CN108842297B - 一种芹菜纤维面膜基布及其制备方法 - Google Patents
一种芹菜纤维面膜基布及其制备方法 Download PDFInfo
- Publication number
- CN108842297B CN108842297B CN201810803148.7A CN201810803148A CN108842297B CN 108842297 B CN108842297 B CN 108842297B CN 201810803148 A CN201810803148 A CN 201810803148A CN 108842297 B CN108842297 B CN 108842297B
- Authority
- CN
- China
- Prior art keywords
- celery
- mask base
- base cloth
- preparation
- spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种芹菜纤维面膜基布及其制备方法，它属于面膜基布制备领域。本发明芹菜粉碎、过筛，制得芹菜干粉用NaOH溶液浸泡，酶解，酶解后灭酶、过滤、滤渣洗涤烘干粉碎制得芹菜纤维素加水，制成纤维浆，加入的N‑甲基吗啉‑N‑氧化物溶液，在70～80℃下缓慢搅拌后，然后在90～105℃，真空度为0.095～0.098MPa下搅拌2～5h使纤维素完全溶解，制得纤维素溶液，过滤脱泡后制得纺丝原液加入多针头静电纺丝箱中进行静电纺丝，纺丝后真空干燥，制得芹菜纤维毡用水刺加固，制得芹菜纤维面膜基布。本发明制备的面膜基布不仅具备植物纤维服帖性透气性好，是精华液良好的载体，具有消炎、抗衰老，清除皮肤重金属离子的功效。
Description
技术领域
本发明属于面膜基布制备领域；具体涉及一种芹菜纤维面膜基布及其制备方法。
背景技术
目前面膜已经是人们生活中不可或缺的一种护肤美容产品，它可以暂时将面部与外界空气污染隔离，促进皮肤毛孔扩张，提高肌肤含氧量，使面膜中的水分和其他有益成分渗入皮肤角质层，从而使皮肤水润富有弹性。而面膜基布作为这一过程的载体，其本身对皮肤的功能性日益受到重视。但是目前的面膜基布大多仅仅作为精华液载体，而忽略了其功能性。植物纤维作为面膜基布是近来化妆品领域的研究热点，植物纤维服帖性透气性高，并且具有良好的韧性和吸水能力，天然环保，而且运用合适的植物纤维作为载体可以发挥其对护肤保健的功能。
芹菜(Apium gravelous L)作为药食同源植物已在维吾尔医药中广泛应用并为大众所熟识，具有很高的营养价值和药理作用。芹菜中含有丰富的功能活性物质，其中黄酮类化合物、挥发油类等可以清除皮肤自由基，良好地抑制多种病原微生物，具有抗衰老、抗氧化和抗菌抑菌等多种药理作用。芹菜中含有丰富的维生素，可以起到美白护肤功能。并且芹菜中不溶性纤维含量丰富，可以很好的契合皮肤，对皮肤中的的重金属等污染有吸附清除功能。因此，芹菜在化妆品领域的研究开发具有很重要的意义。
发明内容
本发明目的是提供了一种芹菜纤维面膜基布及其制备方法。
本发明通过以下技术方案实现：
一种芹菜纤维面膜基布的制备方法，包括如下步骤：
步骤1、芹菜除去腐烂虫害茎叶、洗净、切碎、通风口处风干后烘箱烘干，放入粉碎机中粉碎、过筛，制得芹菜干粉；
步骤2、将步骤1制得的芹菜干粉用NaOH溶液浸泡，酶解，酶解后灭酶、过滤、滤渣洗涤烘干粉碎制得芹菜纤维素；
