CN108589256A - High-whiteness cotton/Tai Ji stone blended yarn weaved fabric and its processing technology - Google Patents
High-whiteness cotton/Tai Ji stone blended yarn weaved fabric and its processing technology Download PDFInfo
- Publication number
- CN108589256A CN108589256A CN201810450920.1A CN201810450920A CN108589256A CN 108589256 A CN108589256 A CN 108589256A CN 201810450920 A CN201810450920 A CN 201810450920A CN 108589256 A CN108589256 A CN 108589256A
- Authority
- CN
- China
- Prior art keywords
- tai
- fabric
- cotton
- stone
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to technical field of textile printing, and in particular to a kind of high-whiteness cotton/Tai Ji stone blended yarn weaved fabric and its processing technology.By cotton/Tai Ji stone fabric is successively by singing → move back boil → special drift → multiple drift → mercerising → wash brighten → brighten wash → tentering softness → preshrunk obtains cotton/Tai Ji stone blended yarn weaved fabric;Special bleaching liquor is the mixture of sodium chlorite, acetic acid and water, and pH value is:3.6~4, speed:85~90m/min, steam box upper temp:90~95 DEG C, steam box temperature of lower:85~90 DEG C;Bleaching liquor is again:H2O2, NaOH, chelating agent, stabilizer, bleeding agent and water, 98~100 DEG C of steamer temperature, 15~20min of heap cloth time.The present invention has the characteristics that Gao Bai, wash resistant, good hand touch, moisture pick-up properties are good, while having excellent wearability;The present invention also provides its processing technology, the mode of production has continuity, can realize that the continuous production of bulk production, efficiency are higher.
Description
Technical field
The invention belongs to technical field of textile printing, and in particular to a kind of high-whiteness cotton/Tai Ji stone blended yarn weaved fabric and its add
Work technique.
Background technology
Cotton/Tai Ji stone blended yarn weaved fabric is:Cotton and Tai Ji stone yarn, Tai Ji stone yarn are currently that Tai Ji stone powder is used
In (polyester or viscose glue) fiber axis, Tai Ji stone health energy fiber is made.Tai Ji stone has refinement hydrone, can improve human body
Blood microcirculation promotes cell activity, Ginkgo Biloba.It (is commonly called as giving birth to the far infrared wavelength 8~14 μm beneficial to human body
Order light wave), the far infrared effect wavelength of Tai Ji stone is 3.9~16 μm, can generate resonant interaction with the hydrone in human body cell;
Enhance blood cell kinetic energy, refinement hydrone, blood energy smooth outflow promote human metabolism;Stablize blood quality, makes one
Body keeps higher immunity, and it is horizontal to promote people's health.
The bleaching method of cotton/Tai Ji stone blended fabric only has market bleach currently on the market, and whitening process is generally adopted
It with some low-affinity class brightening agents, pads, dry completion, the whiteness of the fabric so processed is relatively low, production efficiency is not high, often
It is big to criticize whiteness difference, high-end fabric class is not achieved, and high-grade fabric stay in grade, unified requirement cannot be met.
Invention content
In view of the deficiencies of the prior art, the object of the present invention is to provide a kind of high-whiteness cotton/Tai Ji stone blended yarn weaved fabric, have
The good feature of Gao Bai, wash resistant, good hand touch, moisture pick-up properties, while there is excellent wearability;The present invention also provides its processing
Technique, the mode of production have continuity, can realize that the continuous production of bulk production, efficiency are higher.
High-whiteness cotton of the present invention/Tai Ji stone blended yarn weaved fabric, by cotton ,/Tai Ji stone fabric is successively by singing → is moved back and is boiled
→ special drift → multiple drift → mercerising → wash brighten → brighten wash → tentering softness → preshrunk obtains cotton/Tai Ji stone blended yarn weaved fabric;
Spy's drift:Special bleaching liquor used is the mixture of sodium chlorite, acetic acid and water, and the pH value of special bleaching liquor is:3.6~4, vehicle
Speed:85~90m/min, steam box upper temp:90~95 DEG C, steam box temperature of lower:85~90 DEG C;
Multiple drift:Multiple bleaching liquor used is:H2O2, NaOH, chelating agent, stabilizer, bleeding agent and water, steamer temperature 98~100
DEG C, 15~20min of heap cloth time.
