CN108640695A - 一种高炉炼铁用抗开裂摆动流槽浇注料 - Google Patents
一种高炉炼铁用抗开裂摆动流槽浇注料 Download PDFInfo
- Publication number
- CN108640695A CN108640695A CN201810631073.9A CN201810631073A CN108640695A CN 108640695 A CN108640695 A CN 108640695A CN 201810631073 A CN201810631073 A CN 201810631073A CN 108640695 A CN108640695 A CN 108640695A
- Authority
- CN
- China
- Prior art keywords
- parts
- blast furnace
- fine powder
- cracking resistance
- furnace ironmaking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提出了一种高炉炼铁用抗开裂摆动流槽浇注料,包括以下组分且各组分的质量比例为:优质高铝矾土30~40份;电熔刚玉20~30份;棕刚玉细粉20~30份;氧化铬5~10份;纳米级炭黑15~20份;硅石颗粒30~50份;氧化镁10~15份;分散剂3~5份;铝细粉5~8份;促凝剂5~8份;复合减水剂4~5份。本发明能够使摆动流槽浇注料有很好的耐侵蚀性、耐冲刷性,不易出现裂纹,提升摆动流槽浇注料的使用寿命。
Description
【技术领域】
本发明涉及耐火材料制造的技术领域,特别是一种高炉炼铁用抗开裂摆动流槽浇注料的技术领域。
【背景技术】
随着钢铁新技术的发展,钢铁工业用耐火材料技术也有了划时代的转变和发展,国内外的钢铁厂大力发展炼铁技术,不断提高高炉有效容积,诸多的冶炼技术进步提高了出铁***的负荷。高炉炼铁时,铁水从出铁口流出,经过主沟、铁沟、摆动流槽,最后到达了铁水罐。摆动流槽是更换铁水罐时变换铁水流向的专用设备,其性能直接影响了高炉炼铁的安全生产。大中型高炉通常设有2-4个摆动流槽,高炉炼铁时2-3个摆动流槽轮流出铁,摆动流槽的受铁间歇在2-4小时,受铁时要经受约1400℃高温铁水的冲击磨损,受铁间歇时直接接触空气,承受较大的温度波动,因此摆动溜槽承受着较大的热应力。目前制备摆动溜槽内衬多采用Al2O3-SiC-C质浇注料,该材料具有良好的耐磨性,抗侵蚀性,但此种材料脆性较大,该材料制备的内衬长期经受间歇铁水及热应力冲击,易在流嘴部位内衬出现裂纹,铁水沿着裂纹渗入到流槽内部并扩展,并且裂纹扩展迅速,若没有及时发现,将导致摆动流槽的烧穿漏铁,烧坏摆动流槽支撑梁及下方铁道、鱼雷罐车等,从而造成严重的安全生产事故。
【发明内容】
本发明的目的就是解决现有技术中的问题,提出一种高炉炼铁用抗开裂摆动流槽浇注料,能够使摆动流槽浇注料有很好的耐侵蚀性、耐冲刷性,不易出现裂纹,提升摆动流槽浇注料的使用寿命。
为实现上述目的,本发明提出了一种高炉炼铁用抗开裂摆动流槽浇注料,包括以下组分且各组分的质量比例为:优质高铝矾土30~40份;电熔刚玉20~30份;棕刚玉细粉20~30份;氧化铬5~10份;纳米级炭黑15~20份;硅石颗粒30~50份;氧化镁10~15份;分散剂3~5份;铝细粉5~8份;促凝剂5~8份;复合减水剂4~5份。
作为优选,所述分散剂由己烯基双硬脂酰胺和硅溶胶按照3:5的质量份数混合而成。
作为优选,所述硅石颗粒由粒径为5~6mm部分、粒径为3~4mm部分和粒径为1~2mm部分部分组成,硅石颗粒中粒径为5~6mm部分、粒径为3~4mm部分和粒径为1~2mm部分的质量比例为1:2:4。
作为优选,所述促凝剂是由硅酸钠和硅酸钾按照3:1的质量份数混合而成的混合物。
作为优选,所述复合减水剂由粉末聚羧酸酯和填充料组成按照2:5的质量份数混合而成。
作为优选,所述各组分的质量比例为:优质高铝矾土30份;电熔刚玉20份;棕刚玉细粉30份;氧化铬10份;纳米级炭黑20份;硅石颗粒50份;氧化镁15份;分散剂5份;铝细粉8份;促凝剂8份;复合减水剂5份。
作为优选,所述各组分的质量比例为:优质高铝矾土30份;电熔刚玉20份;棕刚玉细粉20份;氧化铬5份;纳米级炭黑15份;硅石颗粒30份;氧化镁10份;分散剂3份;铝细粉5份;促凝剂5份;复合减水剂4份。
