (4) is completely dried, nano-fluorine carbon paint is sprayed on its surface, forms protective layer.
4. imitative metal finishing board production technology according to claim 3, it is characterized in that：The illusion-colour metallic paint is coloured
After middle layer surface first pass is sprayed and is completely dried, spray second time again.
5. imitative metal finishing board production technology according to claim 3, it is characterized in that：The high-quality cracking resistance seal coat
Dosage is 0.1~0.15kg/m2；The elastic coating with a thickness of 1.2mm；The coloured middle layer with a thickness of 0.15mm；Institute
State effect layer with a thickness of 0.2mm.