CN108659679A - A kind of high-strength wearable aqueous epoxy floor paint and preparation method thereof - Google Patents
A kind of high-strength wearable aqueous epoxy floor paint and preparation method thereof Download PDFInfo
- Publication number
- CN108659679A CN108659679A CN201810630029.6A CN201810630029A CN108659679A CN 108659679 A CN108659679 A CN 108659679A CN 201810630029 A CN201810630029 A CN 201810630029A CN 108659679 A CN108659679 A CN 108659679A
- Authority
- CN
- China
- Prior art keywords
- parts
- aqueous epoxy
- floor paint
- component
- epoxy floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of coatings, more particularly to a kind of high-strength wearable aqueous epoxy floor paint and preparation method thereof.The aqueous epoxy floor paint is made of component A and B component；The raw material for preparing of the component A includes：10~30 parts of 30~50 parts of aqueous epoxy resins and water；The raw material for preparing of the B component includes 0.5~2 part of 20~50 parts of aqueous epoxy curing agent, 10~30 parts of water, 10~60 parts of filler, 2~6 parts of wetting agent, 0.2~0.4 part of antifoaming agent, 5~15 parts of calcium sulfate crystal whiskers, 1~5 part of diatomite and nano-cellulose.The aqueous epoxy floor paint has preferable impact resistance and wearability, and will not significantly improve production cost, and the preparation method is simple and practical, easily operated, has very high economy and practical value.
Description
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of high-strength wearable aqueous epoxy floor paint and its preparation side
Method.
Background technology
Floor paint was invented in 1934 by Germany earliest, mainly by a variety of differences such as oil plant, tree material, color, solvents
Substance is fabricated through many end production process such as mixing, dissolving, dispersion, can be divided into decorative floor paint, heavy antisepsis floor paint,
Resistance to heavy duty floor paint etc., has the characteristics that beautiful, true, beautiful, wear-resisting, waterproof, anti-corrosion.Aqueous epoxy floor paint is attached with its
It is excellent to put forth effort height, corrosion resistance, electrical insulation properties, using water as decentralized medium, smell is small, meets environmental requirement, in addition, water
Property epoxide terrace paint solidification after have a small amount of moisture in film and exist, so dense lead can be cured to avoid solvent type floor coatings
The defects of bubbling caused by causing the steam in concrete to rise, deformation and stripping.
It has been more than solvent type epoxy floor paint in the dosage of developed country, aqueous epoxy floor paint.But China's water-base epoxy
The promotion and application of terrace product are not also very fully that occupation rate of market is not high, and reason is mainly the country in aqueous epoxy floor
The input for painting research and development of products, increased quality etc. is very little so that the performance of this province of product is insufficient, such as intensity is poor and wear-resisting
Performance is bad, while the price of aqueous epoxy floor paint product is generally higher, leads to the competitive advantage of aqueous epoxy floor paint not
Obviously.Therefore, exploitation is good with high intensity and wearability, and moderate aqueous epoxy floor paint is especially necessary.
Invention content
In order to solve the above technical problem, the present invention provides a kind of high-strength wearable aqueous epoxy floor paint and its preparation sides
Method.The aqueous epoxy floor paint has preferable impact resistance and wearability, and will not significantly improve production cost, the system
Preparation Method is simple and practical, easily operated, has very high economy and practical value.
High-strength wearable aqueous epoxy floor paint of the present invention, the aqueous epoxy floor paint is by component A and B component group
At；
Wherein, in parts by weight, the raw material for preparing of the component A includes：30~50 parts of aqueous epoxy resins and water 10~
30 parts；
In parts by weight, the raw material for preparing of the B component includes：20~50 parts of aqueous epoxy curing agent, 10~30 parts of water,
10~60 parts of filler, 2~6 parts of wetting agent, 0.2~0.4 part of antifoaming agent, 5~15 parts of calcium sulfate crystal whiskers, 1~5 part of diatomite and
0.5~2 part of nano-cellulose.
In above-mentioned formula, involved base stock and additive, such as wetting agent, antifoaming agent, filler, this can be selected
Field known common type in preparing aqueous epoxy floor paint, but in order to realize between each component preferably cooperation/collaboration effect
Fruit, the present invention have made following preferred restriction to each component in formula：
Preferably, the aqueous epoxy resins are bisphenol A type epoxy resin, and the bisphenol A type epoxy resin resin is selected from
E44 types (being purchased from Shandong De Yuan epoxies Science and Technology Ltd.), GEM02 or GEM03 (are purchased from the upper sea green good limited public affairs of water paint
Department) in it is one or more.