步骤3、将步骤2制得的芹菜纤维素加水5～10wt％，制成纤维浆，加入10～20wt％的N-甲基吗啉-N-氧化物溶液，在70～80℃下缓慢搅拌后，然后在90～105℃，真空度为0.095～0.098MPa下搅拌2～5h使纤维素完全溶解，制得纤维素溶液，过滤脱泡后制得纺丝原液；
步骤4、将步骤3制得的纺丝原液加入多针头静电纺丝箱中进行静电纺丝，纺丝后真空干燥，制得芹菜纤维毡；
步骤5、将步骤4制得的芹菜纤维毡用水刺加固，制得芹菜纤维面膜基布。
本发明所述的一种芹菜纤维面膜基布的制备方法，步骤1中风干时间2天，烘干温度为50℃，烘干时间2～5h，步骤1中粉碎后过40～60目筛。
本发明所述的一种芹菜纤维面膜基布的制备方法，步骤2中NaOH溶液浓度为质量分数10％，芹菜干粉与NaOH溶液的料液比1：20～1：25g/mL，溶液pH为8.0，浸泡时间70～90min。
本发明所述的一种芹菜纤维面膜基布的制备方法，步骤2中酶解为在浸泡后的溶液中加入1wt％胰蛋白酶，于45℃恒温箱中孵育2h，酶解结束后95℃灭酶10min，滤渣烘干温度为50℃，烘干时间4～6h。
本发明所述的一种芹菜纤维面膜基布的制备方法，步骤3中的N-甲基吗啉-N-氧化物溶液浓度为质量分数70～80％。
本发明所述的一种芹菜纤维面膜基布的制备方法，步骤3中70～80℃下缓慢搅拌时间30～60min，制得的纤维素溶液的浓度为质量分数10～20％。
本发明所述的一种芹菜纤维面膜基布的制备方法，步骤4中纺丝参数为出丝口为6号针头，纺丝电压为15～25千伏，纺丝原液流速为0.20～0.40mL/min，纺丝极距为10～15cm，静电纺丝结束后60℃真空干燥，制得芹菜纤维毡。
本发明所述的一种芹菜纤维面膜基布的制备方法，步骤5中水刺加固为水刺压力20～25bar，水针孔出口直径为0.10～0.14mm。
本发明所述的一种芹菜纤维面膜基布的制备方法，所述的芹菜纤维面膜基布厚度0.35～0.55mm、基布面密度25-45g/m2。
本发明所述的一种芹菜纤维面膜基布的制备方法，所述的芹菜纤维面膜基布的持液率为1425％～1561％。
本发明所述的一种芹菜纤维面膜基布的制备方法，以芹菜为主要原料，经过芹菜超微纤维制备，纤维压片等工艺完成，本发明方法制备的面膜基布不仅具备植物纤维服帖性透气性好，是精华液良好的载体，而且芹菜的消炎、抗衰老，清除皮肤重金属离子等护肤功能得以很好的发挥。
本发明所述的一种芹菜纤维面膜基布的制备方法制备的芹菜纤维面膜基布对金黄色葡萄球菌的抑菌率为99.4％、对大肠杆菌的抑菌率为95.2％、对白色念珠菌抑菌率为98.7％，其抑菌率均大于95％，具有良好的抑菌效果。
本发明所述的一种芹菜纤维面膜基布的制备方法，利用芹菜纤维粗提物中含有较多的功能活性物质，保留了芹菜的护肤功能，并且天然植物纤维对皮肤契合度高，便于携带，易于降解，安全环保。
本发明所述的一种芹菜纤维面膜基布的制备方法，所用的芹菜为鲍芹，芹菜纤维面膜基布作为附加值产品也为鲍芹的多元化发展提供了广阔的前景。
具体实施方式
具体实施方式一：
一种芹菜纤维面膜基布的制备方法，包括如下步骤：
步骤1、芹菜除去腐烂虫害茎叶、洗净、切碎、通风口处风干后烘箱烘干，放入粉碎机中粉碎、过筛，制得芹菜干粉；
步骤2、将步骤1制得的芹菜干粉用NaOH溶液浸泡，酶解，酶解后灭酶、过滤、滤渣洗涤烘干粉碎制得芹菜纤维素；
步骤3、将步骤2制得的芹菜纤维素加水5wt％，制成纤维浆，加入20wt％的N-甲基吗啉-N-氧化物溶液，在75℃下缓慢搅拌后，然后在105℃，真空度为0.095MPa下搅拌3h使纤维素完全溶解，制得纤维素溶液，过滤脱泡后制得纺丝原液；
