CN108610003A - The manufacture craft of sky blue Nixing pottery - Google Patents
The manufacture craft of sky blue Nixing pottery Download PDFInfo
- Publication number
- CN108610003A CN108610003A CN201810523765.1A CN201810523765A CN108610003A CN 108610003 A CN108610003 A CN 108610003A CN 201810523765 A CN201810523765 A CN 201810523765A CN 108610003 A CN108610003 A CN 108610003A
- Authority
- CN
- China
- Prior art keywords
- green body
- temperature
- sky blue
- per hour
- raised
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses the manufacture crafts of sky blue Nixing pottery, include the following steps：1) blank will be prepared；2) sky blue colorant is made in the raw material of following parts by weight：5~10 parts of neodymia, 0.5~1 part of calcium bicarbonate, 1~3 part of the emerging clinker of mud；3) blank forming；4) body drying；5) green body is decorated with sky blue colorant；6) green body decorated is sent into kiln and will be fired, temperature is first raised to 80~120 DEG C with 20~30 DEG C of the speed of heating up per hour, keeps the temperature 20~28 hours；Temperature is raised to 550~700 DEG C with 60~80 DEG C of the speed of heating up per hour again；Then temperature is raised to 1160~1200 DEG C with 40~60 DEG C of the speed of heating up per hour, keeps the temperature 1~2h, stop heating, it is cooling after kiln discharge to get to sky blue Nixing pottery.The present invention decorates Nixing pottery with sky blue colorant, has pure color uniform, fires non-discolouring advantage.
Description
Technical field
The invention belongs to the production methods of Nixing pottery, and in particular to a kind of manufacture craft of sky blue Nixing pottery.
Background technology
The preparation process of traditional Qiezhou Nixing pottery includes mainly following steps：1) blank is prepared：Blank is by clay material
Material is made, and it is raw material to select the distinctive eastern mud in Qiezhou and western mud.The east mud is the Jiang Yidong that admires for crossing Qiezhou urban district
The soil in domain, is mostly stored in low lying areas, and the soil compact substance is soft, is mild-clay, and color is yellow-white, contains micro quartz
Sand.Western mud is then the soil for crossing region to the west of the river of admiring in Qiezhou urban district, and based on hillside, which is compact block on storage ground
Shape is a kind of higher purple mudstone of iron-holder, face containing a small amount of K2O, Na2O, CaO, MgO, Fe2O3, TiO2, SiO2, MnO2
Color is aubergine, and superficial layer has a small amount of irony to disseminate, and is hard paste, plasticity and the more eastern mud of associativity are poor.To the east of mud 40~
60%, the weight percent mixing of western mud 60~40%, blank method is prepared through Nixing pottery that is existing, generally using：Such as may be used
Blank is made in modeling method and slip casting method；2) it is molded：The green body of various types is made of blank；3) repaired biscuit：Green body is modified, with
Reach design requirement；4) body drying：Green body is dried, green body moisture is made to be discharged；For example, by using indoor seasoning method, air-dry
Method, suning method or other existing, feasible drying means；5) green body is decorated：Nixing pottery neither adds any in the production process
Pigment, not glazing, also not on green body with any coloured material drawing colour and pattern, only relying on the transmutation occurred once in a while makes mud
Unpredictable and control color is presented in emerging pottery, and decorates green body using artistic carving.The artistic carving is i.e. with sharp
Steel knife carves out word and pattern on green body, generally uses flat carving technique and embossing technology.Flat carving is the mud wet in half top dry-up
It is carried out on base, piercing, sculpture, the skill and technique such as inlays at wired quarter.Embossment is carried out in absolutely dry green body, there is high relief, bas-relief etc.
Skill and technique.For can more distinct prominent decorative pattern, can also fill out white clay on the pattern carved, it is fired after white clay show slightly light
Yellow and the same warm tones of pottery color, it is remote to see the benefits of pottery is painted in gold, the overall style of Nixing pottery device can be promoted.6) it fires：
The green body loading of kiln decorated is fired；In order to reach higher firing rate and improve transmutation rate, the maximum temperature control that green body is fired
For system at 1100~1200 DEG C, the firing time is 10 hours, and fired rear kiln discharge is Nixing pottery device.Nixing pottery green body be to the east of mud
It being made with two kinds of china clay materials of western mud, non-refractory, firing temperature is more than 1200 DEG C, and billet surface will appear crackle or breakage,
It is serious or even occur blank deformation and caving in.Neodymia belongs to high temperature decorating colour, could stablize at a high temperature of 1300 DEG C or more
Color development, if when with this decorative ornament Nixing pottery green body, there is neodymia and the inconsistent problem of Nixing pottery green body firing temperature.
