CN108641654A - A kind of distress in concrete renovation agent - Google Patents
A kind of distress in concrete renovation agent Download PDFInfo
- Publication number
- CN108641654A CN108641654A CN201810737729.5A CN201810737729A CN108641654A CN 108641654 A CN108641654 A CN 108641654A CN 201810737729 A CN201810737729 A CN 201810737729A CN 108641654 A CN108641654 A CN 108641654A
- Authority
- CN
- China
- Prior art keywords
- parts
- distress
- epoxy resin
- concrete renovation
- renovation agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of distress in concrete renovation agents, belong to technical field of polymer materials.The present invention counts in parts by weight, by 60~100 parts of epoxy resin, 30~40 parts of curing agent, 20~30 parts of diluents, 10~20 parts of greasy filth, 8~10 parts of plasticizer, 20~30 parts of fillers, 3~5 parts of silane coupling agents and 8~10 parts of modified additives are placed in batch mixer, under the conditions of rotating speed is 400~600r/min, it is stirred 40~60min, obtains distress in concrete renovation agent.Distress in concrete renovation agent prepared by technical solution of the present invention has the characteristics that excellent mechanical property, has broad prospects in the development of high polymer material technology industry.
Description
Technical field
The invention discloses a kind of distress in concrete renovation agents, belong to technical field of polymer materials.
Background technology
Concrete structure is in civil engineering using a kind of most structures, construction casting is improper, reinforcing bar prepare it is very little,
Under the influence of many factors such as concrete shrinkage aging, load are overweight, concrete structure usually will appear crack.It deposits in crack
Steam, acid, alkaloid substance etc. can caused to penetrate into structure, causing steel bar corrosion, concrete stripping etc. to structure destructiveness
Damage, and influence bearing capacity and the service life of architectural appearance and concrete structure, thus need to these concrete
Structure carries out crack repairing work.Glued crack construction technology is one of method wherein to mend a split and most common side
Method.Glued crack technology be a kind of wider building of application reinforce with building reinforcing technology, by by the injection material of various ingredients
Material is configured to a kind of flowable slurry by the proportioning of design, and mechanical equipment is used in combination(Such as pump)Or other devices(Such as syringe)It will
It is pressed into the base material crack for needing reinforcing or leak stopping, so that slurries infiltrated, spread in base material crack, slurry then occurs
Chemical reaction, is solidified into solids.Slurry after solidification generates powerful firm bonding force to base material, whole as one with base material
Body achievees the purpose that reinforcing base material, raising load or room oozes leak stopping.Domestic epoxide resin grouting material is widely used in water conservancy project and builds
It builds and is reinforced with the anti-Seepage of crack in dam body;It is various mixed in the engineerings such as highway, bridge, subway, industry and civil buildings
The anti-Seepage consolidation process of solidifying soil cracking seam and basis.Crack repair materials used in early stage be using cement as key component,
Because of the advantages that its source is easy to get, cheap, simple process, it is widely used.
Crack repairing agent type currently on the market is more, can be divided into cement base class, third by its used adhesive material
Ketone-furfural class, unsaturated polyester (UP) class and EP(Epoxy resin)Class etc. can be divided into grouting material, grout material and pressure injection by application range
Glue etc..Wide seam can be perfused in grouting material containing aggregate;Grouting material without coarse aggregate is known as grout material, crack pouring width
For 1.5~5.0mm;Pressure injection glue is usually made of being modified EP Adhesives by low-viscosity, for closing and filling crack
Referred to as crack closure pressure injection glue, the referred to as crack reparation pressure injection of globality and partial intensities for restoring concrete component
Glue.
And traditional distress in concrete renovation agent is there is also the bad problem of mechanical property, to bringing in actual use
Inconvenience, therefore, so that distress in concrete renovation agent is played better performance becomes the art technology urgently to be resolved hurrily
One of problem.
Invention content
The present invention solves the technical problem of:Not for mechanical property existing for traditional distress in concrete renovation agent
The problem of good problem, provide a kind of distress in concrete renovation agent.
