CN108624053A - A kind of plant lamp filament of environment-friendly type explosion-proof and preparation method thereof - Google Patents
A kind of plant lamp filament of environment-friendly type explosion-proof and preparation method thereof Download PDFInfo
- Publication number
- CN108624053A CN108624053A CN201711350233.4A CN201711350233A CN108624053A CN 108624053 A CN108624053 A CN 108624053A CN 201711350233 A CN201711350233 A CN 201711350233A CN 108624053 A CN108624053 A CN 108624053A
- Authority
- CN
- China
- Prior art keywords
- filament
- yttrium oxide
- environment
- friendly type
- plant lamp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of plant lamp filaments of environment-friendly type explosion-proof, including following quality proportioning：Lanthanum compound powder 4 8%, organopolysiloxane 6 12%, yttrium oxide 5 10%, molybdenum dioxide 3 6%, butyl acetate solution 7 14%, tungsten irridium alloy material 8 16%, yttrium oxide powder 2 4%, chloroform antioxidant 4 8%, platinum oxide 4 8% and auxiliary material 7 14%.Invention additionally discloses the preparation methods of the plant lamp filament of environment-friendly type explosion-proof, include the following steps, S1：Raw material weighs；S2：Bed blending；S3：Auxiliary material is added；S4：Pour into grinding tool；S5：Cooling treatment；S6：Final molding.It can be used in long-time to avoid the filament of plant lamp, and in the case of not closing, often it is easy to happen the dangerous situations such as explosion, there is prodigious improvement also for the light conditions of plant, and situations such as avoiding the caused fire because filament explodes occurs, and solves security risk to a certain extent.
Description
Technical field
The present invention relates to plant lamp technical field, the plant lamp filament of specially a kind of environment-friendly type explosion-proof and its preparation side
Method.
Background technology
Light environment is one of indispensable environmental factor of growth and development of plants, in modern planting technology, usual root
According to photosynthesis of plant photosynthetic curve and photosynthetic pigments absorb light quality percentage come determine different wave length light composition and
Proportioning, provides good light environment, to improve the growth rate or fruit bearing rate of plant for the growth of plant.But it is existing
The filament of plant lamp is often easy to happen the dangerous situations such as explosion, completely not in the case where long-time uses and does not close
Conducive to the normal growth of plant, and difficulty is brought for illumination to plant.
Invention content
The purpose of the present invention is to provide a kind of plant lamp filaments of environment-friendly type explosion-proof and preparation method thereof, in solution
State the problem of being proposed in background technology.
To achieve the above object, the present invention provides the following technical solutions：A kind of plant lamp filament of environment-friendly type explosion-proof, packet
Include following quality proportioning：Lanthanum compound powder 4-8%, organopolysiloxane 6-12%, yttrium oxide 5-10%, molybdenum dioxide 3-6%, vinegar
Acid butyl ester solution 7-14%, tungsten irridium alloy material 8-16%, yttrium oxide powder 2-4%, chloroform antioxidant 4-8%, platinum oxide 4-8% and
Auxiliary material 7-14%.
Preferably, including following quality proportioning：Lanthanum compound powder 4%, organopolysiloxane 6%, yttrium oxide 5%, titanium dioxide
Molybdenum 3%, butyl acetate solution 7%, tungsten irridium alloy material 8%, yttrium oxide powder 2%, chloroform antioxidant 4%, platinum oxide 4% and auxiliary material
7%。
Preferably, including following quality proportioning：Lanthanum compound powder 5%, organopolysiloxane 8%, yttrium oxide 6%, titanium dioxide
Molybdenum 3.7%, butyl acetate solution 9%, tungsten irridium alloy material 10%, yttrium oxide powder 2.2%, chloroform antioxidant 5%, 5% and of platinum oxide
Auxiliary material 9%.
Preferably, including following quality proportioning：Lanthanum compound powder 6%, organopolysiloxane 9%, yttrium oxide 7%, titanium dioxide
Molybdenum 4.6%, butyl acetate solution 10%, tungsten irridium alloy material 12%, yttrium oxide powder 2.4%, chloroform antioxidant 6%, 6% and of platinum oxide
Auxiliary material 10%.
