CN108658260A - A kind of sterilizing scale inhibiting agent and preparation method thereof - Google Patents
A kind of sterilizing scale inhibiting agent and preparation method thereof Download PDFInfo
- Publication number
- CN108658260A CN108658260A CN201810529600.5A CN201810529600A CN108658260A CN 108658260 A CN108658260 A CN 108658260A CN 201810529600 A CN201810529600 A CN 201810529600A CN 108658260 A CN108658260 A CN 108658260A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- water
- inhibiting agent
- sterilizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
This application discloses a kind of sterilizing scale inhibiting agents and preparation method thereof, raw material is zinc nitrate, sodium metasilicate, tannin, natrium humate, water, succinic acid, aminotrimethylenephosphonic acid, hydroxy propyl methacrylate, di-iso-amyl phosphate, bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium, isopropanol, 2 bromine, 2 nitro, 1,3 propylene glycol, potassium hydroxide, hydroxy ethylene diphosphonic acid and sodium tetraborate;Product is mainly used for sterilizing, bactericidal, corrosion inhibition rate 98 99.9%, is free of polymer;It prevents incrustation scale to be precipitated on heat-exchange apparatus surface, extends reverse osmosis membrane scavenging period, bactericidal effect is excellent, especially suitable to be used with heat power plant boiler water, reduces water eutrophication pollution;Compounding is easy, and runs concentration 15 35 × 10‑6, scale inhibition performance 99.5 99.9%;50 60 DEG C are placed six months, scale inhibition effect 98 99%.
Description
Technical field
The application belong to cyclization reagent technology field more particularly to a kind of environmental protection, the good sterilizing scale inhibiting agent of corrosion inhibition and its
Preparation method.
Background technology
Antisludging agent(scale inhibitor):Be with can be in disperse water slightly solubility inorganic salts, inhibit or interfere with indissoluble
Precipitation, fouling function of the property inorganic salts in metal surface, and metal equipment is maintained to have a kind of medicament of good heat-transfer effect.
Antisludging agent can remove de-sludging and prevent the formation of incrustation scale, improve heat exchanger effectiveness, reduce electric energy or reduce disappearing for fuel
Consumption;Water process can also reduce blowdown, improve the utilization rate of water, can generally save 60% or more, meet the new policies of China's energy-saving and emission-reduction
Plan.
Research of non-phosphorus scale inhibitor is applicable to different water sources, the product using without phosphorus polymer and dispersed high molecular polymer come
Prevent hardness and oxidation deposition of iron.It is a kind of dynamical liquid dirt dispersion agent, effectively controls calcium carbonate, calcium sulfate, sulfuric acid
Strontium fouling, the LSI of calcium carbonate is up to+3.0 still will not fouling.It can be used for controlling film separation system fouling precipitation and reduce particle and block up
Plug.
Reverse osmosis antisludging agent is used exclusively for reverse osmosis(RO)System and nanofiltration(NF)And ultrafiltration(UF)The antisludging agent of system,
Film surface fouling can be prevented, water yield and production water quality can be improved, reduce operating cost.
RO antisludging agents are one kind of antisludging agent, main component:Organic dispersion, organic complex, antozone hydroxyl are poly-
Close object etc.;The scope of application:The processing of system suitable for pure water system RO process sections.Physical property appearance light color liquid, pH 1.0-
2.5。
Corrosion inhibiter by concentration appropriate and in the form of be present in environment(Medium)When middle, material corrosion can be prevented or slowed down
Chemical substance or compound, therefore corrosion inhibiter is referred to as corrosion inhibitor.Its dosage very little (0.1%~1%), but effect
Significantly.The method of this protection metal claims corrosion inhibiter to protect.Corrosion inhibiter is used for neutral medium(Boiler feed water, recirculated cooling water)、
Acid medium(The hydrochloric acid to descale, the acid dip solution of plating piece derusting before being electroplated)And gas medium(Vapour phase inhibitor).
