CN108659601A - A kind of scale and shell multi-layer waterproof and anticorrosion heat preservation putty and its preparation method and application - Google Patents
A kind of scale and shell multi-layer waterproof and anticorrosion heat preservation putty and its preparation method and application Download PDFInfo
- Publication number
- CN108659601A CN108659601A CN201810358470.3A CN201810358470A CN108659601A CN 108659601 A CN108659601 A CN 108659601A CN 201810358470 A CN201810358470 A CN 201810358470A CN 108659601 A CN108659601 A CN 108659601A
- Authority
- CN
- China
- Prior art keywords
- scale
- heat preservation
- groups
- layer waterproof
- anticorrosion heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of scale and shell multi-layer waterproof and anticorrosion heat preservation putties and its preparation method and application, by mass percentage, including A groups and B groups；Include mainly liquid silica, epoxy resin, polyacrylate, glass flake, hollow glass bead, magnesium silicate aluminium powder, aqueous epoxy curing agent and dispersant.Ageing-resistant, strong adhesive force of the invention, intensity is high, and light anti-corrosion weight waterproof is protected；Such as append one layer of heat preservation scale and shell on structure surface after curing of coatings, superpower weatherability can extending structure body service life；With grain depot cool down gas partiting dampproof, extend warehouse service life and solve the problems, such as that grain storage goes mouldy, with having good waterproof, anti-corrosion, freeze proof, effect on waves splash about area's bridge, have a good application prospect.
Description
Technical field
The invention belongs to putty and its preparation method and application field, more particularly to a kind of scale and shell multi-layer waterproof and anticorrosion is protected
Warm putty and its preparation method and application.
Background technology
China's major part heat insulating work is all made of organic board, inflammable, and inorganic mortar intensity is low, and water suction is non-moistureproof, exists
Many security risks.Although Conventional insulation various types have a single function mostly, growth requirement, Bu Nengquan are not caught up with
Orientation solves the problems, such as.Meanwhile there is also easy to leak water, easy to aging, intensity is low, it is easy to crack, it is functional heat preservation it is fewer and fewer, it is right
It is more difficult to ensure in complex-shaped architecture quality.People's every few years will spend a large amount of fund and labour to return
It repaiies.The normal life, work, the production order of people have not only been upset, but also has directly affected the service life of whole building building.
Therefore, it also needs further to study resistance to ultraviolet irradiation, adhesion strength is big, and waterproof and anticorrosion trapping effect is good, multi-functional
High-quality materials for wall.
Invention content
Technical problem to be solved by the invention is to provide a kind of scale and shell multi-layer waterproof and anticorrosion heat preservation putty and its preparations
Methods and applications, the putty is ageing-resistant, strong adhesive force, and intensity is high, and light anti-corrosion weight waterproof is protected；Such as in structure body surface after curing of coatings
Face appends one layer of heat preservation scale and shell, superpower weatherability can extending structure body service life；Used in grain depot i.e. cool down every
Gas is moisture-proof, extend warehouse service life and solves the problems, such as that grain storage goes mouldy, is good with having on waves splash about area's bridge
Waterproof, anti-corrosion, freeze proof, effect, have a good application prospect.
The present invention provides a kind of scale and shell multi-layer waterproof and anticorrosion heat preservation putties, by mass percentage, including A groups and B groups,
It is specific as follows：
A groups：
The sum of above-mentioned all components are equal to 100%；
B groups：
The sum of above-mentioned all components are equal to 100%.
The emulsifier is OP-10.
The polyvinyl alcohol is solution or colloidal sol.
The grain size of the glass flake is 200-300 mesh.
The antifoaming agent is tributyl.
