CN108751882A - A kind of quick-dry type bi-component water-proof ceramic tile gum and preparation method thereof - Google Patents
A kind of quick-dry type bi-component water-proof ceramic tile gum and preparation method thereof Download PDFInfo
- Publication number
- CN108751882A CN108751882A CN201810750890.6A CN201810750890A CN108751882A CN 108751882 A CN108751882 A CN 108751882A CN 201810750890 A CN201810750890 A CN 201810750890A CN 108751882 A CN108751882 A CN 108751882A
- Authority
- CN
- China
- Prior art keywords
- component
- water
- ceramic tile
- liquid material
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of quick-dry type bi-component water-proof ceramic tile gums, and it includes liquid material component A and powder component B, the weight ratio of the two is 1：(2-3)；The weight percentages of components of liquid material component A is：30.0%-55.0% acrylic emulsions, 5.0%-10.0% styrene-butadiene emulsions, 0.2%-0.3% preservatives, 0.2%-0.3% antifoaming agent, 0-0.5% silane coupling agents, 33.9%-64.6% water；The weight percentages of components of powder component B is：40.0%-45.0% Portland cements, 10.0%-15.0% sulphate aluminium cements, 3.0%-5.0% gypsum, 5.0%-8.0% coarse whitings, 25.91%-41.45% river sands, 0.5%-1.0% water-reducing agents, 0.01%-0.03% antifoaming agent, 0.04%-0.06% cellulose ethers.Also disclose a kind of preparation method of quick-dry type bi-component water-proof ceramic tile gum.The ceramic tile gum of the present invention not only has faster hydration reaction process, and drying time is short, and has water resistance and outstanding adhesion strength.
Description
Technical field
The present invention relates to building, decoration construction technical fields, and in particular to a kind of quick-dry type bi-component water-proof ceramic tile gum
And preparation method thereof.
Background technology
Ceramic tile is applied by a wide range of in inner-outer wall, ground, kitchen, toilet, sun as one kind in building and ornament materials
The places such as platform, pond.But there are stain resistances that poor, surface easily whitens, long-term soaked watermark etc. easily occur and lacks for common ceramic tile
Point, these defects seriously affect the long-term decorative effect of ceramic tile, so people more and more select vitrified tile at present.
Vitrified tile is that water absorption rate is low (0.5% or less), and color saturation is good relative to the advantages of common ceramic tile, brick body compared with
Thin but can still have higher flexural strength, physicochemical property is stablized, good corrosion resistance, and stain resistance is good.The extremely low suction of vitrified tile
Water rate can cause glue for tile to be not easy to be adsorbed on the vitrified tile back side, so easily occurring hollowing when being pasted with glue for tile, flaking, fall off
The problems such as.In order to solve the problems, such as that vitrified tile is not easy to paste, Main is to brush one of ceramic tile gum, purpose at the vitrified tile back side
The adsorption capacity that the vitrified tile back side is improved by this road ceramic tile gum, ensure be not in after pasting vitrified tile with glue for tile
Hollowing, the problems such as flaking, falling off.
But ceramic tile gum is divided into two kinds of products of one-component gum and two-component gum, wherein one-component currently on the market
Gum is a kind of organic material of high molecular polymer, and two-component gum is a kind of inorganic material of cement base class, each
All there is certain defect.One-component gum construction is simple easy to get started, and the publicity of some producers can be pasted brush, but it
There are poor water resistance, cannot be used in as the long-term soaked place such as toilet, pond, main reasons is that glue for tile is inorganic material
Material, one-component gum are organic material, poor compatibility between the two.Two-component gum need completely it is solid after could carry out it is next
Procedure generally requires solid 1 day and can be only achieved requirement, causes construction period longer, but since bi-component gum is inorganic material
Material has good compatibility with glue for tile, can guarantee that it is not in hollowing to be used cooperatively after stickup vitrified tile with glue for tile, flake,
The problems such as falling off.
