CN108802016A - A kind of high selection measures the sensitive material of trace formaldehyde in air - Google Patents
A kind of high selection measures the sensitive material of trace formaldehyde in air Download PDFInfo
- Publication number
- CN108802016A CN108802016A CN201810893743.4A CN201810893743A CN108802016A CN 108802016 A CN108802016 A CN 108802016A CN 201810893743 A CN201810893743 A CN 201810893743A CN 108802016 A CN108802016 A CN 108802016A
- Authority
- CN
- China
- Prior art keywords
- solution
- warming
- hours
- magnesium
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to the sensitive materials that a kind of high selection measures trace formaldehyde in air, it is characterized in that by graphene-supported MgO, ZrO2And Cr2O3The composite powder material of composition, grain size are no more than 45nm, the wherein mass percent of each component ranging from 8-12%MgO, 5-8%ZrO2, 7-13%Cr2O3And 70-80%C.Preparation method is:It converts natural graphite to graphene oxide first, secondly prepares nanoscale magnesium zirconium chromic composite metal oxide using magnesium salts, zirconates and chromic salts, metal composite oxide is finally loaded during graphene oxide is reduced to graphene.The gas sensor made using sensitive material provided by the present invention, can at the scene the trace formaldehyde in Accurate Determining air without being interfered by other common concurrents.
Description
Technical field
The present invention relates to a kind of high selection measure air in trace formaldehyde sensitive material, it is especially graphene-supported by
MgO、ZrO2And Cr2O3The composite powder material of composition, belongs to field of sensing technologies.
Background technology
Formaldehyde is a kind of colourless volatile industrial chemicals, as adhesive raw materials, disinfectant, preservative and finishing agent quilt
It is widely used in the products such as compression plate, coating, paint, cosmetics and packaging material.First of the people to various concentration in air
Aldehyde has different reflections, when concentration of formaldehyde reaches 0.06~0.07mg/m in air3When, children will occur slightly to pant,
Reach 0.1mg/m3When just have peculiar smell and sense of discomfort, reach 0.5mg/m3When eyes can be stimulated to cause to shed tears, reach 0.6mg/m3It can
Cause throat discomfort or pain, reaches 1mg/m3When can cause largely to shed tears, reach 10mg/m3When then feel to have difficulty in breathing, reach
30mg/m3When can make one to suffocate.Long Term Contact low dosage formaldehyde (0.1mg/m3It can cause chronic respiratory disease, female below)
Property pregnancy syndrome, newborn's constitution reduces and the lesions such as chromosome abnormality.
Formaldehyde is confirmed as carcinogen by International Cancer Research Center (IARC), is the main pollution in room air
Object.Animal experiments show that formaldehyde can increase Micronucleus and rate of teratosperm, cause pregnant mouse abortion ratio rise and
Litter size declines, damages mouse spleen and lungs.Studies have reported that the formaldehyde of low concentration can induce leukaemia, since we give birth to
Living and work Formaldehyde in Environment is ubiquitous, therefore the method for studying trace formaldehyde in rapid and accurate determination air has very by force
Realistic meaning.
Measure trace formaldehyde method mainly have photometry, electrochemical process, chromatography, chemoluminescence method, gas chromatography mass spectrometry method,
Liquid Chromatography/Mass Spectrometry and the chromatography of ions etc., since these methods are required for preconcentration and proper treatment that could pass through analytical instrument
It completes to measure, therefore time-consuming is not easy live realization.Inventor is in 2006 in Sensors & Actuators:
Entitled " On-line Monitoring of Formaldehyde in Air by have been delivered on B.Chemical
Nanoscale vanadium titanium (atomic ratio 1: 2) combined oxidation is used in the paper of Cataluminescence-based gas Sensor "
Object, can be with 0.1~40mg/m of on-line checking as sensitive material3Formaldehyde, detection limit is up to 0.06mg/m3, but acetaldehyde and first
Alcohol has interference;In 2008《Chemical journal》On deliver it is entitled " nano composite oxide catalytic luminescence method measure air in
Formaldehyde " paper in use improved nanoscale molybdenum vanadium titanium (atomic ratio 2: 3: 5) composite oxides, can as sensitive material
With 0.07~34mg/m of on-line checking3Formaldehyde, detection limit is up to 0.04mg/m3, but acetaldehyde still has certain interference.
