CN108726955A - A kind of pervious concrete and preparation method thereof - Google Patents
A kind of pervious concrete and preparation method thereof Download PDFInfo
- Publication number
- CN108726955A CN108726955A CN201810878008.6A CN201810878008A CN108726955A CN 108726955 A CN108726955 A CN 108726955A CN 201810878008 A CN201810878008 A CN 201810878008A CN 108726955 A CN108726955 A CN 108726955A
- Authority
- CN
- China
- Prior art keywords
- water
- parts
- pervious concrete
- aggregate
- reducing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of pervious concrete and preparation method thereof, the pervious concrete includes according to mass fraction：2~4 parts of 6~15 parts of cement, 30~45 parts of aggregate, 0.8~1.5 part of biomass carbon, 0.8~1.5 part of colorant, 0.1~0.5 part of water-reducing agent and water.The pervious concrete of the present invention is by being added suitable biomass carbon, inside concrete is set to form the equally distributed honeycomb structure in hole, enhance the aeration and seepage of water of pervious concrete, it can in time absorb water in the rainy day, the harmful substance in runoff water is filtered and adsorbed while water storage and infiltration, to have the function that purifying ecological environment, and the noise in environment can be adsorbed, solves urban surface hardening, Ecological Slope destroys, atmospheric air circulation is unsmooth, the ecological problems such as noise pollution and soil erosion, and various colors, it can adapt to municipal works, a variety of environment such as garden landscape and Ecological Road, development for multi-functional pervious concrete is laid a good foundation.
Description
Technical field
The present invention relates to technical field of concrete, and in particular to a kind of pervious concrete and preparation method thereof.
Background technology
In modern urban construction, most road surface or slope surface all use stone slab, cement square bricks, pipe duct etc. to harden road
Face is a lack of respiratory, absorbs heat and permeates the ability of rainwater although the road surface and slope surface of hardening are neatly durable.Therefore
Many ecological environment problems are brought, the time rainwater that such as rains is blocked the supplement of underground water, and level of ground water is difficult to,
With the loss of rainwater, urban surface drying aggravation is easy to form " tropical island effect ", aggravates city raised dust pollution；On the other hand,
Rainfall is big, and municipal drainage is obstructed, be easy to cause Urban flood, the serious consequence such as traffic jam is caused, for river two
For the slope surface of bank, the protective slope structure and material of hardening can cause river water not smooth, it is difficult to infiltrate, reduced velocity flow causes Ha Noi to give birth to
The deterioration of state has a serious impact the animals and plants of surrounding.Again, the road surface of hardening and slope surface color are relatively simple, unfavorable
In the landscape ecological construction of diversification.
Pervious concrete is a kind of ecological, environmental protective concrete, and pervious concrete is while meeting intensity requirement, it is also necessary to
Perforation hole centainly is kept to meet the requirement of water penetration, therefore is also wanted other than selecting suitable raw material when preparing
Achieve the purpose that proof strength and porosity by mix-design and preparation process and additive.Therefore, permeable coagulation
Soil be it is a kind of not only meeting Pavement Performance, but also the road surface slope surface coordinating material mutually coordinated with natural environment, for improving earth's surface heat
Balance, flow is logical up and down for enhancing earth's surface, alleviates tropical island effect and is of great significance.But big logarithm pervious concrete at this stage
Preparation method it is complicated, be unfavorable for practical application.
Invention content
The purpose of the present invention is to provide a kind of pervious concretes and preparation method thereof, are added by activated carbon, increase mixed
Permeable, the water seepage function for coagulating soil, to increase the water penetration and permeability of concrete.
To achieve the above object, the present invention provides a kind of pervious concretes.Specifically, the pervious concrete is according to matter
Measuring number includes：The pervious concrete includes according to mass fraction：6~15 parts of cement, 30~45 parts of aggregate, biomass carbon
2~4 parts of 0.8~1.5 part, 0.8~1.5 part of colorant, 0.1~0.5 part of water-reducing agent and water.
Preferably, the pervious concrete includes according to mass fraction：8~12 parts of cement, 35~40 parts of aggregate, biomass
2~3 parts of 1.1~1.3 parts of charcoal, 1.1~1.3 parts of colorant, 0.2~0.4 part of water-reducing agent and water.
Preferably, the pervious concrete includes according to mass fraction：10 parts of cement, 38 parts of aggregate, biomass carbon 1.2
Part, 1.2 parts of colorant, 0.3 part of water-reducing agent and 2.7 parts of water.
Preferably, the cement is 42.5 grades of Portland cements.
Preferably, the aggregate size is the simple grain grade rubble of 5~25mm.
Preferably, the water-reducing agent is high performance water reducing agent of polyocarboxy acid.
Second aspect of the present invention provides a kind of preparation method of pervious concrete.Specifically, the method includes following
Step：
It is sufficiently mixed Step 1: water-reducing agent and water are stirred 10~20min, aggregate surface is sprayed in a manner of spray, made
Aggregate must be mixed；
It is sufficiently mixed Step 2: cement, biomass carbon and colorant are stirred 30~40min, intermixture is made；
Step 3: intermixture is sufficiently stirred with aggregate is mixed, pervious concrete is made.
