CN108708222A - A kind of preparation method of Mixidene - Google Patents
A kind of preparation method of Mixidene Download PDFInfo
- Publication number
- CN108708222A CN108708222A CN201810367089.3A CN201810367089A CN108708222A CN 108708222 A CN108708222 A CN 108708222A CN 201810367089 A CN201810367089 A CN 201810367089A CN 108708222 A CN108708222 A CN 108708222A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixidene
- titanium dioxide
- preparation
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of Mixidene, first nano-titanium dioxide is modified using silane coupling agent, modified nano-titanium dioxide is made, then chitosan is added in acetum, stirring is to being completely dissolved, modified nano-titanium dioxide, glycerine, modified starch, moon sodium metasilicate are added while stirring, continues to stir, obtains anti-blushing agent;In anti-blushing agent be added Cypres after, adjust pH to 6-7, be coated on body paper, drying to get.The present invention, to nano-titanium dioxide modified, cooperateed with chitosan using coupling agent and is used as antiseptic, in conjunction with modified starch and moon sodium metasilicate, moisture-proof, antibiotic agent is made, influence of the moisture to food quality can be not only effective against, moreover it is possible to inhibit the growth of microorganism, extend Food Shelf-life.
Description
Technical field
The invention belongs to special paper products technical fields, and in particular to a kind of preparation method of Mixidene.
Background technology
Food packaging is the important component part of food industry, can be in the matter for storing with keeping food in transportational process
Amount and safety, and by preventing unfavorable factor or condition from extending the shelf-life of food.Therefore, packaging material provides object for product
Suitable physical and chemical condition is protected and created to reason, this is for obtaining satisfied shelf life and keeping food quality and safety
It is most important.Other than should have the basic performance of packaging material, should also have some prevents water vapour, oxygen for food packaging
The performance that gas, carbon dioxide and other volatile compounds penetrate.
Moisture control is the important component of food packaging, and in some cases, increased moisture can be led
Food spoilage is caused, and in other cases, the loss of moisture is exactly the reason of food requirement of sense declines.When the presence of moisture has
It can lead to unnecessary chemical reaction and promote the growth of certain micro-organisms;And the loss of moisture also can especially influence the matter of food
The variation of ground and appearance, relative humidity can lead to food surface lack of moisture, lead to many irrational mix defects, such as go out
Now caking, crystallization or viscosity etc..The increase of moisture may also occur due to food in packaging, some water content are higher
Food is for example, vegetables and other fruits and vegetables tissues can release moisture in respiratory.Therefore, food and surrounding are avoided or reduced
Dehydration between environment and water transport, for most important in terms of food quality and safety.Food paper packing material must
It must be according to the demand of packaging food, it is ensured that proper water vapor transmitance extends food to keep the balance of moisture in pack environment
The storage time of object.
Invention content
The object of the present invention is to provide a kind of preparation methods of Mixidene.
A kind of preparation method of Mixidene, includes the following steps:
Step 1, in parts by weight, by nano-titanium dioxide 10 parts add in ethanol water, adjust pH to 4-5, be heated to 60-
70 DEG C, 0.2-0.5 parts, insulation reaction 2-3h of coupling agent, centrifugation are added dropwise under stirring condition, precipitation is cleaned with ethanol water, is done
It is dry, obtain modifying titanium dioxide;
Step 2, in parts by weight, by chitosan 5-10 parts add in 20-40 parts of acetum, stir to being completely dissolved, while stirring
It mixes side and 2-4 parts of modified nano-titanium dioxide, 0.5-1 parts of glycerine, 2-5 parts of modified starch, sodium metasilicate 0.5-1 parts of the moon is added, continue
Stirring, obtains anti-blushing agent;
Step 3, in anti-blushing agent be added Cypres after, adjust pH to 6-7, be coated on body paper, drying to get.
Preferably, the coupling agent is silane coupling agent, preferably A151, A171 and A172.
Preferably, a concentration of 90-95% of the ethanol water.
Preferably, a concentration of 3-5% of the acetum.
Preferably, the Cypres are made of starch, sodium bentonite, cellulose, borax, silicone emulsion, water.
