CN108730303A - 具有耐腐蚀性能的螺栓 - Google Patents
具有耐腐蚀性能的螺栓 Download PDFInfo
- Publication number
- CN108730303A CN108730303A CN201810599256.7A CN201810599256A CN108730303A CN 108730303 A CN108730303 A CN 108730303A CN 201810599256 A CN201810599256 A CN 201810599256A CN 108730303 A CN108730303 A CN 108730303A
- Authority
- CN
- China
- Prior art keywords
- parts
- bolt
- corrosion resistance
- steel
- scraps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了具有耐腐蚀性能的螺栓,包括以下重量份数的原料:40‑60份废钢、30‑40份生铁、10‑25份锰铁、10‑15份钼、10‑15份钒铁、8‑12份铼、10‑15份废铝、10‑20份钢锭、10‑20份硅铁合金、5‑15份锌粉、10‑15份镍粉、10‑15份钛粉、1‑5份氯化铵、5‑8份石墨粒、30‑60份水性丙烯酸改性环氧树脂、5‑8份改良性酚醛氯丁、3‑5份二氧化硅。本发明螺栓耐腐蚀性能好,强度高,耐磨。
Description
技术领域
本发明涉及一种螺栓,具体涉及具有耐腐蚀性能的螺栓。
背景技术
紧固件是紧固两个或两个以上零件(或构件)紧固连接成为一件整体时所采用的一类机械零件的总称,广泛应用于各种机械、设备、车辆、船舶、铁路、桥梁、建筑、结构、工具、仪器、化工、仪表和用品等上面,它的特点是品种规格繁多,性能用途各异,而且标准化、系列化、通用化的程度也极高。
螺栓是一种最常用的紧固用零件,利用物体的斜面圆形旋转和摩擦力的物理学和数学原理,循序渐进的紧固器物机件的工具;在汽车的装配生产中,螺栓也经常被使用,特别是在发动机舱内,用于固定发动机等部件,由于发动机舱内在使用中经常处于高温状态,螺栓在其中经常受到高温和潮湿阴雨的侵袭,往往容易被腐蚀生锈,生锈后的螺栓强度低,容易断裂。
发明内容
本发明所要解决的技术问题是现有的螺栓不耐腐蚀,容易被腐蚀生锈,目的在于提供具有耐腐蚀性能的螺栓,解决现有的螺栓不耐腐蚀,容易被腐蚀生锈的问题。
本发明通过下述技术方案实现:
具有耐腐蚀性能的螺栓,包括以下重量份数的原料:40-60份废钢、30-40份生铁、10-25份锰铁、10-15份钼、10-15份钒铁、8-12份铼、10-15份废铝、10-20份钢锭、10-20份硅铁合金、5-15份锌粉、10-15份镍粉、10-15份钛粉、1-5份氯化铵、5-8份石墨粒、30-60份水性丙烯酸改性环氧树脂、5-8份改良性酚醛氯丁、3-5份二氧化硅。
本发明以废钢、生铁、锰铁、钼、钒铁、铼、废铝、钢锭、硅铁合金为制备螺栓的主要原料,提高了螺栓的强度,达到了高强度螺栓所需的硬度值、强度值,解决了高强度下螺栓的延迟断裂和疲劳断裂;锌粉、镍粉、钛粉、氯化铵、石墨粒作为螺栓的渗碳剂,有利于螺栓的渗碳处理;水性丙烯酸改性环氧树脂、改良性酚醛氯丁、二氧化硅能够在螺栓的表面生成耐腐蚀膜,水性丙烯酸改性环氧树脂是主要的成膜物质,树脂与螺栓的贴合性好,连接牢固,二氧化硅、改良性酚醛氯丁加强了成膜强度。本发明涉及了一种与螺栓贴合牢固的保护膜,增强了螺栓的耐腐蚀性能;本发明改变了螺栓的主要原料,提高了螺栓的强度,增强了螺栓的耐磨性能,强度高、耐磨性能好的螺栓,其耐腐蚀性能也强。
