CN108691408A - A kind of scaffold with wear-and corrosion-resistant coating - Google Patents
A kind of scaffold with wear-and corrosion-resistant coating Download PDFInfo
- Publication number
- CN108691408A CN108691408A CN201710327940.5A CN201710327940A CN108691408A CN 108691408 A CN108691408 A CN 108691408A CN 201710327940 A CN201710327940 A CN 201710327940A CN 108691408 A CN108691408 A CN 108691408A
- Authority
- CN
- China
- Prior art keywords
- scaffold
- wear
- corrosion
- block tongue
- terminal pad
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of scaffolds with wear-and corrosion-resistant coating, the montant being vertically arranged including several and the connecting rod being connected between montant, the terminal pad for being connected to connecting rod on montant is provided on montant, several connecting holes are provided in terminal pad, be additionally provided with buckle structure connecting rod being fixed in terminal pad in the end of connecting rod, the buckle structure includes the button body of two vertical spacings setting, the consistency of thickness of the spacing and terminal pad of two button bodies, the opposite face of button body is additionally provided with block tongue, an accommodating cavity is offered in button body opposite face, block tongue is by an extensible member slip in accommodating cavity, when block tongue stretches out outside accommodating cavity, just it is caught in connecting hole.Wear-and corrosion-resistant coating is coated on the scaffold, obtained coating adhesion is high, and anti-corrosive properties and wearability are strong, coated on scaffold, so that overall wear resistance and the corrosion resistance enhancing of scaffold, extend the service life of scaffold, also bring safety guarantee to construction personnel.
Description
Technical field
The present invention relates to building implement technical fields, more specifically, it relates to a kind of foot with wear-and corrosion-resistant coating
Hand cradle.
Background technology
Scaffold is the various holders set up at the construction field (site) for operation and high-rise working, is the logical of building field
With term, it is mainly used in exterior wall, interior decoration or the higher place that can not directly construct of floor height on building sites.
Currently, used scaffold is made of using tube material mostly, this is because steel strength is high, durability
Good, service life is long, thus receives the favor of workpeople.However used in the natural environment since scaffold is exposed for a long time, by
To expose to the weather, sleet is drenched without any safeguard measure so that scaffold is easily corroded, and scaffold, which is corroded, can make foot
The bearing capacity of hand cradle substantially reduces, and in addition during scaffold long term wear, can make the company between steel pipe and connection card
Receive influence, junction is easy active, these can all operate on scaffold to worker and bring security risk, the use of scaffold
Service life also has a greatly reduced quality.It thus needs to coat last layer wear-and corrosion-resistant coating in the outer surface of scaffold, to prevent scaffold
It excessive wear and is corroded, to improve the service life of scaffold.
In addition the assembly connection mode of existing scaffold is all that terminal pad coordinates with buckle structure, is arranged in terminal pad
There is a connecting hole, it is corresponding on buckle structure to be also equipped with perforation, buckle structure is caught in terminal pad so that on buckle structure
Perforation it is corresponding with the connecting hole in terminal pad, then toward perforation in be inserted into fixed block come realize scaffold assembly clamping, this
The assembly connection mode of sample is cumbersome, takes time and effort.
Invention content
The object of the present invention is to provide a kind of scaffolds with wear-and corrosion-resistant coating that can realize quick assembling connection.
To achieve the above object, it is realized by following technological means:
A kind of scaffold with wear-and corrosion-resistant coating, including several montants being vertically arranged and be connected between montant
Connecting rod, the terminal pad for being connected to connecting rod on montant is provided on montant, several companies are provided in terminal pad
Hole is connect, the buckle structure being fixed on connecting rod in terminal pad is additionally provided in the end of connecting rod, the buckle structure includes
The button body of two vertical spacings setting, the consistency of thickness of the spacing and terminal pad of two button bodies, the opposite face for detaining body are additionally provided with block tongue,
Offer an accommodating cavity in button body opposite face, block tongue by an extensible member slip in accommodating cavity, when block tongue stretches out accommodating cavity
When outer, just it is caught in connecting hole.
