CN108753099A - A kind of anti-ultraviolet paint for textile fabric - Google Patents
A kind of anti-ultraviolet paint for textile fabric Download PDFInfo
- Publication number
- CN108753099A CN108753099A CN201810406283.8A CN201810406283A CN108753099A CN 108753099 A CN108753099 A CN 108753099A CN 201810406283 A CN201810406283 A CN 201810406283A CN 108753099 A CN108753099 A CN 108753099A
- Authority
- CN
- China
- Prior art keywords
- parts
- textile fabric
- ultraviolet
- carboxymethyl cellulose
- ultraviolet paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The modified epoxy that the present invention is made using epoxy resin, ceramic by titanium dioxide, zinc oxide, carboxymethyl cellulose synergistic effect is major ingredient, anti-ultraviolet paint is made with octyl methoxycinnamate, cinnamate and a variety of auxiliary agents in association, the anti-ultraviolet paint is suitable for the final finishing of textile fabric, the ultraviolet resistance of textile fabric can be significantly improved by being acted on after textile fabric, so that UVA transmitances, UVB transmitances is below 4%, UPF and is more than 30;And the textile fabric after collated has preferable preventing ultraviolet effect stability, and stronger ultraviolet resistance is still kept after washing 50 times;It is safe to use simultaneously, any adverse effect will not be caused after long-time service to human body, is avoided using murder by poisoning problem existing for conventional chemical class ultra-violet absorber.
Description
Technical field:
The present invention relates to technical field of textile fabric, and in particular to a kind of anti-ultraviolet paint for textile fabric.
Background technology:
It is also higher for the requirement for wearing quality as people's living standard gradually rises, it does not only require comfortably, also needs
Have both multi-functional, according to different lifestyles, the function of being worn clothes is also different, when climbing the mountain such as, in response to the low of environment
The ultraviolet light of warm, rainy and high mountain exposure, the then clothes worn must then have the functions such as heat preservation, waterproof and uvioresistant;When
When carrying out outdoor sports, then light and handy, moisture absorbing and sweat releasing, rapid-curing cutback and the fabric of the functions such as ventilative are needed, and tradition applies to kinetic system
The knitting fabric of row mostly uses common circular-section terylene low stretch yarn raw material, using manufacture craft after original dyeing, water
It is more poor with light shine fastness to wash loose colour, color becomes to wither dark after long-term outdoor moves dressing, feels hard and sweat is led in moisture absorption
Poor performance, dress is sultry airtight, and comfort is poor;Even if common people do not carry out it is any it is movable in the case of, still require that and worn
Clothes must have the quality of high quality, in addition, as context pollutes getting worse, ciril disease also occurs in succession, such as
Too coarse cloth textile can cause some people skin to generate allergy, or the body of allergy is easy tod produce to external environment
Matter causes modern also gradually to pay attention to the idea of antibacterial, the antibacterial clothing needed for previous only medical staff and antibacterial utensil,
Also the articles for use of daily life are gradually used in.
For human body, suitable ultraviolet radiation has bactericidal effect and can promote the synthesis of vitamin D, is conducive to people
Body health.But under burning sun prolonged exposure, human skin can lose resilience, easily burn, and erythema or bubble occur.It crosses
The ultraviolet light irradiation of amount can also induce skin disease (such as dermatitis, pigment asteatosis cutis) or even cutaneum carcinoma, promote the generation of cataract simultaneously
Reduce the immune function of human body.
Invention content:
Technical problem to be solved by the present invention lies in provide it is a kind of have excellent performance, stability is good, safe is used for
The anti-ultraviolet paint of textile fabric.
The technical problems to be solved by the invention are realized using technical solution below:
A kind of anti-ultraviolet paint for textile fabric is made of the raw material of following parts by weight:Modified epoxy
45-75 parts, 5-12 parts of octyl methoxycinnamate, 8-15 parts of cinnamate, 5-10 parts of potassium dihydrogen phosphate, cation polypropylene acyl
4-9 parts of amine, 3-6 parts of dipropylene glycol methyl ether, 1-5 parts of polyvinyl alcohol, 1-3 parts of glycerol stearate, 0.5-2 parts of carboxymethyl cellulose,
0.3-2 parts of sodium citrate, 0.2-1 parts of Phenoxyethanol, 120-150 parts of deionized water.