In order to solve the above-mentioned technical problem, the technical solution adopted in the present invention is:
A kind of distress in concrete renovation agent, is made of the raw material of following parts by weight:
60~100 parts of epoxy resin
30~40 parts of curing agent
20~30 parts of diluent
10~20 parts of greasy filth
8~10 parts of plasticizer
20~30 parts of filler
3~5 parts of silane coupling agent
Modified 8~10 parts of additive
The preparation process of the distress in concrete renovation agent is:Each raw material is weighed by raw material composition, by epoxy resin, curing agent,
Diluent, greasy filth, plasticizer, filler, silane coupling agent and modified additive are stirred to get distress in concrete renovation agent.
The epoxy resin is any one in epoxy resin E51, epoxy resin E44 or epoxy resin E20.
The curing agent is ethylenediamine, and tetra-methylenedimine is arbitrary in hexamethylene diamine or ten dimethylene diamines
It is a kind of.
The diluent is any one in 660 n-butyl glycidyl ethers and 692 benzyl glycidyl ethers.
The plasticizer is two positive zinc ester of phthalic acid, in dibutyl phthalate or repefral
Any one.
The filler is zeolite, any one in medical stone or diatomite.
The silane coupling agent is silane resin acceptor kh-550, in silane coupling agent KH-560 or Silane coupling reagent KH-570
Any one.
The preparation process of the modified additive is:By rosin and ethanol solution in mass ratio 1:2~1:3 mixing, obtain No. 1
Mixed serum;It counts in parts by weight, by 5~8 parts of sepiolites, 10~20 parts of polyallylamines, 40~60 parts of water are stirred, and obtain 2
Number mixed serum, is counted, in parts by weight by 20~30 parts of No. 1 mixed serums, 20~30 parts of No. 2 mixed serums, 3~5 parts of carbonic acid
Hydrogen calcium constant temperature is stirred, Freezing smashing, crosses the sieve of 60 mesh to get modified additive.
The beneficial effects of the invention are as follows:
First, rosin is dispersed in ethanol solution in preparation process by the modified additive of addition by the present invention, then, will
Sepiolite, polyallylamine and water stirring, sepiolite are dispersed in polyallylamine aqueous solution, sepiolite fibre beam are formed, then by 1
Number mixed serum, No. 2 mixed serums and the mixing of calcium bicarbonate heating stirring, in the process, calcium bicarbonate is thermally decomposed, and is generated
The carbon dioxide of carbon dioxide and calcium carbonate, generation promotes polyallylamine to be crosslinked, and forms three-dimensional network so that sepiolite fibre beam
It is fixed in polyallylamine three-dimensional network with rosin, in use, polyallylamine cross-linked network is heated, internal titanium dioxide
Carbon starts to discharge so that polyallylamine three-dimensional network gradually starts solution crosslinking, and the mobility of system gets a promotion, internal fixed
Rosin and sepiolite fibre beam are released, and rosin molecule long-chain, which mutually tangles, forms thixotroping structure, then agitated, and winding is drawn
The effect of viscosity reduction is opened, meanwhile, rosin can carry sepiolite fibre beam and permeate and be distributed in original concrete and resin circle
At face, the interface cohesion of resin matrix and concrete is improved, to promote the mechanical property of system, in addition, containing pine in rosin
It is fragrant sour, a large amount of double bonds or carboxyl functional group are contained in rosin acid molecular structures, after being added in system, is had with concrete neutral and alkali
Machine Silica hydrogel reacts, to enhance the cohesive strength of system, to promote the mechanical property of system.