Preferably, including following quality proportioning：Lanthanum compound powder 7%, organopolysiloxane 11%, yttrium oxide 9%, dioxy
Change molybdenum 5.5%, butyl acetate solution 12%, tungsten irridium alloy material 14%, yttrium oxide powder 2.7%, chloroform antioxidant 7%, platinum oxide 7%
With auxiliary material 12%.
Preferably, including following quality proportioning：Lanthanum compound powder 8%, organopolysiloxane 12%, yttrium oxide 10%, dioxy
Change molybdenum 6%, butyl acetate solution 14%, tungsten irridium alloy material 16%, yttrium oxide powder 4%, chloroform antioxidant 8%, platinum oxide 8% and auxiliary
Material 14%.
Preferably, the auxiliary material includes following quality proportioning：Curing agent 10-20%, thixotropic agent 5-10%, ether 15-30%,
Neutralizer 20-40%.
A kind of preparation method of the plant lamp filament of environment-friendly type explosion-proof, includes the following steps,
S1：Raw material weighs, by lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, butyl acetate solution, tungsten iridium
Alloy material, yttrium oxide powder, chloroform antioxidant and platinum oxide are taken according to set ratio weighing；
S2：Bed blending, by load weighted lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, tungsten irridium alloy
Material, yttrium oxide powder, chloroform antioxidant and platinum oxide are put into clean container, and start to grind by grinding device,
In process of lapping, the one third of load weighted butyl acetate solution was added every 10 minutes, was added altogether three times, and in vinegar
After the addition of acid butyl ester solution is completed, it is stirred grinding, the agitation grinding time is 30-70 minutes, obtains material solution；
S3：Auxiliary material is added, and curing agent, thixotropic agent, ether and neutralizer are chosen according to set ratio and weighed, and will solidification
Gradually being added in material solution one by one, addition manner are to add one by one, and add for agent, thixotropic agent, ether and neutralizer
Interval time be 10-20 minutes, obtain filament solution；
S4：Grinding tool is poured into, the filament grinding tool that will be cleaned up is chosen, and be put into connecting line wherein, is subsequently poured into filament
Solution, and processing is begun to warm up, heating temperature is 400-700 degree, and heating time is 60-100 minutes；
S5：Cooling treatment puts the filament grinding tool after heating is quiet to room temperature, then obtains filament ontology,
S6：Filament body surface is carried out frosted processing, removes excess thickness and impurity, and dry solidification by final molding
After obtain finished product.
Preferably, the connecting line is the one of which of tungsten filament, gold thread, aluminum steel, copper wire or gold and silver palldium alloy line.
Compared with prior art, the beneficial effects of the invention are as follows：The plant lamp filament of the environment-friendly type explosion-proof, passes through lanthanum
Close object powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, butyl acetate solution, tungsten irridium alloy material, yttrium oxide powder, chlorine
The mutual cooperation effect of imitative antioxidant and platinum oxide, and the auxiliary for being subject to curing agent, thixotropic agent, ether and neutralizer again is made
With, it is possible to produce the plant lamp filament that can be used for a long time can use to avoid the filament of plant lamp in long-time, and not
In the case of closing, the dangerous situations such as explosion are often easy to happen, have prodigious improvement also for the light conditions of plant, and
And situations such as avoiding the caused fire because filament explodes, occurs, and solves security risk to a certain extent.
Specific implementation mode
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
Embodiment one
The present invention provides a kind of technical solution：A kind of plant lamp filament of environment-friendly type explosion-proof, including following quality proportioning：Lanthanum
Close object powder 4%, organopolysiloxane 6%, yttrium oxide 5%, molybdenum dioxide 3%, butyl acetate solution 7%, tungsten irridium alloy material 8%,
Yttrium oxide powder 2%, chloroform antioxidant 4%, platinum oxide 4% and auxiliary material 7%.
The auxiliary material includes following quality proportioning：Curing agent 10%, thixotropic agent 5%, ether 15%, neutralizer 20%.
