CN108585585A - A kind of mortar surfactant preparation method for building - Google Patents
A kind of mortar surfactant preparation method for building Download PDFInfo
- Publication number
- CN108585585A CN108585585A CN201810470379.0A CN201810470379A CN108585585A CN 108585585 A CN108585585 A CN 108585585A CN 201810470379 A CN201810470379 A CN 201810470379A CN 108585585 A CN108585585 A CN 108585585A
- Authority
- CN
- China
- Prior art keywords
- parts
- mortar
- added
- building
- surfactant preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of mortar surfactant preparation methods for building, include following processing step：1）, first 12 14 parts of soda ash and 80 90 parts of spent pulping liquor is put into addition heating vessel in heating to 85 95 DEG C, 89 parts of calcium lignosulfonate is then added, is warming up to 100 110 DEG C, heats 30 40min；2）, to step 1）35 parts of oil emulsion is added in obtained material, continues after boiling 35 45min, into closed mixer, material, with 800 1000r/min rotating speeds, stirs 20 30min in closed mixer；3）, wait for step 2）After obtained material is cooled to room temperature, 0.8 1.2 parts of sodium alkyl benzene sulfonate, 1.5 2.5 parts of citric acid is added, stirs evenly as colloidal liquid product.
Description
Technical field
The present invention relates to grout additive fields, particularly belong to a kind of mortar surfactant preparation method for building.
Background technology
Dry powder and mortar is wider in building trade purposes, is divided into masonry mortar, plastering mortar, ground mortar etc..Currently, dry powder
Mortar generally uses natural sand as main component, is formulated with cement and additive etc., cost is higher, and water-retaining property and resistance to compression
As uniform intensity.Grout additive is commonly called as waterproof sand crystal king, also makes rock smart, cement surfactant is that one kind acting on water
In mud, to improve the substance of cement mortar performance, belong to mixed mud additive scope, main function is the hydrophobic for improving mortar
Property, cement granules can be played diffusion by being added in mortar, reduce the trend of cement granules aggregation, increase the mobility of mortar.
Invention content
The object of the present invention is to provide a kind of mortar surfactant preparation method for building, which is used for sand
The usage amount of lime can be reduced in slurry, while excreting water phenomenon reduces, and improves the bonding force and saturation degree of mortar.
The technical solution adopted in the present invention is as follows：
A kind of mortar surfactant preparation method for building, includes following processing step：
1）, 12-14 parts of soda ash and 80-90 part of spent pulping liquor are put into addition first heat vessel in heating to 85-95 DEG C,
Then 8-9 parts of calcium lignosulfonate is added, is warming up to 100-110 DEG C, heats 30-40min；
2）, to step 1）3-5 parts of oil emulsion is added in obtained material, continues after boiling 35-45min, is stirred into closed
It mixes in machine, material, with 800-1000r/min rotating speeds, stirs 20-30min in closed mixer；
3）, wait for step 2）After obtained material is cooled to room temperature, be added 0.8-1.2 parts sodium alkyl benzene sulfonate, 1.5-2.5 parts
Citric acid, 1.2-1.4 parts of molybdenum disulfide, stirs evenly as colloidal liquid product；
4）By step 3）Obtained colloidal liquid product is put into grinder, and 1-1.5h is to get the surfactant finished product for grinding.
The heating container is magnetic agitation electric jacket.
The oil emulsion is by example 2 in mass ratio：1 base oil, emulsifier composition.
The oil emulsion of the present invention can generate emulsification and the effect of lubrication, and there is sodium alkyl benzene sulfonate foaming effect and dispersion to make
With introducing many small stable bubbles in mortar, improve mortar strength；The surfactant is used to that in mortar stone can be reduced
The usage amount of ash, while excreting water phenomenon reduces, and improves the bonding force and saturation degree of mortar.
Specific implementation mode
Embodiment one：
A kind of mortar surfactant preparation method for building, includes following processing step：
1）, first by 12 parts of soda ash and 80 parts of spent pulping liquor be put into addition heating vessel in heating to 85-95 DEG C, then plus
The calcium lignosulfonate for entering 8 parts is warming up to 100-110 DEG C, heats 30-40min, and heating container is magnetic agitation electric jacket；
2）, to step 1）3 parts of oil emulsion is added in obtained material, continues after boiling 35-45min, into Hermetical stirring
In machine, material, with 800-1000r/min rotating speeds, stirs 20-30min, oil emulsion is by example in mass ratio in closed mixer
2：1 base oil, emulsifier composition；
3）, wait for step 2）After obtained material is cooled to room temperature, be added 0.8 part of sodium alkyl benzene sulfonate, 1.5 parts of citric acid,
1.2 parts of molybdenum disulfide is stirred evenly as colloidal liquid product；
4）By step 3）Obtained colloidal liquid product is put into grinder, and 1-1.5h is to get the surfactant finished product for grinding.
Embodiment two：
A kind of mortar surfactant preparation method for building, includes following processing step：
1）, first by 14 parts of soda ash and 90 parts of spent pulping liquor be put into addition heating vessel in heating to 95 DEG C, be then added 9
The calcium lignosulfonate of part is warming up to 100-110 DEG C, heats 30-40min, and heating container is magnetic agitation electric jacket；
2）, to step 1）5 parts of oil emulsion is added in obtained material, continues after boiling 35-45min, into Hermetical stirring
In machine, material, with 800-1000r/min rotating speeds, stirs 20-30min, oil emulsion is by example in mass ratio in closed mixer
2：1 base oil, emulsifier composition；
3）, wait for step 2）After obtained material is cooled to room temperature, be added 1.2 parts of sodium alkyl benzene sulfonate, 2.5 parts of citric acid,
1.4 parts of molybdenum disulfide is stirred evenly as colloidal liquid product；
4）By step 3）Obtained colloidal liquid product is put into grinder, and 1-1.5h is to get the surfactant finished product for grinding.
Claims (3)
1. a kind of mortar surfactant preparation method for building, which is characterized in that include following processing step：
1）, 12-14 parts of soda ash and 80-90 part of spent pulping liquor are put into addition first heat vessel in heating to 85-95 DEG C,
Then 8-9 parts of calcium lignosulfonate is added, is warming up to 100-110 DEG C, heats 30-40min；
2）, to step 1）3-5 parts of oil emulsion is added in obtained material, continues after boiling 35-45min, is stirred into closed
It mixes in machine, material, with 800-1000r/min rotating speeds, stirs 20-30min in closed mixer；
3）, wait for step 2）After obtained material is cooled to room temperature, be added 0.8-1.2 parts sodium alkyl benzene sulfonate, 1.5-2.5 parts
Citric acid, 1.2-1.4 parts of molybdenum disulfide, stirs evenly as colloidal liquid product；
4）By step 3）Obtained colloidal liquid product is put into grinder, and 1-1.5h is to get the surfactant finished product for grinding.
2. mortar surfactant preparation method for building according to claim 1, which is characterized in that the heating container is
Magnetic agitation electric jacket.
3. mortar surfactant preparation method for building according to claim 1, which is characterized in that the oil emulsion is by pressing
Mass ratio 2：1 base oil, emulsifier composition.