Preferably, the aqueous epoxy curing agent be selected from GCA02 (be purchased from upper sea green good water paint Co., Ltd) or
Sunmide WH-900；SunmideWH-900 is low viscosity, and the modified polyamine system aqueous epoxy curing agent of high molecular weight has
Emulsify the function of various epoxy resin.Coordinate with solid epoxy under the conditions of low temperature, high humidity, has good attachment
Property.
Suitable filler that is added can not only reduce the cost of aqueous epoxy floor paint, shorten film surface drying time, can be with
The mechanical strength of film, wearability, gloss and covering power are improved, reduces volume contraction when solidification, and assign its good storage
Stability is deposited, but excessive addition can then increase the viscosity of water paint, and the levelability of coating is caused to be deteriorated, constructional difficulties, film
Surface effect be deteriorated.Preferably, the filler is talcum powder, barium sulfate, kaolin, quartz sand, sericite, alumina silicate, carbon
One or more of sour calcium, wollastonite；Wherein, hardness can be improved in kaolin, and talcum powder can be improved the suspension of coating, reduce
Crack and gap, quartz sand and barium sulfate can increase the wear-resisting property and hardness of terrace, and sericite can improve the resistance to of terrace
Hou Xing, it reduces permeability, improve chemicals-resistant ability, can be as needed, select suitable cooperation and dosage.
Dispersant is a kind of filler stabilizer, and can be adsorbed on filler grain surface makes to generate repulsion between filler grain
Power makes filler grain stablize by electrostatic repulsion or steric hindrance, avoids filler agglomerating due to flocculation aggregation so that
Filler systems keep stablizing；It therefore, can also be in B component in order to avoid the aggregation of filler causes paint film floating, film to be bubbled
Suitable dispersant is added to increase the uniform and stable property of filler；Preferably, the B component further includes dispersant 0.1~0.7
Part；It is highly preferred that the dispersant is polycarboxylic acids ammonium salt type dispersant, in the preference of the present invention, select Sheng Ruopu sections public
The SN-5029 of department is as dispersant.
Preferably, the antifoaming agent is selected from ethers, long-chain alcohols, fatty acid acyl amine, phosphoric acid ester and organic silicon；
In the preferred embodiment of the present invention, the antifoaming agent is the SN-DEFOAMER318 or SN-DEFOAMER of company of Sheng Ruopu sections
319, this kind of antifoaming agent can quickly defoam and duration suds effect is good, and the film coated surface of formation is smooth pin-free.
It is poor to the wetability of ground since the surface tension of water is higher, especially there is the surface of grease remnants to be more difficult to
Wetting, should be added wetting agent to improve the compatibility of paint and ground；In a preferred embodiment of the invention, the wetting agent is
The wetting agent of BYK-346, BYK-333 of German Bi Ke.
Preferably, the average aspect ratio of the calcium sulfate crystal whiskers be 30~50, a diameter of 1~4 μm；Purchased from the excellent conjunction in Foshan City
Chemical Industry Science Co., Ltd.Calcium sulfate crystal whiskers be it is a kind of with single crystal form grow it is novel it is needle-shaped, there is uniform crosssection, complete
The perfect fiber sub-nanometer material of shape, internal structure.The advantage for integrating both reinforcing fiber and ultra-fine inorganic filler, adds
The effects that enhancing, toughening, thickening, heat-resisting, wear-resisting, oil resistant can be played, is added in aqueous epoxy floor paint, and cost is relatively low.
Preferably, the diatomaceous fineness is 200~300 mesh, and diatomite is common coating additive, has hole
The features such as degree is big, absorbability is strong, chemical property is stable, wear-resisting, heat-resisting, can provide excellent surface property for coating, and increase-volume increases
Thick and raising adhesive force.Since it has larger pore volume, film can be made to shorten drying time.The use of resin can also be reduced
Amount, reduces cost.
Preferably, the nano-cellulose be selected from nanofibrils cellulose (NFC), nano micro crystal cellulose (CNC), it is cloudy from
One or several kinds in sub- nanofibrils cellulose (NFC)；It is highly preferred that the nano-cellulose is nanofibrils fiber
Element.Nano-cellulose is added in aqueous epoxy floor paint can increase the intensity of product, largely be exposed due to its surface
Hydroxyl generates stronger hydrophily, therefore also certain thickening and peptizaiton, additionally it is possible to increase the lower temperature resistance of product
Energy.