A kind of preparation method of the plant lamp filament of environment-friendly type explosion-proof, includes the following steps,
S1：Raw material weighs, by lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, butyl acetate solution, tungsten iridium
Alloy material, yttrium oxide powder, chloroform antioxidant and platinum oxide are taken according to set ratio weighing；
S2：Bed blending, by load weighted lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, tungsten irridium alloy
Material, yttrium oxide powder, chloroform antioxidant and platinum oxide are put into clean container, and start to grind by grinding device,
In process of lapping, the one third of load weighted butyl acetate solution was added every 10 minutes, was added altogether three times, and in vinegar
After the addition of acid butyl ester solution is completed, it is stirred grinding, the agitation grinding time is 30 minutes, obtains material solution；
S3：Auxiliary material is added, and curing agent, thixotropic agent, ether and neutralizer are chosen according to set ratio and weighed, and will solidification
Gradually being added in material solution one by one, addition manner are to add one by one, and add for agent, thixotropic agent, ether and neutralizer
Interval time be 10 minutes, obtain filament solution；
S4：Grinding tool is poured into, the filament grinding tool that will be cleaned up is chosen, and be put into connecting line wherein, is subsequently poured into filament
Solution, and processing is begun to warm up, heating temperature is 400 degree, and heating time is 60 minutes；
S5：Cooling treatment puts the filament grinding tool after heating is quiet to room temperature, then obtains filament ontology,
S6：Filament body surface is carried out frosted processing, removes excess thickness and impurity, and dry solidification by final molding
After obtain finished product.
The connecting line is tungsten filament.
Embodiment two
The present invention provides a kind of technical solution：A kind of plant lamp filament of environment-friendly type explosion-proof, including following quality proportioning：Lanthanum
Close object powder 5%, organopolysiloxane 8%, yttrium oxide 6%, molybdenum dioxide 3.7%, butyl acetate solution 9%, tungsten irridium alloy material
10%, yttrium oxide powder 2.2%, chloroform antioxidant 5%, platinum oxide 5% and auxiliary material 9%.
The auxiliary material includes following quality proportioning：Curing agent 13%, thixotropic agent 7%, ether 19%, neutralizer 25%.
A kind of preparation method of the plant lamp filament of environment-friendly type explosion-proof, includes the following steps,
S1：Raw material weighs, by lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, butyl acetate solution, tungsten iridium
Alloy material, yttrium oxide powder, chloroform antioxidant and platinum oxide are taken according to set ratio weighing；
S2：Bed blending, by load weighted lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, tungsten irridium alloy
Material, yttrium oxide powder, chloroform antioxidant and platinum oxide are put into clean container, and start to grind by grinding device,
In process of lapping, the one third of load weighted butyl acetate solution was added every 10 minutes, was added altogether three times, and in vinegar
After the addition of acid butyl ester solution is completed, it is stirred grinding, the agitation grinding time is 40 minutes, obtains material solution；
S3：Auxiliary material is added, and curing agent, thixotropic agent, ether and neutralizer are chosen according to set ratio and weighed, and will solidification
Gradually being added in material solution one by one, addition manner are to add one by one, and add for agent, thixotropic agent, ether and neutralizer
Interval time be 13 minutes, obtain filament solution；
S4：Grinding tool is poured into, the filament grinding tool that will be cleaned up is chosen, and be put into connecting line wherein, is subsequently poured into filament
Solution, and processing is begun to warm up, heating temperature is 480 degree, and heating time is 70 minutes；
S5：Cooling treatment puts the filament grinding tool after heating is quiet to room temperature, then obtains filament ontology,
S6：Filament body surface is carried out frosted processing, removes excess thickness and impurity, and dry solidification by final molding
After obtain finished product.
The connecting line is gold thread.
Embodiment three
The present invention provides a kind of technical solution：A kind of plant lamp filament of environment-friendly type explosion-proof, including following quality proportioning：Lanthanum
Close object powder 6%, organopolysiloxane 9%, yttrium oxide 7%, molybdenum dioxide 4.6%, butyl acetate solution 10%, tungsten irridium alloy material
12%, yttrium oxide powder 2.4%, chloroform antioxidant 6%, platinum oxide 6% and auxiliary material 10%.