Adsorbed film type corrosion inhibiter is mostly organic inhibitor, they have polarity gene, can by metallic surface charge adsorption,
One layer of monomolecular film is formed in entire anode and cathode region, to prevent or slow down the reaction of corresponding electrochemistry.Contain Ru certain
Nitrogen, sulfur-bearing or hydroxyl, organic compound with surface-active, there are two types of incompatible groups in molecule;It is hydrophilic
Base and lipophilic group.The molecule of these compounds is with hydrophilic group(For example, amino)Be adsorbed on metal surface, formed one layer it is fine and close
Hydrophobic film protects metal surface not by aqueous corrosion.Tallow amine, cetylamine and octadecylamine etc. are referred to as the amine of " film amine ",
It is exactly adsorbed film type corrosion inhibiter common in water process.Mercaptobenzothiazoler, benzotriazole and methylbenzotrazole etc. are coloured
Metal(Especially copper)Ideal corrosion inhibiter.Although they and copper metal itself act on film forming, with above-mentioned typical oxidation film
Type corrosion inhibiter is different, is not formed a film with chemisorption by oxidation by forming complex compound with the copper ion of metal surface
's.When metal surface is cleaning or activated state, such corrosion inhibiter can form the satisfactory adsorbed film of corrosion mitigating effect.But such as
In the case that there is corrosion product in fruit metal surface or has dirt deposition, it is difficult to form the corrosion inhibition film to work well, it at this time can be appropriate
A small amount of surfactant is added, to help such corrosion inhibiter to form a film.
Anti-incrustation corrosion inhibitor is made of organic phosphine, excellent copolymer and copper inhibitor etc., is all had to carbon steel, copper and copper alloy
There is excellent corrosion inhibition, there is remarkable scale inhibition and dispersion performance to calcium carbonate, calcium phosphate.This product is mainly used for open type circulating cooling
Water treatment system is particularly suitable for the system of cupric equipment.This product can be used for the water quality of high pH, high alkalinity, high rigidity, be current
One of the water treatment agent of comparatively ideal uncomfortable pH alkaline operations.
Polyamino polyether base methylenephosphonic acid PAPEMPPAPEMP is latest generation water treatment agent, has very high chelating point
It dissipates performance and very high calcium tolerance and excellent scale-inhibiting properties, the medicament can be used as the scale inhibitor of recirculating cooling water system
Agent, especially suitable for high rigidity, high alkalinity, the recirculating cooling water system of high pH and oil field water process.To calcium carbonate, calcium phosphate,
The scale-inhibiting properties of calcium sulfate are excellent, while can effectively inhibit the formation of silicon dirt, and with good stable metal ion such as zinc,
The effect of manganese, iron.PAPEMP is used for the film antisludging agent of counter-infiltration system, the high salinitys such as multi-stage flash system, high concentrtion, height
The scale inhibition of warm system and inhibition(Such as the scale inhibition of the high muddy water system of coal carburetion system high temperature), textile auxiliary and paper making additive
(Yellowing inhibition agent), alternative EDTA, DTPA, NTA etc..
From the mechanism of action, the solubilization of effect chelating, cohesion and the peptizaiton of antisludging agent, electrostatic repulsion work
Four parts are acted on, crystal lattice distortion.And in laboratory evaluation experiment, peptizaiton is the remedial measure of chelating effect, lattice
Distortion effect is the remedial measure of peptizaiton.
Invention content
The technical issues of solution:
The application in view of the above technical problems, provides a kind of sterilizing scale inhibiting agent and preparation method thereof, solves existing water treatment scale
Agent is of high cost, not environmentally friendly enough, scale inhibition and dispersion is poor and is sustained the technical problems such as poor performance.
Technical solution:
A kind of sterilizing scale inhibiting agent, the raw material of the sterilizing scale inhibiting agent match as follows in parts by weight:5-15 parts of zinc nitrate;Sodium metasilicate
4-8 parts;5-9 parts of tannin;1-5 parts of natrium humate;100 parts of water;3-7 parts of succinic acid;1-3 parts of aminotrimethylenephosphonic acid;Methyl
2.5-6.5 parts of hydroxypropyl acrylate;2-4 parts of di-iso-amyl phosphate;Bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium is 3-7 parts;Isopropyl
4-8 parts of alcohol;6-10 parts of 2- bromo- 2- nitros -1,3- propylene glycol;8-12 parts of potassium hydroxide;8-10 parts of hydroxy ethylene diphosphonic acid;Four
6.5-8.5 parts of Boratex.