Invention content
The purpose of the present invention is overcoming the shortcomings of conventional art, a kind of high selection is provided and measures the quick of trace formaldehyde in air
Feel material and preparation method thereof.It, can be quick at the scene, accurate with the gas sensor for the monitoring formaldehyde that this sensitive material makes
The trace formaldehyde in air is really measured without being interfered by other concurrents.
Sensitive material of the present invention is graphene-supported by MgO, ZrO2And Cr2O3The composite powder material of composition,
Preparation method is as follows:
(1) natural graphite is slowly added in oleum with continuous stirring, after being warming up to 45 DEG C and stirring 2-3 hours
It is slowly added to the oxalic acid with weight such as natural graphites, continues that temperature is kept to stir 1 hour, in filtering and being washed to much filtrate
Property;Filter cake is added in the potassium permanganate concentrated sulfuric acid solution that mass fraction is 15%, is warming up to 50-55 DEG C and to continuously stir 2 small
When, until being slowly added to the aqueous hydrogen peroxide solution to bubble-free that mass fraction is 25%, continues constant temperature and stir 1 hour, filter
And much filtrate is washed to neutrality, obtain graphene oxide;
(2) magnesium salts and zirconates are dissolved in the aqueous hydrochloric acid solution that mass fraction is 15-20% and form solution A, chromic salts is molten
It is to form solution B in 20-30% aqueous citric acid solutions in mass fraction, with continuous stirring, solution A is slowly added to solution B
In, agar powder is added after stirring 2 hours, after being warming up to 92-95 DEG C and stirs to being completely dissolved, is cooled to room temperature to form gel, it will
After the drying of this gel, it is warming up to 200-250 DEG C with the speed per minute for being no more than 3 DEG C in chamber type electric resistance furnace, keeps this temperature 4
Hour, continue to be warming up to 400-450 DEG C with the speed per minute for being no more than 3 DEG C, keeps this temperature 3 hours, naturally cool to room
Temperature is obtained by MgO, ZrO2And Cr2O3The metal composite oxide of composition;
(3) with continuous stirring, the hydrazine hydrate aqueous solution that mass fraction is 15-20% is added in this metal composite oxide
In, then graphene oxide above-mentioned is also added thereto, is warming up to 45 DEG C, constant temperature stirs 4-5 hours, and natural cooling simultaneously filters
After be washed with deionized 3 times, be subsequently placed in 65 DEG C vacuum drying oven dry to get to graphene-supported by MgO, ZrO2With
Cr2O3The composite powder material of composition.
Wherein, magnesium salts is anhydride or the hydration of magnesium chloride, magnesium sulfate, magnesium nitrate, magnesium oxalate, magnesium citrate and magnesium acetate
One or more of mixtures of object, zirconates is the nothing of basic zirconium chloride, acetic acid zirconium, zirconium sulfate, zirconium chloride and nitric acid oxidation zirconium
One or more of mixtures of water object or hydrate, chromic salts be chromium chloride, perchloric acid chromium, chromic acetate, chromium+oxalic acid, chromic nitrate and
The anhydride of chromium sulfate or one or more of mixtures of hydrate.
Each component mass fraction meets MgO (8-12%), ZrO in composite powder material obtained2(5-8%), Cr2O3(7-
13%) it when and C (70-80%), and maximum particle diameter is no more than 45nm, is used as measuring the sensitive material of trace formaldehyde in air
Material.