Invention content
The technical problem to be solved in the present invention is to provide a kind of manufacture craft of sky blue Nixing pottery, this method can solve
Nixing pottery and the inconsistent problem of sky blue colorant firing temperature, the sky blue Nixing pottery pure color of firing are uniform.
Technical solution provided by the invention is the manufacture craft of sky blue Nixing pottery, it is characterised in that：Include the following steps：
1) 4~6 parts by weight of eastern mud, 4~6 parts by weight of western mud are mixed and made into blank；
2) sky blue colorant is made in the raw material of following parts by weight：5~10 parts of neodymia, 0.5~1 part of calcium bicarbonate, mud are emerging
1~3 part of clinker；
3) blank is made to the green body of various types；
4) by body drying；
5) green body is decorated with sky blue colorant；
6) green body decorated is sent into kiln and will be fired, first with 20~30 DEG C of the speed of heating up per hour by temperature
80~120 DEG C are raised to, keeps the temperature 20~28 hours；Temperature is raised to 550~700 with 60~80 DEG C of the speed of heating up per hour again
℃；Then temperature is raised to 1160~1200 DEG C with 40~60 DEG C of the speed of heating up per hour, keeps the temperature 1~2h, stops heating, it is cold
But kiln discharge is to get to sky blue Nixing pottery after.
The parts by weight group of sky blue colorant becomes：7 parts of neodymia, 0.8 part of calcium bicarbonate, 1.5 parts of the emerging clinker of mud.
The preparation method of the Nixing pottery clinker is as follows：
1) pug is prepared：It is most laggard by the eastern mud of select and western mud through weathering, according to the ratio goal, press filtration, vacuum pugging
Row is aging to obtain pug；
2) green body is made：Green body is made in pug；
3) body drying：It is 3~8% that green body, which is put into interior and is dried to green body humidity,；
4) green body is fired：Dry green body is put into kiln, heating rate is to increase 60~80 DEG C per hour, is raised to
180~220 DEG C, and at such a temperature, persistently fire 2~4 hours；Then heating rate is to heat up 80~100 DEG C per hour, directly
To being raised to 500~600 DEG C, and at such a temperature, persistently fire 2~3 hours；After natural cooling, the green body being fired into is taken out,
Complete the firing of green body；
5) Nixing pottery clinker is obtained after being ground the green body after cooking.
In the step 3) of clinker preparation process, the humidity of green body is 5% after drying.
In the step 4) of clinker preparation process, dry green body is put into kiln, heating rate is to heat up per hour
70 DEG C, 200 DEG C are raised to, and at such a temperature, persistently fired 3 hours；Then heating rate is to heat up 90 DEG C per hour, until rising
To 550 DEG C, and at such a temperature, persistently fire 2.5 hours.
The present invention decorates Nixing pottery with sky blue colorant, has pure color uniform, fires non-discolouring advantage.
Specific implementation mode
The present invention is further elaborated for following specific examples, but not as a limitation of the invention.
Embodiment 1
1) pug is prepared：By the eastern mud of select and western mud through weathering, by weight 6:4 proportioning goal, press filtration, vacuum are practiced
Mud finally carries out aging obtaining pug；
2) green body is made：Green body is made in pug；
3) body drying：It is 3% that green body, which is put into interior and is dried to green body humidity,；
4) green body is fired：Dry green body is put into kiln, heating rate is to increase 60 DEG C per hour, is raised to 180
DEG C, and at such a temperature, persistently fire 2 hours；Then heating rate is 80 DEG C of heating per hour, until 500 DEG C are raised to, and
At this temperature, it persistently fires 2 hours；After natural cooling, the green body being fired into is taken out, the firing of green body is completed；
5) Nixing pottery clinker is obtained after being ground the green body after cooking；
6) eastern mud 4kg, western mud 6kg are mixed and made into blank；
7) sky blue colorant is made in the raw material of following parts by weight：The emerging clinker 1kg of neodymia 5kg, calcium bicarbonate 0.5kg, mud；
8) blank of step 6) is made to the green body of various types；
9) by body drying；
10) green body is decorated with sky blue colorant；
11) green body decorated is sent into kiln and will be fired, first with 20 DEG C of the speed of heating up per hour by temperature liter
To 80 DEG C, 20 hours are kept the temperature；Temperature is raised to 550 DEG C with 60 DEG C of the speed of heating up per hour again；Then to heat up 40 per hour
DEG C speed temperature is raised to 1160 DEG C, keep the temperature 1h, stop heating, it is cooling after kiln discharge to get to sky blue Nixing pottery.Blank is sent out
It is colour-stable, pure color.