Invention content
In order to overcome above-mentioned technological deficiency, there is provided a kind of quick-dry type bi-component water-proof ceramic tiles for the first object of the present invention
Gum, with faster hydration reaction process, not only drying time is short, but also can guarantee that early stage just has very outstanding bonding strong
Degree.
To solve the above-mentioned problems, the present invention is achieved by following technical scheme：
A kind of quick-dry type bi-component water-proof ceramic tile gum, including liquid material component A and powder component B, the liquid material component A and
The weight ratio of the powder component B is：1：(2-3)；
The weight percentages of components of the liquid material component A is：
The weight percentages of components of the powder component B is：
Acrylic emulsions and styrene-butadiene emulsion make two-component ceramic tile gum have water resistance, and have with glue for tile good
Adhesion strength；Silane coupling agent can erect " molecular bridge " between inorganic matter and the interface of organic matter, to two kinds of properties
Special material tight combines.
The complex cementitious system of Portland cement and sulphate aluminium cement composition makes two-component ceramic tile gum early stage just
Preferable physical property can be possessed；Gypsum is solidifying as adjusting Portland cement and sulphate aluminium cement complex cementitious system
It ties the time and promotes the auxiliary material of hydration reaction, there is certain water storage performance, can keep the skin wet to cement so that ordinary silicon
The ternary system that acid salt cement, sulphate aluminium cement, gypsum form is realized reaches better water in shorter setting time
Change effect.
Further, it is characterised in that：
The weight percentages of components of the liquid material component A is：
The weight percentages of components of the powder component B is：
Further, in the liquid material component A, the acrylic emulsions are one in styrene-acrylic emulsion or pure-acrylic emulsion
Kind is a variety of；The preservative is isothiazolinone；The antifoaming agent is one kind in mineral oils, organic silicon or polyethers
Or it is a variety of.
Further, in the liquid material component A, the silane coupling agent is vinyl silanes, epoxide function rolls into a ball silane,
It is one or more in methacryloxypropyl silane, γ-aminopropylsilane.
Further, in the powder component B, the Portland cement is 42.5R cement；The aluminium sulfate
Cement is 42.5 low alkali quick hardening sulphoaluminate cements.
Further, in the powder component B, the river sand is 40-70 mesh river sands；The gypsum is anhydrous gypsum；
The water-reducing agent be how be or polycarboxylic acid salt in it is one or more；The antifoaming agent be hydrocarbon, polyethylene glycol and
Silicon ternary mixed-powder antifoaming agent.
Further, in the powder component B, the cellulose ether is hydroxypropyl methyl cellulose ether, methylol fibre
It is one or more in the plain ether of dimension, hydroxyethyl ether cellulose.
In order to overcome above-mentioned technological deficiency, there is provided a kind of quick-dry type bi-component water-proof ceramic tiles for the second object of the present invention
The preparation method of gum, the simple science of the preparation method, convenient for manufacture.
To solve the above-mentioned problems, the present invention is achieved by following technical scheme：
A kind of preparation method of quick-dry type bi-component water-proof ceramic tile gum, includes the following steps：
S1, it is equipped with liquid material component A：It is equipped with by following weight percent：30.0%-55.0% acrylic emulsions,
5.0%-10.0% styrene-butadiene emulsions, 0.2%-0.3% preservatives, 0.2%-0.3% antifoaming agent, 0-0.5% silane coupling agents,
33.9%-64.6% water；
S2, it is equipped with powder component B：It is equipped with by following weight percent：40.0%-45.0% Portland cements,
10.0%-15.0% sulphate aluminium cements, 3.0%-5.0% gypsum, 5.0%-8.0% coarse whitings, the rivers 25.91%-41.45%
Sand, 0.5%-1.0% water-reducing agents, 0.01%-0.03% antifoaming agent, 0.04%-0.06% cellulose ethers；
S3, successively by acrylic emulsions that step S1 is equipped with, the styrene-butadiene emulsion, the preservative, described disappear
Infusion, the silane coupling agent, the water are added in dispersion cylinder, are mixed 10-20 minutes to get liquid material；
S4, the Portland cement for being successively equipped with step S2, the sulphate aluminium cement, the gypsum, institute
It states coarse whiting, the river sand, the water-reducing agent, the antifoaming agent, the cellulose ether to be added in mixing agitator, be mixed
10-20 minutes to get powder；
S5, by powder obtained by liquid material obtained by step S3 and step S4 according to weight ratio it is 1：(2-3) is prepared, and is put into and is stirred
It mixes in cylinder, is mixed 10-20 minutes to get ceramic tile gum finished product.