Specific implementation mode
Embodiment 1
(1) natural graphite is slowly added in oleum with continuous stirring, is warming up to 45 DEG C and delayed after stirring 2 hours
The slow oxalic acid being added with weight such as natural graphites continues that temperature is kept to stir 1 hour, filters and much filtrate is washed to neutrality;
Filter cake is added in the potassium permanganate concentrated sulfuric acid solution that mass fraction is 15%, is warming up to 51 DEG C and continuously stirs 2 hours, slowly
Until the aqueous hydrogen peroxide solution to bubble-free that mass fraction is 25% is added, continues constant temperature and stir 1 hour, filter and will filter out
Object is washed to neutrality, obtains graphene oxide;
(2) magnesium chloride hexahydrate and eight water basic zirconium chlorides are dissolved in the aqueous hydrochloric acid solution that mass fraction is 15% and form solution
A, it is to form solution B in 21% aqueous citric acid solution that chromium chloride hexahydrate, which is dissolved in mass fraction, with continuous stirring, by solution A
It is slowly added in solution B, agar powder, which is added, after stirring 2 hours, after being warming up to 92 DEG C stirs to being completely dissolved, and is cooled to room temperature shape
205 DEG C are warming up to the speed per minute for being no more than 3 DEG C in chamber type electric resistance furnace, keeps this after drying this gel at gel
Temperature 4 hours continues to be warming up to 410 DEG C with the speed per minute for being no more than 3 DEG C, keeps this temperature 3 hours, naturally cool to room
Temperature is obtained by MgO, ZrO2And Cr2O3The metal composite oxide of composition;
(3) with continuous stirring, this metal composite oxide is added in the hydrazine hydrate aqueous solution that mass fraction is 17%,
Then graphene oxide above-mentioned is also added thereto, is warming up to 45 DEG C, constant temperature stirs 4 hours, is used after natural cooling and filtering
Deionized water wash 3 times, be subsequently placed in 65 DEG C vacuum drying oven dry to get to graphene-supported by MgO, ZrO2And Cr2O3
The composite powder material of composition.
Analysis:This composite powder material is tested with transmission electron microscope, maximum particle diameter is no more than 43nm, average grain diameter
About 32nm;Constituent analysis is carried out to it, it is respectively 11.2%MgO, 7.4%ZrO to measure each component mass percent2、
11.1%Cr2O3And 70.3%C.
Using:The formaldehyde in air, range of linearity 0.03- are detected using this composite granule as catalytic luminescence sensitive material
15mg/m3, detect and be limited to 0.01mg/m3, other common concurrents do not interfere with.
Embodiment 2
(1) natural graphite is slowly added in oleum with continuous stirring, is warming up to 45 DEG C and delayed after stirring 3 hours
The slow oxalic acid being added with weight such as natural graphites continues that temperature is kept to stir 1 hour, filters and much filtrate is washed to neutrality;
Filter cake is added in the potassium permanganate concentrated sulfuric acid solution that mass fraction is 15%, is warming up to 54 DEG C and continuously stirs 2 hours, slowly
Until the aqueous hydrogen peroxide solution to bubble-free that mass fraction is 25% is added, continues constant temperature and stir 1 hour, filter and will filter out
Object is washed to neutrality, obtains graphene oxide;
(2) by epsom salt, magnesium acetate and acetic acid zirconium be dissolved in mass fraction be 18% aqueous hydrochloric acid solution in formed it is molten
Liquid A, it is to form solution B in 23% aqueous citric acid solution that perchlorate hexahydrate's chromium and chromium sulfate, which are dissolved in mass fraction, is continuously being stirred
It mixes down, solution A is slowly added in solution B, after stirring 2 hours, agar powder is added after being warming up to 93 DEG C and stirs to being completely dissolved,
It is cooled to room temperature to form gel, after this gel is dried, be warming up to the speed per minute for being no more than 3 DEG C in chamber type electric resistance furnace
It 220 DEG C, keeps this temperature 4 hours, continues to be warming up to 415 DEG C with the speed per minute for being no more than 3 DEG C, keep this temperature 3 hours,
Cooled to room temperature is obtained by MgO, ZrO2And Cr2O3The metal composite oxide of composition;
(3) with continuous stirring, this metal composite oxide is added in the hydrazine hydrate aqueous solution that mass fraction is 18%,
Then graphene oxide above-mentioned is also added thereto, is warming up to 45 DEG C, constant temperature stirs 5 hours, is used after natural cooling and filtering
Deionized water wash 3 times, be subsequently placed in 65 DEG C vacuum drying oven dry to get to graphene-supported by MgO, ZrO2And Cr2O3
The composite powder material of composition.