The present invention also provides a kind of preparation methods of scale and shell multi-layer waterproof and anticorrosion heat preservation putty, including：
(1) first epoxy resin is poured into container in proportion, emulsifier for mixing is then added, add liquid titanium dioxide
Silicon, glass flake, hollow glass bead, magnesium silicate aluminium powder and silane coupling agent are dispersed through to obtain A groups；
(2) polyacrylate, aqueous epoxy curing agent, crosslinking agent, polyvinyl alcohol dispersion mixing are added into glass in proportion
Glass scale and dispersant dispersion mixing, are eventually adding antifoaming agent, obtain B groups；
(3) A groups and B groups are mixed, is stirred evenly, filtered to get scale and shell multi-layer waterproof and anticorrosion heat preservation putty.
Mixing speed in the step (1) is 1000-2000 revs/min, and mixing time is 10-20 minutes.
It is 1000-2000 revs/min that dispersion in the step (1) and (2), which uses high speed dispersor, rotating speed, and the time is
10-20 minutes.
The present invention also provides a kind of application of scale and shell multi-layer waterproof and anticorrosion heat preservation putty, the putty is applied to building
Structure.
Advantageous effect
The present invention is with liquid silica, epoxy resin, polyacrylate, glass flake, hollow glass bead, silicic acid
The two-component of magnesium aluminium powder, aqueous epoxy curing agent and dispersant composition, is a kind of waterproof thermal-insulated putty of inorganic compounding anti-corrosion；This hair
Bright ageing-resistant, strong adhesive force, intensity is high, and light anti-corrosion weight waterproof is protected；After curing of coatings such as one layer of guarantor is appended on structure surface
Warm scale and shell, superpower weatherability can extending structure body service life；Cool down gas partiting dampproof, extension warehouse used in grain depot
Service life but solve the problems, such as grain storage go mouldy, with have on waves splash about area's bridge good waterproof, anti-corrosion, it is freeze proof,
Effect has a good application prospect.
Specific implementation mode
Present invention will be further explained below with reference to specific examples.It should be understood that these embodiments are merely to illustrate the present invention
Rather than it limits the scope of the invention.In addition, it should also be understood that, after reading the content taught by the present invention, people in the art
Member can make various changes or modifications the present invention, and such equivalent forms equally fall within the application the appended claims and limited
Range.
Embodiment 1
By mass percentage, including A groups and B groups, specific as follows：
A groups：
The sum of above-mentioned all components are equal to 100%；
B groups：
The sum of above-mentioned all components are equal to 100%.
Preparation method includes：
(1) first epoxy resin is poured into container in proportion, emulsifier for mixing is then added, add liquid titanium dioxide
Silicon, glass flake, hollow glass bead, magnesium silicate aluminium powder and silane coupling agent are dispersed through to obtain A groups；Wherein, mixing speed is
1000 revs/min, mixing time is 20 minutes；It is 1000 revs/min that dispersion, which uses high speed dispersor, rotating speed, and the time is 20 points
Clock；
(2) polyacrylate, aqueous epoxy curing agent, crosslinking agent, polyvinyl alcohol dispersion mixing are added into glass in proportion
Glass scale and dispersant dispersion mixing, are eventually adding antifoaming agent, obtain B groups；Wherein, disperse using high speed dispersor, rotating speed is
1000 revs/min, the time is 20 minutes；
(3) A groups and B groups are mixed, is stirred evenly, filtered to get scale and shell multi-layer waterproof and anticorrosion heat preservation putty.
Embodiment 2
By mass percentage, including A groups and B groups, specific as follows：
A groups：
The sum of above-mentioned all components are equal to 100%；
B groups：
The sum of above-mentioned all components are equal to 100%.
Preparation method includes：
(1) first epoxy resin is poured into container in proportion, emulsifier for mixing is then added, add liquid titanium dioxide
Silicon, glass flake, hollow glass bead, magnesium silicate aluminium powder and silane coupling agent are dispersed through to obtain A groups；Wherein, mixing speed is
2000 revs/min, mixing time is 10 minutes；It is 2000 revs/min that dispersion, which uses high speed dispersor, rotating speed, and the time is 10 points
Clock；
(2) polyacrylate, aqueous epoxy curing agent, crosslinking agent, polyvinyl alcohol dispersion mixing are added into glass in proportion
Glass scale and dispersant dispersion mixing, are eventually adding antifoaming agent, obtain B groups；Wherein, disperse using high speed dispersor, rotating speed is
2000 revs/min, the time is 10 minutes；
(3) A groups and B groups are mixed, is stirred evenly, filtered to get scale and shell multi-layer waterproof and anticorrosion heat preservation putty.