步骤4、将步骤3制得的纺丝原液加入多针头静电纺丝箱中进行静电纺丝，纺丝后真空干燥，制得芹菜纤维毡；
步骤5、将步骤4制得的芹菜纤维毡用水刺加固，制得芹菜纤维面膜基布。
本实施方式所述的一种芹菜纤维面膜基布的制备方法，步骤1中风干时间2天，烘干温度为50℃，烘干时间3h，步骤1中粉碎后过60目筛。
本实施方式所述的一种芹菜纤维面膜基布的制备方法，步骤2中NaOH溶液浓度为质量分数10％，芹菜干粉与NaOH溶液的料液比1：25g/ml，溶液pH为8.0，浸泡时间90min。
本实施方式所述的一种芹菜纤维面膜基布的制备方法，步骤2中酶解为在浸泡后的溶液中加入1wt％胰蛋白酶，于45℃恒温箱中孵育2h，酶解结束后95℃灭酶10min，滤渣烘干温度为50℃，烘干时间5h。
本实施方式所述的一种芹菜纤维面膜基布的制备方法，步骤3中的N-甲基吗啉-N-氧化物溶液浓度为质量分数70～80％。
本实施方式所述的一种芹菜纤维面膜基布的制备方法，步骤3中70～80℃下缓慢搅拌时间60min，制得的纤维素溶液的浓度为质量分数15％。
本实施方式所述的一种芹菜纤维面膜基布的制备方法，步骤4中纺丝参数为出丝口为6号针头，纺丝电压为15千伏，纺丝原液流速为0.30mL/min，纺丝极距为15cm，静电纺丝结束后60℃真空干燥，制得芹菜纤维毡。
本实施方式所述的一种芹菜纤维面膜基布的制备方法，步骤5中水刺加固为水刺压力20bar，水针孔出口直径为0.10mm。
具体实施方式二：
根据具体实施方式一所述的一种芹菜纤维面膜基布的制备方法制备的芹菜纤维面膜基布，所述的芹菜纤维面膜基布厚度0.4mm、基布面密度35g/m2。
本实施方式所述的一种芹菜纤维面膜基布的制备方法制备的芹菜纤维面膜基布，所述的芹菜纤维面膜基布的持液率为1425％～1561％。
本实施方式所述的一种芹菜纤维面膜基布的制备方法制备的芹菜纤维面膜基布，进行持液能力和抗菌性能测试：
持液率检测：测试方法为将面膜基布(重量为m1)浸入到面膜专用精华液中，充分浸渍10s，然后取出悬空放置1min，称重m2，持液率＝(m2-m1)/m1x100％。测试三次，对照组选取市售的普通面膜，测试结果如表1所示：
表1持液率对比表
从表1中能够看出本实施方式的芹菜纤维面膜基布持液率分别为1425％、1501％、1456％，而普通无纺布面膜基布持液率在383％左右，本实施方式所述的一种芹菜纤维面膜基布的制备方法制备的芹菜纤维面膜基布，持液率是普通基布的3～4倍。
本实施方式所述的一种芹菜纤维面膜基布的制备方法制备的芹菜纤维面膜基布对金黄色葡萄球菌的抑菌率为99.4％、对大肠杆菌的抑菌率为95.2％、对白色念珠菌抑菌率为98.7％，其抑菌率均大于95％，具有良好的抑菌效果。
本实施方式所述的一种芹菜纤维面膜基布的制备方法制备的芹菜纤维面膜基布对金属吸附量进行测试，对照组选取市售的普通面膜，测试结果如表2所示：
表2重金属吸附量对比表(mg/cm2)
从表2中能够看出，本实施方式所述的一种芹菜纤维面膜基布的制备制备的芹菜纤维面膜基布，以芹菜为主要原料，经过芹菜超微纤维制备，纤维压片等工艺完成，制备的面膜基布不仅具备植物纤维服帖性透气性好，是精华液良好的载体，而且具有清除皮肤重金属离子的功效，本实施方式的芹菜纤维面膜基布对重金属离子的吸附量相比于普通面膜基布提高10倍以上，对人体皮肤上涂抹化妆品残留的金属离子具有良好的吸附作用。
具体实施方式三：
一种芹菜纤维面膜基布的制备方法，包括如下步骤：
步骤1、芹菜除去腐烂虫害茎叶、洗净、切碎、通风口处风干后烘箱烘干，放入粉碎机中粉碎、过筛，制得芹菜干粉；