Analysis:This composite powder material is tested with transmission electron microscope, maximum particle diameter is no more than 40nm, average grain diameter
About 30nm;Constituent analysis is carried out to it, it is respectively 9.8%MgO, 6.3%ZrO to measure each component mass percent2, 12.4%
Cr2O3And 71.5%C.
Using:The formaldehyde in air, range of linearity 0.05- are detected using this composite granule as catalytic luminescence sensitive material
17mg/m3, detect and be limited to 0.02mg/m3, other common concurrents do not interfere with.
Embodiment 3
(1) natural graphite is slowly added in oleum with continuous stirring, is warming up to 45 DEG C and delayed after stirring 2 hours
The slow oxalic acid being added with weight such as natural graphites continues that temperature is kept to stir 1 hour, filters and much filtrate is washed to neutrality;
Filter cake is added in the potassium permanganate concentrated sulfuric acid solution that mass fraction is 15%, is warming up to 52 DEG C and continuously stirs 2 hours, slowly
Until the aqueous hydrogen peroxide solution to bubble-free that mass fraction is 25% is added, continues constant temperature and stir 1 hour, filter and will filter out
Object is washed to neutrality, obtains graphene oxide;
(2) magnesium nitrate hexahydrate and tetrahydrated zirconium sulfate are dissolved in the aqueous hydrochloric acid solution that mass fraction is 19% and form solution A,
It is to form solution B in 25% aqueous citric acid solution that six water acetic acid chromium and chromium sulfate, which are dissolved in mass fraction, with continuous stirring, will
Solution A is slowly added in solution B, and agar powder, which is added, after stirring 2 hours, after being warming up to 95 DEG C stirs to being completely dissolved, and is cooled to
Gel formed at room temperature is warming up to 240 DEG C in chamber type electric resistance furnace after drying this gel with the speed per minute for being no more than 3 DEG C,
It keeps this temperature 4 hours, continues to be warming up to 425 DEG C with the speed per minute for being no more than 3 DEG C, keep this temperature 3 hours, it is naturally cold
But it is obtained to room temperature by MgO, ZrO2And Cr2O3The metal composite oxide of composition;
(3) with continuous stirring, this metal composite oxide is added in the hydrazine hydrate aqueous solution that mass fraction is 16%,
Then graphene oxide above-mentioned is also added thereto, is warming up to 45 DEG C, constant temperature stirs 4 hours, is used after natural cooling and filtering
Deionized water wash 3 times, be subsequently placed in 65 DEG C vacuum drying oven dry to get to graphene-supported by MgO, ZrO2And Cr2O3
The composite powder material of composition.
Analysis:This composite powder material is tested with transmission electron microscope, maximum particle diameter is no more than 45nm, average grain diameter
About 32nm;Constituent analysis is carried out to it, it is respectively 8.1%MgO, 5.7%ZrO to measure each component mass percent2, 9.4%
Cr2O3And 76.8%C.
Using:The formaldehyde in air, range of linearity 0.03- are detected using this composite granule as catalytic luminescence sensitive material
15mg/m3, detect and be limited to 0.01mg/m3, other common concurrents do not interfere with.