Embodiment 2
1) pug is prepared：By the eastern mud of select and western mud through weathering, by weight 6:4 proportioning goal, press filtration, vacuum are practiced
Mud finally carries out aging obtaining pug；
2) green body is made：Green body is made in pug；
3) body drying：It is 8% that green body, which is put into interior and is dried to green body humidity,；
4) green body is fired：Dry green body is put into kiln, heating rate is to increase 80 DEG C per hour, is raised to 220
DEG C, and at such a temperature, persistently fire 4 hours；Then heating rate is 100 DEG C of heating per hour, until 600 DEG C are raised to, and
At such a temperature, it persistently fires 3 hours；After natural cooling, the green body being fired into is taken out, the firing of green body is completed；
5) Nixing pottery clinker is obtained after being ground the green body after cooking；
6) eastern mud 6kg, western mud 6kg are mixed and made into blank；
7) sky blue colorant is made in the raw material of following parts by weight：The emerging clinker 3kg of neodymia 10kg, calcium bicarbonate 1kg, mud；
8) blank of step 6) is made to the green body of various types；
9) by body drying；
10) green body is decorated with sky blue colorant；
11) green body decorated is sent into kiln and will be fired, first with 30 DEG C of the speed of heating up per hour by temperature liter
To 120 DEG C, 28 hours are kept the temperature；Temperature is raised to 700 DEG C with 80 DEG C of the speed of heating up per hour again；Then to heat up 60 per hour
DEG C speed temperature is raised to 1200 DEG C, keep the temperature 2h, stop heating, it is cooling after kiln discharge to get to sky blue Nixing pottery.Blank is sent out
It is colour-stable, pure color.
Embodiment 3
1) pug is prepared：By the eastern mud of select and western mud through weathering, by weight 6:4 proportioning goal, press filtration, vacuum are practiced
Mud finally carries out aging obtaining pug；
2) green body is made：Green body is made in pug；
3) body drying：It is 5% that green body, which is put into interior and is dried to green body humidity,；
4) green body is fired：Dry green body is put into kiln, heating rate is to heat up 70 DEG C per hour, is raised to 200
DEG C, and at such a temperature, persistently fire 3 hours；Then heating rate is 90 DEG C of heating per hour, until 550 DEG C are raised to, and
At this temperature, it persistently fires 2.5 hours；After natural cooling, the green body being fired into is taken out, the firing of green body is completed；
5) Nixing pottery clinker is obtained after being ground the green body after cooking；
6) eastern mud 6kg, western mud 4kg are mixed and made into blank；
7) sky blue colorant is made in the raw material of following parts by weight：Neodymia 7kg, calcium bicarbonate 0.8kg, the emerging clinker of mud
1.5kg；
8) blank of step 6) is made to the green body of various types；
9) by body drying；
10) green body is decorated with sky blue colorant；
11) green body decorated is sent into kiln and will be fired, first with 25 DEG C of the speed of heating up per hour by temperature liter
To 100 DEG C, 24 hours are kept the temperature；Temperature is raised to 650 DEG C with 70 DEG C of the speed of heating up per hour again；Then to heat up 50 per hour
DEG C speed temperature is raised to 1180 DEG C, keep the temperature 1.5h, stop heating, it is cooling after kiln discharge to get to sky blue Nixing pottery.Blank
Color development is stablized, pure color.