Wherein:
Special bleaching liquor is:30~40g/L of sodium chlorite, 3~5g/L of acetic acid, surplus are water;
Bleaching liquor is again:H2O22~5g/L of 7~10g/L, NaOH, 5~10g/L of chelating agent, 5~10g/L of stabilizer, infiltration
5~10g/L of agent;It by concentration ratio is 1 that chelating agent, which is SQ~A and 254, in multiple drift:3 mixture, stabilizer 266, bleeding agent are
CH~L.
Spy's drift steam box upper temp:90~95 DEG C, steam box temperature of lower:85~90 DEG C;Steamer temperature 98~100 is floated again
DEG C, 15~20min of heap cloth time;It selects the steamer temperature and drift heap cloth 15min or more can allow cloth fully to bleach again.The present invention
Spy's drift+double bleaching process of multiple drift compared with the existing technology for belong to distinctive technological process.
It washs and brightens:Brightening agent uses dicyan styrene derivative brightening agent EVB, a concentration of 4~6g/L;It brightens and washes:It brightens
Agent uses 1,2 diphenyl ethylene derivatives brightening agent PC, a concentration of 4~12g/L.Dicyan styrene derivative brightening agent EVB and 1,2
Diphenyl ethylene derivatives brightening agent PC is medium or medium higher affinity.The manufacturer of EVB steps for Hensel, the production of PC
Producer is Clariant.
It washs and brightens process:Brightening agent is added in groove, pads cotton/Tai Ji stone blended fabric, liquid carrying rate control 55~
75%, 180 ± 3 DEG C are then warming up to, passing sequentially through 180 ± 3 DEG C of 8 high temperature ovens makes the fabric color development with brightening agent.
It brightens and washes process:Brightening agent is added in groove, pads cotton/Tai Ji stone blended fabric, liquid carrying rate control 55~
75%, 98~100 DEG C are then warming up to, the decatize 50~70 seconds in the guide roll type steaming box full of saturated vapor, then pass through successively
It crosses 50 DEG C to wash 60~80 seconds, in neutralization chamber and 20~30 seconds, pH value is controlled 3.5~4.5, then passes through 50 DEG C of rinsing bowls successively
Washing 60~80 seconds, 90 DEG C~120 DEG C of drying cylinder drying, drying material pH value control below is 6~7.5.
It washs and brightens and brighten the groove volume described in washing as 30~50L.
Softening agent is added in tentering softness step, softening agent selection influences fabric xanthochromia smaller softening agent, softening agent
The phenol xanthochromia of preferably silicone oil softening agent, softening agent is 4 grades or more.
Softening agent is more preferably one or both of TF~4911 or SMI~62, soft smooth;TF~4911
Manufacturer be development of evil in febrile disease Chemical Co., Ltd.;The manufacturer of SMI~62 is Lu Rui Chemical Co., Ltd.s.
The processing technology of high-whiteness cotton of the present invention/Tai Ji stone blended yarn weaved fabric, includes the following steps:
Cotton/Tai Ji stone fabric after singing, moving back and boil, carry out special drift, multiple drift, mercerising, wash brighten, brighten wash, tentering it is soft
Soft, preshrunk obtains cotton/Tai Ji stone blended yarn weaved fabric;
Spy's drift:Special bleaching liquor used is the mixture of sodium chlorite, acetic acid and water, and the pH value of special bleaching liquor is:3.6~4, vehicle
Speed:85~90m/min, steam box upper temp:90~95 DEG C, steam box temperature of lower:85~90 DEG C;
Multiple drift:Multiple bleaching liquor used is:H2O22~5g/L of 7~10g/L, NaOH, 5~10g/L of chelating agent, stabilizer 5
~10g/L, 5~10g/L of bleeding agent, 98~100 DEG C of steamer temperature, 15~20min of heap cloth time;
It washs and brightens process:Brightening agent is added in groove, pads cotton/Tai Ji stone blended fabric, liquid carrying rate control 55~
75%, 180 ± 3 DEG C are then warming up to, passing sequentially through 180 ± 3 DEG C of 8 high temperature ovens makes the fabric color development with brightening agent;
It brightens and washes process:Brightening agent is added in groove, pads cotton/Tai Ji stone blended fabric, liquid carrying rate control 55~
75%, 98~100 DEG C are then warming up to, the decatize 50~70 seconds in the guide roll type steaming box full of saturated vapor, then pass through successively
It crosses 50 DEG C of rinsing bowls to wash 60~80 seconds, in neutralization chamber and 20~30 seconds, pH value control is in 3.5~4.5,50 DEG C of clear water washings 8
~15 seconds, 90 DEG C~120 DEG C of drying cylinder drying, drying material pH value control below was 6~7.5;
Tentering is soft:Silicone oil softening agent is added and carries out tentering softness.
