CN108744013A - The preparation method and application of nano silver-pueraria lobata fiber dressing - Google Patents
The preparation method and application of nano silver-pueraria lobata fiber dressing Download PDFInfo
- Publication number
- CN108744013A CN108744013A CN201810321841.0A CN201810321841A CN108744013A CN 108744013 A CN108744013 A CN 108744013A CN 201810321841 A CN201810321841 A CN 201810321841A CN 108744013 A CN108744013 A CN 108744013A
- Authority
- CN
- China
- Prior art keywords
- pueraria lobata
- solution
- silver
- preparation
- nano silver
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The preparation method of nano silver provided by the invention-pueraria lobata fiber dressing, includes the following steps:Utilize Ag2SO4Solution carries out degumming process to pueraria lobata fiber, and generates silver-pueraria lobata fibrillar precipitate;Neutralisation processing is carried out to silver-pueraria lobata fibrillar precipitate surface;With the silver after 75% ethanol solution dissolution process-pueraria lobata fibrillar precipitate, ultrasonic vibration is until solution becomes stable yellow solution, formation pueraria lobata fiber-Nano silver intermixture;Polyvinylidene fluoride, dimethyl sulfoxide, fatty acid polyethylene glycol ester, surfactant are added in pueraria lobata fiber-Nano silver intermixture, electrostatic spinning liquid is made to uniform in ultrasonic vibration;Using electrostatic spinning solution spinning, nano silver-pueraria lobata fiber dressing is made.The preparation method of the present invention, makes the flavonoid substances composition in pueraria lobata be retained in a large proportion in pueraria lobata cellulose, make made of dressing hemostasis is rapid, good permeability, strong antibacterial.
Description
Technical field
The invention belongs to Biotechnology field, more particularly to the preparation method of nano silver-pueraria lobata fiber dressing and answer
With.
Background technology
Lose blood be the war wound wounded it is dead it is most important due to one of, multi-functional high-end quick hemostatic dressing is
The important tool of first aid is carried out under a situation arises in battlefield and daily various wounds.War wound, which is lost blood, is generally divided into internal bleeding and body
External hemorrhage, internal bleeding are mostly due to Viscera rupture, and external bleeding is substantially since arteriovenous is damaged.If can have in time
The hemostasis of effect ground stablizes the condition of the injury, creates conditions for successive treatment particularly significant to saving wounded's life.Dressing as hemostatic material,
Refer to the covering for covering on wound, having protective effect, control bleeding can be assisted, prevent from infecting and absorbing secretion, stopped blooding
Dressing has great significance for stopping blooding in time.
Pueraria lobata is legume pueraria lobata, is a kind of often feeding vegetables of some provinces and regions of southern china, taste is sweet, cool and tasty, often
It is used as Baoshang.Modern medicine shows:Contain a large amount of Puerarin in pueraria lobata, coronary blood flow can be increased, reduce blood vessel
Resistance, adjusting blood circulation, reduction myocardial oxygen consumption etc., are a kind of relatively conventional myocardial preservation substances, energy relieving spasm and pain, prevention
Hypertension, dizziness headache, coronary heart diseases and angina pectoris, nervous headache etc..But in fact, in addition to Puerarin, in pueraria lobata not because of kind
With at least also containing 12~18% flavonoid substances, Flavonoid substances have expansion peripheral blood vessel, improve microcirculation, dispel saprophytic
Flesh, antipyretic convergent effect are first-class hemostatic materials, along with pueraria lobata fiber it is specially treated after, there is tissue looseness, inhale
The characteristics such as attached power is strong, the two combines the possibility having in fact as high-end rapid hemostatic material, but the country to rarely having in this respect
Research.
Invention content
The purpose of the present invention is in order to solve the above problem, the present invention provides the preparation method of nano silver-pueraria lobata fiber dressing
And application.The technical scheme is that be achieved by the following way.