Through the above technical solutions, buckle structure includes button body and block tongue, block tongue is scalable in button body, when needing to assemble
When scaffold, button body is caught in terminal pad, flexible block tongue makes block tongue be caught in the connecting hole of terminal pad, you can realize to foot hand
The assembly of frame, and block tongue it is flexible by switch automatically control, assemble up in this way it is simple and convenient, it is easy to operate.
Advanced optimize for:The extensible member includes the spring between an electromagnet and connection electromagnet and block tongue, institute
State electromagnet dead electricity is controlled by the control module of a switching circuit, when electromagnet obtains it is electric when, block tongue adsorbed by electromagnet and
It shrinks in accommodating cavity, when electromagnet dead electricity, block tongue stretches out accommodating cavity under the reply force effect of spring, is stuck in connection card
On mounting hole.
Through the above technical solutions, spring connection block tongue and electromagnet, when electromagnet obtains it is electric when, block tongue is inhaled by electromagnet
Attached and shrink in accommodating cavity, when electromagnet dead electricity, block tongue stretches out accommodating cavity under the reply force effect of spring, is stuck in terminal pad
Connecting hole on.The stretching motion of block tongue is controlled with electric power, it is intelligent, simple and convenient, easy to operate.
Advanced optimize for:The block tongue is along terminal pad width radially and width of the connecting hole along terminal pad radially
Unanimously.
Through the above technical solutions, what block tongue was arranged along the width of terminal pad radially is radial along terminal pad with connecting hole
On equivalent width, such block tongue cannot move left and right after being caught in connecting hole, to prevent entire buckle structure from shaking, protect
Connecting rod has been demonstrate,proved fixed to the stability on montant.
It advanced optimizes as a kind of scaffold wear-and corrosion-resistant coating, including the group of following parts by weight are grouped as:
Advanced optimize for:A kind of scaffold wear-and corrosion-resistant coating, including the group of following parts by weight are grouped as:
Advanced optimize for:The solvent is dimethylbenzene and acetone according to weight ratio 5~7:3 preparations obtain.
Advanced optimize for:The color stuffing be graphite, molybdenum disulfide, chrome green, silica, bronze powder,
One or more of titanium oxide combines.
Advanced optimize for:The antifoaming agent is 201 silicone oil.
Advanced optimize for:The coupling agent is one or more of KH-550, KH-560, KH-570 combination.
Advanced optimize for:The preparation method of the coating includes the following steps:
Step 1: weighing each raw material according to components by weight percent;
Step 2: the polyurethane weighed, TDI, butyl acetate, polytetrafluoroethylene (PTFE) are added sequentially in castor oil, so
After be charged with solvent, after solution is mixed, persistently stirred with blender, be used in combination heating water bath, 40~50 DEG C of constant temperature is anti-
3~4h is answered to obtain prepolymer;
Step 3: the prepolymer obtained by step 2 is added in reaction kettle, then it is charged with triethanolamine, two bays
Sour dibutyl tin, color stuffing, coupling agent are heated to 200~300 DEG C, and holding pressure is 0.2~0.3MPa, and 3~4h of reaction to obtain the final product
Preparation coating;
Step 4: antifoaming agent is added into the preparation coating obtained by step 3, room temperature persistently stirs 1~2h, then will most
Final product is filtered to remove dross up to scaffold abrasion resistant anticorrosive paint;
Step 5: the coating obtained by step 4 is coated on scaffold, 24~48h of normal temperature cure is up to scaffold with resistance to
Grind corrosion-inhibiting coating.
Beneficial effects of the present invention are:Color stuffing is all hard particles, there is good wearability, into the component of coating
Color stuffing is added, color stuffing is evenly dispersed during the reaction to come, evenly dispersed in final coating product, improves coating
Wearability, coating is coated on scaffold, and the superpower wear-resistant of coating makes scaffold surface layer abrasion-proof.Simultaneous oxidation object etc. is hard
Matter particle is evenly distributed on the surface of coating, plays a supportive role, and coating hardness is made to increase, and coating abrasion performance is made to enhance.With above
Coating made of material, adhesive force is high, and anti-corrosive properties and wearability are strong, improve mechanical strength, adhesive force and the anticorrosion energy of coating
Coating is coated on scaffold by power etc. so that the overall wear resistance and corrosion resistance of scaffold enhance, and are exposing to the weather, are connecing
It contacts that coating plays the role of protective layer when extraneous sleet washes away, prevents scaffold by sleet erosion, the presence of coating also subtracts
Lacked the abrasion between scaffold connection card and steel pipe, to extend the service life of scaffold, also give construction personnel with
Safety guarantee is carried out.