Compared with prior art, the beneficial effects of the invention are as follows：
(1) a kind of quick-dry type bi-component water-proof ceramic tile gum provided by the invention, by the way that acrylic compounds are added in liquid material
Portland cement, sulphate aluminium cement, gypsum are added in lotion, styrene-butadiene emulsion, silane coupling agent and powder, liquid material
It is proportionally mixed and made into slurry with powder and uniformly brushes at the ceramic tile back side, there is faster hydration reaction process, ensure this
Layer ceramic tile gum can be solid in a relatively short period of time and can be securely attached to the ceramic tile back side, and ceramic tile and ceramic tile are improved to reach
Adhesion strength between glue and load-bearing capacity.For the ceramic tile gum of the present invention, not only solves ceramic tile gum and glue for tile is mixed
Hollowing that used time is likely to occur, the problems such as flaking, falling off, and solve that two-component gum drying time is long, and early stage is viscous simultaneously
The problems such as knotting strength is low.
(2) preparation method of quick-dry type bi-component water-proof ceramic tile gum of the present invention, the simple science of the preparation method,
Convenient for manufacture.
Description of the drawings
Specific embodiments of the present invention will be described in further detail below in conjunction with the accompanying drawings, wherein：
Fig. 1 is the flow chart of the preparation method of quick-dry type bi-component water-proof ceramic tile gum of the present invention.
Specific implementation mode
Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings, it should be understood that preferred reality described herein
Apply example only for the purpose of illustrating and explaining the present invention and is not intended to limit the present invention.
The invention discloses a kind of quick-dry type bi-component water-proof ceramic tile gums, including liquid material component A and powder component B, liquid
Expect that the weight ratio of component A and powder component B is：1：(2-3)；
The weight percentages of components of liquid material component A is：
The weight percentages of components of powder component B is：
Various test apparatuses and reagent are commercial goods, are that can buy to obtain by commercial sources.
Embodiment 1
A kind of quick-dry type bi-component water-proof ceramic tile gum, including liquid material component A and powder component B, liquid material component A and powder
The weight ratio of component B is：1：3；
(1) feeding of liquid material component A and powder component B are as follows：
Liquid material component A includes the component of following weight：
Powder component B includes the component of following weight：
(2) the preparation following steps of quick-dry type bi-component water-proof ceramic tile gum：
S1, it is equipped with liquid material component A：It is equipped with by following weight percent：30kg styrene-acrylic emulsions, 10kg styrene-butadiene emulsions, 0.3kg
Isothiazolinone, 0.3kg silicone emulsions, 0.5kg vinyl silanes, 58.9kg water；
S2, it is equipped with powder component B：It is equipped with by following weight percent：120kg 42.5R cement, 42.5 low alkali of 45kg are fast
Hardening sulphoaluminate cement, 15kg anhydrous gypsums, 24kg coarse whitings, 92.73kg river sands, 3kg β bases naphthalenesulfonate formaldehyde condensation compound,
0.09kg P803 powder antifoaming agent, 0.18kg hydroxypropyl methyl cellulose ethers；
S3, the styrene-acrylic emulsion for being successively equipped with step S1, styrene-butadiene emulsion, isothiazolinone, silicone emulsion, vinyl silicon
Alkane, water are added in dispersion cylinder, are mixed 15 minutes to get liquid material；
S4, the 42.5R cement for being successively equipped with step S2,42.5 low alkali quick hardening sulphoaluminate cements, anhydrous gypsum, again
Mixing agitator is added in calcium, river sand, β bases naphthalenesulfonate formaldehyde condensation compound, P803 powder antifoaming agent, hydroxypropyl methyl cellulose ether
It is interior, 15 minutes are mixed to get powder；
S5, by powder obtained by liquid material obtained by step S3 and step S4 according to weight ratio it is 1：3 prepare, and are put into mixing drum
It is interior, 15 minutes are mixed to get ceramic tile gum finished product.