The preparation method for providing nano silver-pueraria lobata fiber dressing according to an aspect of the present invention, includes the following steps:
(1) Ag is utilized2SO4Solution carries out degumming process to pueraria lobata fiber, and generates silver-pueraria lobata fibrillar precipitate;
(2) neutralisation processing is carried out to silver-pueraria lobata fibrillar precipitate surface;
(3) with the silver after 75% ethanol solution dissolution process-pueraria lobata fibrillar precipitate, ultrasonic vibration is until solution becomes
Stable yellow solution forms pueraria lobata fiber-Nano silver intermixture;
(4) polyvinylidene fluoride, dimethyl sulfoxide, fatty acid polyglycol ethylene glycol are added in pueraria lobata fiber-Nano silver intermixture
Electrostatic spinning liquid is made to uniform in ester, surfactant, ultrasonic vibration;
(5) electrostatic spinning solution spinning is used, nano silver-pueraria lobata fiber dressing is generated.
Wherein, step (1) includes:
Use the H of a concentration of 1~1.5mL/L2SO4Pueraria lobata powder is dissolved, 30~60min in 40 DEG C of water-bath is placed in, is used
Tap water is rinsed to neutrality;It adds by the Na2SiO3 solution of a concentration of 30mL/L, the MgSO that mass concentration is 12.75g/L4
Solution, the NaOH solution and H that mass concentration is 40g/mL2O2The mixed liquor being mixed to form, be placed in 60 in 85 DEG C of water-bath~
80min, stirring;Then the Ag of a concentration of 0.8~1.6g/L is added2SO4Solution is adjusted to neutrality by solution;Yin-Pueraria lobota is obtained by filtration
Root fibrillar precipitate.
Wherein, step (1) includes:H2SO4Bath raio with pueraria lobata powder is 5:1, the bath raio of mixed liquor and pueraria lobata powder is 4:
1。
Wherein, step (1) includes:Pueraria lobata is 250g, H2SO4For 1L, Na2SiO3Solution is 30mL, MgSO4Solution is
100mL, NaOH 210mL, H2O2For 660mL, Ag2SO4Solution is 400mL.
Wherein, step (4) includes:Pueraria lobata fiber-Nano silver intermixture:Polyvinylidene fluoride:Dimethyl sulfoxide:Fatty acid polyglycol
Glycol ester:Surfactant=270~290:35~45:12~15:1~1.5:1~1.5, the ultrasonic vibration time be 30~
50min。
Wherein, step (5) includes:Electrostatic spinning voltage is 6~8kV, the distance between syringe needle and receiver board for 10~
12cm, it is 0.30~0.40mm/h to promote the fltting speed of pump, and spinning environment temperature is 30~35 DEG C.
Wherein, step (2) includes:With warm water washing silver-pueraria lobata fibrillar precipitate, make the table of silver-pueraria lobata fibrillar precipitate
Face is neutrality.
Wherein, step (3) includes:60~90min of ultrasonic vibration.
Nano silver-pueraria lobata fiber dressing of preparation method preparation is provided according to another aspect of the present invention in terms of hemostasis
Application.
The invention has the advantages that:
1. the preparation method of the present invention, makes flavonoid substances in pueraria lobata be retained in a large proportion in pueraria lobata cellulose, therefore
Dressing made of making has good hemostatic function.
2. dressing main ingredient prepared by this method is natural pueraria lobata fiber, the absorbability and material itself to blood are saturating
Gas is superior to common hemostatic function material.
3. the present invention combines pueraria lobata fiber, nano silver and high molecular polymer by electrostatic spinning technique, make to be formed
Dressing has larger specific surface area and microcellular structure, on the one hand can guide fiber rapidly deeply to wound depths, repair by
On the other hand injured tissue makes material have good antibacterial ability, can avoid superinfection.
Specific implementation mode
The illustrative embodiments of the disclosure are described in more detail below.Although showing the disclosure in this specification
Illustrative embodiments, it being understood, however, that may be realized in various forms the disclosure without the embodiment party that should be illustrated here
Formula is limited.It is to be able to be best understood from the disclosure on the contrary, providing these embodiments, and can be by the disclosure
Range is completely communicated to those skilled in the art.
