CN108594608A - 绿色激光打印机干式墨粉及其制备方法 - Google Patents
绿色激光打印机干式墨粉及其制备方法 Download PDFInfo
- Publication number
- CN108594608A CN108594608A CN201810399969.9A CN201810399969A CN108594608A CN 108594608 A CN108594608 A CN 108594608A CN 201810399969 A CN201810399969 A CN 201810399969A CN 108594608 A CN108594608 A CN 108594608A
- Authority
- CN
- China
- Prior art keywords
- parts
- laser printer
- dry type
- type ink
- green laser
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种绿色激光打印机干式墨粉及其制备方法，属于激光打印技术领域。其包括永固黄10~20份、酞青蓝4~8份、含蜡苯丙树脂70~80份、聚乙烯蜡3~6份、电荷调节剂1~3份、硅油3~6份和六甲基硅氮烷12~16份，经混炼、挤塑、粉碎和过筛等步骤而制成。使用这种绿激光打印机干式墨粉在激光打印机中，打印的绿色专门为政府绿头文件研制，颜色亮丽，色彩纯正，满足政府行业绿头文件的印制要求，使打印图像过渡更加平滑，层次的再现也更加的真实。使政府文印具备高品质、稳定性、自动化的全面应用，满足办公打印高品质需求。
Description
技术领域
本发明涉及一种绿色激光打印机干式墨粉及其制备方法，属于激光打印技术领域。
背景技术
印有“绿头”的政府公文通常被统称为“绿头文件”，作为上情下达的正式官方文件，是政府公开文件的一种。绿头激光打印解决方案不仅最大程度的优化了“绿头文件”的印制流程更大幅提升了制作效率，更重要的是将传统繁琐的手工操作环节转化为电子化自动流程，自动完成绿头、正文、序号编注的一键打印输出，并直接自动装订成册，大大缩短了“绿头文件”的印制时间。满足办公打印高品质需求。
发明内容
本发明的目的是克服上述不足之处，提供一种绿色激光打印机干式墨粉及其制备方法，使政府文印具备高品质、稳定性、自动化的全面应用，满足办公打印高品质需求。
本发明的技术方案，一种绿色激光打印机干式墨粉，按重量份计步骤如下：永固黄10~20份、酞青蓝4~8份、含蜡苯丙树脂70~80份、聚乙烯蜡3~6份、电荷调节剂1~3份、硅油3~6份和六甲基硅氮烷12~16份。
所述永固黄：酞青蓝重量比为5：2。
所述绿色激光打印机干式墨粉，按重量份计步骤如下：
（1）初步混合：将永固黄10~20份、酞青蓝4~8份、含蜡苯丙树脂70~80份、聚乙烯蜡3~6份和电荷调节剂1~3份倒入混炼机中，经均匀混合1200~1500r/min混合2~5min，制成混合料；
（2）出片：将步骤（1）所得混合料投入挤塑机中，在90~150℃的温度下将混合料挤出压制成片，然后将片状混合料冷却至40~45℃并粉碎成碎片；
（3）粉碎：用机械粉碎机将步骤（2）所得碎片粉碎成粒径为30~50μm的碎粉；
（4）半成品颗粒制备：用流化床粉碎机对步骤（3）所得碎粉进行进一步气流粉碎，并依次进行分级、分离和收集，得到粒径为7~9μm的半成品颗粒；
（5）二次混合：在步骤（4）所得半成品颗粒中加入硅油3~6份和六甲基硅氮烷12~16份，用1200~1300r/min的混炼机混合7~8min；
（6）过筛：对步骤（5）所得混合物用200~250目筛网过筛，即制得绿色激光打印机干式墨粉。
本发明的有益效果：本发明制备所得绿色激光打印机干式墨粉打印专门为政府绿头文件研制，颜色亮丽，色彩纯正，满足政府行业绿头文件的印制要求，使打印图像过渡更加平滑，层次的再现也更加的真实。
具体实施方式
以下实施例中的电荷调节剂购自日本保土谷化学工业株式会社的产品E-84，所述含蜡苯丙树脂的制备过程如申请号201410178938.2所述。
实施例1
选取10份永固黄、4份酞青蓝、70份的含蜡苯丙树脂、3份的聚乙烯蜡、3份的电荷调节剂、6份的硅油和12份的六甲基硅氮烷，待用。
所述永固黄：酞青蓝重量比为5：2。