所述的具有耐腐蚀性能的螺栓,包括以下重量份数的原料:50-60份废钢、30-35份生铁、20-25份锰铁、12-15份钼、12-15份钒铁、8-10份铼、10-13份废铝、15-20份钢锭、15-20份硅铁合金、5-10份锌粉、12-15份镍粉、12-15份钛粉、1-3份氯化铵、6-8份石墨粒、55-60份水性丙烯酸改性环氧树脂、6-8份改良性酚醛氯丁、3-5份二氧化硅。本发明结合原料的成本及螺栓的综合性能,选择出了最佳的配比范围。
所述的具有耐腐蚀性能的螺栓,包括以下重量份数的原料:55份废钢、35份生铁、23份锰铁、13份钼、14份钒铁、9份铼、12份废铝、18份钢锭、20份硅铁合金、8份锌粉、15份镍粉、13份钛粉、2份氯化铵、7份石墨粒、58份水性丙烯酸改性环氧树脂、7份改良性酚醛氯丁、4份二氧化硅。本发明结合原料的成本及螺栓的综合性能,进一步选择出了最佳的配比范围。
所述的具有耐腐蚀性能的螺栓,还包括以下重量份数的原料:1-5份着色颜料、0.1-1份消泡剂、1-5份成膜助剂。本发明结合原料的成本及螺栓的综合性能,选择出了最佳的配比。
所述的具有耐腐蚀性能的螺栓,包括以下重量份数的原料:3份着色颜料、0.8份消泡剂、3份成膜助剂。
本发明与现有技术相比,具有如下的优点和有益效果:
1、本发明具有耐腐蚀性能的螺栓表面包覆有与螺栓贴合性强的膜,增强了螺栓的耐腐蚀性能;
2、本发明具有耐腐蚀性能的螺栓改变了螺栓的主要原料,提高了螺栓的强度,增强了螺栓的耐磨性能;
3、本发明具有耐腐蚀性能的螺栓的原料在市面上易得,制备简单。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚明白,下面结合实施例,对本发明作进一步的详细说明,本发明的示意性实施方式及其说明仅用于解释本发明,并不作为对本发明的限定。
实施例1
本发明具有耐腐蚀性能的螺栓,包括以下重量份数的原料:40-60份废钢、30-40份生铁、10-25份锰铁、10-15份钼、10-15份钒铁、8-12份铼、10-15份废铝、10-20份钢锭、10-20份硅铁合金、5-15份锌粉、10-15份镍粉、10-15份钛粉、1-5份氯化铵、5-8份石墨粒、30-60份水性丙烯酸改性环氧树脂、5-8份改良性酚醛氯丁、3-5份二氧化硅。
本发明以废钢、生铁、锰铁、钼、钒铁、铼、废铝、钢锭、硅铁合金为制备螺栓的主要原料,提高了螺栓的强度,达到了高强度螺栓所需的硬度值、强度值,解决了高强度下螺栓的延迟断裂和疲劳断裂;锌粉、镍粉、钛粉、氯化铵、石墨粒作为螺栓的渗碳剂,有利于螺栓的渗碳处理;水性丙烯酸改性环氧树脂、改良性酚醛氯丁、二氧化硅能够在螺栓的表面生成耐腐蚀膜,水性丙烯酸改性环氧树脂是主要的成膜物质,树脂与螺栓的贴合性好,连接牢固,二氧化硅、改良性酚醛氯丁加强了成膜强度。本发明涉及了一种与螺栓贴合牢固的保护膜,增强了螺栓的耐腐蚀性能;本发明改变了螺栓的主要原料,提高了螺栓的强度,增强了螺栓的耐磨性能。
实施例2