As a preferred technical solution of the present invention:The raw material of the sterilizing scale inhibiting agent matches as follows in parts by weight:
5 parts of zinc nitrate;4 parts of sodium metasilicate;5 parts of tannin;1 part of natrium humate;100 parts of water;3 parts of succinic acid;Aminotrimethylenephosphonic acid 1
Part;2.5 parts of hydroxy propyl methacrylate;2 parts of di-iso-amyl phosphate;Bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium is 3 parts;Isopropanol
4 parts;6 parts of the bromo- 2- nitros -1,3- propylene glycol of 2-;8 parts of potassium hydroxide;8 parts of hydroxy ethylene diphosphonic acid;6.5 parts of sodium tetraborate.
As a preferred technical solution of the present invention:The raw material of the sterilizing scale inhibiting agent matches as follows in parts by weight:
15 parts of zinc nitrate;8 parts of sodium metasilicate;9 parts of tannin;5 parts of natrium humate;100 parts of water;7 parts of succinic acid;Aminotrimethylenephosphonic acid 3
Part;6.5 parts of hydroxy propyl methacrylate;4 parts of di-iso-amyl phosphate;Bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium is 7 parts;Isopropanol
8 parts;10 parts of the bromo- 2- nitros -1,3- propylene glycol of 2-;12 parts of potassium hydroxide;10 parts of hydroxy ethylene diphosphonic acid;Sodium tetraborate 8.5
Part.
As a preferred technical solution of the present invention:The raw material of the sterilizing scale inhibiting agent matches as follows in parts by weight:
10 parts of zinc nitrate;6 parts of sodium metasilicate;7 parts of tannin;3 parts of natrium humate;100 parts of water;5 parts of succinic acid;Aminotrimethylenephosphonic acid 2
Part;4.5 parts of hydroxy propyl methacrylate;3 parts of di-iso-amyl phosphate;Bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium is 5 parts;Isopropanol
6 parts;8 parts of the bromo- 2- nitros -1,3- propylene glycol of 2-;10 parts of potassium hydroxide;9 parts of hydroxy ethylene diphosphonic acid;7.5 parts of sodium tetraborate.
As a preferred technical solution of the present invention:The preparation method of the sterilizing scale inhibiting agent, includes the following steps:
The first step:Zinc nitrate, sodium metasilicate, tannin, natrium humate, water, succinic acid, amino trimethylene are weighed according to parts by weight proportioning
Methylphosphonic acid, hydroxy propyl methacrylate, di-iso-amyl phosphate, bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium, the bromo- 2- nitros-of 2-
1,3- propylene glycol, potassium hydroxide, hydroxy ethylene diphosphonic acid, sodium tetraborate and isopropanol;
Second step:Phosphorus is added in the four-hole boiling flask equipped with electric mixer, constant pressure funnel, thermometer and reflux condensing tube
Sour diisoamyl ester and water are heated to 50-70 DEG C, stir 40-60min, and zinc nitrate and natrium humate is added dropwise, is warming up to 60-80 DEG C,
React 2-4h;
Third walks:Ethylenediamine, hydroxy propyl methacrylate, tannin and bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium is added, is warming up to
70-90 DEG C, react 1-5h;
4th step:It is warming up to 80-100 DEG C, surplus stock is added, stirs 1-3h, is discharged after being cooled to room temperature up to sterilization scale inhibition
Agent.