The advantages of the present invention over the prior art are that setting buckle structure to button body and the matched knot of block tongue
Structure, block tongue can be slid by a stretching structure in the accommodating cavity of button body, and the electromagnet in stretching structure is controlled by switch electricity
The control module on road is stretched into control block tongue by circuit realize consolidating for connecting rod in the connecting hole of stretching terminal pad in this way
It is fixed, it is intelligent, simple and convenient, easy to operate.
Description of the drawings
Fig. 1 is a kind of structural schematic diagram of scaffold assembly connection in the present embodiment;
Fig. 2 is the cooperation exploded perspective view of buckle and terminal pad in the present embodiment;
Fig. 3 is the section decomposition diagram of buckle button body in the present embodiment;
Fig. 4 is the control switching circuit figure of electromagnet in the present embodiment.
In figure, 1, montant;2, connecting rod;3, terminal pad;4, connecting hole;5, buckle structure;6, body is detained;7, connecting seat;8,
Block tongue;81, tongue end;9, spring;10, accommodating cavity;11, electromagnet;12, control module;13, current-limiting resistance.
Specific implementation mode
It is described in further detail below in conjunction with the accompanying drawings and by specific embodiment to invention, following embodiment is descriptive
, it is not restrictive protection scope of the present invention.
Embodiment 1
As shown in Figure 1, a kind of scaffold with wear-and corrosion-resistant coating, including several montants 1 being vertically arranged and company
The connecting rod 2 being connected between montant 1 is provided with terminal pad 3 on montant 1, multiple connecting holes 4 is provided in terminal pad 3, are being connected
It is provided with buckle structure 5 between the end and terminal pad 3 of bar 2.As shown in Fig. 2, buckle structure 5 includes the button of vertical spacing setting
Body 6 is provided with block tongue 8 on button 6 opposite face of body, detains and is additionally provided with an accommodating cavity 10 on 6 opposite face of body, block tongue 8 is stretched by one
Shrinking structure slides in accommodating cavity 10.It is just caught in the connecting hole 4 of terminal pad 3 when the stretching accommodating cavity 10 of block tongue 8 is outer, block tongue
8 along 3 radial direction of terminal pad width and connecting hole 4 along the equivalent width of 3 radial direction of terminal pad, 8 company of being caught in of such block tongue
Connect behind hole 4 will not left-right and front-back shake.As shown in figure 3, stretching structure includes an electromagnet 11 and is connected to electromagnet 11 and blocks
The shape of spring 9 between tongue 8, block tongue 8 is consistent with the shape of accommodating cavity 10, and 8 slip of block tongue is in accommodating cavity 10, electromagnetism
Iron 11 is controlled by the control module 12 of a switching circuit.As shown in figure 4, switching circuit include a control module 12 and with control mould
Block 12 electromagnet 11 and a current-limiting resistance 13 in parallel, control module 12 include a transmitter and receiver, transmitter transmitting letter
Number give receiver, control together electromagnet 11 dead electricity, the transmitter are the transmitter of refreshing ox DM-16 models, receiver
For the receiver of the silent M11 in model west.When electromagnet 11 must be electric, block tongue 8 is sucked electromagnet 11, and sucking button body 6 houses
In chamber 10, buckle structure 5 is not stuck in terminal pad 3, and connecting rod 2 is not fixedly connected with montant 1;When 11 dead electricity of electromagnet
When, block tongue 8 is stretched out under the reply force effect of spring 9 outside the accommodating cavity 10 for buckleing body 6, is caught in the connecting hole 4 of terminal pad 3, on
It is both provided with block tongue 8 on lower two buttons body 6, upper and lower two block tongue 8 is caught in connecting hole 4, and the tongue end 81 of block tongue 8 is magnetic material system
At then two block tongues 8 are fixed in connecting hole 4, also because magnetic force attracts together to realize connecting rod 2 and montant 1 jointly up and down
Between fixation.