Embodiment 4
1) pug is prepared：By the eastern mud of select and western mud through weathering, by weight 6:4 proportioning goals, press filtration, vacuum are practiced
Mud finally carries out aging obtaining pug；
2) green body is made：Green body is made in pug；
3) body drying：It is 3% that green body, which is put into interior and is dried to green body humidity,；
4) green body is fired：Dry green body is put into kiln, heating rate is to increase 80 DEG C per hour, is raised to 180
DEG C, and at such a temperature, persistently fire 4 hours；Then heating rate is 80 DEG C of heating per hour, until 600 DEG C are raised to, and
At this temperature, it persistently fires 2 hours；After natural cooling, the green body being fired into is taken out, the firing of green body is completed；
5) Nixing pottery clinker is obtained after being ground the green body after cooking；
6) eastern mud 6kg, western mud 4kg are mixed and made into blank；
7) sky blue colorant is made in the raw material of following parts by weight：Neodymia 10kg, calcium bicarbonate 0.5kg, the emerging clinker of mud
3kg；
8) blank of step 6) is made to the green body of various types；
9) by body drying；
10) green body is decorated with sky blue colorant；
11) green body decorated is sent into kiln and will be fired, first with 20 DEG C of the speed of heating up per hour by temperature liter
To 120 DEG C, 20 hours are kept the temperature；Temperature is raised to 550 DEG C with 80 DEG C of the speed of heating up per hour again；Then to heat up 60 per hour
DEG C speed temperature is raised to 1160 DEG C, keep the temperature 2h, stop heating, it is cooling after kiln discharge to get to sky blue Nixing pottery.Blank is sent out
It is colour-stable, pure color.
Claims (5)
1. the manufacture craft of sky blue Nixing pottery, it is characterised in that：Include the following steps：
1) 4~6 parts by weight of eastern mud, 4~6 parts by weight of western mud are mixed and made into blank；
2) sky blue colorant is made in the raw material of following parts by weight：The emerging clinker of 5~10 parts of neodymia, 0.5~1 part of calcium bicarbonate, mud 1
~3 parts；
3) blank is made to the green body of various types；
4) by body drying；
5) green body is decorated with sky blue colorant；
6) green body decorated is sent into kiln and will be fired, be first raised to temperature with 20~30 DEG C of the speed of heating up per hour
80~120 DEG C, keep the temperature 20~28 hours；Temperature is raised to 550~700 DEG C with 60~80 DEG C of the speed of heating up per hour again；It connects
It and temperature is raised to 1160~1200 DEG C with 40~60 DEG C of the speed of heating up per hour, keep the temperature 1~2h, stop heating, after cooling
Kiln discharge is to get to sky blue Nixing pottery.
2. the manufacture craft of sky blue Nixing pottery according to claim 1, it is characterised in that：The parts by weight group of sky blue colorant
Become：7 parts of neodymia, 0.8 part of calcium bicarbonate, 1.5 parts of the emerging clinker of mud.
3. the manufacture craft of sky blue Nixing pottery according to claim 1 or 2, it is characterised in that：The Nixing pottery clinker
Preparation method it is as follows：
1) pug is prepared：By the eastern mud of select and western mud through weathering, according to the ratio goal, press filtration, vacuum pugging, finally carry out old
Corruption obtains pug；
2) green body is made：Green body is made in pug；
3) body drying：It is 3~8% that green body, which is put into interior and is dried to green body humidity,；
4) green body is fired：Dry green body is put into kiln, heating rate is to increase 60~80 DEG C per hour, is raised to 180
~220 DEG C, and at such a temperature, persistently fire 2~4 hours；Then heating rate is to heat up 80~100 DEG C per hour, up to
500~600 DEG C are raised to, and at such a temperature, persistently fired 2~3 hours；After natural cooling, the green body being fired into is taken out, it is complete
At the firing of green body；
5) Nixing pottery clinker is obtained after being ground the green body after cooking.
4. the manufacture craft of sky blue Nixing pottery according to claim 3, it is characterised in that：In step 3), base after drying
The humidity of body is 5%.
5. the manufacture craft of sky blue Nixing pottery according to claim 3, it is characterised in that：In step 4), dry
Green body is put into kiln, and heating rate is to heat up 70 DEG C per hour, is raised to 200 DEG C, and at such a temperature, and it is small persistently to fire 3
When；Then heating rate is to heat up 90 DEG C per hour, until being raised to 550 DEG C, and at such a temperature, is persistently fired 2.5 hours.