The auxiliary material includes following quality proportioning：Curing agent 15%, thixotropic agent 8%, ether 23%, neutralizer 30%.
A kind of preparation method of the plant lamp filament of environment-friendly type explosion-proof, includes the following steps,
S1：Raw material weighs, by lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, butyl acetate solution, tungsten iridium
Alloy material, yttrium oxide powder, chloroform antioxidant and platinum oxide are taken according to set ratio weighing；
S2：Bed blending, by load weighted lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, tungsten irridium alloy
Material, yttrium oxide powder, chloroform antioxidant and platinum oxide are put into clean container, and start to grind by grinding device,
In process of lapping, the one third of load weighted butyl acetate solution was added every 10 minutes, was added altogether three times, and in vinegar
After the addition of acid butyl ester solution is completed, it is stirred grinding, the agitation grinding time is 50 minutes, obtains material solution；
S3：Auxiliary material is added, and curing agent, thixotropic agent, ether and neutralizer are chosen according to set ratio and weighed, and will solidification
Gradually being added in material solution one by one, addition manner are to add one by one, and add for agent, thixotropic agent, ether and neutralizer
Interval time be 15 minutes, obtain filament solution；
S4：Grinding tool is poured into, the filament grinding tool that will be cleaned up is chosen, and be put into connecting line wherein, is subsequently poured into filament
Solution, and processing is begun to warm up, heating temperature is 550 degree, and heating time is 80 minutes；
S5：Cooling treatment puts the filament grinding tool after heating is quiet to room temperature, then obtains filament ontology,
S6：Filament body surface is carried out frosted processing, removes excess thickness and impurity, and dry solidification by final molding
After obtain finished product.
The connecting line is aluminum steel.
Example IV
The present invention provides a kind of technical solution：A kind of plant lamp filament of environment-friendly type explosion-proof, including following quality proportioning：Lanthanum
Close object powder 7%, organopolysiloxane 11%, yttrium oxide 9%, molybdenum dioxide 5.5%, butyl acetate solution 12%, tungsten irridium alloy material
14%, yttrium oxide powder 2.7%, chloroform antioxidant 7%, platinum oxide 7% and auxiliary material 12%.
The auxiliary material includes following quality proportioning：Curing agent 18%, thixotropic agent 9%, ether 27%, neutralizer 35%.
A kind of preparation method of the plant lamp filament of environment-friendly type explosion-proof, includes the following steps,
S1：Raw material weighs, by lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, butyl acetate solution, tungsten iridium
Alloy material, yttrium oxide powder, chloroform antioxidant and platinum oxide are taken according to set ratio weighing；
S2：Bed blending, by load weighted lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, tungsten irridium alloy
Material, yttrium oxide powder, chloroform antioxidant and platinum oxide are put into clean container, and start to grind by grinding device,
In process of lapping, the one third of load weighted butyl acetate solution was added every 10 minutes, was added altogether three times, and in vinegar
After the addition of acid butyl ester solution is completed, it is stirred grinding, the agitation grinding time is 60 minutes, obtains material solution；
S3：Auxiliary material is added, and curing agent, thixotropic agent, ether and neutralizer are chosen according to set ratio and weighed, and will solidification
Gradually being added in material solution one by one, addition manner are to add one by one, and add for agent, thixotropic agent, ether and neutralizer
Interval time be 18 minutes, obtain filament solution；
S4：Grinding tool is poured into, the filament grinding tool that will be cleaned up is chosen, and be put into connecting line wherein, is subsequently poured into filament
Solution, and processing is begun to warm up, heating temperature is 620 degree, and heating time is 90 minutes；
S5：Cooling treatment puts the filament grinding tool after heating is quiet to room temperature, then obtains filament ontology,
S6：Filament body surface is carried out frosted processing, removes excess thickness and impurity, and dry solidification by final molding
After obtain finished product.