It is coated with wear-and corrosion-resistant coating in the outer surface of scaffold, the wear-and corrosion-resistant coating includes following parts by weight
Group be grouped as:
The solvent is dimethylbenzene and acetone according to weight ratio 7:3 preparations obtain.
The color stuffing is the mixture of graphite, molybdenum disulfide, chrome green.
The antifoaming agent is 201 silicone oil.
The coupling agent is KH-560.
The preparation method of the abrasion resistant anticorrosive paint, includes the following steps:
Step 1: weighing each raw material according to components by weight percent;
Step 2: the polyurethane weighed, TDI, butyl acetate, polytetrafluoroethylene (PTFE) are added sequentially in castor oil, so
After be charged with solvent, after solution is mixed, persistently stirred with blender, be used in combination heating water bath, 50 DEG C of reaction 4h of constant temperature
Obtain prepolymer;
Step 3: the prepolymer obtained by step 2 is added in reaction kettle, then it is charged with triethanolamine, two bays
Sour dibutyl tin, color stuffing, coupling agent are heated to 300 DEG C, and holding pressure is 0.3MPa, and reaction 4h is up to preparation coating;
Step 4: antifoaming agent is added into the preparation coating obtained by step 3, room temperature persistently stirs 2h, then will finally produce
Object is filtered to remove dross up to scaffold abrasion resistant anticorrosive paint;
Step 5: the coating obtained by step 4 is coated on scaffold, normal temperature cure 48h is prevented up to scaffold with wear-resisting
Rotten coating.
Embodiment 2
A kind of scaffold with wear-and corrosion-resistant coating, the coating include that the group of following parts by weight is grouped as:
The solvent is dimethylbenzene and acetone according to weight ratio 5:3 preparations obtain.
The color stuffing is the mixture of graphite, molybdenum disulfide.
The antifoaming agent is 201 silicone oil.
The coupling agent is KH-550.
A kind of scaffold with wear-and corrosion-resistant coating, the preparation method of the coating include the following steps:
Step 1: weighing each raw material according to components by weight percent;
Step 2: the polyurethane weighed, TDI, butyl acetate, polytetrafluoroethylene (PTFE) are added sequentially in castor oil, so
After be charged with solvent, after solution is mixed, persistently stirred with blender, be used in combination heating water bath, 40 DEG C of reaction 3h of constant temperature
Obtain prepolymer;
Step 3: the prepolymer obtained by step 2 is added in reaction kettle, then it is charged with triethanolamine, two bays
Sour dibutyl tin, color stuffing, coupling agent are heated to 200 DEG C, and holding pressure is 0.2MPa, and reaction 3h is up to preparation coating;
Step 4: antifoaming agent is added into the preparation coating obtained by step 3, room temperature persistently stirs 1h, then will finally produce
Object is filtered to remove dross up to scaffold abrasion resistant anticorrosive paint;
Step 5: the coating obtained by step 4 is coated on scaffold, normal temperature cure is prevented up to scaffold with wear-resisting for 24 hours
Rotten coating.
Embodiment 3
A kind of scaffold with wear-and corrosion-resistant coating, the coating include that the group of following parts by weight is grouped as:
The solvent is dimethylbenzene and acetone according to weight ratio 5:3 preparations obtain.
The color stuffing is the mixture of molybdenum disulfide, chrome green, silica.
Antifoaming agent is 201 silicone oil.
The coupling agent is KH-570.
A kind of preparation method of hand cradle abrasion resistant anticorrosive paint, includes the following steps:
Step 1: weighing each raw material according to components by weight percent;
Step 2: the polyurethane weighed, TDI, butyl acetate, polytetrafluoroethylene (PTFE) are added sequentially in castor oil, so
After be charged with solvent, after solution is mixed, persistently stirred with blender, be used in combination heating water bath, 42 DEG C of reactions of constant temperature
3.2h obtains prepolymer;
Step 3: the prepolymer obtained by step 2 is added in reaction kettle, then it is charged with triethanolamine, two bays
Sour dibutyl tin, color stuffing, coupling agent are heated to 220 DEG C, and holding pressure is 0.22MPa, and reaction 3.2h is up to preparation coating;
Step 4: antifoaming agent is added into the preparation coating obtained by step 3, room temperature persistently stirs 1.2h, then will be final
Product is filtered to remove dross up to scaffold abrasion resistant anticorrosive paint;
Step 5: the coating obtained by step 4 is coated on scaffold, normal temperature cure 30h is prevented up to scaffold with wear-resisting
Rotten coating.