Embodiment 4
(1) natural graphite is slowly added in oleum with continuous stirring, is warming up to 45 DEG C and delayed after stirring 3 hours
The slow oxalic acid being added with weight such as natural graphites continues that temperature is kept to stir 1 hour, filters and much filtrate is washed to neutrality;
Filter cake is added in the potassium permanganate concentrated sulfuric acid solution that mass fraction is 15%, is warming up to 53 DEG C and continuously stirs 2 hours, slowly
Until the aqueous hydrogen peroxide solution to bubble-free that mass fraction is 25% is added, continues constant temperature and stir 1 hour, filter and will filter out
Object is washed to neutrality, obtains graphene oxide;
(2) oxalic acid dihydrate magnesium and zirconium chloride are dissolved in the aqueous hydrochloric acid solution that mass fraction is 17% and form solution A, it will
It is to form solution B in 27% aqueous citric acid solution that chromium+oxalic acid, which is dissolved in mass fraction, and with continuous stirring, solution A is slowly added to
Agar powder is added in solution B, after stirring 2 hours, after being warming up to 94 DEG C to stir to being completely dissolved, is cooled to room temperature to form gel,
After this gel is dried, 230 DEG C are warming up to the speed per minute for being no more than 3 DEG C in chamber type electric resistance furnace, keeps this temperature 4 small
When, continue to be warming up to 435 DEG C with the speed per minute for being no more than 3 DEG C, keeps this temperature 3 hours, cooled to room temperature obtains
By MgO, ZrO2And Cr2O3The metal composite oxide of composition:
(3) with continuous stirring, this metal composite oxide is added in the hydrazine hydrate aqueous solution that mass fraction is 19%,
Then graphene oxide above-mentioned is also added thereto, is warming up to 45 DEG C, constant temperature stirs 5 hours, is used after natural cooling and filtering
Deionized water wash 3 times, be subsequently placed in 65 DEG C vacuum drying oven dry to get to graphene-supported by MgO, ZrO2And Cr2O3
The composite powder material of composition.
Analysis:This composite powder material is tested with transmission electron microscope, maximum particle diameter is no more than 40nm, average grain diameter
About 30nm;Constituent analysis is carried out to it, it is respectively 8.9%MgO, 6.0%ZrO to measure each component mass percent2, 7.3%
Cr2O3And 77.8%C.
Using:The formaldehyde in air, range of linearity 0.02- are detected using this composite granule as catalytic luminescence sensitive material
15mg/m3, detect and be limited to 0.01mg/m3, other common concurrents do not interfere with.
Embodiment 5
(1) natural graphite is slowly added in oleum with continuous stirring, is warming up to 45 DEG C and delayed after stirring 2 hours
The slow oxalic acid being added with weight such as natural graphites continues that temperature is kept to stir 1 hour, filters and much filtrate is washed to neutrality;
Filter cake is added in the potassium permanganate concentrated sulfuric acid solution that mass fraction is 15%, is warming up to 55 DEG C and continuously stirs 2 hours, slowly
Until the aqueous hydrogen peroxide solution to bubble-free that mass fraction is 25% is added, continues constant temperature and stir 1 hour, filter and will filter out
Object is washed to neutrality, obtains graphene oxide;
(2) magnesium citrate, magnesium acetate and two water nitric acid oxidation zirconiums are dissolved in the aqueous hydrochloric acid solution that mass fraction is 16%
Solution A is formed, it is to form solution B in 29% aqueous citric acid solution that nine water chromic nitrates, which are dissolved in mass fraction, with continuous stirring,
Solution A is slowly added in solution B, agar powder is added after stirring 2 hours, after being warming up to 93 DEG C and stirs to being completely dissolved, cools down
To gel formed at room temperature 248 are warming up to the speed per minute for being no more than 3 DEG C after drying this gel in chamber type electric resistance furnace
DEG C, it keeps this temperature 4 hours, continues to be warming up to 445 DEG C with the speed per minute for being no more than 3 DEG C, keep this temperature 3 hours, from
So it is cooled to room temperature to obtain by MgO, ZrO2And Cr2O3The metal composite oxide of composition;
(3) with continuous stirring, this metal composite oxide is added in the hydrazine hydrate aqueous solution that mass fraction is 17%,
Then graphene oxide above-mentioned is also added thereto, is warming up to 45 DEG C, constant temperature stirs 4 hours, is used after natural cooling and filtering
Deionized water wash 3 times, be subsequently placed in 65 DEG C vacuum drying oven dry to get to graphene-supported by MgO, ZrO2And Cr2O3
The composite powder material of composition.