With reference to JC/T547-2005《Ceramic wall and floor bricks adhesive》With GB 24264-2009《Ornamental stone adhesive》Inspection
Foundation is surveyed, 1 gained ceramic tile gum of embodiment is tested for the property, testing result is as shown in table 1.
Embodiment 2
A kind of quick-dry type bi-component water-proof ceramic tile gum, including liquid material component A and powder component B, liquid material component A and powder
The weight ratio of component B is：1：2；
(1) feeding of liquid material component A and powder component B are as follows：
Liquid material component A includes the component of following weight：
Powder component B includes the component of following weight：
(2) the preparation following steps of quick-dry type bi-component water-proof ceramic tile gum：
S1, it is equipped with liquid material component A：It is equipped with by following weight percent：50kg styrene-acrylic emulsions, 5kg styrene-butadiene emulsions, 0.2kg
Isothiazolinone, 0.2kg silicone emulsions, 0.3kg methacryloxypropyls silane, 44.3kg water；
S2, it is equipped with powder component B：It is equipped with by following weight percent：90kg 42.5R cement, 42.5 low alkali of 20kg are fast
Hardening sulphoaluminate cement, 6kg anhydrous gypsums, 10kg coarse whitings, 72.9kg river sands, 1kg β bases naphthalenesulfonate formaldehyde condensation compound,
0.02kg P803 powder antifoaming agent, 0.08kg hydroxymethyl cellulose ethers；
S3, the styrene-acrylic emulsion for being successively equipped with step S1, styrene-butadiene emulsion, isothiazolinone, silicone emulsion, methacryl
Oxygen propyl group silane, water are added in dispersion cylinder, are mixed 15 minutes to get liquid material；
S4, the 42.5R cement for being successively equipped with step S2,42.5 low alkali quick hardening sulphoaluminate cements, anhydrous gypsum, again
Calcium, river sand, β bases naphthalenesulfonate formaldehyde condensation compound, P803 powder antifoaming agent, hydroxymethyl cellulose ether are added in mixing agitator,
15 minutes are mixed to get powder；
S5, by powder obtained by liquid material obtained by step S3 and step S4 according to weight ratio it is 1：2 prepare, and are put into mixing drum
It is interior, 15 minutes are mixed to get ceramic tile gum finished product.
With reference to JC/T547-2005《Ceramic wall and floor bricks adhesive》With GB 24264-2009《Ornamental stone adhesive》Inspection
Foundation is surveyed, 2 gained ceramic tile gum of embodiment is tested for the property, testing result is as shown in table 1.
Embodiment 3
A kind of quick-dry type bi-component water-proof ceramic tile gum, including liquid material component A and powder component B, liquid material component A and powder
The weight ratio of component B is：1：2.7；
(1) feeding of liquid material component A and powder component B are as follows：
Liquid material component A includes the component of following weight：
Powder component B includes the component of following weight：
(2) the preparation following steps of quick-dry type bi-component water-proof ceramic tile gum：
S1, it is equipped with liquid material component A：It is equipped with by following weight percent：40kg pure-acrylic emulsions, 7kg styrene-butadiene emulsions, 0.25kg
Isothiazolinone, 0.25kg silicone emulsions, 0.4kg γ-aminopropylsilanes, 52.1kg water；
S2, it is equipped with powder component B：It is equipped with by following weight percent：116.1kg 42.5R cement, 35.1kg42.5 are low
Alkali quick hardening sulphoaluminate cement, 10.8kg anhydrous gypsums, 16.2kg coarse whitings, 89.721kg river sands, 1.89kg sulfamates,
0.054kg P803 powder antifoaming agent, 0.135kg hydroxyethyl ether celluloses；
S3, the pure-acrylic emulsion for being successively equipped with step S1, styrene-butadiene emulsion, isothiazolinone, silicone emulsion, aminopropyl silicon
Alkane, water are added in dispersion cylinder, are mixed 15 minutes to get liquid material；
S4, the 42.5R cement for being successively equipped with step S2,42.5 low alkali quick hardening sulphoaluminate cements, anhydrous gypsum, again
Calcium, river sand, sulfamate, P803 powder antifoaming agent, hydroxyethyl ether cellulose are added in mixing agitator, are mixed 15 points
Clock is to get powder；
S5, by powder obtained by liquid material obtained by step S3 and step S4 according to weight ratio it is 1：2.7 prepare, and are put into stirring
In cylinder, 15 minutes are mixed to get ceramic tile gum finished product.
