CN108691401A - A kind of UV fluorine carbon plate - Google Patents
A kind of UV fluorine carbon plate Download PDFInfo
- Publication number
- CN108691401A CN108691401A CN201710135145.6A CN201710135145A CN108691401A CN 108691401 A CN108691401 A CN 108691401A CN 201710135145 A CN201710135145 A CN 201710135145A CN 108691401 A CN108691401 A CN 108691401A
- Authority
- CN
- China
- Prior art keywords
- fluorine carbon
- photocurings
- carbon plate
- fibre reinforced
- roller coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of UV fluorine carbon plate be using special fibre reinforced cement board as base material, surface through being polished for a plurality of times, permeating, after waterproof roller coating or showering colour UV F-C paints made of ultraviolet light solidification with the novel UV fluorine carbon plate such as water-fast, fire resisting, resistant, scratch resistance, rub resistance, impact resistance, UV resistant, weather-proof.Reticular structure made of UV fluororine-carbon coatings are the acrylate being modified by fluoric ether and monomer is cross-linked with each other, coating is fine and close, and coating surface tension is low, and anti-pollution is not easy dust accumulation.It since F-C key bond energys are strong, is difficult to be broken under the action of light and heat, UV degradation, anti-powdering under rugged environment, keeps inherent colour and gloss, be not in explosion, peel off, there is the weatherability of overlength, service life to be up to 25 years or more.Fluorine atom volume is big in fluorocarbon chain section and tight C-C chains, in the shape of a spiral structure, forms very strong space Folding-Screen and covers effect, any atom or atomic group are all difficult intrusion, show high chemical inertness, have fabulous acid and alkali resistance and solvent corrosion performance.
Description
One, technical field
The present invention relates to a kind of UV fluorine carbon plates, have water-fast, fire resisting, resistant, scratch resistance, rub resistance, acid-alkali-corrosive-resisting, resistance to punching
It hits, UV resistant, the characteristics such as weather-proof, it is related decorating outer wall of building plank.
Two, background technology
A kind of F-C paint that UV fluorine carbon plate uses refers to the coating using fluororesin as main film forming substance;Also known as F-C paint,
Fluoro coatings, fluorine resin coating etc..Among various coating, fluorine resin coating is since the fluorine element electronegativity of introducing is big, carbon-fluorine bond
Can be strong, there are especially advantageous properties.Weatherability, heat resistance, lower temperature resistance, chemical resistance, and with uniqueness
Non-stick and low abrasiveness.By the fast development of decades, fluoro coatings are in building, chemical industry, electric appliance and electronic industry, machine
Tool industry, aerospace industries, household supplies every field be used widely.As after acrylic coating, polyurethane painting
After the high performance coating such as material, organosilicon coating, the highest coating brand of comprehensive performance.Currently, using more extensive fluorine tree
Grease coating material mainly has the three categories type such as PTFE, PVDF, PEVE, and F-C paint has following several big excellent compared with other traditional coatings
Point:(1) excellent Corrosion Protection-has benefited from chemical substances and a variety ofization such as fabulous chemical inertness, paint film acid and alkali resistance, salt
Solvent is learned, protective barrier is provided for base material;The paint film is tough and tensile-and case hardness height, impact resistance, anti-buckling, wearability be good, display
Go out splendid physical mechanical property.(2) non-maintaining, automatically cleaning-fluororine-carbon coating has extremely low surface energy, surface dirt that can pass through
Rainwater is self-cleaning, fabulous hydrophobicity (maximum water absorption rate is less than 5%) and reprimand oil, minimum friction coefficient (0.15-0.17), no
Meeting non-dust absorption and non-fouling, soil resistance are good.(3) strong adhesion-the plastics such as the metals such as copper, stainless steel, polyester, polyurethane, vinyl chloride,
All there is its excellent adhesive force, basic display to go out preferably to invest the characteristic of any material on the surfaces such as cement, composite material.Height decoration
Property --- in 60 degree of gloss meters, 80% or more high glaze can be reached.(4) containing a large amount of in overlength weatherability-coating
F--C keys, determine its superpower stability, not dusting, colour-fast, and service life is up to 20 years, is had and is applied than any other class
Expect more excellent performance.Excellent application property-bi-component package, storage period are long, easy for construction.
A kind of special fibre reinforced cement board that UV fluorine carbon plate is voluntarily developed using company as base material, surface through being polished for a plurality of times,
It, will be in advance through being derived from lithotome color made of polychrome printing after two layers of UV fluorine carbon priming paint of roller coating or showering after infiltration, waterproof
With the UV fluorocarbon films of decorative pattern, the transfer of UV fluorocarbon films is solidificated on base material by caloric transfer printing technology, then two layers of UV of roller coating or showering
Fluorocarbon varnish passes through novel inorganic flame-proof finishing plate made of ten three times ultraviolet light solidification.