Preferably, the dosage of each component is by weight in the Cypres:20-40 parts of starch, sodium bentonite
3-5 parts, 2-4 parts of cellulose, 3-8 parts of borax, 1-2 parts of silicone emulsion, 30-50 parts of water.
The present invention, to nano-titanium dioxide modified, cooperateed with chitosan using coupling agent and is used as antiseptic, is formed sediment in conjunction with modified
Powder and moon sodium metasilicate, are made moisture-proof, antibiotic agent, can not only be effective against influence of the moisture to food quality, moreover it is possible to inhibit micro- life
The growth of object extends Food Shelf-life.
Specific implementation mode
Embodiment 1
A kind of preparation method of Mixidene, includes the following steps:
Step 1, in parts by weight, by nano-titanium dioxide 10 parts add in ethanol water, adjust pH to 4, be heated to 60 DEG C,
0.2 part, insulation reaction 3h of coupling agent, centrifugation are added dropwise under stirring condition, precipitation is cleaned with ethanol water, dry, is modified
Titanium dioxide;
Step 2, in parts by weight, by chitosan 5 parts add in 20 parts of acetum, stir to being completely dissolved, while stirring plus
Enter 2 parts of modified nano-titanium dioxide, 0.5 part of glycerine, 0.5 part of 2 part, month sodium metasilicate of modified starch, continues to stir, obtain moisture-proof
Agent;
Step 3, in anti-blushing agent be added Cypres after, adjust pH to 6, be coated on body paper, drying to get.
Wherein, the coupling agent is silane coupling A 151.A concentration of the 90% of the ethanol water.The acetic acid is molten
A concentration of the 3% of liquid.
The Cypres are made of starch, sodium bentonite, cellulose, borax, silicone emulsion, water, specifically,
The dosage of each component is by weight:20 parts of starch, 5 parts of sodium bentonite, 2 parts of cellulose, 3 parts of borax, 1 part of silicone emulsion,
30 parts of water.
Embodiment 2
A kind of preparation method of Mixidene, includes the following steps:
Step 1, in parts by weight, by nano-titanium dioxide 10 parts add in ethanol water, adjust pH to 4, be heated to 65 DEG C,
0.4 part, insulation reaction 2h of coupling agent, centrifugation are added dropwise under stirring condition, precipitation is cleaned with ethanol water, dry, is modified
Titanium dioxide;
Step 2, in parts by weight, by chitosan 7 parts add in 25 parts of acetum, stir to being completely dissolved, while stirring plus
Enter 3 parts of modified nano-titanium dioxide, 0.7 part of glycerine, 0.8 part of 3 part, month sodium metasilicate of modified starch, continues to stir, obtain moisture-proof
Agent;
Step 3, in anti-blushing agent be added Cypres after, adjust pH to 7, be coated on body paper, drying to get.
Wherein, the coupling agent is silane coupling A 171.A concentration of the 90% of the ethanol water.The acetic acid is molten
A concentration of the 4% of liquid.
The Cypres are made of starch, sodium bentonite, cellulose, borax, silicone emulsion, water, specifically,
The dosage of each component is by weight:27 parts of starch, 3 parts of sodium bentonite, 3 parts of cellulose, 5 parts of borax, silicone emulsion 1.5
Part, 40 parts of water.
Embodiment 3
A kind of preparation method of Mixidene, includes the following steps:
Step 1, in parts by weight, by nano-titanium dioxide 10 parts add in ethanol water, adjust pH to 5, be heated to 70 DEG C,
0.4 part, insulation reaction 2h of coupling agent, centrifugation are added dropwise under stirring condition, precipitation is cleaned with ethanol water, dry, is modified
Titanium dioxide;
Step 2, in parts by weight, by chitosan 7 parts add in 32 parts of acetum, stir to being completely dissolved, while stirring plus
Enter 3 parts of modified nano-titanium dioxide, 0.8 part of glycerine, 0.7 part of 4 part, month sodium metasilicate of modified starch, continues to stir, obtain moisture-proof
Agent;
Step 3, in anti-blushing agent be added Cypres after, adjust pH to 7, be coated on body paper, drying to get.
Wherein, the coupling agent is silane coupling A 172.A concentration of the 95% of the ethanol water.The acetic acid is molten
A concentration of the 4% of liquid.