Analysis:This composite powder material is tested with transmission electron microscope, maximum particle diameter is no more than 44nm, average grain diameter
About 32nm;Constituent analysis is carried out to it, it is respectively 10.5%MgO, 5.2%ZrO to measure each component mass percent2、
10.7%Cr2O3And 73.6%C.
Using:The formaldehyde in air, range of linearity 0.03- are detected using this composite granule as catalytic luminescence sensitive material
15mg/m3, detect and be limited to 0.01mg/m3, other common concurrents do not interfere with.
Claims (2)
1. a kind of high selection measures the sensitive material of trace formaldehyde in air, it is characterized in that graphene-supported by MgO, ZrO2With
Cr2O3Composite powder material of the grain size of composition no more than 45nm, the wherein mass percent of each component ranging from 8-12%MgO,
5-8%ZrO2, 7-13%Cr2O3And 70-80%C, preparation method are:(1) natural graphite is slowly added to continuous stirring
It in oleum, is warming up to 45 DEG C and is slowly added to the oxalic acid with weight such as natural graphites after stirring 2-3 hours, continue to keep temperature
Degree stirring 1 hour, filters and much filtrate is washed to neutrality;The potassium permanganate concentrated sulfuric acid that mass fraction is 15% is added in filter cake
It in solution, is warming up to 50-55 DEG C and continuously stirs 2 hours, be slowly added to the aqueous hydrogen peroxide solution that mass fraction is 25% extremely
Until bubble-free, continues constant temperature and stir 1 hour, filter and much filtrate is washed to neutrality, obtain graphene oxide;(2) by magnesium
Salt and zirconates, which are dissolved in the aqueous hydrochloric acid solution that mass fraction is 15-20%, forms solution A, and it is 20- that chromic salts, which is dissolved in mass fraction,
Solution B is formed in 30% aqueous citric acid solution, and with continuous stirring, solution A is slowly added in solution B, after stirring 2 hours,
Agar powder is added after being warming up to 92-95 DEG C to stir to being completely dissolved, is cooled to room temperature to form gel, after this gel is dried,
It is warming up to 200-250 DEG C with the speed per minute for being no more than 3 DEG C in chamber type electric resistance furnace, keeps this temperature 4 hours, is continued with every point
Speed of the clock no more than 3 DEG C is warming up to 400-450 DEG C, keeps this temperature 3 hours, cooled to room temperature is obtained by MgO, ZrO2
And Cr2O3The metal composite oxide of composition;(3) with continuous stirring, it is by this metal composite oxide addition mass fraction
In the hydrazine hydrate aqueous solution of 15-20%, then graphene oxide above-mentioned is also added thereto, is warming up to 45 DEG C, constant temperature stirring
4-5 hours, natural cooling was simultaneously washed with deionized 3 times after filtering, and is subsequently placed in 65 DEG C of vacuum drying oven and dries to get to stone
The load of black alkene by MgO, ZrO2And Cr2O3The composite powder material of composition.
2. a kind of high selection according to claim 1 measures the sensitive material of trace formaldehyde in air, it is characterized in that described
Magnesium salts be the anhydride of magnesium chloride, magnesium sulfate, magnesium nitrate, magnesium oxalate, magnesium citrate and magnesium acetate or one kind of hydrate or
Several mixtures, zirconates are anhydride or the hydration of basic zirconium chloride, acetic acid zirconium, zirconium sulfate, zirconium chloride and nitric acid oxidation zirconium
One or more of mixtures of object, chromic salts is the nothing of chromium chloride, perchloric acid chromium, chromic acetate, chromium+oxalic acid, chromic nitrate and chromium sulfate
One or more of mixtures of water object or hydrate.