Three, invention content
It is an object of the invention to using use be using special fibre reinforced cement board as base material, surface through being polished for a plurality of times,
Infiltration, after waterproof, roller coating or showering colour UV F-C paints are made of ultraviolet light solidification with water-fast, fire resisting, resistant, resistance to
Scrape, rub resistance, acid-alkali-corrosive-resisting, impact resistance, UV resistant, the novel UV fluorine carbon plate such as weather-proof.UV fluororine-carbon coatings are by fluoroalkane
Reticular structure made of the acrylate and monomer that hydrocarbon is modified are cross-linked with each other, coating is fine and close, and coating surface tension is low, anti-pollution,
It is not easy dust accumulation.Since F-C key bond energys are strong, be difficult to be broken under the action of light and heat, under rugged environment UV degradation,
Anti-powdering keeps inherent colour and gloss, is not in explosion, peels off, and has the weatherability of overlength, service life to be up to 25 years or more.
Fluorine atom volume is big in fluorocarbon chain section and tight C-C chains, and structure, forms very strong space Folding-Screen and cover effect in the shape of a spiral,
Any atom or atomic group are all difficult intrusion, show high chemical inertness, have fabulous acid and alkali resistance and solvent corrosion
Energy.
According to a kind of UV fluorine carbon plate in summary, it is characterised in that:Special fibre reinforced cement board is with preferred natural
Reinforcing fiber, high strength portland cement, flyash, SILICA FUME, additive composition pass through compression moulding, and density domination is 1.4
~1.6g/cm3。
According to a kind of UV fluorine carbon plate in summary, it is characterised in that:Colored F-C paint is mainly made of following proportioning:
According to a kind of UV fluorine carbon plate in summary, it is characterised in that:A kind of UV fluorine carbon plate preparation process is:A. prefabricated first
Special fibre reinforced cement board, according to a certain ratio by natural reinforcing fiber, high strength portland cement, flyash, SILICA FUME, add
Agent etc. is added to be sufficiently mixed, b. is made after the saturated vapor of 7000 tons of press compression mouldings, 10 atmospheric pressure conserves 10-20d
Special fibre reinforced cement board is used as the substrate of UV fluorine carbon plates.Substrate automatic wire charging → bottom water-protected enclosure → UV light is solid
Finely polishing → plate face infiltration closing → UV photocurings → two layers of the roller coating putty → UV photocurings → fine polishing of change → plate surface
The roller coating of → plate face, two layers of priming paint of showering → UV photocurings → fine polishing → transfer height emulation UV fluorocarbon films → UV photocurings → rolling
Classify stacking → sampling Detection → qualification of (showering) two layers of finishing coat → UV photocurings → appearance test → overlay film is protected → is applied to be put in storage.
The present invention is a kind of UV fluorine carbon plate, has water-fast, fire resisting, resistant, scratch resistance, rub resistance, acid-alkali-corrosive-resisting, resistance to punching
It hits, UV resistant, the characteristics such as weather-proof, it is related decorating outer wall of building plank.
Four, specific implementation mode
Embodiment 1
It is base material that a kind of UV fluorine carbon plate of the present invention, which is special fibre reinforced cement board, surface through being polished for a plurality of times, permeating,
After waterproof, roller coating or showering colour UV F-C paints are made up of ultraviolet light solidification.Wherein special fibre reinforced cement board is with excellent
Natural reinforcing fiber, high strength portland cement, flyash, SILICA FUME, the additive composition of choosing pass through compression moulding, density control
System is in 1.4g/cm3.Colored F-C paint is mainly formed according to following quality:
Preparation process is:A. special fibre reinforced cement board prefabricated first, according to a certain ratio by natural reinforcing fiber, height
Strength silicate cement, flyash, SILICA FUME, additive etc. are sufficiently mixed, and b. is in 7000 tons of press compression mouldings, 10 atmospheric pressure
Saturated vapor maintenance 10d after special fibre reinforced cement board has been made, be used as the substrate of UV fluorine carbon plates.On substrate is automatic
Finely polishing → plate face permeates closing → UV photocurings → two layers of roller coating to line → bottom water-protected enclosure → UV photocurings → plate surface
Putty → UV photocurings → fine polishing → plate face roller coating, two layers of priming paint of showering → UV photocurings → fine polishing → transfer Gao Fang
The true colored F-C paint → UV photocurings → appearance test of UV fluorocarbon films → UV photocurings → two layers of roller coating (showering) → overlay film protection
→ classification stacking → sampling Detection → qualification storage.