The present invention also provides the preparation methods of aqueous epoxy floor paint, include the following steps：
Component A manufacturing method is：Aqueous epoxy resins are mixed for 30~50 parts with water 10~30, at 300~500rpm
It is stirred 5~10min, is packed；
B component manufacturing method is：To 10~60 parts of filler, 5~15 parts of calcium sulfate crystal whiskers, 1~5 part of diatomite and nanometer
0.5~2 part of cellulose carries out that 10~30 parts of water is added after tentatively mixing, the reduction of speed after 1000~1800rpm stirs 15~25min
To 500~800rpm, 20~50 parts of aqueous epoxy curing agent is added, 0.2~0.4 part of 2~6 parts of wetting agent and antifoaming agent continue to stir
5~10min is mixed, is packed.
When in use, component A and B component are mixed, the mass ratio of the component A and B component is 1:(2.5~
4)。
Compared with prior art, it is an advantage of the invention that：
(1) it is formulated reasonable design, indices meet the national standard of epoxy flooring coating；In addition, it has been found that
The wear-resisting property of product and resistance to punching can be significantly improved by adding suitable calcium sulfate crystal whiskers, diatomite and nano-cellulose
Performance is hit, and the inexpensive manufacturing cost of product raw material is relatively low.
(2) due to using double aqueous components, having the characteristics that Environmental Safety, energy saving.
(3) it is formulated by improving, adjusts the ratio between each component, drying time is short, hard after obtained water paint application
It is fast to change speed.
Specific implementation mode
The invention discloses a kind of high-strength wearable aqueous epoxy floor paint and preparation method thereof, those skilled in the art can be with
Present disclosure is used for reference, technological parameter realization is suitably modified.In particular, it should be pointed out that all similar substitutions and modifications are to ability
It is it will be apparent that they are considered as being included in the present invention for field technique personnel.The method and application of the present invention has been led to
Preferred embodiment is crossed to be described, related personnel obviously can not depart from the content of present invention, in spirit and scope to this paper institutes
The methods and applications stated are modified or suitably change and combine, to realize and apply the technology of the present invention.
It is common commercially available product in supplementary material according to the present invention if not specified, can be bought and be obtained by market.
The above case study on implementation be to the present invention be specifically described for example, technical staff belonging to the present invention can be with
Various concrete cases are modified or supplemented.
Embodiment 1
1) aqueous epoxy floor paint formula (in parts by weight)：
Component A：20 parts of 40 parts of bisphenol A type epoxy resin (GEM02 types) and water；
B component：35 parts of aqueous epoxy curing agent (GCA02 types), 20 parts of water, 35 parts of filler (talcum powder), wetting agent (BYK-
346) 4 parts, 0.4 part of dispersant (SN-5029), 0.3 part of antifoaming agent (SN-DEFOAMER 319), 10 parts of calcium sulfate crystal whiskers, diatom
Native 3.5 parts and 1.0 parts of nanofibrils cellulose.
2) preparation method includes the following steps：
Component A manufacturing method is：The epoxy resin and water of formula ratio are added in material-compound tank, by the rotational speed regulation of blender
To 300~500rpm, it is stirred 5~10min, is packed；
B component manufacturing method is：Be added in material-compound tank the filler of formula ratio, dispersant, calcium sulfate crystal whiskers, diatomite with
And nanofibrils cellulose, it is slowly stirred lower addition water, after water is added, mixing speed is opened to 1000~1800rpm, stirs
Reduction of speed is mixed after 15~25min to 500~800rpm, be added aqueous epoxy curing agent and remaining additive continue stirring 5~
10min, packaging.
Embodiment 2
1) aqueous epoxy floor paint formula (in parts by weight)：
Component A：10 parts of 30 parts of bisphenol A type epoxy resin (GEM02 types) and water；
B component：20 parts of aqueous epoxy curing agent (Sunmide WH-900), 20 parts of water, 10 parts of filler (quartz sand), wetting
2 parts of agent (BYK-333), 0.2 part of dispersant (SN-5029), 0.2 part of antifoaming agent (SN-DEFOAMER 318), calcium sulfate crystal whiskers 5
0.5 part of part, 1 part of diatomite and nano micro crystal cellulose.
2) the preparation method is the same as that of Example 1.
Embodiment 3
1) aqueous epoxy floor paint formula (in parts by weight)：
Component A：30 parts of 50 parts of bisphenol A type epoxy resin (GEM02 types) and water；
B component：50 parts of aqueous epoxy curing agent (Sunmide WH-900), 30 parts of water, 60 parts of filler (talcum powder), wetting
6 parts of agent (BYK-333), 0.4 part of dispersant (SN-5029), 0.4 part of antifoaming agent (SN-DEFOAMER 318), calcium sulfate crystal whiskers 15
2 parts of part, 5 parts of diatomite and nano-cellulose.
2) the preparation method is the same as that of Example 1.