Advantageous effect:
A kind of sterilizing scale inhibiting agent of the present invention and preparation method thereof using above technical scheme is compared with the prior art, have with
Lower technique effect:1, product is mainly used for sterilizing, and calcium tolerance is good, and scale inhibition and dispersion is good, and bactericidal is environmentally safe,
Corrosion inhibition rate 98-99.9% is free of polymer;2, incrustation scale is prevented to be precipitated on heat-exchange apparatus surface, when extending reverse osmosis membrane cleaning
Between, bactericidal effect is excellent, especially suitable to be used with heat power plant boiler water, reduces water eutrophication pollution;3, compounding is easy,
With conventional formulation medicament operation concentration 300-400 × 10-6It compares, this product antisludging agent usage amount is few, operation concentration 15-35 × 10-6, save use cost, scale inhibition performance 99.5-99.9%;4, effect is lasting, and 50-60 DEG C is placed six months, scale inhibition effect 98-99%,
Temperature resistance and scale inhibition stability are good, and corrosion inhibition is good, of low cost, easy to operate, and no waste mine generates in building-up process, three wastes
Discharge can produce and constantly replace current material extensively.
Specific implementation mode
Embodiment 1:
5 parts of zinc nitrate is weighed according to parts by weight proportioning;4 parts of sodium metasilicate;5 parts of tannin;1 part of natrium humate;100 parts of water;Amber
3 parts of acid;1 part of aminotrimethylenephosphonic acid;2.5 parts of hydroxy propyl methacrylate;2 parts of di-iso-amyl phosphate;Bromination dimethyl ten
Dialkylbenzyl ammonium is 3 parts;4 parts of isopropanol;6 parts of the bromo- 2- nitros -1,3- propylene glycol of 2-;8 parts of potassium hydroxide;Hydroxy ethylene
8 parts of di 2 ethylhexyl phosphonic acid;6.5 parts of sodium tetraborate.
Phosphoric acid is added in the four-hole boiling flask equipped with electric mixer, constant pressure funnel, thermometer and reflux condensing tube
Diisoamyl ester and water are heated to 50 DEG C, stir 40min, and zinc nitrate and natrium humate is added dropwise, and are warming up to 60 DEG C, react 2h.
Ethylenediamine, hydroxy propyl methacrylate, tannin and bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium is added, is warming up to 70
DEG C, react 1h.
80 DEG C are warming up to, surplus stock is added, stirs 1h, is discharged after being cooled to room temperature up to sterilizing scale inhibiting agent.
Product is mainly used for sterilizing, and calcium tolerance is good, and scale inhibition and dispersion is good, and bactericidal is environmentally safe, corrosion inhibition rate
98%, be free of polymer;It prevents incrustation scale to be precipitated on heat-exchange apparatus surface, extends reverse osmosis membrane scavenging period, bactericidal effect is excellent
It is good, it is especially suitable to be used with heat power plant boiler water, reduce water eutrophication pollution;Compounding is easy, with conventional formulation medicament
Run concentration 300 × 10-6It compares, this product antisludging agent usage amount is few, runs concentration 35 × 10-6, save use cost, scale inhibition performance
99.5%;Effect is lasting, and 50 DEG C are placed six months, and scale inhibition effect 98%, temperature resistance and scale inhibition stability are good, and corrosion inhibition is good, at
This is cheap, easy to operate, and no waste mine generates in building-up process, three-waste free discharge, can produce extensively and constantly replace existing material
Material.
Embodiment 2:
15 parts of zinc nitrate is weighed according to parts by weight proportioning;8 parts of sodium metasilicate;9 parts of tannin;5 parts of natrium humate;100 parts of water;Amber
7 parts of acid;3 parts of aminotrimethylenephosphonic acid;6.5 parts of hydroxy propyl methacrylate;4 parts of di-iso-amyl phosphate;Bromination dimethyl ten
Dialkylbenzyl ammonium is 7 parts;8 parts of isopropanol;10 parts of the bromo- 2- nitros -1,3- propylene glycol of 2-;12 parts of potassium hydroxide;Hydroxyl Asia second
10 parts of base di 2 ethylhexyl phosphonic acid;8.5 parts of sodium tetraborate.
Phosphoric acid is added in the four-hole boiling flask equipped with electric mixer, constant pressure funnel, thermometer and reflux condensing tube
Diisoamyl ester and water are heated to 70 DEG C, stir 60min, and zinc nitrate and natrium humate is added dropwise, and are warming up to 80 DEG C, react 4h.