Specific implementation mode
The ethanol solution in mass ratio 1 for being 70~80% by rosin and mass fraction:2~1:3 are placed in No. 1 beaker, in turn
Under the conditions of speed is 300~500r/min, it is stirred 40~60min, obtains No. 1 mixed serum;It counts in parts by weight, by 5~8 parts
Sepiolite, 10~20 parts of polyallylamines, 40~60 parts of water are placed in No. 2 beakers, under the conditions of rotating speed is 400~600r/min,
It is stirred 40~60min, No. 2 mixed serums is obtained, counts in parts by weight, by 20~30 parts of No. 1 mixed serums, 20~30 part 2
Number mixed serum, 3~5 parts of calcium bicarbonates are placed in No. 3 beakers, and three-necked flask is placed in digital display and is tested the speed constant temperature blender with magnetic force
In, under the conditions of temperature is 80~95 DEG C, constant temperature is stirred 40~60min, obtains mixed slurry, is then placed in mixture cold
Freezing smashing in agar millstone crosses the sieve of 60 mesh to get modified additive;It counts in parts by weight, by 60~100 parts of asphalt mixtures modified by epoxy resin
Fat, 30~40 parts of curing agent, 20~30 parts of diluents, 10~20 parts of greasy filth, 8~10 parts of plasticizer, 20~30 parts of fillers, 3~5
Part silane coupling agent and 8~10 parts of modified additives are placed in batch mixer, under the conditions of rotating speed is 400~600r/min, stirring
40~60min is mixed, distress in concrete renovation agent is obtained.The epoxy resin is epoxy resin E51, epoxy resin E44 or epoxy
Any one in resin E20.The curing agent is ethylenediamine, tetra-methylenedimine, hexamethylene diamine or ten dimethylenes two
Any one in amine.The diluent is any one in 660 n-butyl glycidyl ethers or 692 benzyl glycidyl ethers
Kind.The plasticizer is two positive zinc ester of phthalic acid, arbitrary in dibutyl phthalate or repefral
It is a kind of.The filler is zeolite, any one in medical stone or diatomite.The silane coupling agent is silane coupling agent KH-
Any one in 550, silane coupling agent KH-560 or Silane coupling reagent KH-570.
The ethanol solution in mass ratio 1 for being 80% by rosin and mass fraction:3 are placed in No. 1 beaker, in rotating speed be 500r/
Under the conditions of min, it is stirred 60min, obtains No. 1 mixed serum;It counts in parts by weight, by 8 parts of sepiolites, 20 parts of polyallylamines,
60 parts of water are placed in No. 2 beakers, under the conditions of rotating speed is 600r/min, is stirred 60min, is obtained No. 2 mixed serums, by weight
Number meter, by 30 parts of No. 1 mixed serums, 30 parts of No. 2 mixed serums, 5 parts of calcium bicarbonates are placed in No. 3 beakers, and three mouthfuls are burnt
Bottle is placed in digital display and tests the speed in constant temperature blender with magnetic force, and under the conditions of temperature is 95 DEG C, constant temperature is stirred 60min, obtains mixing slurry
Mixture is then placed in Freezing smashing in Freezing smashing device by material, crosses the sieve of 60 mesh to get modified additive;In parts by weight
Meter, by 100 parts of epoxy resin, 40 parts of curing agent, 30 parts of diluents, 20 parts of greasy filth, 10 parts of plasticizer, 30 parts of fillers, 5 parts of silane
Coupling agent and 10 parts of modified additives are placed in batch mixer, under the conditions of rotating speed is 600r/min, is stirred 60min, is obtained mixed
Solidifying soil crack repairing agent.The epoxy resin is any one in epoxy resin E51, epoxy resin E44 or epoxy resin E20.
The curing agent is ethylenediamine.The diluent is 660 n-butyl glycidyl ethers.The plasticizer be phthalic acid two just
Zinc ester.The filler is zeolite.The silane coupling agent is silane resin acceptor kh-550.