Embodiment 4
1) aqueous epoxy floor paint formula (in parts by weight)：
Component A：27 parts of 40 parts of bisphenol A type epoxy resin (GEM02 types) and water；
B component：48 parts of aqueous epoxy curing agent (GCA02 types), 18 parts of water, 50 parts of filler (kaolin), wetting agent (BYK-
346) 4.5 parts, 0.4 part of dispersant (SN-5029), 0.25 part of antifoaming agent (SN-DEFOAMER 319), 13 parts of calcium sulfate crystal whiskers,
1.6 parts of 4 parts of diatomite and nano micro crystal cellulose.
2) the preparation method is the same as that of Example 1.
Embodiment 5
1) aqueous epoxy floor paint formula (in parts by weight)：
Component A：25 parts of 35 parts of bisphenol A type epoxy resin (GEM02 types) and water；
B component：50 parts of aqueous epoxy curing agent (GCA02 types), 15 parts of water, 35 parts of filler (talcum powder), wetting agent (BYK-
346) 5 parts, 0.6 part of dispersant (SN-5029), 0.35 part of antifoaming agent (SN-DEFOAMER 319), 7 parts of calcium sulfate crystal whiskers, diatom
Native 2 parts and 1.2 parts of nano-cellulose.
2) the preparation method is the same as that of Example 1.
Embodiment 6
By the two component epoxy floor paint of embodiment 1 according to component A and B component 1:3 mass ratio is mixed, then
It tests according to GB/T22374-2008, while that detects also has comparative example 1-2, comparative example 1 (component A and B component=1:3)
Formula in, do not add diatomite and nano-cellulose, remaining formula and the preparation method is the same as that of Example 1；Comparative example 2 (component A with
B component=1:3) in formula, calcium sulfate crystal whiskers are not added, remaining is formulated and the preparation method is the same as that of Example 1, as a result such as the following table 1
It is shown：
Table 1
By table 1 it is found that the test event that aqueous epoxy floor paint provided by the invention is carried out meets national standard,
Compared with comparative example 1-2, has in terms of wearability, impact resistance and increase significantly.
Claims (9)
1. a kind of high-strength wearable aqueous epoxy floor paint, which is characterized in that the aqueous epoxy floor paint is by component A and B component
Composition；
Wherein, in parts by weight, the raw material for preparing of the component A includes：10~30 parts of 30~50 parts of aqueous epoxy resins and water；
In parts by weight, the raw material for preparing of the B component includes：20~50 parts of aqueous epoxy curing agent, 10~30 parts of water, filler
10~60 parts, 2~6 parts of wetting agent, 0.2~0.4 part of antifoaming agent, 5~15 parts of calcium sulfate crystal whiskers, 1~5 part of diatomite and nanometer
0.5~2 part of cellulose.
2. aqueous epoxy floor paint according to claim 1, which is characterized in that the aqueous epoxy resins are bisphenol A-type
Epoxy resin, the bisphenol A type epoxy resin resin are one or more in E44 types, GEM02 or GEM03.
3. aqueous epoxy floor paint according to claim 1, which is characterized in that the aqueous epoxy curing agent is selected from
GCA02 or Sunmide WH-900.
4. aqueous epoxy floor paint according to claim 1, which is characterized in that the filler is talcum powder, barium sulfate, height
One or more of ridge soil, quartz sand, sericite, alumina silicate, calcium carbonate, wollastonite.
5. aqueous epoxy floor paint according to claim 1, which is characterized in that the B component further include dispersant 0.1~
0.7 part.
6. aqueous epoxy floor paint according to claim 1, which is characterized in that the average aspect ratio of the calcium sulfate crystal whiskers
It is 30~50, a diameter of 1~4 μm.
7. aqueous epoxy floor paint according to claim 1, which is characterized in that the diatomaceous fineness is 200~300
Mesh.
8. aqueous epoxy floor paint according to claim 1, which is characterized in that the nano-cellulose is selected from nanofibrils
One or several kinds in cellulose (NFC), nano micro crystal cellulose (CNC), anion nanofibrils cellulose (NFC).
9. a kind of preparation method of high-strength wearable aqueous epoxy floor paint, which is characterized in that include the following steps：
Component A manufacturing method is：Aqueous epoxy resins are mixed for 30~50 parts with water 10~30, are stirred at 300~500rpm
Mix 5~10min, packaging；
B component manufacturing method is：To 10~60 parts of filler, 5~15 parts of calcium sulfate crystal whiskers, 1~5 part of diatomite and nanofiber
Element 0.5~2 part carry out tentatively mix after be added 10~30 parts of water, 1000~1800rpm stir 15~25min after reduction of speed extremely
500~800rpm, is added 20~50 parts of aqueous epoxy curing agent, and 0.2~0.4 part of 2~6 parts of wetting agent and antifoaming agent continue to stir
5~10min, packaging.