所述绿色激光打印机干式墨粉，按重量份计步骤如下：
（1）初步混合：将永固黄、酞青蓝、含蜡苯丙树脂、聚乙烯蜡和电荷调节剂倒入混炼机中，经均匀混合1200r/min混合5min，制成混合料；
（2）出片：将步骤（1）所得混合料投入挤塑机中，在90℃的温度下将混合料挤出压制成片，然后将片状混合料冷却至40℃并粉碎成碎片；
（3）粉碎：用机械粉碎机将步骤（2）所得碎片粉碎成粒径为30~50μm的碎粉；
（4）半成品颗粒制备：用流化床粉碎机对步骤（3）所得碎粉进行进一步气流粉碎，并依次进行分级、分离和收集，得到粒径为7~9μm的半成品颗粒；
（5）二次混合：在步骤（4）所得半成品颗粒中加入硅油和六甲基硅氮烷，用1200r/min的混炼机混合8min；
（6）过筛：对步骤（5）所得混合物用200目筛网过筛，即制得绿色激光打印机干式墨粉。
实施例2
选取15份永固黄、6份酞青蓝、80份的含蜡苯丙树脂、6份的聚乙烯蜡、1份的电荷调节剂、3份的硅油和16份的六甲基硅氮烷，待用。
所述永固黄：酞青蓝重量比为5：2。
所述绿色激光打印机干式墨粉，按重量份计步骤如下：
（1）初步混合：将永固黄、酞青蓝、含蜡苯丙树脂、聚乙烯蜡和电荷调节剂倒入混炼机中，经均匀混合1500r/min混合2min，制成混合料；
（2）出片：将步骤（1）所得混合料投入挤塑机中，在150℃的温度下将混合料挤出压制成片，然后将片状混合料冷却至40℃并粉碎成碎片；
（3）粉碎：用机械粉碎机将步骤（2）所得碎片粉碎成粒径为30~50μm的碎粉；
（4）半成品颗粒制备：用流化床粉碎机对步骤（3）所得碎粉进行进一步气流粉碎，并依次进行分级、分离和收集，得到粒径为7~9μm的半成品颗粒；
（5）二次混合：在步骤（4）所得半成品颗粒中加入硅油和六甲基硅氮烷，用1300r/min的混炼机混合7min；
（6）过筛：对步骤（5）所得混合物用250目筛网过筛，即制得绿色激光打印机干式墨粉。
实施例3
选取20份永固黄、6份酞青蓝、75份的含蜡苯丙树脂、5份的聚乙烯蜡、2份的电荷调节剂、5份的硅油和14份的六甲基硅氮烷，待用。
所述永固黄：酞青蓝重量比为5：2。
所述绿色激光打印机干式墨粉，按重量份计步骤如下：
（1）初步混合：将永固黄、酞青蓝、含蜡苯丙树脂、聚乙烯蜡和电荷调节剂倒入混炼机中，经均匀混合1350r/min混合3min，制成混合料；
（2）出片：将步骤（1）所得混合料投入挤塑机中，在130℃的温度下将混合料挤出压制成片，然后将片状混合料冷却至43℃并粉碎成碎片；
（3）粉碎：用机械粉碎机将步骤（2）所得碎片粉碎成粒径为30~50μm的碎粉；
（4）半成品颗粒制备：用流化床粉碎机对步骤（3）所得碎粉进行进一步气流粉碎，并依次进行分级、分离和收集，得到粒径为7~9μm的半成品颗粒；
（5）二次混合：在步骤（4）所得半成品颗粒中加入硅油和六甲基硅氮烷，用1250r/min的混炼机混合7min；
（6）过筛：对步骤（5）所得混合物用230目筛网过筛，即制得绿色激光打印机干式墨粉。
Claims (3)
1.一种绿色激光打印机干式墨粉，其特征是按重量份计步骤如下：永固黄10~20份、酞青蓝4~8份、含蜡苯丙树脂70~80份、聚乙烯蜡3~6份、电荷调节剂1~3份、硅油3~6份和六甲基硅氮烷12~16份。
2.如权利要求1所述绿色激光打印机干式墨粉，其特征是：所述永固黄：酞青蓝重量比为5：2。
3.如权利要求1所述绿色激光打印机干式墨粉，其特征是按重量份计步骤如下：
（1）初步混合：将永固黄10~20份、酞青蓝4~8份、含蜡苯丙树脂70~80份、聚乙烯蜡3~6份和电荷调节剂1~3份倒入混炼机中，经均匀混合1200~1500r/min混合2~5min，制成混合料；
（2）出片：将步骤（1）所得混合料投入挤塑机中，在90~150℃的温度下将混合料挤出压制成片，然后将片状混合料冷却至40~45℃并粉碎成碎片；
（3）粉碎：用机械粉碎机将步骤（2）所得碎片粉碎成粒径为30~50μm的碎粉；
（4）半成品颗粒制备：用流化床粉碎机对步骤（3）所得碎粉进行进一步气流粉碎，并依次进行分级、分离和收集，得到粒径为7~9μm的半成品颗粒；
（5）二次混合：在步骤（4）所得半成品颗粒中加入硅油3~6份和六甲基硅氮烷12~16份，用1200~1300r/min的混炼机混合7~8min；
（6）过筛：对步骤（5）所得混合物用200~250目筛网过筛，即制得绿色激光打印机干式墨粉。