The connecting line is copper wire.
Embodiment five
The present invention provides a kind of technical solution：A kind of plant lamp filament of environment-friendly type explosion-proof, including following quality proportioning：Lanthanum
Close object powder 8%, organopolysiloxane 12%, yttrium oxide 10%, molybdenum dioxide 6%, butyl acetate solution 14%, tungsten irridium alloy material
16%, yttrium oxide powder 4%, chloroform antioxidant 8%, platinum oxide 8% and auxiliary material 14%.
The auxiliary material includes following quality proportioning：Curing agent 20%, thixotropic agent 10%, ether 30%, neutralizer 40%.
A kind of preparation method of the plant lamp filament of environment-friendly type explosion-proof, includes the following steps,
S1：Raw material weighs, by lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, butyl acetate solution, tungsten iridium
Alloy material, yttrium oxide powder, chloroform antioxidant and platinum oxide are taken according to set ratio weighing；
S2：Bed blending, by load weighted lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, tungsten irridium alloy
Material, yttrium oxide powder, chloroform antioxidant and platinum oxide are put into clean container, and start to grind by grinding device,
In process of lapping, the one third of load weighted butyl acetate solution was added every 10 minutes, was added altogether three times, and in vinegar
After the addition of acid butyl ester solution is completed, it is stirred grinding, the agitation grinding time is 70 minutes, obtains material solution；
S3：Auxiliary material is added, and curing agent, thixotropic agent, ether and neutralizer are chosen according to set ratio and weighed, and will solidification
Gradually being added in material solution one by one, addition manner are to add one by one, and add for agent, thixotropic agent, ether and neutralizer
Interval time be 20 minutes, obtain filament solution；
S4：Grinding tool is poured into, the filament grinding tool that will be cleaned up is chosen, and be put into connecting line wherein, is subsequently poured into filament
Solution, and processing is begun to warm up, heating temperature is 700 degree, and heating time is 100 minutes；
S5：Cooling treatment puts the filament grinding tool after heating is quiet to room temperature, then obtains filament ontology,
S6：Filament body surface is carried out frosted processing, removes excess thickness and impurity, and dry solidification by final molding
After obtain finished product.
The connecting line is gold and silver palldium alloy line.
By by comparing five set embodiment, it has been found that it is required that us can be made in five set embodiment
Laser plant filament, the plant lamp filament of the environment-friendly type explosion-proof, by lanthanum compound powder, organopolysiloxane, yttrium oxide,
The mutual cooperation of molybdenum dioxide, butyl acetate solution, tungsten irridium alloy material, yttrium oxide powder, chloroform antioxidant and platinum oxide is made
With, and it is subject to the booster action of curing agent, thixotropic agent, ether and neutralizer again, it is possible to produce the plant that can be used for a long time
Object lamp filament can use in long-time to avoid the filament of plant lamp and in the case of not closing, often be easy to happen explosion
Equal dangerous situations, have prodigious improvement also for the light conditions of plant, and avoid because filament explosion is caused
Situations such as fire, occurs, and solves security risk to a certain extent.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (9)
1. a kind of plant lamp filament of environment-friendly type explosion-proof, which is characterized in that including following quality proportioning：Lanthanum compound powder 4-
8%, organopolysiloxane 6-12%, yttrium oxide 5-10%, molybdenum dioxide 3-6%, butyl acetate solution 7-14%, tungsten irridium alloy material
8-16%, yttrium oxide powder 2-4%, chloroform antioxidant 4-8%, platinum oxide 4-8% and auxiliary material 7-14%.
2. a kind of plant lamp filament of environment-friendly type explosion-proof according to claim 1, it is characterised in that：Including following quality
Proportioning：Lanthanum compound powder 4%, organopolysiloxane 6%, yttrium oxide 5%, molybdenum dioxide 3%, butyl acetate solution 7%, tungsten iridium close
Golden material 8%, yttrium oxide powder 2%, chloroform antioxidant 4%, platinum oxide 4% and auxiliary material 7%.