The ethanol solution in mass ratio 1 for being 80% by rosin and mass fraction:3 are placed in No. 1 beaker, in rotating speed be 500r/
Under the conditions of min, it is stirred 60min, obtains No. 1 mixed serum;It counts in parts by weight, by 8 parts of sepiolites, 20 parts of polyallylamines,
60 parts of water are placed in No. 2 beakers, under the conditions of rotating speed is 600r/min, is stirred 60min, is obtained No. 2 mixed serums, by weight
Number meter, by 30 parts of No. 1 mixed serums, 30 parts of No. 2 mixed serums, 5 parts of calcium bicarbonates are placed in No. 3 beakers, and three mouthfuls are burnt
Bottle is placed in digital display and tests the speed in constant temperature blender with magnetic force, and under the conditions of temperature is 95 DEG C, constant temperature is stirred 60min, obtains mixing slurry
Mixture is then placed in Freezing smashing in Freezing smashing device by material, crosses the sieve of 60 mesh to get modified additive;In parts by weight
Meter, by 100 parts of epoxy resin, 40 parts of curing agent, 30 parts of diluents, 10 parts of plasticizer, 30 parts of fillers, 5 parts of silane coupling agents and
10 parts of modified additives are placed in batch mixer, under the conditions of rotating speed is 600r/min, is stirred 60min, is obtained distress in concrete
Renovation agent.The epoxy resin is any one in epoxy resin E51, epoxy resin E44 or epoxy resin E20.The solidification
Agent is ethylenediamine.The diluent is 660 n-butyl glycidyl ethers.The plasticizer is two positive zinc ester of phthalic acid.Institute
It is zeolite to state filler.The silane coupling agent is silane resin acceptor kh-550.
The ethanol solution in mass ratio 1 for being 80% by rosin and mass fraction:3 are placed in No. 1 beaker, in rotating speed be 500r/
Under the conditions of min, it is stirred 60min, obtains No. 1 mixed serum;It counts in parts by weight, by 8 parts of sepiolites, 20 parts of polyallylamines,
60 parts of water are placed in No. 2 beakers, under the conditions of rotating speed is 600r/min, is stirred 60min, is obtained No. 2 mixed serums, by weight
Number meter, by 30 parts of No. 1 mixed serums, 30 parts of No. 2 mixed serums, 5 parts of calcium bicarbonates are placed in No. 3 beakers, and three mouthfuls are burnt
Bottle is placed in digital display and tests the speed in constant temperature blender with magnetic force, and under the conditions of temperature is 95 DEG C, constant temperature is stirred 60min, obtains mixing slurry
Mixture is then placed in Freezing smashing in Freezing smashing device by material, crosses the sieve of 60 mesh to get modified additive;In parts by weight
Meter, by 100 parts of epoxy resin, 40 parts of curing agent, 30 parts of diluents, 20 parts of greasy filth, 10 parts of plasticizer, 5 parts of silane coupling agents and
10 parts of modified additives are placed in batch mixer, under the conditions of rotating speed is 600r/min, is stirred 60min, is obtained distress in concrete
Renovation agent.The epoxy resin is any one in epoxy resin E51, epoxy resin E44 or epoxy resin E20.The solidification
Agent is ethylenediamine.The diluent is 660 n-butyl glycidyl ethers.The plasticizer is two positive zinc ester of phthalic acid.Institute
It is silane resin acceptor kh-550 to state silane coupling agent.
The ethanol solution in mass ratio 1 for being 80% by rosin and mass fraction:3 are placed in No. 1 beaker, in rotating speed be 500r/
Under the conditions of min, it is stirred 60min, obtains No. 1 mixed serum;It counts in parts by weight, by 100 parts of epoxy resin, 40 parts of solidifications
Agent, 30 parts of diluents, 20 parts of greasy filth, 10 parts of plasticizer, 30 parts of fillers and are placed in batch mixer 5 parts of silane coupling agents, in rotating speed
Under the conditions of 600r/min, it is stirred 60min, obtains distress in concrete renovation agent.The epoxy resin is epoxy resin E51,
Any one in epoxy resin E44 or epoxy resin E20.The curing agent is ethylenediamine.The diluent contracts for 660 normal-butyls
Water glycerin ether.The plasticizer is two positive zinc ester of phthalic acid.The filler is zeolite.The silane coupling agent is that silane is even
Join agent KH-550.
