CN108808125A - 一种胶体电池电解液 - Google Patents

一种胶体电池电解液 Download PDF

Info

Publication number
CN108808125A
CN108808125A CN201810963176.5A CN201810963176A CN108808125A CN 108808125 A CN108808125 A CN 108808125A CN 201810963176 A CN201810963176 A CN 201810963176A CN 108808125 A CN108808125 A CN 108808125A
Authority
CN
China
Prior art keywords
parts
electrolyte
sulfuric acid
gas phase
glycerine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810963176.5A
Other languages
English (en)
Inventor
戴文刚
李健明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan De Dong Science And Technology Co Ltd
Original Assignee
Dongguan De Dong Science And Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongguan De Dong Science And Technology Co Ltd filed Critical Dongguan De Dong Science And Technology Co Ltd
Priority to CN201810963176.5A priority Critical patent/CN108808125A/zh
Publication of CN108808125A publication Critical patent/CN108808125A/zh
Pending legal-status Critical Current

Abstract

本发明涉及电解液技术领域，具体涉及一种胶体电池电解液一种胶体电池电解液，其特征在于：该电解液的组分及重量份如下:2～5份的气相SiO2、0.2～0.4份的聚丙烯酰胺、2～4份的甘油、0.5～3份的H3PO4、0.5‑2.5份的无水硫酸钠、34‑38份的硫酸、0.5～0.8份的EDTA、0.1～0.5份的氢氧化铝以及0.5～1份的丙三醇溶液，其余为水。本发明的电解液中增加了丙三醇溶液，增强了保湿功能，进而提高胶体电池在高温条件下的循环寿命。另外，本发明通过气相SiO2水溶胶，加入硫酸后使得胶体蓄电池性能稳定，触变性好，同时又满足了蓄电池的电化学性能指标。

Description

一种胶体电池电解液
技术领域
本发明涉及电解液技术领域，具体涉及一种胶体电池电解液。
背景技术
胶体电池属于铅酸蓄电池的一种发展分类，方法是在硫酸中添加胶凝剂，使硫酸电液变为胶态。电液呈胶态的电池通常称之为胶体电池。 胶体电池与常规铅酸电池的区别，从最初理解的电解质胶凝，进一步发展至电解质基础结构的电化学特性研究，以及在板栅和活性物质中的应用推广。其最重要的特点为：用较小的工业代价，制造出更优质的电池，其放电曲线平直，拐点高，其能量和功率要比常规铅酸电池大20% 以上，寿命一般也是常规铅酸电池长一倍左右，高温及低温特性要好得多。
胶体电池由于其特有的凝胶技术，其常温性能的优越性逐渐得到客户的认可。但随着应用场合不断扩大，胶体电池在环境温度偏高的场合下使用，其优越性不是那么明显。当然影响的因素多种多样，其中一个重要原因是现有胶体电池电解液的保湿功能较差，致使在高温环境下电池内部的水份逐渐减少，从而使电解液与极板表面亲合力逐渐下降，接触内阻逐渐增大，导致电池失效。
发明内容
本发明的目的是针对现有技术中的上述不足，提供了一种胶体电池电解液。
本发明的目的通过以下技术方案实现：一种胶体电池电解液，该电解液的组分及重量百分比如下: 2～5份的气相SiO2、0.2～0.4份的聚丙烯酰胺、2～4份的甘油、0.5～3份的H3PO4、0.5-2.5份的无水硫酸钠、34-38份的硫酸、0.5～ 0.8份的EDTA、0.1～0.5份的氢氧化铝以及0.5～1份的丙三醇溶液。
本发明进一步设置为，该电解液由3～5份的气相SiO2、0.3～0.4份的聚丙烯酰胺、3～4份的甘油、2～3份的H3PO4、2-2.5份的无水硫酸钠、35-38份的硫酸、0.6～ 0.8份的EDTA、0.3～0.5份的氢氧化铝以及0.8～1份的丙三醇溶液组成。
本发明进一步设置为，该电解液由2～4份的气相SiO2、0.2～0.3份的聚丙烯酰胺、2～3份的甘油、0.5～1.3份的H3PO4、0.5-2.2份的无水硫酸钠、34-36份的硫酸、0.5～ 0.7份的EDTA、0.1～0.3份的氢氧化铝以及0.5～0.8份的丙三醇溶液组成。
本发明进一步设置为，该电解液由3份的气相SiO2、0.3份的聚丙烯酰胺、3份的甘油、2份的H3PO4、2份的无水硫酸钠、35份的硫酸、0.6份的EDTA、0.3份的氢氧化铝以及0.8份的丙三醇溶液组成。
本发明进一步设置为，该电解液由2份的气相SiO2、0.5份的聚丙烯酰胺、2份的甘油、1.3份的H3PO4、2份的无水硫酸钠、38份的硫酸、0.8份的EDTA、0.1份的氢氧化铝以及1份的丙三醇溶液组成，其余为水。
本发明的有益效果：本发明的电解液中增加了丙三醇溶液，增强了保湿功能，从而提高了电解液与极板表面的亲合力，降低接触内阻，进而提高胶体电池在高温条件下的循环寿命。另外，本发明仅需气相SiO2水溶胶，加入硫酸后形成的强酸性分散液，即可达到相应的分散效果，避免了对高速剪切机的腐蚀破坏，用这种电解液灌制的胶体蓄电池性能稳定，触变性好，同时又满足了蓄电池的电化学性能指标。
具体实施方式
结合以下实施例对本发明作进一步描述。
本实施例所述的一种胶体电池电解液，该电解液的组分及重量百分比如下: 2～5份的气相SiO2、0.2～0.4份的聚丙烯酰胺、2～4份的甘油、0.5～3份的H3PO4、0.5-2.5份的无水硫酸钠、34-38份的硫酸、0.5～ 0.8份的EDTA、0.1～0.5份的氢氧化铝以及0.5～1份的丙三醇溶液。
实施例2，
本实施例所述的一种胶体电池电解液，该电解液由3～5份的气相SiO2、0.3～0.4份的聚丙烯酰胺、3～4份的甘油、2～3份的H3PO4、2-2.5份的无水硫酸钠、35-38份的硫酸、0.6～0.8份的EDTA、0.3～0.5份的氢氧化铝以及0.8～1份的丙三醇溶液组成。
实施例3，
本实施例所述的一种胶体电池电解液，该电解液由2～4份的气相SiO2、0.2～0.3份的聚丙烯酰胺、2～3份的甘油、0.5～1.3份的H3PO4、0.5-2.2份的无水硫酸钠、34-36份的硫酸、0.5～ 0.7份的EDTA、0.1～0.3份的氢氧化铝以及0.5～0.8份的丙三醇溶液组成。
实施例4，
本实施例所述的一种胶体电池电解液，该电解液由3份的气相SiO2、0.3份的聚丙烯酰胺、3份的甘油、2份的H3PO4、2份的无水硫酸钠、35份的硫酸、0.6份的EDTA、0.3份的氢氧化铝以及0.8份的丙三醇溶液组成。
实施例5，
本实施例所述的一种胶体电池电解液，该电解液由2份的气相SiO2、0.5份的聚丙烯酰胺、2份的甘油、1.3份的H3PO4、2份的无水硫酸钠、38份的硫酸、0.8份的EDTA、0.1份的氢氧化铝以及1份的丙三醇溶液组成，其余为水。
最后应当说明的是，以上实施例仅用以说明本发明的技术方案，而非对本发明保护范围的限制，尽管参照较佳实施例对本发明作了详细地说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的实质和范围。