With reference to JC/T547-2005《Ceramic wall and floor bricks adhesive》With GB 24264-2009《Ornamental stone adhesive》Inspection
Foundation is surveyed, 3 gained ceramic tile gum of embodiment is tested for the property, testing result is as shown in table 1.
Embodiment 4
A kind of quick-dry type bi-component water-proof ceramic tile gum, including liquid material component A and powder component B, liquid material component A and powder
The weight ratio of component B is：1：2.3；
(1) feeding of liquid material component A and powder component B are as follows：
Liquid material component A includes the component of following weight：
Powder component B includes the component of following weight：
(2) the preparation following steps of quick-dry type bi-component water-proof ceramic tile gum：
S1, it is equipped with liquid material component A：It is equipped with by following weight percent：30kg pure-acrylic emulsions, 10kg styrene-butadiene emulsions, 0.3kg
Isothiazolinone, 0.3kg silicone emulsions, 59.4kg water；
S2, it is equipped with powder component B：It is equipped with by following weight percent：92kg 42.5R cement, 42.5 low alkali of 34.5kg
Quick hardening sulphoaluminate cement, 11.5kg anhydrous gypsums, 18.4kg coarse whitings, 71.093kg river sands, 2.3kg sulfamates,
0.069kg P803 powder antifoaming agent, 0.138kg hydroxyethyl ether celluloses；
Dispersion is added in S3, the pure-acrylic emulsion for being successively equipped with step S1, styrene-butadiene emulsion, isothiazolinone, silicone emulsion, water
In cylinder, 15 minutes are mixed to get liquid material；
S4, the 42.5R cement for being successively equipped with step S2,42.5 low alkali quick hardening sulphoaluminate cements, anhydrous gypsum, again
Calcium, river sand, sulfamate, P803 powder antifoaming agent, hydroxyethyl ether cellulose are added in mixing agitator, are mixed 15 points
Clock is to get powder；
S5, by powder obtained by liquid material obtained by step S3 and step S4 according to weight ratio it is 1：2.3 prepare, and are put into stirring
In cylinder, 15 minutes are mixed to get ceramic tile gum finished product.
With reference to JC/T547-2005《Ceramic wall and floor bricks adhesive》With GB 24264-2009《Ornamental stone adhesive》Inspection
Foundation is surveyed, 4 gained ceramic tile gum of embodiment is tested for the property, testing result is as shown in table 1.