The raw material of the anti-ultraviolet paint for textile fabric, preferably following parts by weight is made:Modified epoxy tree
60 parts of fat, 9 parts of octyl methoxycinnamate, 12 parts of cinnamate, 8 parts of potassium dihydrogen phosphate, 7 parts of cationic polyacrylamide, two
5 parts of propylene glycol monomethyl ether, 3 parts of polyvinyl alcohol, 2 parts of glycerol stearate, 1.2 parts of carboxymethyl cellulose, 1 part of sodium citrate, benzene oxygen second
0.6 part of alcohol, 140 parts of deionized water.
The modified epoxy is made of epoxy resin, ceramic, titanium dioxide, zinc oxide, carboxymethyl cellulose,
Preparation method is:Epoxy resin and ceramic are mixed evenly, the anhydrous second that 3-5 times of weight is inwardly added is stirred
Alcohol stirs to being completely dissolved, titanium dioxide, zinc oxide and the 95wt% concentrated sulfuric acids is added, in microwave frequency after being sufficiently mixed
Microwave treatment 10-30min under 2450MHz, power 700W, adds carboxymethyl cellulose, with the blender of 800-1000r/min
After stirring 5-10 minutes, then with microwave treatment 10-20min, it is transferred to sealing and standing in -5 DEG C of environment immediately after microwave treatment
Then mixture is sent into spray dryer by 3h, powder is made to get modified epoxy tree in the dry gained ground machine of particle
Fat.
The epoxy resin, ceramic, titanium dioxide, zinc oxide, carboxymethyl cellulose mass fraction ratio are 5:2:1:
2:0.5。
The anti-ultraviolet paint for textile fabric, preparation method include the following steps:
(1) potassium dihydrogen phosphate, cationic polyacrylamide, polyvinyl alcohol, deionized water are mixed, is heated to 120-150
DEG C insulated and stirred mixes 10-20min, adds glycerol stearate, and after stirring evenly, mixing is kept the temperature at a temperature of 120-130 DEG C
5-10min obtains substance I;
(2) substance I, dipropylene glycol methyl ether, carboxymethyl cellulose are added into modified epoxy, stirs evenly and heats
To 100-130 DEG C of heat preservation mixing 15-25min, substance II is obtained;
(3) octyl methoxycinnamate, cinnamate are added into substance II, is put into blender and is stirred, stirs
Speed is 800-1000r/min, and mixing time is 10-20 minutes, obtains substance III;
(4) sodium citrate, Phenoxyethanol are added into substance III, puts it into microwave frequency after mixing
Up to anti-ultraviolet paint after microwave treatment 5-15min under 2450MHz, output power 700W, standing 10min.
The beneficial effects of the invention are as follows:The present invention passes through titanium dioxide, zinc oxide, carboxylic first with epoxy resin, ceramic
The modified epoxy that base cellulose synergistic effect makes is major ingredient, and association is with octyl methoxycinnamate, cinnamate and more
Anti-ultraviolet paint is made in kind auxiliary agent, which is suitable for the final finishing of textile fabric, is acted on woven face
The ultraviolet resistance that textile fabric can be significantly improved after material makes UVA transmitances, UVB transmitances be below 4%, UPF and is more than
30;And the textile fabric after collated has preferable preventing ultraviolet effect stability, still keeps stronger after washing 50 times
Ultraviolet resistance;It is safe to use simultaneously, any adverse effect will not be caused after long-time service to human body, is avoided using normal
Advise murder by poisoning problem existing for chemical classes ultra-violet absorber.
Specific implementation mode:
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment 1
A kind of anti-ultraviolet paint for textile fabric is made of the raw material of following parts by weight:45 parts of epoxy resin,
5 parts of octyl methoxycinnamate, 8 parts of cinnamate, 5 parts of potassium dihydrogen phosphate, 4 parts of cationic polyacrylamide, dipropylene glycol first
3 parts of ether, 1 part of polyvinyl alcohol, 1 part of glycerol stearate, 0.5 part of carboxymethyl cellulose, 0.3 part of sodium citrate, Phenoxyethanol 0.2
Part, 120 parts of deionized water.
The anti-ultraviolet paint for textile fabric, preparation method include the following steps:
(1) potassium dihydrogen phosphate, cationic polyacrylamide, polyvinyl alcohol, deionized water are mixed, is heated to 120 DEG C of guarantors
Temperature is stirred 10min, adds glycerol stearate, and after stirring evenly, heat preservation mixing 5min, obtains object at a temperature of 120 DEG C
Matter I;
(2) substance I, dipropylene glycol methyl ether, carboxymethyl cellulose are added into epoxy resin, stirs evenly and is heated to
100 DEG C of heat preservation mixing 15min, obtain substance II;
(3) octyl methoxycinnamate, cinnamate are added into substance II, is put into blender and is stirred, stirs
Speed is 800r/min, and mixing time is 10 minutes, obtains substance III;
(4) sodium citrate, Phenoxyethanol are added into substance III, after mixing up to antiultraviolet after standing 10min
Coating.