Ethylenediamine, hydroxy propyl methacrylate, tannin and bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium is added, is warming up to 90
DEG C, react 5h.
100 DEG C are warming up to, surplus stock is added, stirs 3h, is discharged after being cooled to room temperature up to sterilizing scale inhibiting agent.
Product is mainly used for sterilizing, and calcium tolerance is good, and scale inhibition and dispersion is good, and bactericidal is environmentally safe, corrosion inhibition rate
99%, be free of polymer;It prevents incrustation scale to be precipitated on heat-exchange apparatus surface, extends reverse osmosis membrane scavenging period, bactericidal effect is excellent
It is good, it is especially suitable to be used with heat power plant boiler water, reduce water eutrophication pollution;Compounding is easy, with conventional formulation medicament
Run concentration 350 × 10-6It compares, this product antisludging agent usage amount is few, runs concentration 25 × 10-6, save use cost, scale inhibition performance
99.7%;Effect is lasting, and 55 DEG C are placed six months, and scale inhibition effect 98.5%, temperature resistance and scale inhibition stability are good, and corrosion inhibition is good,
Of low cost, easy to operate, no waste mine generates in building-up process, three-waste free discharge, can produce and constantly replace existing extensively
Material.
Embodiment 3:
10 parts of zinc nitrate is weighed according to parts by weight proportioning;6 parts of sodium metasilicate;7 parts of tannin;3 parts of natrium humate;100 parts of water;Amber
5 parts of acid;2 parts of aminotrimethylenephosphonic acid;4.5 parts of hydroxy propyl methacrylate;3 parts of di-iso-amyl phosphate;Bromination dimethyl ten
Dialkylbenzyl ammonium is 5 parts;6 parts of isopropanol;8 parts of the bromo- 2- nitros -1,3- propylene glycol of 2-;10 parts of potassium hydroxide;Hydroxy ethylene
9 parts of di 2 ethylhexyl phosphonic acid;7.5 parts of sodium tetraborate.
Phosphoric acid is added in the four-hole boiling flask equipped with electric mixer, constant pressure funnel, thermometer and reflux condensing tube
Diisoamyl ester and water are heated to 60 DEG C, stir 50min, and zinc nitrate and natrium humate is added dropwise, and are warming up to 70 DEG C, react 3h.
Ethylenediamine, hydroxy propyl methacrylate, tannin and bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium is added, is warming up to 80
DEG C, react 3h.
90 DEG C are warming up to, surplus stock is added, stirs 2h, is discharged after being cooled to room temperature up to sterilizing scale inhibiting agent.
Product is mainly used for sterilizing, and calcium tolerance is good, and scale inhibition and dispersion is good, and bactericidal is environmentally safe, corrosion inhibition rate
99.9%, be free of polymer;It prevents incrustation scale to be precipitated on heat-exchange apparatus surface, extends reverse osmosis membrane scavenging period, bactericidal effect is excellent
It is good, it is especially suitable to be used with heat power plant boiler water, reduce water eutrophication pollution;Compounding is easy, with conventional formulation medicament
Run concentration 400 × 10-6It compares, this product antisludging agent usage amount is few, runs concentration 15 × 10-6, save use cost, scale inhibition performance
99.9%;Effect is lasting, and 60 DEG C are placed six months, and scale inhibition effect 99%, temperature resistance and scale inhibition stability are good, and corrosion inhibition is good, at
This is cheap, easy to operate, and no waste mine generates in building-up process, three-waste free discharge, can produce extensively and constantly replace existing material
Material.
Composition all components in above example can be commercially available.
The above embodiments are merely intended to illustrate the present invention rather than to limit it, therefore with the present invention's
Any change in the comparable meaning and scope of claims, should be construed as being included in the scope of the claims.