Embodiment 2
It is base material that a kind of UV fluorine carbon plate of the present invention, which is special fibre reinforced cement board, surface through being polished for a plurality of times, permeating,
After waterproof, roller coating or showering colour UV F-C paints are made up of ultraviolet light solidification.Wherein special fibre reinforced cement board is with excellent
Natural reinforcing fiber, high strength portland cement, flyash, SILICA FUME, the additive composition of choosing pass through compression moulding, density control
System is in 1.5g/cm3.Colored F-C paint is mainly formed according to following quality:
Preparation process is:A. special fibre reinforced cement board prefabricated first, according to a certain ratio by natural reinforcing fiber, height
Strength silicate cement, flyash, SILICA FUME, additive etc. are sufficiently mixed, and b. is in 7000 tons of press compression mouldings, 10 atmospheric pressure
Saturated vapor maintenance 20d after special fibre reinforced cement board has been made, be used as the substrate of UV fluorine carbon plates.On substrate is automatic
Finely polishing → plate face permeates closing → UV photocurings → two layers of roller coating to line → bottom water-protected enclosure → UV photocurings → plate surface
Putty → UV photocurings → fine polishing → plate face roller coating, two layers of priming paint of showering → UV photocurings → fine polishing → transfer Gao Fang
The true colored F-C paint → UV photocurings → appearance test of UV fluorocarbon films → UV photocurings → two layers of roller coating (showering) → overlay film protection
→ classification stacking → sampling Detection → qualification storage.
Embodiment 3
It is base material that a kind of UV fluorine carbon plate of the present invention, which is special fibre reinforced cement board, surface through being polished for a plurality of times, permeating,
After waterproof, roller coating or showering colour UV F-C paints are made up of ultraviolet light solidification.Wherein special fibre reinforced cement board is with excellent
Natural reinforcing fiber, high strength portland cement, flyash, SILICA FUME, the additive composition of choosing pass through compression moulding, density control
System is in 1.6g/cm3.Colored F-C paint is mainly formed according to following quality:
Preparation process is:A. special fibre reinforced cement board prefabricated first, according to a certain ratio by natural reinforcing fiber, height
Strength silicate cement, flyash, SILICA FUME, additive etc. are sufficiently mixed, and b. is in 7000 tons of press compression mouldings, 10 atmospheric pressure
Saturated vapor maintenance 15d after special fibre reinforced cement board has been made, be used as the substrate of UV fluorine carbon plates.On substrate is automatic
Finely polishing → plate face permeates closing → UV photocurings → two layers of roller coating to line → bottom water-protected enclosure → UV photocurings → plate surface
Putty → UV photocurings → fine polishing → plate face roller coating, two layers of priming paint of showering → UV photocurings → fine polishing → transfer Gao Fang
The true colored F-C paint → UV photocurings → appearance test of UV fluorocarbon films → UV photocurings → two layers of roller coating (showering) → overlay film protection
→ classification stacking → sampling Detection → qualification storage.
Three of the above physical property is as follows:
| Project | Measured value 1 | Measured value 2 | Measured value 3 |
| Full water flexural strength MPa | 16 | 17 | 18 |
| Moisture content % | 10 | 9 | 8 |
| Impact strength KJ/ ㎡ | 2.8 | 2.9 | 3.0 |
| After 75 Frozen-thawed cycleds | Crack-free, layering | Crack-free, layering | Crack-free, layering |
| Acid resistance 168h | 0.7 | 0.7 | 0.7 |
| Alkali resistance 168h | It is qualified | It is qualified | It is qualified |
| Water resistance 168h | It is qualified | It is qualified | It is qualified |
| Solvent resistant Ca Shixing >100 times | It is qualified | It is qualified | It is qualified |
| Combustibility | A1 | A1 | A1 |
Claims (4)
1. a kind of UV fluorine carbon plate, it is characterised in that:It is using special fibre reinforced cement board as base material, surface is through being polished for a plurality of times, oozing
Thoroughly, after waterproof, roller coating or showering colour UV F-C paints are made up of ultraviolet light solidification.
2. a kind of UV fluorine carbon plate according to claim 1, it is characterised in that:Special fibre reinforced cement board is with preferred day
Right reinforcing fiber, high strength portland cement, flyash, SILICA FUME, additive composition pass through compression moulding, and density domination exists
1.4~1.6g/cm3。
3. a kind of UV fluorine carbon plate according to claim 1, it is characterised in that:Colored F-C paint is mainly made of following proportioning:
。
4. a kind of UV fluorine carbon plate according to claim 1, it is characterised in that:A kind of UV fluorine carbon plate preparation process is:A. first
Prefabricated special fibre reinforced cement board, according to a certain ratio by natural reinforcing fiber, high strength portland cement, flyash, micro- silicon
Powder, additive etc. are sufficiently mixed, and b. makes after the saturated vapor of 7000 tons of press compression mouldings, 10 atmospheric pressure conserves 10-20d
At special fibre reinforced cement board, it is used as the substrate of UV fluorine carbon plates.Substrate automatic wire charging → bottom water-protected enclosure → UV
Fine polishing → plate face infiltration closing → UV photocurings → two layers of the roller coating putty → UV photocurings → fine of photocuring → plate surface
Polishing → plate face roller coating, two layers of priming paint of showering → UV photocurings → fine polishing → transfer height emulation UV fluorocarbon films → UV photocurings
Colored F-C paint → UV photocurings → the appearance test → overlay film is protected → of two layers of → roller coating (showering) is classified stacking → sampling Detection
→ qualification storage.