The Cypres are made of starch, sodium bentonite, cellulose, borax, silicone emulsion, water, specifically,
The dosage of each component is by weight:30 parts of starch, 3 parts of sodium bentonite, 4 parts of cellulose, 5 parts of borax, 2 parts of silicone emulsion,
40 parts of water.
Embodiment 4
A kind of preparation method of Mixidene, includes the following steps:
Step 1, in parts by weight, by nano-titanium dioxide 10 parts add in ethanol water, adjust pH to 5, be heated to 70 DEG C,
0.5 part, insulation reaction 2h of coupling agent, centrifugation are added dropwise under stirring condition, precipitation is cleaned with ethanol water, dry, is modified
Titanium dioxide;
Step 2, in parts by weight, by chitosan 10 parts add in 40 parts of acetum, stir to being completely dissolved, while stirring plus
Enter 4 parts of modified nano-titanium dioxide, 1 part of glycerine, 1 part of 5 part, month sodium metasilicate of modified starch, continues to stir, obtain anti-blushing agent;
Step 3, in anti-blushing agent be added Cypres after, adjust pH to 6, be coated on body paper, drying to get.
Wherein, the coupling agent is silane coupling A 151.A concentration of the 95% of the ethanol water.The acetic acid is molten
A concentration of the 5% of liquid.
The Cypres are made of starch, sodium bentonite, cellulose, borax, silicone emulsion, water, specifically,
The dosage of each component is by weight:40 parts of starch, 3 parts of sodium bentonite, 3 parts of cellulose, 7 parts of borax, 1 part of silicone emulsion,
50 parts of water.
Fresh beef is taken, is cleaned with distilled water, is divided into size several pieces identical, the meat piece that segmentation is completed is put into pot and is boiled
To 10min, postcooling is taken out, meat piece is packed using 1 gained wrapping paper of embodiment, with no with any packaging material packet
The cooked beef of dress carries out preservation as blank control under the conditions of 4 DEG C.The 0th day and the 12nd day to percentage of water loss, pH value(GB/
T9695.5-2008), total plate count(GB/T4789.2-2010)It is measured.
The results show that the meat piece packed using the wrapping paper of embodiment 1, the 12nd day is 2.13%;PH value is 5.99;
It is 3.987 that 0th day total plate count, which is 3.201, the 12nd days,.
Blank control, the 12nd day is 55.16%;PH value is 5.99;0th day total plate count is 3.201, the 12nd days to be
5.072。
Claims (6)
1. a kind of preparation method of Mixidene, it is characterised in that:Include the following steps:
Step 1, in parts by weight, by nano-titanium dioxide 10 parts add in ethanol water, adjust pH to 4-5, be heated to 60-
70 DEG C, 0.2-0.5 parts, insulation reaction 2-3h of coupling agent, centrifugation are added dropwise under stirring condition, precipitation is cleaned with ethanol water, is done
It is dry, obtain modifying titanium dioxide;
Step 2, in parts by weight, by chitosan 5-10 parts add in 20-40 parts of acetum, stir to being completely dissolved, while stirring
It mixes side and 2-4 parts of modified nano-titanium dioxide, 0.5-1 parts of glycerine, 2-5 parts of modified starch, sodium metasilicate 0.5-1 parts of the moon is added, continue
Stirring, obtains anti-blushing agent;
Step 3, in anti-blushing agent be added Cypres after, adjust pH to 6-7, be coated on body paper, drying to get.
2. the preparation method of Mixidene according to claim 1, it is characterised in that:The coupling agent is silane
Coupling agent, preferably A151, A171 and A172.
3. the preparation method of Mixidene according to claim 1, it is characterised in that:The ethanol water
A concentration of 90-95%.
4. the preparation method of Mixidene according to claim 1, it is characterised in that:The acetum it is dense
Degree is 3-5%.
5. the preparation method of Mixidene according to claim 1, it is characterised in that:The Cypres are
It is made of starch, sodium bentonite, cellulose, borax, silicone emulsion, water.
6. the preparation method of Mixidene according to claim 1, it is characterised in that:In the Cypres
The dosage of each component is by weight:20-40 parts of starch, 3-5 parts of sodium bentonite, 2-4 parts of cellulose, 3-8 parts of borax, emulsification
1-2 parts of silicone oil, 30-50 parts of water.