The preparation method and application of 1 nano silver of embodiment-pueraria lobata fiber dressing X1
Include the following steps:
Use the H of a concentration of 1mL/L of 1L2SO4250g pueraria lobata powder is dissolved, 45min in 40 DEG C of water-bath is placed in, with certainly
Water is rinsed to the PH most 7 of solution;It adds by the Na of a concentration of 30mL/L of 30mL2SiO3Solution, 100mL mass concentrations are
12.75g/L MgSO4The H of solution, the NaOH solution and 660mL that 210mL mass concentrations are 40g/mL2O2The mixing being mixed to form
Liquid is placed in 80min in 85 DEG C of water-bath, stirs 10min;Then the Ag of a concentration of 1.5g/L of 400mL is added2SO4Solution makes
Obtain the PH most 7 of solution;.Silver-pueraria lobata fibrillar precipitate is obtained with filtered on buchner funnel;Use 30 DEG C of warm water washing Yin-Pueraria lobota
Root fibrillar precipitate, until the pH value on the surface of silver-pueraria lobata fibrillar precipitate is 7.2;After 75% ethanol solution dissolution process
Silver-pueraria lobata fibrillar precipitate, ultrasonic vibration 90min to solution becomes stable yellow solution, forms pueraria lobata fiber-Nano silver
Intermixture;Polyvinylidene fluoride, dimethyl sulfoxide, fatty acid polyethylene glycol ester, table are added in pueraria lobata fiber-Nano silver intermixture
Electrostatic spinning liquid is made, wherein pueraria lobata fiber-Nano silver intermixture to uniform in face activating agent, ultrasonic vibration 30min:Poly- inclined two
Vinyl fluoride:Dimethyl sulfoxide:Fatty acid polyethylene glycol ester:Surfactant=270:40:12:1.5:1.5;It is molten using electrostatic spinning
Nano silver-pueraria lobata fiber dressing X1 is made in liquid spinning, and wherein electrostatic spinning voltage is 6kV, the distance between syringe needle and receiver board
For 10cm, it is 0.40mm/h to promote the fltting speed of pump, and spinning environment temperature is 30 DEG C.
The flavonoid substances content of nano silver-pueraria lobata fiber dressing X1 is surveyed using high performance liquid chromatography (HPLC)
Fixed, flavonoid substances content is 15g in X1 after testing, therefore the recovery rate of the preparation method flavones of embodiment 1 is 6%.
The preparation method and application of 2 nano silvers of embodiment-pueraria lobata fiber dressing X2
Include the following steps:
Use the H of a concentration of 1mL/L of 0.4L2SO4100g pueraria lobata powder is dissolved, 45min in 40 DEG C of water-bath is placed in, is used
Tap water is rinsed to the PH most 7.3 of solution;It adds by the Na of a concentration of 30mL/L of 12mL2SiO3Solution, 40mL mass concentrations
For the MgSO of 12.75g/L4The H of solution, the NaOH solution and 264mL that 84mL mass concentrations are 40g/mL2O2What is be mixed to form is mixed
Liquid is closed, 80min in 85 DEG C of water-bath is placed in, stirs 5min;Then the Ag of a concentration of 1.5g/L of 160mL is added2SO4Solution
So that the PH most 7.4 of solution;.Silver-pueraria lobata fibrillar precipitate is obtained with filtered on buchner funnel;Use 50 DEG C of warm water washing
Silver-pueraria lobata fibrillar precipitate, until the pH value on the surface of silver-pueraria lobata fibrillar precipitate is 7.5;At 75% ethanol solution dissolving
Silver-pueraria lobata fibrillar precipitate after reason, ultrasonic vibration 60min to solution become stable yellow solution, form pueraria lobata fiber-and receive
The silver-colored intermixture of rice;Polyvinylidene fluoride, dimethyl sulfoxide, fatty acid polyglycol ethylene glycol are added in pueraria lobata fiber-Nano silver intermixture
Electrostatic spinning liquid is made, wherein pueraria lobata fiber-Nano silver intermixture to uniform in ester, surfactant, ultrasonic vibration 35min:
Polyvinylidene fluoride:Dimethyl sulfoxide:Fatty acid polyethylene glycol ester:Surfactant=290:45:15:1.2:1.5;Use electrostatic
Nano silver-pueraria lobata fiber dressing X3 is made in spinning solution spinning, and wherein electrostatic spinning voltage is 8kV, between syringe needle and receiver board
Distance be 10cm, promote pump fltting speed be 0.30mm/h, spinning environment temperature be 35 DEG C.
The flavonoid substances content of nano silver-pueraria lobata fiber dressing X2 is surveyed using high performance liquid chromatography (HPLC)
Fixed, flavonoid substances content is 6.2g in X2 after testing, therefore the recovery rate of the preparation method flavones of embodiment 2 is 6.2%.