Comparative example 1
Common two-component ceramic tile gum, includes the weight of liquid material component A and powder component B, liquid material component A and powder component B
Measuring the ratio between part is：1：3；
Liquid material component A includes the component of following weight：
Powder component B includes the component of following weight：
(2) the preparation following steps of common two-component ceramic tile gum：
S1, it is equipped with liquid material component A：It is equipped with by following weight percent：30kg styrene-acrylic emulsions, 10kg styrene-butadiene emulsions, 0.3kg
Isothiazolinone, 0.3kg silicone emulsions, 59.4kg water；
S2, it is equipped with powder component B：It is equipped with by following weight percent：150kg 42.5R cement, 30kg coarse whitings,
116.73kg river sands, 3kg β bases naphthalenesulfonate formaldehyde condensation compound, 0.09kg P803 powder antifoaming agent, 0.18kg hydroxypropyl methyls
Cellulose ether；
Dispersion is added in S3, the styrene-acrylic emulsion for being successively equipped with step S1, styrene-butadiene emulsion, isothiazolinone, silicone emulsion, water
In cylinder, 15 minutes are mixed to get liquid material；
S4, the 42.5R cement for being successively equipped with step S2, coarse whiting, river sand, β bases naphthalenesulfonate formaldehyde condensation compound, P803 powder
Last antifoaming agent, hydroxypropyl methyl cellulose ether are added in mixing agitator, are mixed 15 minutes to get powder；
S5, by powder obtained by liquid material obtained by step S3 and step S4 according to weight ratio it is 1：3 prepare, and are put into mixing drum
It is interior, 15 minutes are mixed to get ceramic tile gum finished product.
With reference to JC/T547-2005《Ceramic wall and floor bricks adhesive》With GB 24264-2009《Ornamental stone adhesive》Inspection
Foundation is surveyed, 1 gained ceramic tile gum of comparative example is tested for the property, testing result is as shown in table 1.
Comparative example 2
Common two-component ceramic tile gum, includes the weight of liquid material component A and powder component B, liquid material component A and powder component B
Amount part, which matches, is：1：2；
(1) feeding of liquid material component A and powder component B are as follows：
Liquid material component A includes the component of following weight：
Powder component B includes the component of following weight：
(2) the preparation following steps of common two-component ceramic tile gum：
S1, it is equipped with liquid material component A：It is equipped with by following weight percent：50kg styrene-acrylic emulsions, 5kg styrene-butadiene emulsions, 0.2kg
Isothiazolinone, 0.2kg silicone emulsions, 44.6kg water；
S2, it is equipped with powder component B：It is equipped with by following weight percent：90kg 42.5R cement, 20kg coarse whitings, 88.9kg
River sand, 1kg β bases naphthalenesulfonate formaldehyde condensation compound, 0.02kg P803 powder antifoaming agent, 0.08kg hydroxymethyl cellulose ethers；
Dispersion is added in S3, the styrene-acrylic emulsion for being successively equipped with step S1, styrene-butadiene emulsion, isothiazolinone, silicone emulsion, water
In cylinder, 15 minutes are mixed to get liquid material；
S4, the 42.5R cement for being successively equipped with step S2, coarse whiting, river sand, β bases naphthalenesulfonate formaldehyde condensation compound, P803 powder
Last antifoaming agent, hydroxymethyl cellulose ether are added in mixing agitator, are mixed 15 minutes to get powder；
S5, by powder obtained by liquid material obtained by step S3 and step S4 according to weight ratio it is 1：2 prepare, and are put into mixing drum
It is interior, 15 minutes are mixed to get ceramic tile gum finished product.
With reference to JC/T547-2005《Ceramic wall and floor bricks adhesive》With GB 24264-2009《Ornamental stone adhesive》Inspection
Foundation is surveyed, 2 gained ceramic tile gum of comparative example is tested for the property, testing result is as shown in table 1.
Effete test embodiment 1
By the quick-dry type bi-component water-proof ceramic tile gum obtained by embodiment 1-4 and common pair obtained by comparative example 1-2
Component ceramic tile gum carries out performance detection.
With reference to JC/T547-2005《Ceramic wall and floor bricks adhesive》With GB 24264-2009《Ornamental stone adhesive》Inspection
Foundation and criterion are surveyed, is tested for the property, testing result is as shown in table 1.
1 detection data of table
As shown in Table 1, the ceramic tile gum obtained by the present invention has water resistance and good adhesion strength.
Effete test embodiment 2
By the quick-dry type bi-component water-proof ceramic tile gum obtained by embodiment 1-4 and common pair obtained by comparative example 1-2
Component ceramic tile gum carries out the setting time comparison under the conditions of varying environment, and the results are shown in Table 2.
2 detection data of table
As shown in Table 2, the ceramic tile gum setting time obtained by the present invention is short.