Comparative example:The distress in concrete renovation agent of Qingdao construction material Co., Ltd production.
The distress in concrete renovation agent and comparative example product of example 1 to 4 gained of example are subjected to performance detection, it is specific to detect
Method is as follows:
1. compressive strength:According to GB/T2567 standards, it is measured using universal testing machine(Specimen molding and maintenance exist(23
±2)It is carried out in DEG C environment, conserves 7d);
2. buckling strength:According to GB50728 standards, it is measured using universal testing machine(Specimen molding and maintenance exist(23±
2)It is carried out in DEG C environment, conserves 7d);
3. tensile shear strength:According to GB/T7124 standards, it is measured that (specimen molding and maintenance exist using universal testing machine
(23±2)It is carried out in DEG C environment, conserves 7d, base material is steel).
Specific testing result is as shown in table 1:
The 1 specific testing result of distress in concrete renovation agent of table
Detection project | Example 1 | Example 2 | Example 3 | Example 4 | Comparative example |
Compressive strength/MPa | 40.01 | 39.89 | 39.70 | 39.63 | 39.20 |
Buckling strength/MPa | 6.27 | 6.22 | 6.19 | 6.13 | 6.01 |
Tensile shear strength/MPa | 116 | 92 | 87 | 73 | 54 |
By 1 testing result of table it is found that distress in concrete renovation agent prepared by technical solution of the present invention has excellent mechanical property
The characteristics of, it has broad prospects in the development of high polymer material technology industry.
Claims (8)
1. a kind of distress in concrete renovation agent, it is characterised in that:It is made of the raw material of following parts by weight:
60~100 parts of epoxy resin
30~40 parts of curing agent
20~30 parts of diluent
10~20 parts of greasy filth
8~10 parts of plasticizer
20~30 parts of filler
3~5 parts of silane coupling agent
Modified 8~10 parts of additive
The preparation process of the distress in concrete renovation agent is:Each raw material is weighed by raw material composition, by epoxy resin, curing agent,
Diluent, greasy filth, plasticizer, filler, silane coupling agent and modified additive are stirred to get distress in concrete renovation agent.
2. a kind of distress in concrete renovation agent according to claim 1, it is characterised in that:The epoxy resin is epoxy resin
Any one in E51, epoxy resin E44 or epoxy resin E20.
3. a kind of distress in concrete renovation agent according to claim 1, it is characterised in that:The curing agent be ethylenediamine, four
Any one in methylene diamine, hexamethylene diamine or ten dimethylene diamines.
4. a kind of distress in concrete renovation agent according to claim 1, it is characterised in that:The diluent is 660 normal-butyls
Any one in glycidol ether or 692 benzyl glycidyl ethers.
5. a kind of distress in concrete renovation agent according to claim 1, it is characterised in that:The plasticizer is phthalic acid
Two positive zinc esters, any one in dibutyl phthalate or repefral.
6. a kind of distress in concrete renovation agent according to claim 1, it is characterised in that:The filler is zeolite, medical stone
Or any one in diatomite.
7. a kind of distress in concrete renovation agent according to claim 1, it is characterised in that:The silane coupling agent is that silane is even
Join agent KH-550, any one in silane coupling agent KH-560 or Silane coupling reagent KH-570.
8. a kind of distress in concrete renovation agent according to claim 1, it is characterised in that:The preparation of the modified additive
Cheng Wei:By rosin and ethanol solution in mass ratio 1:2~1:3 mixing, obtain No. 1 mixed serum;It counts in parts by weight, by 5~8 parts
Sepiolite, 10~20 parts of polyallylamines, 40~60 parts of water are stirred, and are obtained No. 2 mixed serums, are counted in parts by weight, by 20~
30 parts of No. 1 mixed serums, 20~30 parts of No. 2 mixed serums, 3~5 parts of calcium bicarbonate constant temperature are stirred, Freezing smashing, cross 60
Purpose sieve is to get modified additive.