Compared with prior art, the present invention has the following advantages:
(1) high-whiteness cotton of the present invention/Tai Ji stone blended yarn weaved fabric has Gao Bai, wash resistant, good hand touch, hygroscopicity
The good feature of energy, while there is excellent wearability.
(2) bottom that compounding feed liquid can increase fabric in special drift~double drifts of multiple drift increases in vain to 75 or more to make high whiteness
Fine flour material provides basis.In such a way that the present invention brightens, brightening agent can abundant color development, effectively improve cotton/Tai Ji stone is blended and knit
The whiteness of object is to 140 or more, and cotton/Tai Ji stone blended fabric color and luster after brightening is beautiful, and soaping fastness reaches 4 grades or more.
(3) the present invention also provides its processing technologys, are a kind of environment-friendly high-efficiency whitening process, and the mode of production has continuity,
It can realize that the continuous production of bulk production, efficiency are higher;It singes:Remove the mixed and disorderly filoplume of fabric surface;It moves back and boils:Reject cloth starch adhesive
Material and impurity;Spy's drift and multiple drift:Achieve the purpose that raising fabric bottom is white by compounding feed liquid and process conditions;It brightens:Fully hair
Color improves whiteness;Tentering:Improve fabric feeling, increases the added value of fabric.
Specific implementation mode
With reference to embodiment, the present invention will be further described.
Embodiment 1
Warp-wise cotton broadwise cotton/Tai Ji stone fabric:CM50*COTTON/TJS50*160*90*57/58 organizes 2/1S.
A kind of processing technology of high-whiteness cotton/Tai Ji stone blended yarn weaved fabric, steps are as follows:
After singing, moving back and boil, carry out special drift, multiple drift, mercerising, wash brighten, brighten wash, tentering softness, preshrunk obtain cotton/
Tai Ji stone blended yarn weaved fabric;
Spy's drift:Sodium chlorite:38g/L acetic acid:3.5g/L speed:85m/min, hopper pH value:3.6, steam box upper temp:
92 DEG C, steam box temperature of lower:85℃
Multiple drift:H2O27g/L, NaOH 2g/L, chelating agent 5g/L, stabilizer 5g/L, bleeding agent 5g/L, steamer temperature 98
DEG C, heap cloth time 15min.
It washs and brightens process:The dicyan styrene derivative brightening agent EVB of a concentration of 4g/L is added in groove, pad cotton/
Tai Ji stone blended fabric, liquid carrying rate are controlled 55%, are then warming up to 180 DEG C, passing sequentially through 180 DEG C of 8 high temperature ovens makes
Fabric color development with brightening agent.
It brightens and washes process:The 1 of a concentration of 12g/L, 2 diphenyl ethylene derivatives brightening agent PC is added in groove, pad cotton/
Tai Ji stone blended fabric, liquid carrying rate are controlled 65%, 98 DEG C are then warming up to, in the guide roll type steaming box full of saturated vapor
Decatize 50 seconds, then pass through 50 DEG C successively and wash 60 seconds, in neutralization chamber and 20 seconds, pH value control is washed 8 seconds in 3.5,50 DEG C of clear water,
90 DEG C of drying cylinder drying, drying material pH value control below is 6.
Tentering is soft:Silicone oil softening agent TF~4911 is added and carries out tentering softness.
142.3~0.65 can be reached using finished product whiteness after above-mentioned process, 4.5 grades of soaping fastness.
Comparative example 1
Comparative example 1 is following two points using fabric identical with embodiment and processing technology, difference:
Brighten that wash process different from embodiment 1, comparative example 1 is brightened using tradition washes technique:PC:10g/L, temperature:70℃*
6+95 DEG C of+60 DEG C * 6 of * 6 roads road, speed:100m/min;
Special drift+multiple bleaching process is not used, but uses common (multiple drift) bleaching whitening process, bleaching:H2O27g/L,
NaOH2g/L, chelating agent 5g/L, stabilizer 5g/L, bleeding agent 5g/L, 98 DEG C of steamer temperature, heap cloth time 15min.