作为优选,所述各组分的质量比例为:优质高铝矾土35份;电熔刚玉25份;棕刚玉细粉25份;氧化铬8份;纳米级炭黑17份;硅石颗粒40份;氧化镁12份;分散剂4份;铝细粉6份;促凝剂6份;复合减水剂5份。
本发明的有益效果:本发明发现浇注料的损毁速率与碳源相关,经过多次现场试验,得到了炭黑的最佳配比,使得产品的损毁速率显著降低,不易产生裂纹,产品中加入了球磨机和气流式粉碎分离机磨出来的碳化硅细粉和棕刚玉细粉,粒度均匀,从而使产品具有很好的耐侵蚀性、耐冲刷性,引入不同粒径的硅石颗粒和氧化镁,提升了浇注料的耐磨性能,改善了浇注料的流动性能,增加了浇注料的致密性,进一步提高其强度,能够使摆动流槽浇注料有很好的耐侵蚀性、耐冲刷性,不易出现裂纹,提升摆动流槽浇注料的使用寿命。
本发明的特征及优点将通过实施例进行详细说明。
【具体实施方式】
本发明一种高炉炼铁用抗开裂摆动流槽浇注料,包括以下组分且各组分的质量比例为:优质高铝矾土30~40份;电熔刚玉20~30份;棕刚玉细粉20~30份;氧化铬5~10份;纳米级炭黑15~20份;硅石颗粒30~50份;氧化镁10~15份;分散剂3~5份;铝细粉5~8份;促凝剂5~8份;复合减水剂4~5份,所述分散剂由己烯基双硬脂酰胺和硅溶胶按照3:5的质量份数混合而成,所述硅石颗粒由粒径为5~6mm部分、粒径为3~4mm部分和粒径为1~2mm部分部分组成,硅石颗粒中粒径为5~6mm部分、粒径为3~4mm部分和粒径为1~2mm部分的质量比例为1:2:4,所述促凝剂是由硅酸钠和硅酸钾按照3:1的质量份数混合而成的混合物,所述复合减水剂由粉末聚羧酸酯和填充料组成按照2:5的质量份数混合而成。
实施例一
所述各组分的质量比例为:优质高铝矾土30份;电熔刚玉20份;棕刚玉细粉30份;氧化铬10份;纳米级炭黑20份;硅石颗粒50份;氧化镁15份;分散剂5份;铝细粉8份;促凝剂8份;复合减水剂5份。
实施例二
所述各组分的质量比例为:优质高铝矾土30份;电熔刚玉20份;棕刚玉细粉20份;氧化铬5份;纳米级炭黑15份;硅石颗粒30份;氧化镁10份;分散剂3份;铝细粉5份;促凝剂5份;复合减水剂4份。
实施例三
所述各组分的质量比例为:优质高铝矾土35份;电熔刚玉25份;棕刚玉细粉25份;氧化铬8份;纳米级炭黑17份;硅石颗粒40份;氧化镁12份;分散剂4份;铝细粉6份;促凝剂6份;复合减水剂5份。
上述实施例是对本发明的说明,不是对本发明的限定,任何对本发明简单变换后的方案均属于本发明的保护范围。
Claims (8)
1.一种高炉炼铁用抗开裂摆动流槽浇注料,其特征在于:包括以下组分且各组分的质量比例为:优质高铝矾土30~40份;电熔刚玉20~30份;棕刚玉细粉20~30份;氧化铬5~10份;纳米级炭黑15~20份;硅石颗粒30~50份;氧化镁10~15份;分散剂3~5份;铝细粉5~8份;促凝剂5~8份;复合减水剂4~5份。
2.如权利要求1所述的一种高炉炼铁用抗开裂摆动流槽浇注料,其特征在于:所述分散剂由己烯基双硬脂酰胺和硅溶胶按照3:5的质量份数混合而成。
3.如权利要求1所述的一种高炉炼铁用抗开裂摆动流槽浇注料,其特征在于:所述硅石颗粒由粒径为5~6mm部分、粒径为3~4mm部分和粒径为1~2mm部分部分组成,硅石颗粒中粒径为5~6mm部分、粒径为3~4mm部分和粒径为1~2mm部分的质量比例为1:2:4。
4.如权利要求1所述的一种高炉炼铁用抗开裂摆动流槽浇注料,其特征在于:所述促凝剂是由硅酸钠和硅酸钾按照3:1的质量份数混合而成的混合物。
5.如权利要求1所述的一种高炉炼铁用抗开裂摆动流槽浇注料,其特征在于:所述复合减水剂由粉末聚羧酸酯和填充料组成按照2:5的质量份数混合而成。
6.如权利要求1所述的一种高炉炼铁用抗开裂摆动流槽浇注料,其特征在于:所述各组分的质量比例为:优质高铝矾土30份;电熔刚玉20份;棕刚玉细粉30份;氧化铬10份;纳米级炭黑20份;硅石颗粒50份;氧化镁15份;分散剂5份;铝细粉8份;促凝剂8份;复合减水剂5份。
7.如权利要求1所述的一种高炉炼铁用抗开裂摆动流槽浇注料,其特征在于:所述各组分的质量比例为:优质高铝矾土30份;电熔刚玉20份;棕刚玉细粉20份;氧化铬5份;纳米级炭黑15份;硅石颗粒30份;氧化镁10份;
分散剂3份;铝细粉5份;促凝剂5份;复合减水剂4份。
8.如权利要求1所述的一种高炉炼铁用抗开裂摆动流槽浇注料,其特征在于:所述各组分的质量比例为:优质高铝矾土35份;电熔刚玉25份;棕刚玉细粉25份;氧化铬8份;纳米级炭黑17份;硅石颗粒40份;氧化镁12份;分散剂4份;铝细粉6份;促凝剂6份;复合减水剂5份。