The preparation method and application of 3 nano silvers of embodiment-pueraria lobata fiber dressing X3
Use the H of a concentration of 1mL/L of 0.1L2SO425g pueraria lobata powder is dissolved, 45min in 40 DEG C of water-bath is placed in, with certainly
Water is rinsed to the PH most 6.8 of solution;It adds by the Na of a concentration of 30mL/L of 3mL2SiO3Solution, 10mL mass concentrations are
12.75g/L MgSO4The H of solution, the NaOH solution and 66mL that 21mL mass concentrations are 40g/mL2O2The mixing being mixed to form
Liquid is placed in 80min in 85 DEG C of water-bath, stirs 7min;Then the Ag of a concentration of 1.5g/L of 40mL is added2SO4Solution makes
The PH of solution most 7.1;.Silver-pueraria lobata fibrillar precipitate is obtained with filtered on buchner funnel;Use 50 DEG C of warm water washing Yin-Pueraria lobota
Root fibrillar precipitate, until the pH value on the surface of silver-pueraria lobata fibrillar precipitate is 7.1;After 75% ethanol solution dissolution process
Silver-pueraria lobata fibrillar precipitate, ultrasonic vibration 80min to solution becomes stable yellow solution, forms pueraria lobata fiber-Nano silver
Intermixture;Polyvinylidene fluoride, dimethyl sulfoxide, fatty acid polyethylene glycol ester, table are added in pueraria lobata fiber-Nano silver intermixture
Electrostatic spinning liquid is made, wherein pueraria lobata fiber-Nano silver intermixture to uniform in face activating agent, ultrasonic vibration 45min:Poly- inclined two
Vinyl fluoride:Dimethyl sulfoxide:Fatty acid polyethylene glycol ester:Surfactant=270:35:14:1:1;It is spun using electrostatic spinning solution
Nano silver-pueraria lobata fiber dressing X2 is made in silk, and wherein electrostatic spinning voltage is 8kV, and the distance between syringe needle and receiver board are
12cm, it is 0.40mm/h to promote the fltting speed of pump, and spinning environment temperature is 32 DEG C.
The flavonoid substances content of nano silver-pueraria lobata fiber dressing X3 is surveyed using high performance liquid chromatography (HPLC)
Fixed, flavonoid substances content is 1.38g in X2 after testing, therefore the recovery rate of the preparation method flavones of embodiment 2 is 5.52%.
1 blood absorption of experimental example is tested
1. experimental procedures:It weighs 20ml blood to be placed in beaker, cuts out nano silver-pueraria lobata of 1cm*1cm sizes respectively
In fiber dressing X1~X3 input beakers, the thickness of wherein nano silver-pueraria lobata fiber dressing X1~X3 is 0.3 millimeter, record
It the time required to adsorbing whole blood, cannot such as complete to adsorb, record the maximum adsorption time.
2. experimental results:
Nano silver-pueraria lobata fiber dressing X1~X3 smoothly completes absorption, needed for wherein nano silver-pueraria lobata fiber dressing X1
Time is 8s, is 10s the time required to nano silver-pueraria lobata fiber dressing X2, is 10s the time required to propolis-Nanometer silver dressing X3.
The hemostasis experiment of experimental example 2
1. experimental procedures:The Belgian screech owl rabbit that 30 weight are 6.0~6.3kg is chosen, is randomly divided into 3 groups, every group 10
Only, hemostasis test experiments are carried out.After slowly injecting Nembutal sodium solution anesthesia by 40mg/kg dosage vein, by its central ear
Arteriosomes preserved skin, disinfection cut skin along arteria auricularis direction, and blunt separation goes out arteria auricularis, vein and nerve, then uses scalpel
The material to be tested and use pull and push dynamometer that transversely cutting artery is immediately 1*1cm with 1 layer of size after blood is gushed out apply 3N
Pressure, observe hemostasis every 10s, until record bleeding stopping period after final hemostasis completely, calculate every group used in mean time
Between.A kind of wherein every group nano silver-pueraria lobata fiber dressing used in Examples 1 to 3 is as material to be tested.
2. experimental results:
The average bleeding stopping period of nano silver-pueraria lobata fiber X1~X3 is respectively 100s, 105s and 111s.
Experimental example 3
Experiment material:Thickness is nano silver-pueraria lobata fiber dressing X1~X3 and pure cotton fabric Y of 0.620mm, wherein pure
The specification of cotton fabric Y is shown in Table 1.