Whiteness only has 135.7~0.45, and 3 grades of soaping fastness, embodiment 1 is obviously better than comparative example 1.
Embodiment 2
Warp-wise cotton broadwise cotton/Tai Ji stone fabric:CM60*COTTON/TJS60*220*120*57/58 organizes 4/1 satin weave.
A kind of processing technology of high-whiteness cotton/Tai Ji stone blended yarn weaved fabric, steps are as follows:
After singing, moving back and boil, carry out special drift, multiple drift, mercerising, wash brighten, brighten wash, tentering softness, preshrunk obtain cotton/
Tai Ji stone blended yarn weaved fabric;
Spy's drift:Sodium chlorite:40g/L acetic acid:5g/L speeds:90m/min, hopper pH value:4, steam box upper temp:95
DEG C, steam box temperature of lower:90℃
Multiple drift:H2O210g/L, NaOH 5g/L, chelating agent 10g/L, stabilizer 10g/L, bleeding agent 10g/L, steamer temperature
100 DEG C, heap cloth time 20min.
It washs and brightens process:The dicyan styrene derivative brightening agent EVB of a concentration of 5g/L is added in groove, pad cotton/
Tai Ji stone blended fabric, liquid carrying rate are controlled 75%, are then warming up to 180 DEG C, passing sequentially through 8 180 DEG C of high temperature ovens makes band
There is the fabric color development of brightening agent.
It brightens and washes process:The 1 of a concentration of 12g/L, 2 diphenyl ethylene derivatives brightening agent PC is added in groove, pad cotton/
Tai Ji stone blended fabric, liquid carrying rate are controlled 75%, 100 DEG C are then warming up to, in the guide roll type steaming box full of saturated vapor
Interior decatize 70 seconds, then pass through 50 DEG C of rinsing bowl successively and wash 80 seconds, in neutralization chamber and 30 seconds, pH value control is clear at 4.5,50 DEG C
Water is washed 15 seconds, 120 DEG C of drying cylinder drying, and drying material pH value control below is 7.5.
Tentering is soft:Silicone oil softening agent is added and carries out tentering softness.
145~0.45 can be reached using finished product whiteness after above-mentioned process, 4 grades of soaping fastness.
Comparative example 2
Comparative example 2 is following two points using fabric identical with embodiment and processing technology, difference:
Brighten that wash process different from embodiment 2, comparative example 2 is brightened using tradition washes technique:PC:10, temperature:70 DEG C of * 4 road
+ 95 DEG C of * 6+60 DEG C * 4 of road road, speed:90m/min;
Special drift+multiple bleaching process is not used, but uses common (multiple drift) bleaching whitening process, bleaching:H2O210g/L,
NaOH5g/L, chelating agent 10g/L, stabilizer 10g/L, bleeding agent 10g/L, 100 DEG C of steamer temperature, heap cloth time 20min.
Whiteness only has 132.5~0.25, and 3 grades of soaping fastness, embodiment 2 is obviously better than comparative example 2.
Claims (10)
1. a kind of high-whiteness cotton/Tai Ji stone blended yarn weaved fabric, it is characterised in that:By cotton ,/Tai Ji stone fabric is successively by singing → moves back
Boil → special drift → multiple drift → mercerising → wash brighten → brighten wash → tentering softness → preshrunk obtains cotton/Tai Ji stone blended yarn weaved fabric;
Spy's drift:Special bleaching liquor used is the mixture of sodium chlorite, acetic acid and water, and the pH value of special bleaching liquor is:3.6~4, speed:
85~90m/min, steam box upper temp:90~95 DEG C, steam box temperature of lower:85~90 DEG C;
Multiple drift:Multiple bleaching liquor used is:H2O2, NaOH, chelating agent, stabilizer, bleeding agent and water, 98~100 DEG C of steamer temperature,
15~20min of heap cloth time.
2. high-whiteness cotton according to claim 1/Tai Ji stone blended yarn weaved fabric, it is characterised in that:
Special bleaching liquor is:30~40g/L of sodium chlorite, 3~5g/L of acetic acid, surplus are water;
Bleaching liquor is again:H2O22~5g/L of 7~10g/L, NaOH, 5~10g/L of chelating agent, 5~10g/L of stabilizer, bleeding agent 5
~10g/L;It by concentration ratio is 1 that chelating agent, which is SQ~A and 254, in multiple drift:3 mixture, stabilizer 266, bleeding agent CH
~L.