Embodiment 2
A kind of anti-ultraviolet paint for textile fabric is made of the raw material of following parts by weight:Modified epoxy
75 parts, 12 parts of octyl methoxycinnamate, 15 parts of cinnamate, 10 parts of potassium dihydrogen phosphate, 9 parts of cationic polyacrylamide, two
6 parts of propylene glycol monomethyl ether, 5 parts of polyvinyl alcohol, 3 parts of glycerol stearate, 2 parts of carboxymethyl cellulose, 2 parts of sodium citrate, Phenoxyethanol 1
Part, 150 parts of deionized water.
The modified epoxy is made of epoxy resin, ceramic, titanium dioxide, zinc oxide, carboxymethyl cellulose,
Preparation method is:Epoxy resin and ceramic are mixed evenly, the absolute ethyl alcohol that 4 times of weight is inwardly added is stirred,
Stirring adds titanium dioxide, zinc oxide and the 95wt% concentrated sulfuric acids, in microwave frequency after being sufficiently mixed to being completely dissolved
Microwave treatment 20min under 2450MHz, power 700W, adds carboxymethyl cellulose, and 10 points are stirred with the blender of 900r/min
Zhong Hou, then with microwave treatment 15min, it is transferred to sealing and standing 3h in -5 DEG C of environment immediately after microwave treatment, it then will mixing
Object is sent into spray dryer, and powder is made to get modified epoxy in the dry gained ground machine of particle.
The epoxy resin, ceramic, titanium dioxide, zinc oxide, carboxymethyl cellulose mass fraction ratio are 5:2:1:
2:0.5。
The anti-ultraviolet paint for textile fabric, preparation method include the following steps:
(1) potassium dihydrogen phosphate, cationic polyacrylamide, polyvinyl alcohol, deionized water are mixed, is heated to 150 DEG C of guarantors
Temperature is stirred 20min, adds glycerol stearate, and after stirring evenly, heat preservation mixing 10min, obtains object at a temperature of 130 DEG C
Matter I;
(2) substance I, dipropylene glycol methyl ether, carboxymethyl cellulose are added into modified epoxy, stirs evenly and heats
To 130 DEG C of heat preservation mixing 25min, substance II is obtained;
(3) octyl methoxycinnamate, cinnamate are added into substance II, is put into blender and is stirred, stirs
Speed is 1000r/min, and mixing time is 20 minutes, obtains substance III;
(4) sodium citrate, Phenoxyethanol are added into substance III, after mixing up to antiultraviolet after standing 10min
Coating.
Embodiment 3
A kind of anti-ultraviolet paint for textile fabric is made of the raw material of following parts by weight:Modified epoxy
60 parts, 9 parts of octyl methoxycinnamate, 12 parts of cinnamate, 8 parts of potassium dihydrogen phosphate, 7 parts of cationic polyacrylamide, dipropyl
5 parts of glycol methyl ether, 3 parts of polyvinyl alcohol, 2 parts of glycerol stearate, 1.2 parts of carboxymethyl cellulose, 1 part of sodium citrate, Phenoxyethanol
0.6 part, 140 parts of deionized water.
The modified epoxy is made of epoxy resin, ceramic, titanium dioxide, zinc oxide, carboxymethyl cellulose,
Preparation method is:Epoxy resin and ceramic are mixed evenly, the absolute ethyl alcohol that 4 times of weight is inwardly added is stirred,
Stirring adds titanium dioxide, zinc oxide and the 95wt% concentrated sulfuric acids, in microwave frequency after being sufficiently mixed to being completely dissolved
Microwave treatment 20min under 2450MHz, power 700W, adds carboxymethyl cellulose, and 10 points are stirred with the blender of 900r/min
Zhong Hou, then with microwave treatment 15min, it is transferred to sealing and standing 3h in -5 DEG C of environment immediately after microwave treatment, it then will mixing
Object is sent into spray dryer, and powder is made to get modified epoxy in the dry gained ground machine of particle.