Embodiment 3
By mass percentage, including A groups and B groups, specific as follows：
A groups：
The sum of above-mentioned all components are equal to 100%；
B groups：
The sum of above-mentioned all components are equal to 100%.
Preparation method includes：
(1) first epoxy resin is poured into container in proportion, emulsifier for mixing is then added, add liquid titanium dioxide
Silicon, glass flake, hollow glass bead, magnesium silicate aluminium powder and silane coupling agent are dispersed through to obtain A groups；Wherein, mixing speed is
2000 revs/min, mixing time is 10 minutes；It is 2000 revs/min that dispersion, which uses high speed dispersor, rotating speed, and the time is 10 points
Clock；
(2) polyacrylate, aqueous epoxy curing agent, crosslinking agent, polyvinyl alcohol dispersion mixing are added into glass in proportion
Glass scale and dispersant dispersion mixing, are eventually adding antifoaming agent, obtain B groups；Wherein, disperse using high speed dispersor, rotating speed is
1000 revs/min, the time is 10 minutes；
(3) A groups and B groups are mixed, is stirred evenly, filtered to get scale and shell multi-layer waterproof and anticorrosion heat preservation putty.
Claims (9)
1. a kind of scale and shell multi-layer waterproof and anticorrosion heat preservation putty, it is characterised in that：By mass percentage, including A groups and B groups, tool
Body is as follows：
A groups：
The sum of above-mentioned all components are equal to 100%；
B groups：
The sum of above-mentioned all components are equal to 100%.
2. a kind of scale and shell multi-layer waterproof and anticorrosion heat preservation putty according to claim 1, it is characterised in that：The emulsifier
For OP-10.
3. a kind of scale and shell multi-layer waterproof and anticorrosion heat preservation putty according to claim 1, it is characterised in that：The polyethylene
Alcohol is solution or colloidal sol.
4. a kind of scale and shell multi-layer waterproof and anticorrosion heat preservation putty according to claim 1, it is characterised in that：The glass squama
The grain size of piece is 200-300 mesh.
5. a kind of scale and shell multi-layer waterproof and anticorrosion heat preservation putty according to claim 1, it is characterised in that：The antifoaming agent
For tributyl.
6. a kind of preparation method of scale and shell multi-layer waterproof and anticorrosion heat preservation putty as described in claim 1, including：
(1) first epoxy resin is poured into container in proportion, emulsifier for mixing is then added, add liquid silica, glass
Glass scale, hollow glass bead, magnesium silicate aluminium powder and silane coupling agent are dispersed through to obtain A groups；
(2) polyacrylate, aqueous epoxy curing agent, crosslinking agent, polyvinyl alcohol dispersion mixing are added into glass squama in proportion
Piece and dispersant dispersion mixing, are eventually adding antifoaming agent, obtain B groups；
(3) A groups and B groups are mixed, is stirred evenly, filtered to get scale and shell multi-layer waterproof and anticorrosion heat preservation putty.
7. a kind of preparation method of scale and shell multi-layer waterproof and anticorrosion heat preservation putty according to claim 6, it is characterised in that：
Mixing speed in the step (1) is 1000-2000 revs/min, and mixing time is 10-20 minutes.
8. a kind of preparation method of scale and shell multi-layer waterproof and anticorrosion heat preservation putty according to claim 6, it is characterised in that：
It is 1000-2000 revs/min that dispersion in the step (1) and (2), which uses high speed dispersor, rotating speed, and the time is 10-20 points
Clock.
9. a kind of application of scale and shell multi-layer waterproof and anticorrosion heat preservation putty as described in claim 1, it is characterised in that：It is described greasy
Son is applied to building structure.