3. high-whiteness cotton according to claim 1/Tai Ji stone blended yarn weaved fabric, it is characterised in that:It washs and brightens:Brightening agent uses
Dicyan styrene derivative brightening agent EVB, a concentration of 4~6g/L;It brightens and washes:Brightening agent is increased using 1,2 diphenyl ethylene derivatives
White agent PC, a concentration of 4~12g/L.
4. high-whiteness cotton according to claim 3/Tai Ji stone blended yarn weaved fabric, it is characterised in that:It washs and brightens process:It will brighten
Agent is added in groove, pads cotton/Tai Ji stone blended fabric, and liquid carrying rate is controlled 55~75%, is then warming up to 180 ± 3 DEG C, according to
Secondary 8 high temperature ovens by 180 ± 3 DEG C make the fabric color development with brightening agent.
5. high-whiteness cotton according to claim 3/Tai Ji stone blended yarn weaved fabric, it is characterised in that:It brightens and washes process:It will brighten
Agent is added in groove, pads cotton/Tai Ji stone blended fabric, and liquid carrying rate is controlled 55~75%, is then warming up to 98~100 DEG C,
The decatize 50~70 seconds in the guide roll type steaming box full of saturated vapor, then pass through 50 DEG C of rinsing bowls successively and wash 60~80 seconds,
In neutralization chamber and 20~30 seconds, pH value control is washed 8~15 seconds in 3.5~4.5,50 DEG C of clear water, and 90 DEG C~120 DEG C of drying cylinder dries
Dry, drying material pH value control below is 6~7.5.
6. high-whiteness cotton according to claim 5/Tai Ji stone blended yarn weaved fabric, it is characterised in that:It washs in brightening and brighten and washing
The groove volume is 30~50L.
7. high-whiteness cotton according to claim 1/Tai Ji stone blended yarn weaved fabric, it is characterised in that:Add in tentering softness step
Enter softening agent.
8. high-whiteness cotton according to claim 6/Tai Ji stone blended yarn weaved fabric, it is characterised in that:Softening agent is that silicone oil is soft
Soft dose.
9. high-whiteness cotton according to claim 8/Tai Ji stone blended yarn weaved fabric, it is characterised in that:Softening agent is TF~4911
Or one or both of SMI~62.
10. a kind of processing technology of any high-whiteness cotton/Tai Ji stone blended yarn weaved fabric of claim 1~9, feature exist
In:Include the following steps:
Cotton/Tai Ji stone fabric after singing, moving back and boil, carry out special drift, multiple drift, mercerising, wash brighten, brighten wash, tentering is soft, in advance
Contracting obtains cotton/Tai Ji stone blended yarn weaved fabric;
Spy's drift:Special bleaching liquor used is the mixture of sodium chlorite, acetic acid and water, and the pH value of special bleaching liquor is:3.6~4, speed:
85~90m/min, steam box upper temp:90~95 DEG C, steam box temperature of lower:85~90 DEG C;
Multiple drift:Multiple bleaching liquor used is:H2O22~5g/L of 7~10g/L, NaOH, 5~10g/L of chelating agent, stabilizer 5~
10g/L, 5~10g/L of bleeding agent, 98~100 DEG C of steamer temperature, 15~20min of heap cloth time;
It washs and brightens process:Brightening agent is added in groove, pads cotton/Tai Ji stone blended fabric, liquid carrying rate control 55~75%,
Then 180 ± 3 DEG C are warming up to, passing sequentially through 180 ± 3 DEG C of 8 high temperature ovens makes the fabric color development with brightening agent;
It brightens and washes process:Brightening agent is added in groove, pads cotton/Tai Ji stone blended fabric, liquid carrying rate control 55~75%,
Then 98~100 DEG C are warming up to, the decatize 50~70 seconds in the guide roll type steaming box full of saturated vapor, then pass through 50 DEG C successively
Rinsing bowl is washed 60~80 seconds, and in neutralization chamber and 20~30 seconds, pH value control is washed 8~15 seconds in 3.5~4.5,50 DEG C of clear water,
90 DEG C~120 DEG C of drying cylinder drying, drying material pH value control below is 6~7.5;
Tentering is soft:Silicone oil softening agent is added and carries out tentering softness.