步骤2、将步骤1制得的芹菜干粉用NaOH溶液浸泡，酶解，酶解后灭酶、过滤、滤渣洗涤烘干粉碎制得芹菜纤维素；
步骤3、将步骤2制得的芹菜纤维素加水5～10wt％，制成纤维浆，加入10～20wt％的N-甲基吗啉-N-氧化物溶液，在70～80℃下缓慢搅拌后，然后在90～105℃，真空度为0.095～0.098MPa下搅拌2～5h使纤维素完全溶解，制得纤维素溶液，过滤脱泡后制得纺丝原液；
步骤4、将步骤3制得的纺丝原液加入多针头静电纺丝箱中进行静电纺丝，纺丝后真空干燥，制得芹菜纤维毡；
步骤5、将步骤4制得的芹菜纤维毡用水刺加固，制得芹菜纤维面膜基布。
具体实施方式四：
根据具体实施方式三所述的一种芹菜纤维面膜基布的制备方法，步骤1中风干时间2天，烘干温度为50℃，烘干时间2～5h，步骤1中粉碎后过40～60目筛。
具体实施方式五：
根据具体实施方式三所述的一种芹菜纤维面膜基布的制备方法，步骤2中NaOH溶液浓度为质量分数10％，芹菜干粉与NaOH溶液的料液比1：20～1：25g/ml，溶液pH为8.0，浸泡时间70～90min。
具体实施方式六：
根据具体实施方式三所述的一种芹菜纤维面膜基布的制备方法，步骤2中酶解为在浸泡后的溶液中加入1wt％胰蛋白酶，于45℃恒温箱中孵育2h，酶解结束后95℃灭酶10min，滤渣烘干温度为50℃，烘干时间4～6h。
具体实施方式七：
根据具体实施方式三所述的一种芹菜纤维面膜基布的制备方法，步骤3中的N-甲基吗啉-N-氧化物溶液浓度为质量分数70～80％。
具体实施方式八：
根据具体实施方式三所述的一种芹菜纤维面膜基布的制备方法，步骤3中70～80℃下缓慢搅拌时间30～60min，制得的纤维素溶液的浓度为质量分数10～20％。
具体实施方式九：
根据具体实施方式三所述的一种芹菜纤维面膜基布的制备方法，步骤4中纺丝参数为出丝口为6号针头，纺丝电压为15～25千伏，纺丝原液流速为0.20～0.40mL/min，纺丝极距为10～15cm，静电纺丝结束后60℃真空干燥，制得芹菜纤维毡。
具体实施方式十：
根据具体实施方式三所述的一种芹菜纤维面膜基布的制备方法，步骤5中水刺加固为水刺压力20～25bar，水针孔出口直径为0.10～0.14mm。
具体实施方式十一：
根据具体实施方式三所述的一种芹菜纤维面膜基布的制备制备的芹菜纤维面膜基布，所述的芹菜纤维面膜基布厚度0.35～0.55mm、基布面密度25-45g/m2。
本实施方式所述的一种芹菜纤维面膜基布的制备制备的芹菜纤维面膜基布，所述的芹菜纤维面膜基布的持液率为1425％～1561％。
本实施方式所述的一种芹菜纤维面膜基布的制备制备的芹菜纤维面膜基布，对金黄色葡萄球菌的抑菌率为99.4％、对大肠杆菌的抑菌率为95.2％、对白色念珠菌抑菌率为98.7％。
本实施方式所述的一种芹菜纤维面膜基布的制备制备的芹菜纤维面膜基布，以芹菜为主要原料，经过芹菜超微纤维制备，纤维压片等工艺完成，制备的面膜基布不仅具备植物纤维服帖性透气性好，是精华液良好的载体，而且芹菜的消炎、抗衰老，清除皮肤重金属离子等护肤功能得以很好的发挥。
本实施方式所述的一种芹菜纤维面膜基布的制备制备的芹菜纤维面膜基布，利用芹菜纤维粗提物中含有较多的功能活性物质，保留了芹菜的护肤功能，并且天然植物纤维对皮肤契合度高，便于携带，易于降解，安全环保。
本实施方式所述的一种芹菜纤维面膜基布的制备制备的芹菜纤维面膜基布，所用的芹菜为鲍芹，芹菜纤维面膜基布作为附加值产品也为鲍芹的多元化发展提供了广阔的前景。