Embodiment 4
A kind of scaffold with wear-and corrosion-resistant coating, the coating include that the group of following parts by weight is grouped as:
The solvent is dimethylbenzene and acetone according to weight ratio 7:3 preparations obtain.
The color stuffing is the mixture of chrome green, silica, bronze powder.
Antifoaming agent is 201 silicone oil.
The coupling agent is KH-570.
A kind of scaffold with wear-and corrosion-resistant coating, the preparation method of the coating include the following steps:
Step 1: weighing each raw material according to components by weight percent;
Step 2: the polyurethane weighed, TDI, butyl acetate, polytetrafluoroethylene (PTFE) are added sequentially in castor oil, so
After be charged with solvent, after solution is mixed, persistently stirred with blender, be used in combination heating water bath, 48 DEG C of reactions of constant temperature
3.8h obtains prepolymer;
Step 3: the prepolymer obtained by step 2 is added in reaction kettle, then it is charged with triethanolamine, two bays
Sour dibutyl tin, color stuffing, coupling agent are heated to 280 DEG C, and holding pressure is 0.28MPa, and reaction 3.8h is up to preparation coating;
Step 4: antifoaming agent is added into the preparation coating obtained by step 3, room temperature persistently stirs 1.8h, then will be final
Product is filtered to remove dross up to scaffold abrasion resistant anticorrosive paint;
Step 5: the coating obtained by step 4 is coated on scaffold, normal temperature cure 40h is prevented up to scaffold with wear-resisting
Rotten coating.
Embodiment 5
A kind of scaffold with wear-and corrosion-resistant coating, the coating include that the group of following parts by weight is grouped as:
The solvent is dimethylbenzene and acetone according to weight ratio 6:3 preparations obtain.
Advanced optimize for:The color stuffing is the mixture of graphite, molybdenum disulfide, titanium oxide.
Advanced optimize for:The antifoaming agent is 201 silicone oil.
Advanced optimize for:The coupling agent is KH-550.
A kind of scaffold with wear-and corrosion-resistant coating, the preparation method of the coating include the following steps:
Step 1: weighing each raw material according to components by weight percent;
Step 2: the polyurethane weighed, TDI, butyl acetate, polytetrafluoroethylene (PTFE) are added sequentially in castor oil, so
After be charged with solvent, after solution is mixed, persistently stirred with blender, be used in combination heating water bath, 45 DEG C of reactions of constant temperature
3.5h obtains prepolymer;
Step 3: the prepolymer obtained by step 2 is added in reaction kettle, then it is charged with triethanolamine, two bays
Sour dibutyl tin, color stuffing, coupling agent are heated to 250 DEG C, and holding pressure is 0.25MPa, and reaction 3.5h is up to preparation coating;
Step 4: antifoaming agent is added into the preparation coating obtained by step 3, room temperature persistently stirs 1.5h, then will be final
Product is filtered to remove dross up to scaffold abrasion resistant anticorrosive paint;
Step 5: the coating obtained by step 4 is coated on scaffold, normal temperature cure 36h is prevented up to scaffold with wear-resisting
Rotten coating.
The segment that the montant of scaffold is intercepted one section of long 120mm uses the scaffold obtained by embodiment 1-5 as sample
The adhesive force and hardness of wear-and corrosion-resistant coating are tested by GB1720-1979 and GB 1727-70 respectively, will be applied cated
Montant sample is placed in 280 DEG C of constant temperature oven, toasts 3h, and whether observation coating, which has, falls off, blisters, it is attached to test its to be cracked
The situation of change puted forth effort.According to GB1763-1989 standards, the steel pipe sample for making coating is respectively put into corrosive medium and is carried out
Soak test is with the medium corrosion resistance of testing coating.Using JM-IV type paint film abrasion instruments, in the examination of 750g loads, 75r/min
It is tested under the conditions of testing, the wearability (GB/T1768-2006) of paint film is indicated with the weightlessness of paint film.Show that the performance of coating refers to
Mark is as shown in table 1.