The above described is only a preferred embodiment of the present invention, be not intended to limit the present invention in any form, therefore
It is every without departing from technical solution of the present invention content, according to the technical essence of the invention to made by above example it is any modification,
Equivalent variations and modification, in the range of still falling within technical solution of the present invention.
Claims (8)
1. a kind of quick-dry type bi-component water-proof ceramic tile gum, it is characterised in that：
Including liquid material component A and the weight ratio of powder component B, the liquid material component A and the powder component B are：1：(2-
3)；
The weight percentages of components of the liquid material component A is：
The weight percentages of components of the powder component B is：
2. quick-dry type bi-component water-proof ceramic tile gum according to claim 1, it is characterised in that：
The weight percentages of components of the liquid material component A is：
The weight percentages of components of the powder component B is：
3. quick-dry type bi-component water-proof ceramic tile gum according to claim 1, it is characterised in that：In the liquid material component A
In, the acrylic emulsions are one or more in styrene-acrylic emulsion or pure-acrylic emulsion；The preservative is isothiazolinone；
The antifoaming agent is one or more in mineral oils, organic silicon or polyethers.
4. quick-dry type bi-component water-proof ceramic tile gum according to claim 1, it is characterised in that：In the liquid material component A
In, the silane coupling agent is vinyl silanes, epoxide function group silane, methacryloxypropyl silane, γ-aminopropylsilane
In it is one or more.
5. quick-dry type bi-component water-proof ceramic tile gum according to claim 1, it is characterised in that：In the powder component B
In, the Portland cement is 42.5R cement；The sulphate aluminium cement is 42.5 low alkali quick hardening sulphoaluminate cements.
6. quick-dry type bi-component water-proof ceramic tile gum according to claim 1, it is characterised in that：In the powder component B
In, the river sand is 40-70 mesh river sands；The gypsum is anhydrous gypsum；The water-reducing agent be how be or polycarboxylic acid salt in
It is one or more；The antifoaming agent is hydrocarbon, polyethylene glycol and silicon ternary mixed-powder antifoaming agent.
7. quick-dry type bi-component water-proof ceramic tile gum according to claim 1, it is characterised in that：In the powder component B
In, the cellulose ether is hydroxypropyl methyl cellulose ether, hydroxymethyl cellulose ether, one kind in hydroxyethyl ether cellulose or more
Kind.
8. a kind of preparation method according to claim 1~7 any one of them quick-dry type bi-component water-proof ceramic tile gum, special
Sign is, includes the following steps：
S1, it is equipped with liquid material component A：It is equipped with by following weight percent：30.0%-55.0% acrylic emulsions, 5.0%-
10.0% styrene-butadiene emulsion, 0.2%-0.3% preservatives, 0.2%-0.3% antifoaming agent, 0-0.5% silane coupling agents, 33.9%-
64.6% water；
S2, it is equipped with powder component B：It is equipped with by following weight percent：40.0%-45.0% Portland cements, 10.0%-
15.0% sulphate aluminium cement, 3.0%-5.0% gypsum, 5.0%-8.0% coarse whitings, 25.91%-41.45% river sands, 0.5%-
1.0% water-reducing agent, 0.01%-0.03% antifoaming agent, 0.04%-0.06% cellulose ethers；
S3, the acrylic emulsions for being successively equipped with step S1, the styrene-butadiene emulsion, the preservative, the antifoaming agent,
The silane coupling agent, the water are added in dispersion cylinder, are mixed 10-20 minutes to get liquid material；
It is S4, the Portland cement for being successively equipped with step S2, the sulphate aluminium cement, the gypsum, described heavy
Calcium, the river sand, the water-reducing agent, the antifoaming agent, the cellulose ether are added in mixing agitator, and 10-20 is mixed
Minute is to get powder；
S5, by powder obtained by liquid material obtained by step S3 and step S4 according to weight ratio it is 1：(2-3) is prepared, and is put into mixing drum
It is interior, 10-20 minutes are mixed to get ceramic tile gum finished product.