3. a kind of plant lamp filament of environment-friendly type explosion-proof according to claim 1, it is characterised in that：Including following quality
Proportioning：Lanthanum compound powder 5%, organopolysiloxane 8%, yttrium oxide 6%, molybdenum dioxide 3.7%, butyl acetate solution 9%, tungsten iridium
Alloy material 10%, yttrium oxide powder 2.2%, chloroform antioxidant 5%, platinum oxide 5% and auxiliary material 9%.
4. a kind of plant lamp filament of environment-friendly type explosion-proof according to claim 1, it is characterised in that：Including following quality
Proportioning：Lanthanum compound powder 6%, organopolysiloxane 9%, yttrium oxide 7%, molybdenum dioxide 4.6%, butyl acetate solution 10%, tungsten iridium
Alloy material 12%, yttrium oxide powder 2.4%, chloroform antioxidant 6%, platinum oxide 6% and auxiliary material 10%.
5. a kind of plant lamp filament of environment-friendly type explosion-proof according to claim 1, it is characterised in that：Including following quality
Proportioning：Lanthanum compound powder 7%, organopolysiloxane 11%, yttrium oxide 9%, molybdenum dioxide 5.5%, butyl acetate solution 12%, tungsten
Iridium alloy material 14%, yttrium oxide powder 2.7%, chloroform antioxidant 7%, platinum oxide 7% and auxiliary material 12%.
6. a kind of plant lamp filament of environment-friendly type explosion-proof according to claim 1, it is characterised in that：Including following quality
Proportioning：Lanthanum compound powder 8%, organopolysiloxane 12%, yttrium oxide 10%, molybdenum dioxide 6%, butyl acetate solution 14%, tungsten iridium
Alloy material 16%, yttrium oxide powder 4%, chloroform antioxidant 8%, platinum oxide 8% and auxiliary material 14%.
7. a kind of plant lamp filament of environment-friendly type explosion-proof according to claim 1, it is characterised in that：The auxiliary material includes
Following quality proportioning：Curing agent 10-20%, thixotropic agent 5-10%, ether 15-30%, neutralizer 20-40%.
8. a kind of preparation method of the plant lamp filament of environment-friendly type explosion-proof as described in claim 1-7, it is characterised in that：Packet
Include following steps,
S1：Raw material weighs, by lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, butyl acetate solution, tungsten iridium
Alloy material, yttrium oxide powder, chloroform antioxidant and platinum oxide are taken according to set ratio weighing；
S2：Bed blending, by load weighted lanthanum compound powder, organopolysiloxane, yttrium oxide, molybdenum dioxide, tungsten irridium alloy
Material, yttrium oxide powder, chloroform antioxidant and platinum oxide are put into clean container, and start to grind by grinding device,
In process of lapping, the one third of load weighted butyl acetate solution was added every 10 minutes, was added altogether three times, and in vinegar
After the addition of acid butyl ester solution is completed, it is stirred grinding, the agitation grinding time is 30-70 minutes, obtains material solution；
S3：Auxiliary material is added, and curing agent, thixotropic agent, ether and neutralizer are chosen according to set ratio and weighed, and will solidification
Gradually being added in material solution one by one, addition manner are to add one by one, and add for agent, thixotropic agent, ether and neutralizer
Interval time be 10-20 minutes, obtain filament solution；
S4：Grinding tool is poured into, the filament grinding tool that will be cleaned up is chosen, and be put into connecting line wherein, is subsequently poured into filament
Solution, and processing is begun to warm up, heating temperature is 400-700 degree, and heating time is 60-100 minutes；
S5：Cooling treatment puts the filament grinding tool after heating is quiet to room temperature, then obtains filament ontology,
S6：Filament body surface is carried out frosted processing, removes excess thickness and impurity, and dry solidification by final molding
After obtain finished product.
9. a kind of preparation method of the plant lamp filament of environment-friendly type explosion-proof according to claim 8, it is characterised in that：Institute
State the one of which that connecting line is tungsten filament, gold thread, aluminum steel, copper wire or gold and silver palldium alloy line.