本实施方式所述的一种芹菜纤维面膜基布的制备方法制备的芹菜纤维面膜基布对使用效果进行测试，选择120名22-52岁的面部有红血丝或红疹等炎症问题的女性试用本发明，本发明经过普通黄瓜水(如千纤草黄瓜水)浸泡，试用时间为3个月，测试结果如表3所示(普通面膜基布作为对照)，每组试用普通面膜基布和本发明各10人：
表3试用效果对比表
从表3中能够看出，本实施方式所述的一种芹菜纤维面膜基布的制备制备的芹菜纤维面膜基布，以芹菜为主要原料，经过芹菜超微纤维制备，纤维压片等工艺完成，制备的面膜基布不仅具备植物纤维服帖性透气性好，是精华液良好的载体，而且具有清除皮肤重金属离子和消炎的功效。
Claims (9)
1.一种芹菜纤维面膜基布的制备方法，其特征在于：包括如下步骤：
步骤1、芹菜除去腐烂虫害茎叶、洗净、切碎、通风口处风干后烘箱烘干，放入粉碎机中粉碎、过筛，制得芹菜干粉；
步骤2、将步骤1制得的芹菜干粉用NaOH溶液浸泡，酶解，酶解后灭酶、过滤、滤渣洗涤烘干粉碎制得芹菜纤维素；
步骤3、将步骤2制得的芹菜纤维素加水5～10wt％，制成纤维浆，加入10～20wt％的N-甲基吗啉-N-氧化物溶液，在70～80℃下缓慢搅拌后，然后在90～105℃，真空度为0.095～0.098MPa下搅拌2～5h使纤维素完全溶解，制得纤维素溶液，过滤脱泡后制得纺丝原液；
步骤4、将步骤3制得的纺丝原液加入多针头静电纺丝箱中进行静电纺丝，纺丝后真空干燥，制得芹菜纤维毡；
步骤5、将步骤4制得的芹菜纤维毡用水刺加固，制得芹菜纤维面膜基布；
步骤2中酶解为在浸泡后的溶液中加入1wt％胰蛋白酶，于45℃恒温箱中孵育2h，酶解结束后95℃灭酶10min，滤渣烘干温度为50℃，烘干时间4～6h；
芹菜纤维面膜基布对重金属离子的吸附量相比于普通面膜基布提高10倍以上，对人体皮肤上涂抹化妆品残留的金属离子具有良好的吸附作用。
2.根据权利要求1所述的一种芹菜纤维面膜基布的制备方法，其特征在于：步骤1中风干时间2天，烘干温度为50℃，烘干时间2～5h，步骤1中粉碎后过40～60目筛。
3.根据权利要求1所述的一种芹菜纤维面膜基布的制备方法，其特征在于：步骤2中NaOH溶液浓度为质量分数10％，芹菜干粉与NaOH溶液的料液比1：20～1：25g/mL，溶液pH为8.0，浸泡时间70～90min。
4.根据权利要求1所述的一种芹菜纤维面膜基布的制备方法，其特征在于：步骤3中的N-甲基吗啉-N-氧化物溶液浓度为质量分数70～80％。
5.根据权利要求1所述的一种芹菜纤维面膜基布的制备方法，其特征在于：步骤3中70～80℃下缓慢搅拌时间30～60min，制得的纤维素溶液的浓度为质量分数10～20％。
6.根据权利要求1所述的一种芹菜纤维面膜基布的制备方法，其特征在于：步骤4中纺丝参数为出丝口为6号针头，纺丝电压为15～25千伏，纺丝原液流速为0.20～0.40mL/min，纺丝极距为10～15cm，静电纺丝结束后60℃真空干燥，制得芹菜纤维毡。
7.根据权利要求1所述的一种芹菜纤维面膜基布的制备方法，其特征在于：步骤5中水刺加固为水刺压力20～25bar，水针孔出口直径为0.10～0.14mm。
8.一种权利要求1-7之一所述的一种芹菜纤维面膜基布的制备方法制备的芹菜纤维面膜基布，其特征在于：所述的芹菜纤维面膜基布厚度0.35～0.55mm、基布面密度25-45g/m2。
9.根据权利要求8所述的一种芹菜纤维面膜基布的制备方法制备的芹菜纤维面膜基布，其特征在于：所述的芹菜纤维面膜基布的持液率为1425％～1561％。