Experimental procedure:It is breathed freely successively to dressing X1~X3 and pure cotton fabric Y using GELLOWEN air permeability testers
Degree test, each testing of materials 10 times, it is the air permeability of this kind of material to take mean value.
Experimental result:After testing the average air permeability degree of nano silver-pueraria lobata fiber dressing X1~X3 be respectively 38.7L/min,
32.9L/min and 35.7L/min, and the average air permeability degree of pure cotton fabric Y is 15.1L/min.
In conclusion nano silver-pueraria lobata fiber dressing prepared by the present invention is in addition to excellent absorption and hemostatic capability,
Its gas permeability is more better than the pure cotton fabric of same thickness.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, the change or replacement that can be readily occurred in,
It should be covered by the protection scope of the present invention.Therefore, protection scope of the present invention should be with the protection model of the claim
Subject to enclosing.
Claims (9)
1. the preparation method of nano silver-pueraria lobata fiber dressing, which is characterized in that include the following steps:
(1) Ag is utilized2SO4Solution carries out degumming process to pueraria lobata fiber, and generates silver-pueraria lobata fibrillar precipitate;
(2) neutralisation processing is carried out to silver-pueraria lobata fibrillar precipitate surface;
(3) with the silver after 75% ethanol solution dissolution process-pueraria lobata fibrillar precipitate, ultrasonic vibration is until solution becomes stable
Yellow solution, formed pueraria lobata fiber-Nano silver intermixture;
(4) polyvinylidene fluoride, dimethyl sulfoxide, fatty acid polyethylene glycol ester, table are added in pueraria lobata fiber-Nano silver intermixture
Electrostatic spinning liquid is made to uniform in face activating agent, ultrasonic vibration;
(5) electrostatic spinning solution spinning is used, nano silver-pueraria lobata fiber dressing is made.
2. preparation method as described in claim 1, which is characterized in that the step (1) includes:
Use the H of a concentration of 1~1.5mL/L2SO4Pueraria lobata powder is dissolved, 30~60min in 40 DEG C of water-bath is placed in, with originally
Water is rinsed to neutrality;It adds by the Na of a concentration of 30mL/L2SiO3Solution, the MgSO that mass concentration is 12.75g/L4Solution,
Mass concentration is the NaOH solution and H of 40g/mL2O2The mixed liquor being mixed to form, be placed in 60 in 85 DEG C of water-bath~
80min, stirring;Then the Ag of a concentration of 0.8~1.6g/L is added2SO4Solution is adjusted to neutrality by solution;Yin-Pueraria lobota is obtained by filtration
Root fibrillar precipitate.
3. preparation method as claimed in claim 2, which is characterized in that the step (1) includes:
Wherein, H2SO4Bath raio with pueraria lobata powder is 5:1, the bath raio of mixed liquor and pueraria lobata powder is 4:1.
4. preparation method as claimed in claim 2, which is characterized in that the step (1) includes:
Wherein, pueraria lobata 250g, H2SO4For 1L, Na2SiO3Solution is 30mL, MgSO4Solution is 100mL, NaOH 210mL,
H2O2For 660mL, Ag2SO4Solution is 400mL.
5. preparation method as described in claim 1, which is characterized in that the step (4) includes:
Pueraria lobata fiber-Nano silver intermixture:Polyvinylidene fluoride:Dimethyl sulfoxide:Fatty acid polyethylene glycol ester:Surfactant=
(270~290):(35~45):(12~15):(1~1.5):(1~1.5), ultrasonic vibration time are 30~50min.
6. preparation method as described in claim 1, which is characterized in that the step (5) includes:
Electrostatic spinning voltage is 6~8kV, and the distance between syringe needle and receiver board are 10~12cm, promote the fltting speed of pump to be
0.30~0.40mm/h, spinning environment temperature are 30~35 DEG C.
7. preparation method as described in claim 1, which is characterized in that the step (2) includes:
With warm water washing silver-pueraria lobata fibrillar precipitate, it is neutrality to make the surface of silver-pueraria lobata fibrillar precipitate.
8. preparation method as described in claim 1, which is characterized in that the step (3) includes:
60~90min of ultrasonic vibration.
9. nano silver-pueraria lobata fiber dressing prepared by a kind of preparation method as described in claim 1~8 is any is in terms of hemostasis
Application.