The epoxy resin, ceramic, titanium dioxide, zinc oxide, carboxymethyl cellulose mass fraction ratio are 5:2:1:
2:0.5。
The anti-ultraviolet paint for textile fabric, preparation method include the following steps:
(1) potassium dihydrogen phosphate, cationic polyacrylamide, polyvinyl alcohol, deionized water are mixed, is heated to 140 DEG C of guarantors
Temperature is stirred 15min, adds glycerol stearate, and after stirring evenly, heat preservation mixing 8min, obtains substance at a temperature of 15 DEG C
I;
(2) substance I, dipropylene glycol methyl ether, carboxymethyl cellulose are added into modified epoxy, stirs evenly and heats
To 120 DEG C of heat preservation mixing 20min, substance II is obtained;
(3) octyl methoxycinnamate, cinnamate are added into substance II, is put into blender and is stirred, stirs
Speed is 900r/min, and mixing time is 15 minutes, obtains substance III;
(4) sodium citrate, Phenoxyethanol are added into substance III, puts it into microwave frequency after mixing
Up to anti-ultraviolet paint after microwave treatment 10min under 2450MHz, output power 700W, standing 10min.
Table 1 is through anti-ultraviolet paint of the present invention treated textile fabric ultraviolet resistance
Control group is commercially available common anti-ultraviolet cloth.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (5)
1. a kind of anti-ultraviolet paint for textile fabric is made of the raw material of following parts by weight:
45-75 parts of modified epoxy, 5-12 parts of octyl methoxycinnamate, 8-15 parts of cinnamate, potassium dihydrogen phosphate 5-10
Part, 4-9 parts of cationic polyacrylamide, 3-6 parts of dipropylene glycol methyl ether, 1-5 parts of polyvinyl alcohol, 1-3 parts of glycerol stearate, carboxylic first
0.5-2 parts of base cellulose, 0.3-2 parts of sodium citrate, 0.2-1 parts of Phenoxyethanol, 120-150 parts of deionized water.
2. the anti-ultraviolet paint according to claim 1 for textile fabric, which is characterized in that preferred following parts by weight
Several raw materials are made:60 parts of modified epoxy, 9 parts of octyl methoxycinnamate, 12 parts of cinnamate, 8 parts of potassium dihydrogen phosphate,
7 parts of cationic polyacrylamide, 5 parts of dipropylene glycol methyl ether, 3 parts of polyvinyl alcohol, 2 parts of glycerol stearate, carboxymethyl cellulose 1.2
Part, 1 part of sodium citrate, 0.6 part of Phenoxyethanol, 140 parts of deionized water.
3. the anti-ultraviolet paint according to claim 1 or 2 for textile fabric, it is characterised in that:The modified ring
Oxygen resin is made of epoxy resin, ceramic, titanium dioxide, zinc oxide, carboxymethyl cellulose, and preparation method is:By ring
Oxygen resin is mixed evenly with ceramic, stirs the absolute ethyl alcohol that 3-5 times of weight is inwardly added, stirring to being completely dissolved,
Titanium dioxide, zinc oxide and the 95wt% concentrated sulfuric acids are added, it is micro- under microwave frequency 2450MHz, power 700W after being sufficiently mixed
Wave handles 10-30min, adds carboxymethyl cellulose, after being stirred 5-10 minutes with the blender of 800-1000r/min, then uses
Microwave treatment 10-20min is transferred to sealing and standing 3h in -5 DEG C of environment after microwave treatment, is then sent into mixture immediately
In spray dryer, powder is made to get modified epoxy in the dry gained ground machine of particle.
4. the anti-ultraviolet paint according to claim 3 for textile fabric, it is characterised in that:The epoxy resin,
Ceramic, titanium dioxide, zinc oxide, carboxymethyl cellulose mass fraction ratio are 5:2:1:2:0.5.
5. the anti-ultraviolet paint according to claim 1 or 2 for textile fabric, which is characterized in that preparation method
Include the following steps:
(1) potassium dihydrogen phosphate, cationic polyacrylamide, polyvinyl alcohol, deionized water are mixed, is heated to 120-150 DEG C of guarantor
Temperature is stirred 10-20min, adds glycerol stearate, after stirring evenly, heat preservation mixing 5- at a temperature of 120-130 DEG C
10min obtains substance I;
(2) substance I, dipropylene glycol methyl ether, carboxymethyl cellulose are added into modified epoxy, stirs evenly and is heated to
100-130 DEG C of heat preservation mixing 15-25min, obtains substance II;
(3) octyl methoxycinnamate, cinnamate are added into substance II, is put into blender and is stirred, mixing speed
For 800-1000r/min, mixing time is 10-20 minutes, obtains substance III;
(4) sodium citrate, Phenoxyethanol are added into substance III, puts it into microwave frequency 2450MHz, defeated after mixing
Go out microwave treatment 5-15min under power 700W, stands after 10min up to anti-ultraviolet paint.