基于实施例1,所述的具有耐腐蚀性能的螺栓,包括以下重量份数的原料:50-60份废钢、30-35份生铁、20-25份锰铁、12-15份钼、12-15份钒铁、8-10份铼、10-13份废铝、15-20份钢锭、15-20份硅铁合金、5-10份锌粉、12-15份镍粉、12-15份钛粉、1-3份氯化铵、6-8份石墨粒、55-60份水性丙烯酸改性环氧树脂、6-8份改良性酚醛氯丁、3-5份二氧化硅。本发明结合原料的成本及螺栓的综合性能,选择出了最佳的配比范围。
实施例3
基于上述实施例,所述的具有耐腐蚀性能的螺栓,包括以下重量份数的原料:55份废钢、35份生铁、23份锰铁、13份钼、14份钒铁、9份铼、12份废铝、18份钢锭、20份硅铁合金、8份锌粉、15份镍粉、13份钛粉、2份氯化铵、7份石墨粒、58份水性丙烯酸改性环氧树脂、7份改良性酚醛氯丁、4份二氧化硅。本发明结合原料的成本及螺栓的综合性能,进一步选择出了最佳的配比范围。本发明螺栓硬度达45-50HRC、抗拉强度达到1300Mpa,屈服强度达到1320Mpa,延伸率大于12%,断面收缩率大于38%,冲击韧性大于65J/cm2,综合机械性能比现有螺栓高12-15%。
实施例4
基于上述实施例,所述的具有耐腐蚀性能的螺栓,还包括以下重量份数的原料:1-5份着色颜料、0.1-1份消泡剂、1-5份成膜助剂。本发明结合原料的成本及螺栓的综合性能,选择出了最佳的配比。
实施例5
基于上述实施例,所述的具有耐腐蚀性能的螺栓,包括以下重量份数的原料:3份着色颜料、0.8份消泡剂、3份成膜助剂。
以上所述的具体实施方式,对本发明的目的、技术方案和有益效果进行了进一步详细说明,所应理解的是,以上所述仅为本发明的具体实施方式而已,并不用于限定本发明的保护范围,凡在本发明的精神和原则之内,所做的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (5)
1.具有耐腐蚀性能的螺栓,其特征在于,包括以下重量份数的原料:40-60份废钢、30-40份生铁、10-25份锰铁、10-15份钼、10-15份钒铁、8-12份铼、10-15份废铝、10-20份钢锭、10-20份硅铁合金、5-15份锌粉、10-15份镍粉、10-15份钛粉、1-5份氯化铵、5-8份石墨粒、30-60份水性丙烯酸改性环氧树脂、5-8份改良性酚醛氯丁、3-5份二氧化硅。
2.根据权利要求1所述的具有耐腐蚀性能的螺栓,其特征在于,包括以下重量份数的原料:50-60份废钢、30-35份生铁、20-25份锰铁、12-15份钼、12-15份钒铁、8-10份铼、10-13份废铝、15-20份钢锭、15-20份硅铁合金、5-10份锌粉、12-15份镍粉、12-15份钛粉、1-3份氯化铵、6-8份石墨粒、55-60份水性丙烯酸改性环氧树脂、6-8份改良性酚醛氯丁、3-5份二氧化硅。
3.根据权利要求2所述的具有耐腐蚀性能的螺栓,其特征在于,包括以下重量份数的原料:55份废钢、35份生铁、23份锰铁、13份钼、14份钒铁、9份铼、12份废铝、18份钢锭、20份硅铁合金、8份锌粉、15份镍粉、13份钛粉、2份氯化铵、7份石墨粒、58份水性丙烯酸改性环氧树脂、7份改良性酚醛氯丁、4份二氧化硅。
4.根据权利要求1所述的具有耐腐蚀性能的螺栓,其特征在于,还包括以下重量份数的原料:1-5份着色颜料、0.1-1份消泡剂、1-5份成膜助剂。
5.根据权利要求4所述的具有耐腐蚀性能的螺栓,其特征在于,包括以下重量份数的原料:3份着色颜料、0.8份消泡剂、3份成膜助剂。