CN108789179A - 一种磨钢球砂轮配方 - Google Patents

一种磨钢球砂轮配方 Download PDF

Info

Publication number
CN108789179A
CN108789179A CN201810535218.5A CN201810535218A CN108789179A CN 108789179 A CN108789179 A CN 108789179A CN 201810535218 A CN201810535218 A CN 201810535218A CN 108789179 A CN108789179 A CN 108789179A
Authority
CN
China
Prior art keywords
parts
abrasive
abrasion
steel ball
wheel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810535218.5A
Other languages
English (en)
Inventor
方元文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Bless Technology Co Ltd
Original Assignee
Anhui Bless Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Bless Technology Co Ltd filed Critical Anhui Bless Technology Co Ltd
Priority to CN201810535218.5A priority Critical patent/CN108789179A/zh
Publication of CN108789179A publication Critical patent/CN108789179A/zh
Pending legal-status Critical Current

Abstract

本发明涉及砂轮技术领域，具体是公开了本发明所述的一种磨钢球砂轮配方，由下列重量份的原料制成：一种磨钢球砂轮配方，由下列重量份的原料制成：棕刚玉磨料18～24份，白刚玉磨料6～12份，碳化硅磨料10～20份，长石20～30份，粘土15～20份，硼玻璃2～5份，结合剂25～40份，本发明克服了现有技术的不足，利用棕刚玉磨料，白刚玉磨料，碳化硅磨料，长石，粘土，硼玻璃，结合剂制作出磨钢球砂轮，不仅有较高的耐用度又有较高的磨削效率，同时耐热性能好，在焙烧中成品率高。

