CN108751879A - A kind of cement pavement fast repairing material - Google Patents
A kind of cement pavement fast repairing material Download PDFInfo
- Publication number
- CN108751879A CN108751879A CN201810517519.5A CN201810517519A CN108751879A CN 108751879 A CN108751879 A CN 108751879A CN 201810517519 A CN201810517519 A CN 201810517519A CN 108751879 A CN108751879 A CN 108751879A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- water
- repairing
- repairing material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cement pavement fast repairing materials, include the raw material of following parts by weight：10-20 parts of natural sand, 10-15 parts of diamond dust, 8-12 parts of atomization drying adhesive, 0.2-0.7 parts of tartaric acid, 2-7 parts of water-reducing agent, 20-30 parts of Portland cement, 5-20 parts of microfilament end hook, 2-4 parts of polypropylene fibre, 0.5-0.8 parts of boric acid, 3-8 parts of silica, 0.7-0.9 parts of rust remover, 0.3-0.5 parts of cellulose ether, 20-30 parts of sulphur aluminium system cement, 0.7-1.5 parts of lithium sulfate, 5-10 parts of four water gypsum, 10-20 parts of bauxite, 15-20 parts of miberal powder, 1-6 parts of lithium metasilicate.Patching material of the present invention is that infiltration combines and gluing is reacted with the combination on original road surface, the time of repairing is fast, intensity is high, stable and sustainable growth, with high cold-resistant, high anti-attenuation, heat-resisting ability, color and original pavement-height coincide after repairing, the case where avoiding secondary damage after repairing occurs, material non-toxic pollution-free, environmentally protective of the present invention.
Description
Technical field
The invention belongs to road engineering material fields, specifically, being related to a kind of cement pavement fast repairing material.
Background technology
Cement pavement will appear diseases, the diseases such as pitted skin, hollowing, peeling, shelling, crack, dew muscle and once goes out in use
It is existing, it is expert at and sails the influence of Cyclic Loading and environmental factor, disease will extend at any time to be run through, and causes road surface crack occur, even
Large area falls off, and destroys the globality on road surface, seriously affects driving safety.It is currently used after disease occurs in cement pavement
Mixed compensating method is to overhaul, and disease part road surface is cut, and builds cement pavement after handling base again, and this method exists
Cost is high, the construction time is long, is unfavorable for the shortcomings of open to traffic.
In view of this special to propose the present invention.
Invention content
The technical problem to be solved in the present invention is to overcome the deficiencies of the prior art and provide a kind of cement pavement Rapid-Repair
Material, in order to solve the above technical problems, the present invention is using the basic conception of technical solution：
A kind of cement pavement fast repairing material, includes the raw material of following parts by weight：10-20 parts of natural sand, diamond dust 10-
15 parts, 8-12 parts of atomization drying adhesive, 0.2-0.7 parts of tartaric acid, 2-7 parts of water-reducing agent, 20-30 parts of Portland cement,
5-20 parts of microfilament end hook, 2-4 parts of polypropylene fibre, 0.5-0.8 parts of boric acid, 3-8 parts of silica, 0.7-0.9 parts of rust remover, fibre
Plain 0.3-0.5 parts of the ether of dimension, 20-30 parts of sulphur aluminium system cement, 0.7-1.5 parts of lithium sulfate, 5-10 parts of four water gypsum, bauxite 10-
20 parts, 15-20 parts of miberal powder, 1-6 parts of lithium metasilicate.
Further, include the raw material of following parts by weight：15 parts of natural sand, 12 parts of diamond dust, atomization drying adhesive 10
Part, 0.5 part of tartaric acid, 5 parts of water-reducing agent, 25 parts of Portland cement, 13 parts of microfilament end hook, 3 parts of polypropylene fibre, boric acid
0.7 part, 5 parts of silica, 0.8 part of rust remover, 0.4 part of cellulose ether, 25 parts of sulphur aluminium system cement, 1.1 parts of lithium sulfate, four water
8 parts of gypsum, 15 parts of bauxite, 17 parts of miberal powder, 4 parts of lithium metasilicate.
Further, the natural sand is 20-100 mesh natural sands, and the diamond dust is 80 mesh diamond dust, the ordinary silicon
Acid salt cement marked as 42.5, the sulphur aluminium system cement marked as 42.5.
Further, including 10-16 parts of alkalescent water.
Further, the alkalescent water is 13 parts.
After adopting the above technical scheme, the present invention has the advantages that compared with prior art.
Patching material of the present invention and the combination on original road surface be infiltration combine and it is glued react, time of repairing soon,
Intensity height, stable and sustainable growth, have high cold-resistant, high anti-attenuation, heat-resisting ability, color and original pavement-height after repairing
The case where coincideing, avoiding secondary damage after repairing occurs, and material non-toxic pollution-free, environmentally protective of the present invention is easy to use,
Suitable for various cement pavements, ground, bridge, high ferro, airport pavement, the repairing in road face and conventional repair.
Specific implementation mode
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below to the technical side in embodiment
Case is clearly and completely described, and the following examples are used to illustrate the present invention, but are not intended to limit the scope of the present invention..If not
It refers in particular to, all parts, percentage are unit of weight.
Embodiment 1
A kind of cement pavement fast repairing material, weighs the raw material of following parts by weight：100 10 parts of mesh natural sands, 80 mesh gold
It is 10 parts of emery, 8 parts of atomization drying adhesive, 0.2 part of tartaric acid, 2 parts of water-reducing agent, (42.5) 20 parts of Portland cement, micro-
5 parts of end hook of silk, 2 parts of polypropylene fibre, 0.5 part of boric acid, 3 parts of silica, 0.7 part of rust remover, 0.3 part of cellulose ether, sulphur aluminium
(42.5) 20 parts of system cement, 0.7 part of lithium sulfate, 5 parts of four water gypsum, 10 parts of bauxite, 15 parts of miberal powder, 1 part of lithium metasilicate, weak base
10 parts of water of property.
