CN108794724A - A kind of tough pet toy and manufacturing method - Google Patents
A kind of tough pet toy and manufacturing method Download PDFInfo
- Publication number
- CN108794724A CN108794724A CN201710303510.XA CN201710303510A CN108794724A CN 108794724 A CN108794724 A CN 108794724A CN 201710303510 A CN201710303510 A CN 201710303510A CN 108794724 A CN108794724 A CN 108794724A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixture
- pet toy
- polyether
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to toy material processing technique field, especially a kind of manufacturing method of pet toy materials, by being made according to the following raw material of mass percent meter when processing:High activity end hydroxy polyether(FA703)50 parts, high activity graft polyether(KGF545)50 parts, polyether modified siloxane(DC2525)0.25 part, 33% triethylenediamine solution(A-33)0.7 part, catalyst(A-300)0.8 part, 1.4- butanediols(1.4BD)8-12 parts, catalyst(A-1)0.15 part, water(H20)0.2 part, a fluorine dichloroethanes(141b)15-25 parts and more phenylmethane polyisocyanates(SUP-2433);The material is not have good toughness, anti-tear stinging property, the short problem of service life existing for the material that solves used in current pet toy.
Description
Technical field
The present invention relates to toy material processing technique field, especially a kind of manufacturing method of pet toy materials.
Background technology
It is rubber, silica gel, lint etc. that the material of pet toy on the market is more at present, these materials do not have good
Toughness, anti-tear stinging property is very limited, and service life is short.
Invention content
The present invention using one kind is special to solve the above problems, manufacture pet toy from skinning material, good toughness can be held
Power is pullled by 60 kilograms of biting forces and 20 kilograms, service life is long.
The material of a kind of tough pet toy of the present invention, by being made according to the raw material of following proportioning:
By high activity end hydroxy polyether(FA703)50 parts, high activity graft polyether(KGF545)50 parts, polyether modified siloxane
(DC2525)0.25 part, 33% triethylenediamine solution(A-33)0.7 part, catalyst(A-300)0.8 part, 1.4- butanediols
(1.4BD)8-12 parts, catalyst(A-1)0.15 part, water(H20)0.2 part, a fluorine dichloroethanes(141b)15-25 parts composition
Mixture A and more phenylmethane polyisocyanates(SUP-2433), wherein mixture A and more phenylmethane polyisocyanates
(SUP-2433)Ratio be 100:52-55.
A kind of manufacturing method of tough pet toy materials, includes the following steps:
Step 1:Every ingredient in mixture A is mixed 90 minutes according to the proportioning;
Step 2:By the mixture A stirred and more phenylmethane polyisocyanates(SUP-2433)With 100:The ratio of 52-55
It is uniformly mixed in polyurethane foaming machine;
Step 3:By mixture A and more phenylmethane polyisocyanates(SUP-2433)Mixture cast in a mold, pass through
45 degree of high temperature foaming in 6 minutes, can be obtained the product after die sinking.
Specific implementation mode
Below by specific implementation mode, the present invention is described in further detail, but the present invention is not only limited in these
Example.
Step 1:By high activity end hydroxy polyether(FA703)50 parts, high activity graft polyether(KGF545)50 parts, polyethers
Modified siloxane(DC2525)0.25 part, 33% triethylenediamine solution(A-33)0.7 part, catalyst(A-300)0.8 part,
1.4- butanediol(1.4BD)8-12 parts, catalyst(A-1)0.15 part, water(H20)0.2 part, a fluorine dichloroethanes(141b)15-
25 parts successively put into agitator tank in be mixed 90 minutes, obtain mixture A;
Step 2:By the mixture A stirred and more phenylmethane polyisocyanates(SUP-2433)With 100:The ratio of 52-55
It is uniformly mixed in polyurethane foaming machine;
Step 3:By mixture A and more phenylmethane polyisocyanates(SUP-2433)Mixture cast in a mold, pass through
45 degree of high temperature foaming in 6 minutes, can be obtained the product after die sinking.
According to the pet toy good toughness that step as above manufactures, the biting force that can bear 60 kilograms and 20 kilograms pull power,
Service life is long.
The present invention is not limited to above-mentioned specific embodiment, those skilled in the art from above-mentioned design,
Without performing creative labour, made various transformation are within the scope of the present invention.
Claims (4)
1. a kind of tough pet toy, which is characterized in that including by high activity end hydroxy polyether(FA703)50 parts, high activity connects
Branch polyethers(KGF545)50 parts, polyether modified siloxane(DC2525)0.25 part, 33% triethylenediamine solution(A-33)0.7
Part, catalyst(A-300)0.8 part, 1.4- butanediols(1.4BD)8-12 parts, catalyst(A-1)0.15 part, water(H20)0.2 part,
One fluorine dichloroethanes(141b)The 15-25 parts of mixture A formed and more phenylmethane polyisocyanates(SUP-2433)Group
At.
2. tough pet toy according to claim 1, it is characterised in that mixture A and more phenylmethane polyisocyanates
(SUP-2433)Ratio be 100:52-55.
3. the tough pet toy according to claim 1 and 2, it is characterised in that can bear 60 kilograms biting force and 20 kilograms
Pull power.
4. a kind of manufacturing method of tough pet toy, which is characterized in that include the following steps:
Step 1:By high activity end hydroxy polyether(FA703)50 parts, high activity graft polyether(KGF545)It is 50 parts, polyether-modified
Siloxanes(DC2525)0.25 part, 33% triethylenediamine solution(A-33)0.7 part, catalyst(A-300)0.8 part, 1.4- fourths
Glycol(1.4BD)8-12 parts, catalyst(A-1)0.15 part, water(H20)0.2 part, a fluorine dichloroethanes(141b)15-25 parts according to
It is mixed 90 minutes in secondary input agitator tank, obtains mixture A;
Step 2:By the mixture A stirred and more phenylmethane polyisocyanates(SUP-2433)With 100:The ratio of 52-55
It is uniformly mixed in polyurethane foaming machine;
Step 3:By mixture A and more phenylmethane polyisocyanates(SUP-2433)Mixture cast in a mold, pass through
45 degree of high temperature foaming in 6 minutes, can be obtained the product after die sinking.