The performance indicator of 1 embodiment of table, 1 to 5 gained scaffold wear-and corrosion-resistant coating
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (10)
1. a kind of scaffold with wear-and corrosion-resistant coating, including several montants (1) being vertically arranged and it is connected to montant (1)
Between connecting rod (2), the terminal pad (3) for being connected to connecting rod (2) on montant (1), connection are provided on montant (1)
Several connecting holes (4) are provided on disk (3), which is characterized in that be additionally provided with connecting rod (2) in the end of connecting rod (2)
The buckle structure (5) being fixed in terminal pad (3), the buckle structure (5) include two vertical spacings setting button body (6), two
The consistency of thickness of the spacing and terminal pad (3) of body (6) is detained, the opposite face of button body (6) is additionally provided with block tongue (8), and button body (6) is opposite
An accommodating cavity (10) is offered in face, block tongue (8) is interior in accommodating cavity (10) by an extensible member slip, when block tongue (8) are stretched out
When accommodating cavity (10) is outer, just it is caught in connecting hole (4).
2. a kind of scaffold with wear-and corrosion-resistant coating according to claim 1, which is characterized in that the extensible member
Including the spring (9) between an electromagnet (11) and connection electromagnet (11) and block tongue (8), the electromagnet (11) obtains dead electricity
It is controlled by the control module (12) of a switching circuit, when electromagnet (11) must be electric, block tongue (8) is adsorbed and contracted by electromagnet (11)
In accommodating cavity (10), when electromagnet (11) dead electricity, block tongue (8) stretches out accommodating cavity under the reply force effect of spring (9)
(10), it is stuck on the connecting hole (4) of terminal pad (3).
3. a kind of scaffold with wear-and corrosion-resistant coating according to claim 1, which is characterized in that the block tongue (8)
Along the width of terminal pad (3) radially and equivalent width of the connecting hole (4) along terminal pad (3) radially.
4. a kind of scaffold with wear-and corrosion-resistant coating according to claim 1, which is characterized in that the coating includes
The group of following parts by weight is grouped as:
5. a kind of scaffold with wear-and corrosion-resistant coating according to claim 4, which is characterized in that the coating includes
The group of following parts by weight is grouped as:
6. a kind of scaffold with wear-and corrosion-resistant coating according to any one of claim 4 to 5, which is characterized in that
The solvent is dimethylbenzene and acetone according to weight ratio 5~7:3 preparations obtain.
7. a kind of scaffold with wear-and corrosion-resistant coating according to any one of claim 4 to 5, which is characterized in that
The color stuffing is one or more of graphite, molybdenum disulfide, chrome green, silica, bronze powder, titanium oxide group
It closes.
8. a kind of scaffold with wear-and corrosion-resistant coating according to any one of claim 4 to 5, which is characterized in that
The antifoaming agent is 201 silicone oil.
9. a kind of scaffold with wear-and corrosion-resistant coating according to any one of claim 4 to 5, which is characterized in that
The coupling agent is one or more of KH-550, KH-560, KH-570 combination.
10. a kind of scaffold with wear-and corrosion-resistant coating according to any one of claim 4 to 5, which is characterized in that
The preparation method of the coating includes the following steps:
Step 1: weighing each raw material according to components by weight percent;
Step 2: the polyurethane weighed, TDI, butyl acetate, polytetrafluoroethylene (PTFE) are added sequentially in castor oil, it is then past
Solvent is wherein added, after solution is mixed, is persistently stirred with blender, is used in combination heating water bath, 40~50 DEG C of reactions 3 of constant temperature~
4h obtains prepolymer;
Step 3: the prepolymer obtained by step 2 is added in reaction kettle, then it is charged with triethanolamine, tin dilaurate two
Butyl tin, color stuffing, coupling agent are heated to 200~300 DEG C, and holding pressure is 0.2~0.3MPa, and 3~4h of reaction is up to preparation
Coating;
Step 4: antifoaming agent is added into the preparation coating obtained by step 3, room temperature persistently stirs 1~2h, then will finally produce
Object is filtered to remove dross up to scaffold abrasion resistant anticorrosive paint;
Step 5: the coating obtained by step 4 is coated on scaffold, 24~48h of normal temperature cure is prevented up to scaffold with wear-resisting
Rotten coating.