Claims (5)

1.一种胶体电池电解液，其特征在于：该电解液的组分及重量份如下: 2～5份的气相SiO2、0.2～0.4份的聚丙烯酰胺、2～4份的甘油、0.5～3份的H3PO4、0.5-2.5份的无水硫酸钠、34-38份的硫酸、0.5～0.8份的EDTA、0.1～0.5份的氢氧化铝以及0.5～1份的丙三醇溶液，其余为水。
2.根据权利要求1所述的一种胶体电池电解液，其特征在于：该电解液由3～5份的气相SiO2、0.3～0.4份的聚丙烯酰胺、3～4份的甘油、2～3份的H3PO4、2-2.5份的无水硫酸钠、35-38份的硫酸、0.6～ 0.8份的EDTA、0.3～0.5份的氢氧化铝以及0.8～1份的丙三醇溶液组成，其余为水。
3.根据权利要求1所述的一种胶体电池电解液，其特征在于：该电解液由2～4份的气相SiO2、0.2～0.3份的聚丙烯酰胺、2～3份的甘油、0.5～1.3份的H3PO4、0.5-2.2份的无水硫酸钠、34-36份的硫酸、0.5～ 0.7份的EDTA、0.1～0.3份的氢氧化铝以及0.5～0.8份的丙三醇溶液组成，其余为水。
4.根据权利要求1所述的一种胶体电池电解液，其特征在于：该电解液由3份的气相SiO2、0.3份的聚丙烯酰胺、3份的甘油、2份的H3PO4、2份的无水硫酸钠、35份的硫酸、0.6份的EDTA、0.3份的氢氧化铝以及0.8份的丙三醇溶液组成，其余为水。
5.根据权利要求1所述的一种胶体电池电解液，其特征在于：该电解液由2份的气相SiO2、0.5份的聚丙烯酰胺、2份的甘油、1.3份的H3PO4、2份的无水硫酸钠、38份的硫酸、0.8份的EDTA、0.1份的氢氧化铝以及1份的丙三醇溶液组成，其余为水。
CN201810963176.5A 2018-08-22 2018-08-22 一种胶体电池电解液 Pending CN108808125A (zh)