Preferably, it is uniformly sprayed on the aggregate surface by different level after water-reducing agent in the step 1 and water being mixed.
Preferably, the mixing aggregate is to be sufficiently humidified so as to and flow out state without water droplet.
Preferably, the pervious concrete is that intermixture mutually wraps up and with aggregate is mixed without stream shape slurry outflow shape
State.
The method of the present invention has the following advantages that：
The pervious concrete of the present invention is cooperated by intermixture with aggregate is mixed, and the equally distributed honeycomb in hole is formed
Shape structure can in time absorb water, water storage and infiltration to enhance the aeration and seepage of water of pervious concrete in the rainy day
The harmful substance in runoff water is filtered and adsorbed simultaneously, to have the function that purifying ecological environment, and environment can be adsorbed
In noise, solve that urban surface hardening, Ecological Slope destroys, atmospheric air circulation is unsmooth, noise pollution and water to a certain extent
The ecological problems such as soil loss；
Secondly, pervious concrete performance of the invention is higher, and various colors can adapt to various municipal works, Landscape
Sight and Ecological Road etc., there is unique artistry and appreciation.
Specific implementation mode
The following examples are used to illustrate the present invention, but are not intended to limit the scope of the present invention..
Embodiment 1
The preparation method of the pervious concrete of the present embodiment, prepares according to the following steps：
Step 1: 0.3 part of high performance water reducing agent of polyocarboxy acid and 2.7 parts of water stirring 15min are sufficiently mixed, by different level uniformly
It is sprayed on the simple grain grade rubble surface that 38 parts of grain sizes are 20mm, mixing aggregate is made and (is sufficiently humidified so as to without water with aggregate surface
Drip goes out to be advisable)；
Step 2: 10 parts of 42.5 grades of Portland cements, 1.2 parts of biomass carbons and 1.2 parts of colorants are stirred 40min
It is sufficiently mixed, intermixture is made；
Step 3: intermixture is sufficiently stirred with aggregate is mixed, pervious concrete is made and (is uniformly adequately encased with slurry
Aggregate, the slurry without flowing shape, which flows down, to be advisable).
Step 4: to the pervious concrete after construction, kept the temperature, moisturizing, watering covering.
Embodiment 2
The preparation method of the pervious concrete of the present embodiment, prepares according to the following steps：
Step 1: 0.5 part of high performance water reducing agent of polyocarboxy acid and 2 parts of water stirring 18min are sufficiently mixed, uniformly spray by different level
It spills in the simple grain grade rubble surface that 35 parts of grain sizes are 5mm, mixing aggregate is made and (is sufficiently humidified so as to without water droplet stream with aggregate surface
Go out to be advisable)；
Step 2: 8 parts of 42.5 grades of Portland cements, 1.1 parts of biomass carbons and 1.5 parts of colorants are stirred 30min
It is sufficiently mixed, intermixture is made；
Step 3: intermixture is sufficiently stirred with aggregate is mixed, pervious concrete is made and (is uniformly adequately encased with slurry
Aggregate, the slurry without flowing shape, which flows down, to be advisable).
Step 4: to the pervious concrete after construction, kept the temperature, moisturizing, watering covering.
Embodiment 3
The preparation method of the pervious concrete of the present embodiment, prepares according to the following steps：
Step 1: 0.1 part of high performance water reducing agent of polyocarboxy acid and 3 parts of water stirring 10min are sufficiently mixed, uniformly spray by different level
It spills in the simple grain grade rubble surface that 45 parts of grain sizes are 8mm, mixing aggregate is made and (is sufficiently humidified so as to without water droplet stream with aggregate surface
Go out to be advisable)；
Step 2: 15 parts of 42.5 grades of Portland cements, 0.8 part of biomass carbon and 1.3 parts of colorants are stirred 36min
It is sufficiently mixed, intermixture is made；
Step 3: intermixture is sufficiently stirred with aggregate is mixed, pervious concrete is made and (is uniformly adequately encased with slurry
Aggregate, the slurry without flowing shape, which flows down, to be advisable).
Step 4: to the pervious concrete after construction, kept the temperature, moisturizing, watering covering.
Embodiment 4
The preparation method of the pervious concrete of the present embodiment, prepares according to the following steps：
Step 1: 0.4 part of high performance water reducing agent of polyocarboxy acid and 4 parts of water stirring 14min are sufficiently mixed, uniformly spray by different level
It spills in the simple grain grade rubble surface that 30 parts of grain sizes are 25mm, mixing aggregate is made and (is sufficiently humidified so as to without water droplet with aggregate surface
Outflow is advisable)；
Step 2: 12 parts of 42.5 grades of Portland cements, 1.5 parts of biomass carbons and 0.8 part of colorant are stirred 38min
It is sufficiently mixed, intermixture is made；
Step 3: intermixture is sufficiently stirred with aggregate is mixed, pervious concrete is made and (is uniformly adequately encased with slurry
Aggregate, the slurry without flowing shape, which flows down, to be advisable).