Above-mentioned each component is mixed evenly up to cement pavement fast repairing material, using this example materials repairing road surface,
Technical indicator：1d age compression strength 25MPa, 24 hours flexural strength 3.8MPa.
Embodiment 2
A kind of cement pavement fast repairing material, weighs the raw material of following parts by weight：60 15 parts of mesh natural sands, 80 mesh Buddha's warrior attendants
12 parts of sand, 10 parts of atomization drying adhesive, 0.5 part of tartaric acid, 5 parts of water-reducing agent, (42.5) 25 parts of Portland cement, microfilament
13 parts of end hook, 3 parts of polypropylene fibre, 0.7 part of boric acid, 5 parts of silica, 0.8 part of rust remover, 0.4 part of cellulose ether, sulphur aluminium body
(42.5) 25 parts of series cement, 1.1 parts of lithium sulfate, 8 parts of four water gypsum, 15 parts of bauxite, 17 parts of miberal powder, 4 parts of lithium metasilicate, alkalescent
Water is 13 parts.
Above-mentioned each component is mixed evenly up to cement pavement fast repairing material, using this example materials repairing road surface,
Technical indicator：1d age compression strength 26MPa, 24 hours flexural strength 3.9MPa.
Embodiment 3
A kind of cement pavement fast repairing material, weighs the raw material of following parts by weight：20 parts of natural sand, the 80 mesh gold of 20 mesh
It is 15 parts of emery, 12 parts of atomization drying adhesive, 0.7 part of tartaric acid, 7 parts of water-reducing agent, (42.5) 30 parts of Portland cement, micro-
20 parts of end hook of silk, 4 parts of polypropylene fibre, 0.8 part of boric acid, 8 parts of silica, 0.9 part of rust remover, 0.5 part of cellulose ether, sulphur aluminium
(42.5) 30 parts of system cement, 1.5 parts of lithium sulfate, 10 parts of four water gypsum, 20 parts of bauxite, 20 parts of miberal powder, 6 parts of lithium metasilicate, it is weak
16 parts of alkaline water.
Above-mentioned each component is mixed evenly up to cement pavement fast repairing material, using this example materials repairing road surface,
Technical indicator：1d age compression strength 27MPa, 24 hours flexural strength 4.1MPa.
Patching material of the present invention and the combination on original road surface be infiltration combine and it is glued react, time of repairing soon,
Intensity height, stable and sustainable growth, have high cold-resistant, high anti-attenuation, heat-resisting ability, color and original pavement-height after repairing
The case where coincideing, avoiding secondary damage after repairing occurs, and material non-toxic pollution-free, environmentally protective of the present invention is easy to use,
Suitable for various cement pavements, ground, bridge, high ferro, airport pavement, the repairing in road face and conventional repair.
The above is only presently preferred embodiments of the present invention, is not intended to limit the present invention in any form, though
So the present invention has been disclosed as a preferred embodiment, and however, it is not intended to limit the invention, any technology people for being familiar with this patent
Member without departing from the scope of the present invention, when the technology contents using above-mentioned prompt make it is a little change or be modified to
The equivalent embodiment of equivalent variations, it is right according to the technical essence of the invention as long as being the content without departing from technical solution of the present invention
Any simple modification, equivalent change and modification made by above example, in the range of still falling within the present invention program.
Claims (5)
1. a kind of cement pavement fast repairing material, which is characterized in that include the raw material of following parts by weight：10-20 parts of natural sand,
10-15 parts of diamond dust, 8-12 parts of atomization drying adhesive, 0.2-0.7 parts of tartaric acid, 2-7 parts of water-reducing agent, Portland cement
20-30 parts, 5-20 parts of microfilament end hook, 2-4 parts of polypropylene fibre, 0.5-0.8 parts of boric acid, 3-8 parts of silica, rust remover 0.7-
0.9 part, 0.3-0.5 parts of cellulose ether, 20-30 parts of sulphur aluminium system cement, 0.7-1.5 parts of lithium sulfate, 5-10 parts of four water gypsum, aluminium
10-20 parts of alumina, 15-20 parts of miberal powder, 1-6 parts of lithium metasilicate.
2. a kind of cement pavement fast repairing material according to claim 1, which is characterized in that including following parts by weight
Raw material：15 parts of natural sand, 12 parts of diamond dust, 10 parts of atomization drying adhesive, 0.5 part of tartaric acid, 5 parts of water-reducing agent, common silicic acid
25 parts of salt cement, 13 parts of microfilament end hook, 3 parts of polypropylene fibre, 0.7 part of boric acid, 5 parts of silica, 0.8 part of rust remover, fiber
0.4 part of plain ether, 25 parts of sulphur aluminium system cement, 1.1 parts of lithium sulfate, 8 parts of four water gypsum, 15 parts of bauxite, 17 parts of miberal powder, lithium metasilicate
4 parts.
3. a kind of cement pavement fast repairing material according to claim 1 or 2, which is characterized in that the natural sand is
20-100 mesh natural sands, the diamond dust be 80 mesh diamond dust, the Portland cement marked as 42.5, the sulphur aluminium
System cement marked as 42.5.
4. a kind of cement pavement fast repairing material according to claim 1 or 2, which is characterized in that further include alkalescent
10-16 parts of water.
5. a kind of cement pavement fast repairing material according to claim 4, which is characterized in that the alkalescent water is 13
Part.