Claims (5)
1. a kind of sterilizing scale inhibiting agent, it is characterised in that the raw material of the sterilizing scale inhibiting agent matches as follows in parts by weight:Zinc nitrate
5-15 parts;4-8 parts of sodium metasilicate;5-9 parts of tannin;1-5 parts of natrium humate;100 parts of water;3-7 parts of succinic acid;Aminotrimethylene phosphine
It is 1-3 parts sour;2.5-6.5 parts of hydroxy propyl methacrylate;2-4 parts of di-iso-amyl phosphate;Bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium
It is 3-7 parts;4-8 parts of isopropanol;6-10 parts of 2- bromo- 2- nitros -1,3- propylene glycol;8-12 parts of potassium hydroxide;Hydroxy ethylene two
8-10 parts of phosphonic acids;6.5-8.5 parts of sodium tetraborate.
2. a kind of sterilizing scale inhibiting agent according to claim 1, it is characterised in that the sterilizing scale inhibiting agent raw material is by weight
Number proportioning is as follows:5 parts of zinc nitrate;4 parts of sodium metasilicate;5 parts of tannin;1 part of natrium humate;100 parts of water;3 parts of succinic acid;Amino trimethylene
1 part of methylphosphonic acid;2.5 parts of hydroxy propyl methacrylate;2 parts of di-iso-amyl phosphate;Bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium is 3
Part;4 parts of isopropanol;6 parts of the bromo- 2- nitros -1,3- propylene glycol of 2-;8 parts of potassium hydroxide;8 parts of hydroxy ethylene diphosphonic acid;Tetraboric acid
6.5 parts of sodium.
3. a kind of sterilizing scale inhibiting agent according to claim 1, it is characterised in that the sterilizing scale inhibiting agent raw material is by weight
Number proportioning is as follows:15 parts of zinc nitrate;8 parts of sodium metasilicate;9 parts of tannin;5 parts of natrium humate;100 parts of water;7 parts of succinic acid;Amino three
3 parts of methylene phosphonic acid;6.5 parts of hydroxy propyl methacrylate;4 parts of di-iso-amyl phosphate;Bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium
It is 7 parts;8 parts of isopropanol;10 parts of the bromo- 2- nitros -1,3- propylene glycol of 2-;12 parts of potassium hydroxide;10 parts of hydroxy ethylene diphosphonic acid;
8.5 parts of sodium tetraborate.
4. a kind of sterilizing scale inhibiting agent according to claim 1, it is characterised in that the sterilizing scale inhibiting agent raw material is by weight
Number proportioning is as follows:10 parts of zinc nitrate;6 parts of sodium metasilicate;7 parts of tannin;3 parts of natrium humate;100 parts of water;5 parts of succinic acid;Amino three
2 parts of methylene phosphonic acid;4.5 parts of hydroxy propyl methacrylate;3 parts of di-iso-amyl phosphate;Bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium
It is 5 parts;6 parts of isopropanol;8 parts of the bromo- 2- nitros -1,3- propylene glycol of 2-;10 parts of potassium hydroxide;9 parts of hydroxy ethylene diphosphonic acid;Four
7.5 parts of Boratex.
5. the preparation method of sterilizing scale inhibiting agent described in a kind of claim 1, which is characterized in that include the following steps:
The first step:Zinc nitrate, sodium metasilicate, tannin, natrium humate, water, succinic acid, amino trimethylene are weighed according to parts by weight proportioning
Methylphosphonic acid, hydroxy propyl methacrylate, di-iso-amyl phosphate, bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium, the bromo- 2- nitros-of 2-
1,3- propylene glycol, potassium hydroxide, hydroxy ethylene diphosphonic acid, sodium tetraborate and isopropanol;
Second step:Phosphorus is added in the four-hole boiling flask equipped with electric mixer, constant pressure funnel, thermometer and reflux condensing tube
Sour diisoamyl ester and water are heated to 50-70 DEG C, stir 40-60min, and zinc nitrate and natrium humate is added dropwise, is warming up to 60-80 DEG C,
React 2-4h;
Third walks:Ethylenediamine, hydroxy propyl methacrylate, tannin and bromination dimethyl dodecyl base hexadecyldimethyl benzyl ammonium is added, is warming up to
70-90 DEG C, react 1-5h;
4th step:It is warming up to 80-100 DEG C, surplus stock is added, stirs 1-3h, is discharged after being cooled to room temperature up to sterilization scale inhibition
Agent.