Step 4: to the pervious concrete after construction, kept the temperature, moisturizing, watering covering.
Embodiment 5
The preparation method of the pervious concrete of the present embodiment, prepares according to the following steps：
Step 1: 0.2 part of high performance water reducing agent of polyocarboxy acid and 2 parts of water stirring 20min are sufficiently mixed, uniformly spray by different level
It spills in the simple grain grade rubble surface that 40 parts of grain sizes are 13mm, mixing aggregate is made and (is sufficiently humidified so as to without water droplet with aggregate surface
Outflow is advisable)；
Step 2: 6 parts of 42.5 grades of Portland cements, 1.3 parts of biomass carbons and 1.1 parts of colorants are stirred 34min
It is sufficiently mixed, intermixture is made；
Step 3: intermixture is sufficiently stirred with aggregate is mixed, pervious concrete is made and (is uniformly adequately encased with slurry
Aggregate, the slurry without flowing shape, which flows down, to be advisable).
Step 4: to the pervious concrete after construction, kept the temperature, moisturizing, watering covering.
By the pervious concrete of each group distribution ratio and method preparation in Examples 1 to 5, according to GB/T16925-1997
《Test method for abrasion resistance of concrete and its products》Compression strength, tensile splitting strength and coefficient of permeability is carried out to be detected,
It the results are shown in Table 1.
Table 1 is the pervious concrete all technical that Examples 1 to 5 is prepared
Test result shows that permeation coefficient of permeable concrete average out to 4.2mm/s prepared by the present invention, intensity are more than
25MPa or more has high intensity and high water-permeability and good aeration, can in time absorb water in the rainy day, water storage and infiltration；
Secondly, the pervious concrete of the present embodiment can effectively adsorb the harmful substance in rainwater (such as by the way that biomass carbon is added：Dioxy
Change sulphur, nitrate etc.) and noise, the ecological problems such as atmospheric air circulation, noise pollution and soil erosion are solved, nature is kept and purify
Ecological environment；Finally, the pervious concrete various colors of the present embodiment, can adapt to various municipal works, garden landscape and life
State road etc. has unique artistry and appreciation.
Although above having used general explanation and specific embodiment, the present invention is described in detail, at this
On the basis of invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Therefore,
These modifications or improvements without departing from theon the basis of the spirit of the present invention belong to the scope of protection of present invention.
Claims (10)
1. a kind of pervious concrete, it is characterised in that：The pervious concrete includes according to mass fraction：6~15 parts of cement, bone
2~4 parts of 30~45 parts of material, 0.8~1.5 part of biomass carbon, 0.8~1.5 part of colorant, 0.1~0.5 part of water-reducing agent and water.
2. pervious concrete according to claim 1, it is characterised in that：The pervious concrete is according to mass fraction packet
It includes：8~12 parts of cement, 35~40 parts of aggregate, 1.1~1.3 parts of biomass carbon, 1.1~1.3 parts of colorant, water-reducing agent 0.2~
0.4 part and 2~3 parts of water.
3. pervious concrete according to claim 2, it is characterised in that：The pervious concrete is according to mass fraction packet
It includes：2.7 parts of 10 parts of cement, 38 parts of aggregate, 1.2 parts of biomass carbon, 1.2 parts of colorant, 0.3 part of water-reducing agent and water.
4. according to claim 1-3 any one of them pervious concretes, it is characterised in that：The cement is 42.5 grades of ordinary silicons
Acid salt cement.
5. according to claim 1-3 any one of them pervious concretes, it is characterised in that：The aggregate size is 5~25mm
Simple grain grade rubble.
6. according to claim 1-3 any one of them pervious concretes, it is characterised in that：The water-reducing agent is the high property of polycarboxylic acids
It can water-reducing agent.
7. a kind of preparation method of pervious concrete, it is characterised in that：The preparation method comprises the following steps：
It is sufficiently mixed Step 1: water-reducing agent and water are stirred 10~20min, aggregate surface is sprayed in a manner of spray, be made mixed
Close aggregate；
It is sufficiently mixed Step 2: cement, biomass carbon and colorant are stirred 30~40min, intermixture is made；
Step 3: intermixture is sufficiently stirred with aggregate is mixed, pervious concrete is made.
8. preparation method according to claim 7, it is characterised in that：Divide after water-reducing agent in the step 1 and water are mixed
Even layers are sprayed on the aggregate surface.
9. preparation method according to claim 7, it is characterised in that：The mixing aggregate is to be sufficiently humidified so as to and do not have water droplet
Outflow state.
10. preparation method according to claim 7, it is characterised in that：The pervious concrete be intermixture with mix bone
Material mutually wraps up and flows out state without stream shape slurry.