Description

一种磨钢球砂轮配方
技术领域
本发明涉及砂轮技术领域，具体属于一种磨钢球砂轮配方。
背景技术
磨钢球砂轮是用于磨削直径在 76.20mm 以下球形钢球的专用砂轮，具有规格大、粒度细、硬度高、密度大等特点，广泛应用于机械、轴承工业。目前，所有磨钢球砂轮生产厂家在配方设计时，都是采用棕刚玉和碳化硅的混合磨料制造磨钢球砂轮，因为磨钢砂轮密度大、硬度高，单纯采用提高成型压强来提高其密度是有一定限度的，故要求砂轮烧后有较大收缩来提高砂轮密度。而结合剂的耐火度不宜偏高，因此，如采用单一棕刚玉的细粒度磨料，因其中杂质含量较高，砂轮焙烧过程极易整个发泡 ；适当加入碳化硅磨料，可改善制品的性能，有利于提高制品的强度和硬度。但随着国民经济的发展，砂轮使用厂家对磨钢球砂轮的要求越来越高，不但要求砂轮具有较高的耐用度，同时还要求其具有较高的磨削效率。众所周知，要使磨钢球砂轮具有较高的耐用度，则砂轮的硬度较高，这时其磨削效率下降；反之，若要提高磨削效率，则必须降低砂轮的硬度，耐用度下降。因此，在不降低磨钢球砂轮的硬度前提下、提高其磨削效率，提高耐热性，以及砂轮得成品率，成为砂轮制造行业的一个难题。
发明内容
本发明的目的是提供了一种磨钢球砂轮配方，克服了现有技术的不足，利用棕刚玉磨料，白刚玉磨料，碳化硅磨料，长石，粘土，硼玻璃，结合剂制作出磨钢球砂轮，不仅有较高的耐用度又有较高的磨削效率，同时耐热性能好，在焙烧中成品率高。
为解决上述问题，本发明所采取的技术方案如下：
一种磨钢球砂轮配方，由下列重量份的原料制成：棕刚玉磨料18～24 份，白刚玉磨料6～12 份，碳化硅磨料 10～20 份，长石 20～30 份，粘土 15～20份，硼玻璃2～5份，结合剂25～40份。
进一步，由下列重量份的原料制成：棕刚玉磨料120 份，白刚玉磨料8 份，碳化硅磨料 16份，长石 26份，粘土 17 份，硼玻璃3份，结合剂30份。
进一步，所述的结合剂由下列重量份的原料制成：氧化硅40～60份、氧化铝20～30份、氧化铁0.5～2份、氧化钙0.1～0.5份、氧化硼1～3份、氧化锰2～5份。
进一步，所述结合剂由下列重量份的原料制成：氧化硅45份、氧化铝23份、氧化铁0.9份、氧化钙0.3份、氧化硼2.1份、氧化锰4份。
进一步，所述的棕刚玉磨料，白刚玉磨料，碳化硅磨料粒度为F170～F220
本发明与现有技术相比较，本发明的实施效果如下：
本发明所述一种磨钢球砂轮配方，利用棕刚玉磨料，白刚玉磨料，碳化硅磨料，长石，粘土，硼玻璃，结合剂制作出磨钢球砂轮，不仅有较高的耐用度又有较高的磨削效率，同时耐热性能好，在焙烧中成品率高。
具体实施方式
下面结合实施例对本发明作进一步的描述，但本发明不仅限于这些实例，在为脱离本发明宗旨的前提下，所为任何改进均落在本发明的保护范围之内。
实施例1
本发明所述的一种磨钢球砂轮配方，由下列重量份的原料制成：一种磨钢球砂轮配方，由下列重量份的原料制成：棕刚玉磨料18～24 份，白刚玉磨料6～12 份，碳化硅磨料 10～20 份，长石 20～30 份，粘土 15～20份，硼玻璃2～5份，结合剂25～40份。
进一步，所述的结合剂由下列重量份的原料制成：氧化硅40～60份、氧化铝20～30份、氧化铁0.5～2份、氧化钙0.1～0.5份、氧化硼1～3份、氧化锰2～5份。
进一步，所述的棕刚玉磨料，白刚玉磨料，碳化硅磨料粒度为F170～F220
实施例2
本发明一种磨钢球砂轮配方，由下列重量份的原料制成：棕刚玉磨料120 份，白刚玉磨料8 份，碳化硅磨料 16份，长石 26份，粘土 17 份，硼玻璃3份，结合剂30份。
所述结合剂由下列重量份的原料制成：氧化硅45份、氧化铝23份、氧化铁0.9份、氧化钙0.3份、氧化硼2.1份、氧化锰4份。
所述的棕刚玉磨料，白刚玉磨料，碳化硅磨料粒度为F170～F220
以上内容仅仅是对本发明构思所作的举例和说明，所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，只要不偏离发明的构思或者超越本权利要求书所定义的范围，均应属于本发明的保护范围。

Claims (5)

1.一种磨钢球砂轮配方，其特征在于：由下列重量份的原料制成：棕刚玉磨料18～24份，白刚玉磨料6～12 份，碳化硅磨料 10～20 份，长石 20～30 份，粘土 15～20份，硼玻璃2～5份，结合剂25～40份。
2.根据权利要求1所述的一种磨钢球砂轮配方，其特征在于：由下列重量份的原料制成：棕刚玉磨料120 份，白刚玉磨料8 份，碳化硅磨料 16份，长石 26份，粘土 17 份，硼玻璃3份，结合剂30份。
3.根据权利要求1或2任一项所述的一种磨钢球砂轮配方，其特征在于：所述的结合剂由下列重量份的原料制成：氧化硅40～60份、氧化铝20～30份、氧化铁0.5～2份、氧化钙0.1～0.5份、氧化硼1～3份、氧化锰2～5份。
4.根据权利要求3任一项所述的一种磨钢球砂轮配方，其特征在于：所述结合剂由下列重量份的原料制成：氧化硅45份、氧化铝23份、氧化铁0.9份、氧化钙0.3份、氧化硼2.1份、氧化锰4份。
5.根据权利要求1或2任一项所述的一种磨钢球砂轮配方，其特征在于：所述的棕刚玉磨料，白刚玉磨料，碳化硅磨料粒度为F170～F2201。
CN201810535218.5A 2018-05-30 2018-05-30 一种磨钢球砂轮配方 Pending CN108789179A (zh)